Development of a method for the preparation of zirconium-89 radiolabelled chitosan nanoparticles as an application for leukocyte
trafficking with positron emission tomography.
M. Fairclough1*, B. Ellis2, H. Boutin1, A.K.P. Jones3 A. McMahon1, S. Alzabin4, A. Gennari5
and C. Prenant1
1. Wolfson Molecular Imaging Centre, Manchester, UK. 2. Nuclear Medicine Centre, Central Manchester University Hospital, NHS Foundation Trust, UK. 3. Clinical Sciences Building, Salford Royal NHS Foundation Trust, Manchester, UK. 4. Epistem Ltd, Manchester, UK. 5. Division of Pharmacy & Optometry, School of Health Sciences, University of Manchester, Manchester, UK.
*Correspondence to: M. Fairclough, Wolfson Molecular Imaging Centre, The University of Manchester, 27 Palatine Road, Manchester M20 3LJ, UK. Tel.: +44(0)1612750034E-mail: [email protected]
AbstractPositron Emission Tomography is an attractive imaging modality for monitoring the
migration of cells to pathological tissue. We evaluated a new method for radiolabelling
leukocytes with zirconium-89 (89Zr) using chitosan nanoparticles (CN, Z-average size 343 ±
210 nm and zeta potential +46 ± 4 mV) as the carrier. We propose that cell uptake of 89Zr-
loaded CN occurred in a two-step process; cell membrane interaction with 89Zr-loaded CN
was followed by a slower cell internalisation step.
KeywordsPET; Zr-89; chitosan; nanoparticles; leukocyte trafficking; inflammation imaging.
IntroductionNanoparticles (NPs) have been extensively used for in-vivo imaging of macrophages
using modalities such as Magnetic Resonance Imaging (MRI), Positron Emission
Tomography (PET), Single Photon Emission Computed Tomography (SPECT) or
fluorescence (Majmudar et al., 2013, Keliher et al., 2011, Jaffer et al., 2006, Devaraj et al.,
2009). Application of macrophage-targeting nanoparticles as diagnostic tools for cancer,
atherosclerosis or myocardial infarction has been actively investigated (Weissleder et al.,
2014).
1
Among the nanomaterial-based imaging agents described, chitosan is attractive for
clinical applications due to its bio-compatibility, bio-degradability and apparent low toxicity
(Kean and Thanou, 2010). Chitosan has reached applications in a number of fields including,
but not limited to, drug and gene delivery systems (Nam et al., 2009, Prabaharan, 2015,
Sarvaiya and Agrawal, 2015), and wound dressing and as scaffolds for tissue engineering
(Jayakumar et al., 2010). Chitosan is a linear polysaccharide consisting of randomly
distributed β-1-4-linked D-glucosamine and N-acetyl-D-glucosamine units and has metal
chelating properties (Varma et al., 2004, Clark et al., 2016, Tshuva et al., 2001). It is
proposed that the amine and the secondary hydroxyl groups of the glucosamine moieties
contribute to the metal complexation as represented in Figure 1. The polymer is commercially
available and can be obtained at various molecular weights and with different degrees of
deacetylation (DD); furthermore nanoparticles of chitosan can be conveniently produced.
Figure 1: Postulated representation of the binding of zirconium-89 to chitosan
Different techniques are described for chitosan nanoparticles (CN) production
(Chandra Hembram et al., 2016, Nagpal et al., 2010). Ionotropic gelation is attractive owing
to the mild aqueous conditions used in comparison to other mechanisms of nanoparticle
formation such as micro-emulsification or complex coacervation (Nagpal et al., 2010). The
method of complex coacervation requires a negatively charged polyelectrolyte to be mixed
with positively charged chitosan and so is not applicable to CN labelling with positively
2
charged 89Zr. Although micro-emulsion has the advantage of producing nanoparticles with a
narrow size distribution (< 100 nm), this method has major drawbacks in the context of cell
radiolabelling. The use of organic solvent as well as a time-consuming preparation process
and complex washing steps means that micro-emulsification is simply not appropriate for
imaging of leukocyte trafficking using PET. By using ionotropic gelation, nanoparticles are
formed by crosslinking the linear chitosan polymer chains using the nontoxic polyanion
pentasodium tripolyphosphate (TPP). The strong electrostatic interactions of TPP with the
polycationic chitosan results in a fast gel formation (Calvo et al., 1997, Gan et al., 2005,
Nagpal et al., 2010).
In-vivo imaging of leukocytes with PET can be used in immunological studies to track
the selective recruitment of specific immune cells during pathogenesis, to detect
infectious/inflammatory foci and also to devise rational therapeutic strategies based on
longitudinal studies. In a previous publication (Fairclough et al., 2016) we reported on the
use of CN for leucocyte labelling with 89Zr for inflammation imaging with PET. In the
present study we aimed at improving CN preparation for optimum 89Zr-loading and cell
uptake in order to optimize the leukocyte labelling method. Size and surface charge of
nanoparticles have been examined as determinant properties for the cell uptake efficiency.
The affinity of CN for 89Zr and the subsequent uptake and retention of 89Zr-loaded CN into
mixed human leukocyte cells have been investigated.
Experimental
Materials and Equipment89Zr-oxalate was purchased from Perkin Elmer (US)/BV cyclotron (Netherlands) and
chitosan (15 kDa, > 85% DD) was purchased from Tebu-bio (France). Acetic acid,
hydrochloric acid, sodium hydroxide, sodium tripolyphosphate (TPP) and fluorescein
isothiocyanate were all purchased from Sigma Aldrich (UK) and were used without any
further purification. For isolation of mixed leukocyte cells, Acid Citrate Dextrose (formula A)
was purchased from Huddersfield Pharmacy Manufacturing Unit (UK) and HES 6% solution
(hydroxyethyl starch) was purchased from Grifols (UK). Conjugated antibodies to human
CD11b, CD14, CD15, CD16 and CD68 were purchased from Thermo Fisher Scientific UK
(formerly eBioscience). FACS buffer was prepared using phosphate buffered saline,
3
penicillin (1 %), streptomycin (Sigma Aldrich, UK), EDTA (Invitrogen, UK) and 5% Foetal
bovine serum (Gibco, UK).
CN were purified using Pur-A-Lyzer Maxi dialysis tubes (12 kDa molecular weight
cut off) from Sigma Aldrich (UK). A PK121R multispeed refrigerated centrifuge from
Thermo Scientific (UK) was used along with a Micro Centaur centrifuge (MSE, UK) for
mixed leukocyte isolation. A Thermo Shaker PHMT (from Grant Instruments UK) was used
to incubate solutions of leukocytes and CN with zirconium-89. Separation of mixed
leukocytes from whole blood was performed in a SafeFlow 1.2 safety cabinet from Bioair
Instruments (Italy). Measurement of radioactive samples was performed using an Isomed
2000 dose calibrator from MED (Germany). CN hydrodynamic diameter (Z-average size),
polydispersity (PDI) and zeta potential (ζ-potential) were measured at a temperature of 25 °C
using a Zetasizer Nano ZS instrument (Model ZEN3600, Malvern Instruments Ltd., UK)
equipped with a solid state HeNe laser (λ = 633 nm) and at a scattering angle of 173°. Size
measurement data were analysed by using the General purpose algorithm. The electrophoretic
mobility of the samples was converted in zeta potential by using the Smolikowski equation.
Fluorescence-activated cell sorting (FACS) analysis of labelled cells was performed
on a MACSQuant analyser (Miltenyi Biotec, Germany).
Preparation of CN and radiolabelling with 89Zr
Chitosan (15 kDa, > 85% degree of deacetylation, 14 mg) was solubilised in HCl (4.6
mM, 20 mL) to form a 0.7 mg/ml solution, and was left to stir for 24 hours. The pH of the
chitosan solution was then adjusted to 5 with the drop-wise addition of sodium hydroxide
(0.1 M). Meanwhile, a 1 mg/ml solution of TPP was prepared (10 mg TPP in 10 mL of
deionised water, pH adjusted to 5) and both the TPP and the chitosan solutions were filtered
through a 0.22 µm filter membrane. Next nanoparticles were produced with various
chitosan:TPP ratios (w/w) by the addition of 72 µL, 80 µL, 90 µL and 120 µL of TPP
solution to 928 µL, 917 µL, 903 µL and 860 µL of chitosan solution to obtain chitosan:TPP
ratios (w/w) of 9:1, 8:1, 7:1 and 5:1 respectively. The mixtures were allowed to stir for 30
minutes before being transferred to Pur-A-Lyzer Maxi dialysis tubes (12 kDa molecular
weight cut off) and were dialysed against de-ionised water for 24 hours (water was refreshed
every 3 hours) to remove the excess of TPP cross-linking agent. The CN solution was then
recovered and stored at 2-4 ºC (this temperature is reported to have no effect on size and
physical stability of the particles (Thakur et al., 1977). CN were characterised for size and ζ -
4
potential by DLS. From previous work we found that approximately 26% of chitosan
polymer forms nanoparticles by ionotropic gelation (Fairclough et al., 2016).
CN (300 µL) were incubated with 89Zr (approximately 17 MBq as 89Zr-oxalate) in a
Thermo-shaker at room temperature for 45 minutes. Following incubation, the 89Zr-loaded
CN were separated from free 89Zr by centrifugation (11600 g for 10 min) and washed twice
with deionised water. The supernatant (containing free 89Zr) and the pellet of 89Zr-loaded CN
were measured for radioactivity; radiolabelling efficiency is expressed as percentage of the
ratio between radioactivity associated with the CN and total radioactivity. The pellet of 89Zr-
loaded CN was then re-suspended in saline (200 µL) for further experiments.
Isolation of mixed human leukocytes and measurement of leukocyte
radiolabelling efficiency and retention of [89Zr]-loaded CN
Each experiment was carried out using mixed leukocytes freshly isolated from whole
blood following erythrocyte sedimentation according to a reported procedure (Ellis, 2011,
Fairclough et al., 2016). In order to evaluate leukocyte radiolabelling efficiency, the pellet of
mixed leukocytes was divided into 8 samples at a density of 3-5 x 107 cells in 200μl of saline
per sample. Next 200 µL of the 89Zr-loaded CN re-suspended in saline was added to each
sample with gentle mixing. Next the samples were incubated in a thermo-shaker at 37 ˚C, at
1400 rpm for 30 minutes (n=2), 1 hour (n=2), 2 hours (n=2), 3 hours (n=1) and 24 hours
(n=1). Following incubation, leukocyte radiolabelling was terminated at each time interval by
the addition of cell free plasma (CFP, 1 mL). The radiolabelled leukocytes were separated
from the mixture by centrifugation (150 g for 5 minutes) to leave a pellet of 89Zr-labelled
leukocytes. The radioactivity in the supernatant and the pellet was measured and
radiolabelling efficiency was expressed as a percentage of the ratio between radioactivity
associated with the leukocytes and total radioactivity. To ensure co-precipitation of 89Zr-
loaded CN with leukocytes was not occurring; suspensions of 89Zr-loaded CN were spun by
centrifugation at 150 g for 5 minutes. In these conditions no 89Zr-loaded CN was found to
precipitate as a pellet.
To assess the retention of 89Zr in leukocytes, cells (3-5 x 107 in 200μl saline) were
radiolabelled with 89Zr-loaded CN as described above (2 hours incubation) followed by
centrifugation (150 g for 5 minutes). The recovered pellet of 89Zr-labelled leukocytes was
then re-suspended in CFP and allowed to incubate for 24 hours at 37˚ C. At intervals of 1, 2,
3, and 24 hours (n=2 for all time-points), the mixture was centrifuged (150 g for 5 minutes),
5
the supernatant was removed and the pellet containing 89Zr-labelled leukocytes was re-
suspended in fresh CFP. Removed CFP fractions and leukocyte pellets were measured for
radioactivity and the radioactivity efflux rate determined over 24 hours. The results for both
uptake and efflux of 89Zr in leukocytes cell can be seen in Figure 4 and Figure 5.
Fluorescent labelling of CN, labelling of mixed leukocyte cells with FITC-CN and flow cytometry
Chitosan was labelled with fluorescein isothiocyanate (FITC) according to a
previously reported method (Huang et al., 2002) with some adaptions. Briefly, chitosan (150
mg) was added to a 1% acetic acid (60 mL) and left to stir overnight. Next FITC (7 mg) was
dissolved in anhydrous methanol (60 mL) and was combined with the chitosan solution. The
reaction was allowed to proceed at room temperature for 4 hours under stirring in darkness.
Upon completion, NaOH (1 M) was added to the reaction mixture to raise the pH and
precipitate FITC labelled chitosan from the solution. Precipitated FITC-chitosan was
collected by centrifugation at 3,025 g for 10 minutes at 4 ˚C. The solid was washed with
70:30 ethanol:water until there were no traces of free FITC (by HPLC analysis). After FITC-
chitosan had been washed sufficiently, the precipitate was allowed to dry overnight. FITC
labelled chitosan nanoparticles (FITC-CN) were prepared from FITC-chitosan in the same
way as the non-fluorescently tagged chitosan nanoparticles. Mixed leukocytes suspended in
saline (200 µL) were incubated at 37 ˚C with FITC-CN (300 µL) for 2 hours after which
radiolabelling was terminated by the addition of CFP (1 mL). The FITC-CN labelled
leukocytes were separated from the mixture by centrifugation (150 g for 5 minutes) to leave a
pellet of FITC-labelled leukocytes which was washed again in CFP and then again with
FACS buffer (1XPBS with 2mM EDTA, 5%Foetal bovine serum and 1% penicillin and
streptomycin). Next FITC-CN-labelled cells were incubated for 20 minutes with conjugated
antibodies to human CD11b, CD14, CD15, CD16 and CD68 in order to assess the updatake
of FITC-CN on monocytes. Following this, the cells were washed again with FACS buffer
and FITC-CN uptake was measured using MACSQuant analyser.
Results
CN properties
Table 1 shows how CN physical properties vary when different chitosan:TPP weigh
ratios are used to construct CN. Nanoparticles obtained from 8:1 chitosan:TPP weight ratio
6
were used for leukocyte radiolabelling, these conditions were selected as they yielded the
smallest CN hydrodynamic diameter (343 ± 210 nm), with a polydispersity index (pdi) of
0.38 (Figure 2). These pdi values and size distribution plots are consistent with those
reported in the literature (Ing et al., 2012, Zhang et al., 2010). In addition, the positive
surface charge of CN produced from 8:1 chitosan:TPP weight ratio reached +46 ± 4
mV(Figure 3).
CS:TPP ratio
(w/w)
CN Hydrodynamic
diameter (nm)
pdi CN ζ-potential
9:1 545 ± 360 0.44 +48 ± 3
8:1 343 ± 210 0.38 +46 ± 4
7:1 412 ± 263 0.40 +43 ± 4
5:1 451 ± 256 0.32 +40 ± 4Table 1: Effect of chitosan:TPP weight ratio on the hydrodynamic diameter, polydispersity index (pdi)
and ζ-potential of CN.
1 10 100 1000 100000
2
4
6
8
10
12
Size (d.nm)
Inte
nsity
(%)
Figure 2: CN size distribution by intensity of scattered light for CN produced from a 8 :1 chitosan:TPP
weight ratio. The average size of CN produced from this chitosan:TPP ratio was 343 nm with a pdi of
0.38.
7
-148
-131
-115 -99 -82
.7-66
.5-50
.2-33
.9-17
.7-1.
4314
.831
.147
.363
.679
.996
.1 112
129
0
50000
100000
150000
200000
250000
300000
350000
Zeta Potential (mV)
Tota
l Cou
nts
Figure 3: CN zeta potential distribution of CN produced from a 8:1 chitosan:TPP weight ratio.
Affinity of 89Zr for CN
The fraction of 89Zr associated with the CN after 45 minutes incubation at room
temperature in the Thermo-shaker at 1400 rpm attained 31 ± 6 % (n = 15) following washing.
These conditions were found to be optimal in our previous work in which 74 % incorporation
of 89Zr into CN was reported (Fairclough et al., 2016).
Uptake and Retention of 89Zr-loaded CN in mixed leukocytes
Figure 4 and Figure 5 show, respectively, 89Zr-loaded CN uptake into and the egress
from leukocyte cells (monocytes and neutrophils). The plots shown in Figure 4 and Figure 5
are consistent with a two-step uptake mechanism. We suggest a mechanism in which 89Zr-
loaded CN is initially attracted to the cell surface, resulting in adhesion-dependent fast
accumulation to the cell membrane. It is postulated that this is then followed by a slower
internalisation step.
8
0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 250%
10%
20%
30%
40%
50%
60%
70%
80%
90%
100%
14.7%
21.9%
33.8%
44.9%
73.3%
Time (hours)
Upt
ake
of 8
9Zr
into
the
cell
Figure 4: Uptake of 89Zr-loaded CN in mixed human leukocyte cells.
0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25
0%
10%
20%
30%
40%
50%
60%
70%
80%
90%
100%
32.2%
50.2%
64.4%
78.8%
Time (hours)
% E
gres
s of 8
9Zr
from
leuk
ocyt
e ce
lls
Figure 5: Egress of 89Zr-loaded CN in mixed human leukocyte cells. Rate of efflux was measured in
leukocytes which were radiolabelled with 89Zr-loaded CN following 2 hour incubation.
9
FACS analysis of FITC-CN labelled mixed leukocytesFACS analysis was used to determine the uptake of FITC-CN by the neutrophil
population of peripheral blood mononuclear cells. PBMCs were isolated from a healthy
donor as described above and cells were stained with a cocktail of antibodies prior to analysis
using the MACSQuant FACS analyser. The neutrophil population was visualised by gating
first on cells with a high granularity and cell size (Figure 6A) followed by exclusion of
monocytes and macrophages by conjugated antibodies to CD68, CD16 and CD11b. Figure 6
shows the density dot plots of VioBlue-CD15+ cells (neutrophil marker) against CN (Figure
6B) fluorescent intensity of FITC-CN.
Figure 6: CN uptake by neutrophils. FACS dot plots showing A) Gating strategy on the neutrophil population by granularity and size inclusion and B) Cell expression analysis of a neutrophil surface receptor CD15 in cells which have not been incubated with CN and C) Expression of CN in CD15 expressing neutrophils which have been incubated with CN.
10
Discussion
CN properties
Size and surface charge of nanoparticles are critical parameters determining cell
uptake mechanism and efficiency. The surface charge of NPs is crucial to the initial
electrostatic attraction of the NPs to the negatively charged cell membrane and the size of the
NP is important to determining the mechanism of cell uptake. Both of these CN parameters
are very adaptive to changes in chitosan and polyanion (TPP) ratio (Ing et al., 2012).
Initial addition of the TPP poly-anion to solvated, positively charged chitosan chains
produced intra and intermolecular cross-linking which initiated the formation of
nanoparticles. Increasing the amount of TPP further increased the degree of reticulation in the
nanoparticles, expelling water molecules and producing more compact, smaller size CN.
Further TPP addition resulted in CN size increase while the ζ-potential continued to decrease.
This could be attributed to the neutralisation of the nanoparticle positive surface charge by
excess TPP causing particle build-up by accretion of free chitosan chains. Alternatively, a
large excess of TPP might promote CN aggregation due to TPP acting as an inter-particle
cross linker.
The high ζ–potential of CN produced from an 8:1 chitosan:TPP ratio (Figure 3)
confirms the absence of excess TPP at the CN surface and ensures CN stability by preventing
inter-particle attraction and formation of aggregates. Additionally the high ζ-potential favours
CN interaction with the leukocyte cell membrane.
Affinity of 89Zr for CN
The incorporation of 89Zr by CN was previously measured by us as 74 % (Fairclough
et al., 2016) but here the efficiency of 89Zr loading by CN was lower. The difference can be
attributed to the CN purification technique used. The centrifugation technique used in our
previous report has the drawback of leaving an excess of TPP on CN surface. Since TPP has
metal chelation properties, it is important to eliminate it from the CN formulation. In this
work, the use of dialysis instead of centrifugation ensures the total removal of TPP from CN
formulations. Further, optimisation of the radiolabelling of CN with 89Zr may be possible by
altering the pH of the 89Zr-oxalate solution.
11
Uptake and Retention of 89Zr-loaded CN in mixed leukocytes
Cell uptake of charged NPs is commonly described as a two-step process, the
internalization proceeds interaction of the NP with the cell membrane (Lesniak et al., 2013).
The initial interaction with the membrane is determined by the physico-chemical features of
the NPs and particularly their surface charge. It has been shown that higher positive charge
on NPs enhance cellular uptake which is attributed to the electrostatic interaction with the
negatively charged cell membrane (Foged et al., 2005, Gustafson et al., 2015, Forest et al.,
2015, Roser et al., 1998, He et al., 2010, Tabata and Ikada, 1988).
Membrane-wrapping of the NPs by the cell could be the limiting step in the kinetics
of the uptake (He et al., 2010). The broad size dispersion of the CN (343 ± 210 nm) might
result in a variable internalization time and involve different, size-dependant, endocytosis
processes such as phagocytosis, macropinocytosis and clathrin-dependent and -independent
mechanisms, (Reno et al., 2013, Kuhn et al., 2014, Zhao et al., 2011, Nam et al., 2009).
Figure 5 demonstrates that after two hours incubation of the 89Zr-loaded CN with
leukocytes, the 89Zr-loaded CN may only be partially internalized, and the rest remain
membrane bond. This could account for the relatively fast initial loss of 89Zr from the cell
(Figure 5) which we hypothesise may be due to the activation of the leukocyte population
following their exposure to 89Zr-loaded CN. Upon cellular activation, endocytosis is triggered
which causes a change in pH and leads to a change in the charge on the cell membrane,
therefore, it is possible that during these changes, the affinity towards 89Zr-loaded CN is lost.
The slow internalisation of 89Zr-loaded CN by leukocytes and the residual 89Zr-loaded CN
bound to the cell membrane appears to make this technique for leukocyte tracking with PET
less favourable to routine clinical applications, although it would be adequate for research
purposes. The stability of the internalised radioactivity in this technique of leukocyte
radiolabelling is attractive for preclinical studies of inflammation. Furthermore the technique
could be refined on two levels; first removal of 89Zr-loaded CN bound to the cell membrane
could be made more effective by using a more dynamic CFP wash. Secondly a more optimal
CN size could be produced for a faster cell uptake step. In a study of phagocytosis of latex
particles by leukocytes, Kawaguchi et al showed that latex particles with a diameter ranging
between 0.6 and 1.0 µM are more easily phagocytosed than particles outside of this range
(Kawaguchi et al., 1986). CN with sizes ranging between 0.6 and 1.0 µM can be produced by
12
using a higher chitosan:TPP ratio and it should also be possible to select CN of a specific
diameter by filtration.
FACS analysis of FITC-CN labelled mixed leukocytesFACS analysis of CD15+ neutrophils revealed a strong signal in the FITC-channel,
corresponding to FITC labelled CN (Figure 6C). This confirms an uptake of our CN by the
neutrophil population although the method of uptake i.e. cells surface adhesion; phagocytosis
or a receptor based mechanism has not been addressed in this study. The uptake of FITC-CN
by neutrophils is an encouraging result as these cells are central to any inflammatory response
in the body. Neutrophils are often the first cells to respond to inflammatory stimuli and
migrate to sites of inflammation where they can phagocytose foreign/self-antigens (Botelho
et al., 2002). Ultimately, our aim is to develop a new imaging tool to monitor the migration of
white blood cells using PET. Whilst this study has assessed CN uptake by neutrophils as the
carrier cell type, other phagocytes may also be used. Neutrophils are useful to image early
states of inflammation, but they also do possessed the shortest life span of all leucocytes.
Therefore, optimising uptake with other cell types will be useful for imaging later stages of
inflammation. The timing and duration of uptake will differ on a cell to cell basis and should
be considered in the design of future studies
Conclusion This work described the preparation of CN as a carrier of 89Zr into human leukocytes.
The production of CN by process of ionic gelation has benefits of using low concentration of
both chitosan and TPP which will therefore lower any possible cytotoxicity effects, in
addition, the process negates the use of organic solvents. CN with an average size of 343 ±
210 nm and surface charge of +46 ± 4 mV were obtained from 8:1 chitosan:TPP weight ratio
yielding the lowest pdi (0.38). CN produced by this method were successfully loaded with 89Zr with 31 ± 6 % (n = 15) of 89Zr being loaded. With CN produced by this method, a two-
step mechanism of 89Zr-loaded CN uptake by leukocytes was proposed. A cell membrane
interaction with 89Zr-loaded CN was followed by a slower internalisation step.
We have shown that these 89Zr-loaded CN can be used to radiolabel mixed human
leukocytes and the relative stability of 89Zr in leukocyte cells from 3 hours to 24 hours is
encouraging for pre-clinical PET imaging of leukocyte cells. The technique could also be
amendable for clinical application by optimising the CN size and using an appropriate
13
chitosan:TPP ratio. The cell uptake mechanism of CN detailed here may be useful to
understand the mechanism of cationic chitosan-mediated drug delivery or gene transport
across cell membranes for cell transfection. Additionally, the versatility of this method
means that it could be transferable to radiolabelling of other cell types such as macrophages
or stem cells for in vivo tracking with PET.
Acknowledgements Funding: This work was funded by the NIHR Manchester Musculoskeletal Biomedical
Research Unit (Grant number: R114999). MF PhD studentship was funded by the Wolfson
Molecular Imaging Centre, University of Manchester.
Competing interests: The authors declare that they have no competing interests.
ReferencesBOTELHO, R. J., TAPPER, H., FURUYA, W., MOJDAMI, D. & GRINSTEIN, S. 2002.
FcγR-Mediated Phagocytosis Stimulates Localized Pinocytosis in Human Neutrophils. The Journal of Immunology, 169, 4423-4429.
CALVO, P., REMUÑÁN-LÓPEZ, C., VILA-JATO, J. L. & ALONSO, M. J. 1997. Novel hydrophilic chitosan-polyethylene oxide nanoparticles as protein carriers. Journal of Applied Polymer Science, 63, 125-132.
CHANDRA HEMBRAM, K., PRABHA, S., CHANDRA, R., AHMED, B. & NIMESH, S. 2016. Advances in preparation and characterization of chitosan nanoparticles for therapeutics. Artificial Cells, Nanomedicine, and Biotechnology, 44, 305-314.
CLARK, W. D., AKURATHI, G., VALLE, H. U. & HOLLIS, T. K. 2016. Crystal structure of tris(dimethylamido-κN)bis(dimethylamine-κN)zirconium(IV) iodide. Acta Crystallographica Section E: Crystallographic Communications, 72, 73-75.
DEVARAJ, N. K., KELIHER, E. J., THURBER, G. M., NAHRENDORF, M. & WEISSLEDER, R. 2009. 18F Labeled Nanoparticles for in Vivo PET-CT Imaging. Bioconjugate Chemistry, 20, 397-401.
ELLIS, B. 2011. Radiolabelling of Blood Cells: theory and practice. In: THEOBOLD, T. (ed.) Sampson's Book of Radiopharmacy.
FAIRCLOUGH, M., PRENANT, C., ELLIS, B., BOUTIN, H., MCMAHON, A., BROWN, G., LOCATELLI, P. & JONES, A. K. P. 2016. A new technique for the radiolabelling of mixed leukocytes with zirconium-89 for inflammation imaging with positron emission tomography. Journal of Labelled Compounds and Radiopharmaceuticals, 59, 270-276.
FOGED, C., BRODIN, B., FROKJAER, S. & SUNDBLAD, A. 2005. Particle size and surface charge affect particle uptake by human dendritic cells in an in vitro model. International Journal of Pharmaceutics, 298, 315-322.
FOREST, V., COTTIER, M. & POURCHEZ, J. 2015. Electrostatic interactions favor the binding of positive nanoparticles on cells: A reductive theory. Nano Today, 10, 677-680.
14
GAN, Q., WANG, T., COCHRANE, C. & MCCARRON, P. 2005. Modulation of surface charge, particle size and morphological properties of chitosan–TPP nanoparticles intended for gene delivery. Colloids and Surfaces B: Biointerfaces, 44, 65-73.
GUSTAFSON, H. H., HOLT-CASPER, D., GRAINGER, D. W. & GHANDEHARI, H. 2015. Nanoparticle uptake: The phagocyte problem. Nano Today, 10, 487-510.
HE, C., HU, Y., YIN, L., TANG, C. & YIN, C. 2010. Effects of particle size and surface charge on cellular uptake and biodistribution of polymeric nanoparticles. Biomaterials, 31, 3657-3666.
HUANG, M., MA, Z., KHOR, E. & LIM, L.-Y. 2002. Uptake of FITC-Chitosan Nanoparticles by A549 Cells. Pharmaceutical Research, 19, 1488-1494.
ING, L. Y., ZIN, N. M., SARWAR, A. & KATAS, H. 2012. Antifungal Activity of Chitosan Nanoparticles and Correlation with Their Physical Properties. International Journal of Biomaterials, 2012, 9.
JAFFER, F. A., NAHRENDORF, M., SOSNOVIK, D., KELLY, K. A., AIKAWA, E. & WEISSLEDER, R. 2006. Cellular Imaging of Inflammation in Atherosclerosis Using Magnetofluorescent Nanomaterials. Molecular Imaging, 5.
JAYAKUMAR, R., MENON, D., MANZOOR, K., NAIR, S. V. & TAMURA, H. 2010. Biomedical applications of chitin and chitosan based nanomaterials—A short review. Carbohydrate Polymers, 82, 227-232.
KAWAGUCHI, H., KOIWAI, N., OHTSUKA, Y., MIYAMOTO, M. & SASAKAWA, S. 1986. Phagocytosis of latex particles by leucocytes. I. Dependence of phagocytosis on the size and surface potential of particles. Biomaterials, 7, 61-66.
KEAN, T. & THANOU, M. 2010. Biodegradation, biodistribution and toxicity of chitosan. Advanced Drug Delivery Reviews, 62, 3-11.
KELIHER, E. J., YOO, J., NAHRENDORF, M., LEWIS, J. S., MARINELLI, B., NEWTON, A., PITTET, M. J. & WEISSLEDER, R. 2011. 89Zr-labeled dextran nanoparticles allow in vivo macrophage imaging. Bioconjug Chem, 22, 2383-9.
KUHN, D. A., VANHECKE, D., MICHEN, B., BLANK, F., GEHR, P., PETRI-FINK, A. & ROTHEN-RUTISHAUSER, B. 2014. Different endocytotic uptake mechanisms for nanoparticles in epithelial cells and macrophages. Beilstein J Nanotechnol, 5, 1625-36.
LESNIAK, A., SALVATI, A., SANTOS-MARTINEZ, M. J., RADOMSKI, M. W., DAWSON, K. A. & ÅBERG, C. 2013. Nanoparticle Adhesion to the Cell Membrane and Its Effect on Nanoparticle Uptake Efficiency. Journal of the American Chemical Society, 135, 1438-1444.
MAJMUDAR, M. D., YOO, J., KELIHER, E. J., TRUELOVE, J. J., IWAMOTO, Y., SENA, B., DUTTA, P., BORODOVSKY, A., FITZGERALD, K., DI CARLI, M. F., LIBBY, P., ANDERSON, D. G., SWIRSKI, F. K., WEISSLEDER, R. & NAHRENDORF, M. 2013. Polymeric Nanoparticle PET/MR Imaging Allows Macrophage Detection in Atherosclerotic Plaques. Circulation Research, 112, 755-761.
NAGPAL, K., SINGH, S. K. & MISHRA, D. N. 2010. Chitosan Nanoparticles: A Promising System in Novel Drug Delivery. Chemical and Pharmaceutical Bulletin, 58, 1423-1430.
NAM, H. Y., KWON, S. M., CHUNG, H., LEE, S.-Y., KWON, S.-H., JEON, H., KIM, Y., PARK, J. H., KIM, J., HER, S., OH, Y.-K., KWON, I. C., KIM, K. & JEONG, S. Y. 2009. Cellular uptake mechanism and intracellular fate of hydrophobically modified glycol chitosan nanoparticles. Journal of Controlled Release, 135, 259-267.
PRABAHARAN, M. 2015. Chitosan-based nanoparticles for tumor-targeted drug delivery. International Journal of Biological Macromolecules, 72, 1313-1322.
15
RENO, F., CARNIATO, F., RIZZI, M., OLIVERO, F., PITTARELLA, P. & MARCHESE, L. 2013. Flow cytometry evidence of human granulocytes interaction with polyhedral oligomeric silsesquioxanes: effect of nanoparticle charge. Nanotechnology, 24, 185101.
ROSER, M., FISCHER, D. & KISSEL, T. 1998. Surface-modified biodegradable albumin nano- and microspheres. II: effect of surface charges on in vitro phagocytosis and biodistribution in rats. European Journal of Pharmaceutics and Biopharmaceutics, 46, 255-263.
SARVAIYA, J. & AGRAWAL, Y. K. 2015. Chitosan as a suitable nanocarrier material for anti-Alzheimer drug delivery. International Journal of Biological Macromolecules, 72, 454-465.
TABATA, Y. & IKADA, Y. 1988. Effect of the size and surface charge of polymer microspheres on their phagocytosis by macrophage. Biomaterials, 9, 356-362.
THAKUR, M. L., LAVENDER, J. P., ARNOT, R. N., SILVESTER, D. J. & SEGAL, A. W. 1977. Indium-111-labeled autologous leukocytes in man. Journal of Nuclear Medicine, 18, 1014-1021.
TSHUVA, E. Y., GOLDBERG, I., KOL, M. & GOLDSCHMIDT, Z. 2001. Zirconium Complexes of Amine−Bis(phenolate) Ligands as Catalysts for 1-Hexene Polymerization: Peripheral Structural Parameters Strongly Affect Reactivity. Organometallics, 20, 3017-3028.
VARMA, A. J., DESHPANDE, S. V. & KENNEDY, J. F. 2004. Metal complexation by chitosan and its derivatives: a review. Carbohydrate Polymers, 55, 77-93.
WEISSLEDER, R., NAHRENDORF, M. & PITTET, M. J. 2014. Imaging macrophages with nanoparticles. Nat Mater, 13, 125-138.
ZHANG, H.-L., WU, S.-H., TAO, Y., ZANG, L.-Q. & SU, Z.-Q. 2010. Preparation and Characterization of Water-Soluble Chitosan Nanoparticles as Protein Delivery System. Journal of Nanomaterials, 2010.
ZHAO, F., ZHAO, Y., LIU, Y., CHANG, X., CHEN, C. & ZHAO, Y. 2011. Cellular uptake, intracellular trafficking, and cytotoxicity of nanomaterials. Small, 7, 1322-37.
16