aluminium aw 6082 t6 round
TRANSCRIPT
Aluminium AW 6082 T6 roundAlloy 6082 is a heat treatable mediumhighstrength construction alloy with mediumhigh fatigue strength. It offers acombination of very good corrosion resistance and very good weldability due to its lowered strength values in the weldingzone. Good machinability and good cold formability after stabilising heat treatment are important benefits. This product isnot suitable for complex sections.
Applications:• Heavy duty structures in rail coaches, truck frames, ship building, bridges, military bridges and bicycles
• Masts and beams for ship building
• Tubes for scaffolding, framework for tents and halls
• Piping and tubing in machinery
The information on our web site is accurate to the best of our knowledge and understanding. Although every effort has been made to ensureaccuracy, the company cannot accept any responsibility for any direct or indirect damages resulting from possible errors or incorrect
application of the information of this publication. We reserve the right to make changes.
Copyright © 2013 Rautaruukki Corporation. All rights reserved.
Document printed on 04.03.2013 www.ruukki.com
Dimensions
• Material according to EN 5733
• Mechanical properties according to EN 7552
• Tolerances according to EN 7557
• Material certificate EN 10204 / 2.1
• Length L=6m
Dimensions mm Theor. weightd s kg/m
60 5 2.33
Properties
Chemical properties
According to EN 5733
Element Si Fe Cu Mn Mg Cr Ni Zn Ti Ga V Remarks Others/E Others/T Al
Weight % 0.701.3 0.50 0.10 0.401.0 0.61.2 0.25 0.20 0.10 0.05 0.15 Remainder
Mechanical properties
According to EN 7552
Temper Dimensions mm Rm Rp0.2 A % A50 mm
O/ H111 ≤ 25 max 160 max 110 14 12
T4 ≤ 25 205 110 14 12
T6 ≤ 5 290 250 8 6
5 < e ≤ 25 310 260 10 8
e = wall thickness
Physical properties
Density: 2.71 g/cm3 Specific heat capacity: 894 J/(kgK)
Melting Point: 650°C Thermal Expansion: 23.1 µm/(mK)
Modulus of Elasticity: 70000 MPA Resistivity: 39 nΩm
Modulus of Rigidity: 26400 MPA Thermal Conductivity: 172 W/(mK)
Poisson's ratio: 0.33 Electrical Conductivity: 44 %IACS
The content of this document has been created from web page last updated 12 Nov 2012Our sales and technical support are happy to give you more information. Visit www.ruukki.com/contactus.
Aluminium AW 6082 T6 round
2