kingfisher technical data file no. 0002 metallic …m7 c3 eutectic carbides austenite machinability...

K-CLAD 800 RANGEK-CLAD 801 - MILD STEEL BACKING PLATE FORTEMPERATURES UP TO 450 DEGREES TYPICAL HARDNESS 60 HRC

K-CLAD

801 (MILD STEEL)

S801 (STAINLESS STEEL)

As above but with 304L Stainless Steel Backing Plate

TYPICAL ANALYSIS OFHARDFACING LAYER

C : 5.0Mn : 0.7Cr : 30.0

TYPICALHARDNESS

60 HRC

STRUCTURE

Primary carbidesM7 C3 eutectic

carbidesAustenite

MACHINABILITY

Only by grinding

PROPERTIES & APPLICATIONS

Highly resistant to extremeabrasion and gouging at

temperatures up tp 450˚C.

Typical applications:dredge pump parts, hoppers,

wearplates, crusher rolls,screw conveyors, shovel

bucket teeth, palm oil expellerscrews, catalytic pipes, etc.

CARBON CHROME WITH MOLYBDENUM / WORKING TEMPERATURE UP TO 450˚C

TECHNICAL DATAFILE NO. 0002

K-CLAD

803 (MILD STEEL)

S803 (STAINLESS STEEL)

As above but with 304L Stainless Steel Backing Plate

TYPICAL ANALYSIS OFHARDFACING LAYER

C : 5.0Mn : 0.75

N : 5.0Cr : 30.0

TYPICALHARDNESS

59 HRC

STRUCTURE

Primary carbidesM7 C3 eutectic

carbides Austenite

MACHINABILITY

Only by grinding

PROPERTIES & APPLICATIONS

Resists corrosive wear andabrasive wear.

Typical applications: chutes, feeders, scrolls

CARBON CHROME NICKEL FOR CORROSIVE ENVIRONMENT / WORKING TEMPERATURE UP TO 450˚C

K-CLAD

802 (MILD STEEL)

S802 (STAINLESS STEEL)

As above but with 304L Stainless Steel Backing Plate

TYPICAL ANALYSIS OFHARDFACING LAYER

C : 5.0Mn : 0.7

Si : 0.5Mo : 7.0Nb : 7.0W : 2.0Cr : 22.0

TYPICALHARDNESS

20c:62 HRC550c:54 HRC650c:50 HRC

STRUCTURE

Austenitic matrix with various

complex carbides such as chromium

rich hexagonal primary carbides, complex eutectic

and globular niobium rich

carbides

MACHINABILITY

Only by grinding

PROPERTIES & APPLICATIONS

Resists severe high stressabrasion resistant at

temperatures up to 750˚C.Typical applications:

blast furnace bells andhoppers, sinter plant, cement

kilns, screens, exhaust fanblades, pearlite crushers, etc.

COMPLEX CARBIDE DEPOSIT OF CHROMIUM, MOLYBDENUM, NIOBIUM, VANADIUM & TUNGSTEN / WORKING TEMPERATURES UP TO 750˚C

K-CLAD 802 - STAINLESS STEEL BACKING PLATE FORTEMPERATURES UP TO 750 DEGREES TYPICAL HARDNESS 50-62 HRC

K-CLAD 803 - STAINLESS STEEL BACKING PLATE FORCORROSIVE ENVIRONMENTS

METALLIC TECHNICAL DATA

KingfisherTE

EM

ILD

S

K-C

LAD

800

K-CLAD 800 Wear Life Comparison

The information contained on this product information sheet is to be used as guidance only. The advice and technical data given is done so in good faith and does not constitute any warranty or guarantee on product performance or suitability. We hereby reserve the right to change the technical information herewith without notification or prior agreement.

T +44 (0)1384 410 777F +44 (0)1384 410 877E enquiries@kingfisher-industrial.comwww.kingfisher-industrial.com

Kingfisher IndustrialCradley Business ParkOverend RoadCradley HeathWest MidlandsUnited Kingdom B64 7DW

Protecting Industry WorldwideKingfisher