Complaint No: _______________ Complaint Received Date: ________________
Product Name: ________________ Lot Number: _____________________
Material Delivered Date: _____________ Quantity Supplied: _________________
Customer Name: _________________________________________________________
Nature of Complaint: _____________________________________________________
1. Establishing the Team
Based on nature of complaint form active team, team members from various departments (Production, Quality & Marketing).
2. Problem Description
Poor Nodularity due to low recovery of Magnesium.
3. Corrective Action
Before planning our representative must know about customer practice.
a. Collect FeSiMg sample from customer from analysis.
b. Collect process data’s from customer
i. Heat No
ii. Base metal composition
iii. Quantity treated
iv. Treatment type
v. Treatment or pouring temperature
Minex Metallurgical Co. Ltd.Customer Complaint Analysis/ Handling Report
vi. Holding time
vii. Amount of treatment alloy added
viii. Microstructure of Ductile Iron produced
4. List the possible Causes
Following factors are affecting the Nodularity of Ductile Iron.
a. Chemical Composition of treatment alloy (FeSiMg)b. Size of Treatment Alloy (FeSiMg)c. Base Metal Compositiond. Excess or Insufficient addition Nodular Alloye. Base metal Temperature or Treatment Temperaturef. Treatment Time or Long holding Time and Metal Filling
Timeg. Slag in Molten Metal
5. Define the Route Causes
Analyze possible causes one by one and state the Route causes for Poor Nodularity.
i. Chemical Composition of treatment alloy (FeSiMg)
Mg and other elements percentage is correct (as per customer’s specification) go for next step.
ii. Size of Treatment Alloy (FeSiMg)
A wide alloy sizing gives dense bulk packing in the pocket. The alloy will then fuse and react (dissolve) slowly in a controlled manner with a minimum of pieces floating. Lumps floating and burning on the surface are a waste.
iii. Base Metal CompositionHigh Sulfur, Ti, Al, Sb, Pb, Bi and Sn (Very small amounts) in Base Iron and Low Residual Magnesium in ductile iron.
iv. Excess or Insufficient addition Nodular AlloyCheck the treatment alloys is added correctly or not. It should neutralize the effect of Anti-Spheroidising Elements (neutralized by rare earth addition) & high sulfur neutralized with Magnesium addition.
v. Base metal Temperature or Treatment TemperatureHigher treatment temperature affects the recovery of Magnesium. Treatment temperature is based on the holding time.
vi. Treatment Time or Long holding Time and Metal Filling Time
Long holding time gives Magnesium fading in ductile iron.
vii. Slag in Molten MetalBefore adding the treatment alloy slag is removed from the molten metal (Magnesium react with slag its resulting poor nodularity).
6. Chose and Implement the Corrective action
After finding the Route causes, chose the corrective action to solve Route cause and Implement it.
Complaint Closed Date: _________________
Quantity of Rejected Material: ________________
Attach all the documents (data’s given by customer, chemical analysis report, if need third party analysis report & etc,). Send a copy of report to customer and top management.
Signature of Representative Respective Department Head
_______________. _________________.