BOPP-FILMSTECHNICAL DATA SHEETS

TRANSPARENT FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .4HGPL Heat sealable transparent film with – standard coefficient of friction . . . . . . . . . . . . . 4

HGHL Heat sealable transparent film with low coefficient of friction . . . . . . . . . . . . . . . . . . . . . 6

HGFL Heat sealable transparent film with high coefficient of friction for

special purposes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8

PGR Transparent release film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .10

HGSL Heat sealable transparent film for hot climate . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .12

HGHW Heat sealable transparent with a wide temperature sealing range . . . . . . . . . . . . . .14

PGP Non heat sealable for printing and lamination . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .16

METALLIZED FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .18HMPL.M Metallized heat sealable film for general purposes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .18

HMPLB.M Metallized heat sealable film with improved barrier properties . . . . . . . . . . . . . . . . . . .20

HOHMLB.M Metallized white pearlised heat sealable film with improved barrier

properties . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .22

HMIL.M Metallized heat sealable for printing and lamination . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .24

PMD.M Metallized non heat sealable film for the production of decorative packaging . .26

HMPLA.M Metallized heat sealable with low sealing threshold . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .28

PMP.M Metallized non heat sealable both side treated . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .30

HMHW.M Metallized heat sealable with a wide range of welding . . . . . . . . . . . . . . . . . . . . . . . . . . . .32

NON-FOOD FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .34PGA Transparent non heat sealable film for general purposes and

production of adhesive tapes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .34

PGD Transparent non heat sealable film for general purposes and

decorative packaging. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .36

PGT Transparent non heat sealable for general purposes and decorative

overwrapping . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .38

PWA White none heat sealable opaque for general purposes and

production of adhesive tapes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .40

MATT FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .42MGS One side matt non heat sealable film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .42MGD Both side matt non heat sealable film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .44MGPL Matt heat sealable film with low seal initiation temperature . . . . . . . . . . . . . . . . . . . . . .46MGR Matte release film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .48

OPAQUE FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .50HOHL Heat sealable white-pearlised film with low seal initiation temperature . . . . . . . .50HWHL White heat sealable film with low seal-initiation temperature . . . . . . . . . . . . . . . . . . . .52HOHW White Pearlised film with wide heatsealing range . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .54HOHG White Pearlised film both side corona treated with a standard

coefficient of friction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .56HWHW White heat sealable film with low seal intention temperature . . . . . . . . . . . . . . . . . . . .58HOHC Heat sealable white-pearlised with high yield . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .60

LABEL FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .62LGBA Transparent film for labels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .62LOBA White Pearlised film for full-wrap label . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .64LOBB White Pearlised film for full-wrap label with improved gloss . . . . . . . . . . . . . . . . . . . . .66LOBC White Pearlised film for full-wrap label with high yield . . . . . . . . . . . . . . . . . . . . . . . . . . . .68LOHM.M White pearlised metallized film for bottle labeling . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .70LOMB Matt White Pearlised microporous film . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .72LGBL Transparent for self-adhesive labels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .74LWBL Solid white for self-adhesive labels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .76SOI White-pearlised for self-adhesive labels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .78SOIL White-pearlised for inmould labels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .80

TOBACCO FILMS . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .82TSHL Heat shrinkable non treated-film for «rigid» carton pack overwrapping . . . . . . . .82TSHD Heat shrinkable – non treated film for «rigid» carton pack

overwrapping for ultra high speed machines . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .84TSHT Heat shrinkable treated film «rigid» carton pack overwrapping . . . . . . . . . . . . . . . . . .86

STORAGE AND HANDLING

Rolls should be stored In their original wrapping on pallets in dry closed sun protected place minimum 1 meter from heating units.

Storage conditions should eliminate any risk of wrapping deterioration. If stored in unheated area Biaxplen films should be placed at room temperature and humidity at least for 48 hours before converting.

It’ is recommended to corona pre treat fi lm before printing Guaranteed storage life is 6 months from the date of production.

SURFACE TREATMENT

Metallized film surface energy Is affected by temperature and storage life. Biaxplen guarantees surface treatment level of metallized films higher than 36 dynes within 15 days after metallization. In order to minimize the deterioration of surface energy it is recommended to store film below 30°C and to convert it asap. Should film be used for specific application, it is advisable to measure surface energy in order to prove if it suits. Standard roll- outside corona treated web. Metallized film is advised to be primer covered before printing. Metallized film can be laminated with a number of materials.

It’s highly recommended that the film should be used according to the application recommended by the Producer.

DIMENSIONS

ApplicationMax outer

diameter, mmCore

diameter,mm

Tolerance

Width, mm Order weight

For tobaccofilms

50076

120 152

± 0,5± 10%*450

400

300 < 2000 kg ± 20%

For allpackaging

films

98076

152

± 3 mm> 2000 kg ± 10%

780 > 5000 kg ± 5%

580 ± 2 mm >10000 kg ± 2%

Information given in Techical data sheets is based on typical values checked in standard production. Techical data sheet has not to be considered a product specification.

* 500 kg

4

TRANSPARENT FILMS

Biaxplen HGPL

DESCRIPTION:Heat sealable transparent BOPP film with a standard coefficient of friction and low heat sealing threshold for packaging machines.For high quality rotogravure and flexographic printing and lamination.

B Treated modified heat sealable copolymer skin layer

C Transparent oriented polypropylene core layer

D Heat sealable, non treated skin layer with low seal intention temperature and standard coefficient of friction

MAIN PROPERTIES:• A wide range of heat sealing;• contains slip-antistatic and antiblocking additives;• excellent optical properties;• good physical and mechanical properties;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of decorative packaging for flowers, gift wrap and etc.;• for cold seal glue frame coating onto UT film side (if necessary).

Properties Methods Unit HGPL

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40 48

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89

Tensile strength, not lessMD

GOST 14236 ISO 527 ASTM D882

N/mm2, MPa

130 140

TD 230 250

Elongation at break, not moreMD

%220 200

TD 80 70

Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295ASTM

D 1894 — 0,3

+ 0,10

- 0,15

Thermal shrinkage at 120 °C, 5 min, not moreMD

GOST 18616 ISO 11501ASTM D1204

%5 4

TD 3 2

Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527

ASTM D 882,

ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8

Haze, not more GOST 15875 ISO 14782ASTM

D 1003% 2,5 3,0 3,2

Gloss at 45 °, not less T BIAXPLEN ISO 2813ASTM

D 2457% 85

Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °C 105–140

Treatment level, not less T BIAXPLEN ISO 8296ASTM

D 2578Dyne/cm,

mN/m38

MD — Machine, longitudinal direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards * Typical value

6

TRANSPARENT FILMS

Biaxplen HGHL

DESCRIPTION:Heat sealable transparent BOPP film with low coefficient of friction and low heat sealing threshold for high-speed packaging machines.For high quality rotogravure and flexographic printing and lamination.



D Heat sealable, non treated skin layer with low seal intention temperature and low coefficient of friction

MAIN PROPERTIES:• A wide range of heat sealing;• contains slip-antistatic and antiblocking additives;• excellent optical properties;• good mechanical properties;• intended for contact with food;• both side low coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for high-speed vertical VFFS and horizontal HFFS packaging machines.

Properties Methods Unit HGHL

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40 48

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89



N/mm2, MPa

130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of friction UT/UT

GOST 27492 ISO 8295ASTM

D 1894 — 0,2

+0,05

Т/Т -0,1



%5 4

TD 3 2


ASTM D 882,

ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8


D 1003% 2,5 3,0 3,2


D 2457% 85

Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °C 105 - 140


D 2578Dyne/cm,

mN/m38


8

TRANSPARENT FILMS

Biaxplen HGFL

DESCRIPTION:Heat-sealing transparent BOPP film with a low threshold of welding, with high coefficient of friction for a special purposes, for high quality rotogravure and flexographic printing and lamination.



D Heat sealable, non treated skin layer with low seal intention temperature and high coefficient of friction

MAIN PROPERTIES:• A wide range of heat sealing;• contains antistatic and antiblocking additives;• excellent optical properties;• good mechanical properties;• intended for contact with food;• high coefficient of friction stable in time;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• laminating with PE and CPP films with a high content of slipping additives;• to reduce the impact of slip additives transition from PE or CPP film to the BOPP film

side, which leads to a significant coefficient of friction reduction. The high coefficient of friction of the HGFL film, provides a certain margin in this case;

• for a case in which the bondage process of packed products is present, for example, in pasta packaging;

• to save the packed packages in a single group without sliding over each other (if necessary);

• in the other cases, when slip reduction on BOPP side of the flexible packaging is necessary;

• for cold seal glue frame coating onto UT film side (if necessary).

Properties Methods Unit HGFL

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40 48

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89



N/mm2, MPa

130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of friction UT/UT


D 1894 — 0,45

+ 0,20

- 0,05



%5 4

TD 3 2


ASTM D 882,

ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8


D 1003% 2,5 3,0 3,2


D 2457% 85



D 2578Dyne/cm,

mN/m38


10

TRANSPARENT FILMS

Biaxplen PGR

DESCRIPTION:Transparent release BOPP film for high quality rotogravure and flexographic printing and lamination; for the production of flexible packaging with frame cold seal glue.

B Treated modified copolymer skin layer


D Non heat sealable, untreated release skin layer with low coefficient of friction

MAIN PROPERTIES:• UT side has a release properties to the latex cold seal glue;• high optical: transparency and gloss and high physical and mechanical properties;• low coefficient of friction, including hot surfaces, specially for HFFS machines;• contains antistatic, slip-antiblocking and release additives;• intended for contact with food;• chemically resistant to oils, fats and chemicals.

APPLICATION:• High quality rotogravure and flexographic solvent printing;• solvent or solventless polyurethane laminating adhesives;• for the production of flexible packaging (typically duplex) with frame cold seal glue.

Properties Methods Unit PGR

Thickness, ± 5%

BIAXPLEN

mkm 15 20 25 30 35

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 18,20 22,75 27,30 31,85

Yield, ± 5% m2/kg 73,26 54,95 43,96 36,63 31,40



N/mm2, MPa150 140

TD 250


%200

TD 70

Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,25+0,10

-0,15


GOST 18616 ISO 11501 ASTM D1204 %5 4

TD 2 2

Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 2

Gloss at 45 °, not less UT — ISO 2813 ASTM D 2457 % 85

Treatment level, not less T — ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38


12

TRANSPARENT FILMS

Biaxplen HGSL

DESCRIPTION:Heat sealable transparent BOPP film for hot climate with a standard coefficient of friction and low heat sealing threshold for packaging machines.For high quality rotogravure and flexographic printing and lamination.




MAIN PROPERTIES:• A wide range of heat sealing;• contains low speed migratory slip-antistatic additives;• less slippery surface in comparison with HGPL film;• contains an antiblock additives;• stable optical properties;• good physical and mechanical properties;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS packaging machines as film in laminate, turned to pulling belts;• for horizontal HFFS packaging machines as internal film in laminate (turned to the

product);• production of decorative packaging for flowers, gift wrap and etc.;• for cold seal glue frame coating onto UT film side (if necessary).

Properties Methods Unit HGSL

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40 48

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89



N/mm2, MPa

130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295ASTM

D 1894 — 0,35

+ 0,10

- 0,15



%5 4

TD 3 2


ASTM D 882,

ASTM F 88N/15 mm 2,0 2,2 2,3 2,5 2,8


D 1003% 2,3 2,8 3,0


D 2457% 85

Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °C 105–140


D 2578Dyne/cm,

mN/m38


14

TRANSPARENT FILMS

Biaxplen HGHW

DESCRIPTION:Transparent heat sealable BOPP film with a wide temperature sealing rangeand low coefficient of friction for high speed packaging machinesfor high quality rotogravure and flexographic printing.



D Heat sealable, non treated skin layer with very low seal intention temperature and standard coefficient of friction

MAIN PROPERTIES:• A very wide range of heat sealing;• sufficiently low coefficient of friction, including the heated surfaces for high-speed

packaging machines;• contains slip-antistatic and antiblocking additives;• excellent optical properties;• good mechanical properties;• intended for contact with food;• permanent coefficient of friction, even after printing and lamination;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for high speed vertical VFFS and horizontal HFFS packaging machines;• for heatsealing by UT / UT (fin seam) and UT / T (overlap) film sides;.• for applications requiring temperature decrease or increase the speed of heat sealing;• not for corona treatment of UT side and not for cold seal coating of UT side.

Properties Methods Unit HGHW

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40 48

Density * g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47 22,89



N/mm2, MPa

130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of frictionUT / UT


D 1894— 0,25

+ 0,10

Т / Т - 0,15

Thermal shrinkage at 120 ˚C, 5 min, not moreMD


%5 4

TD 3 2

Heat sealing strength at 130 ˚C, 1bar, 1 sec, not less UT / T GOST 27319 ISO 527

ASTM D 882, ASTM F 88

N/15mm 2,0 2,2 2,3 2,5 2,8


D 1003% 2,5 3 3,2

Gloss at 45˚, not less T BIAXPLEN ISO 2813ASTM

D 2457% 85

Heat sealing range at 1bar, 1sec.*UT/ UT

BIAXPLEN ˚C75 - 140

T / T 100 - 140 *


D 2578

Dyne/cm,

mN/m36

MD — Machine, longitudinal direction T — Treated side of the film GOST — Russian Federation standardsTD — Transverse direction UT — Untreated side of the film * Typical value

16

TRANSPARENT FILMS

Biaxplen PGP

DESCRIPTION:Transparent non heat sealable BOPP filmfor printing and lamination

B Glossy, flame treated, none heat sealable polypropylene skin layer

C Transparent biaxially oriented polypropylene

D Glossy, none treated, none heat sealable polypropylene skin layer

MAIN PROPERTIES:• Film with high transparency and gloss;• high and long time surface tension;• high adhesion of printing and lamination;• good sliding UT side for all known surfaces;• good physical and mechanical properties;• contains slip-antistatic and antiblocking additives;• intended for contact with food;• without coatings and primers.

APPLICATION:• As front film of the film in the production of flexible packaging with outstanding brilliance;• the production of packaging for horizontal HFFS and VFFS vertical packaging machines;• high quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• in cases in which the exception of heat sealability is required for front side of flexible

packaging;• the production of packaging for hand or machine wrap boxes and gifts;• not for use in original form (without lamination) in the production of packets of any kind.

Properties Methods Unit PGP

Thickness, ± 5%

BIAXPLEN

mkm 20 25 30 35 40 48


Weight, ± 5% g/m2 18,2 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 54,95 43,96 36,63 31,40 27,47 22,89



N/mm2, MPa

140

TD 250


%200

TD 70

Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295ASTM

D 1894— 0,3

+ 0,1

- 0,1



%4

TD 2

Heat sealing strength at 130 ˚C, 1bar, 1 sec, not less UT/UT GOST 27319 ISO 527

ASTM D 882,

ASTM F 88N/15mm Non heat sealable


D 1003% 2

Gloss at 45˚, not less T BIAXPLEN ISO 2813ASTM

D 2457% 90

Heat sealing range at 1bar, 1sec.* UT / UT BIAXPLEN ˚C Non heat sealable


D 2578Dyne/cm,

mN/m44

MD — Machine, longitudinal direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards* Typical value

18

METALLIZED FILMS

Biaxplen HMPL.M

DESCRIPTION: Metallized heat sealable BOPP film with a low sealing intention temperature and standard coefficient of friction for printing and lamination.

B Aluminum layer

C Treated modified copolymer layer for aluminum adhesion

D Transparent oriented polypropylene core layer

E Heat sealable non treated, skin layer with standard coefficient of friction

F

MAIN PROPERTIES:• Good adhesion of the aluminum layer;• excellent optical and barrier properties of the metallized films;• low threshold for welding, high adhesion of aluminum, good mechanical properties;• stable standard coefficient of friction;• contains slip-antiblock additives;• intended for contact with food;• without coatings and primers;• UT side is allowed to accept activation inline on the printing press or laminator

(if necessary).

APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for food products;• packaging for vertical VFFS and horizontal HFFS packaging machines;• for production of fully wrapped labels for bottles;• UT side can be coated by frame cold seal glue.

Properties Methods Unit HMPL.M

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47



N/mm2, MPa130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of friction UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,15

- 0,15


GOST 18616 ISO 11501 ASTM D1204 %5 4

TD 3 2

Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527ASTM D 882, ASTM F 88

N/15 mm 2,0 2,2 2,3 2,5 2,8

Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °С 105 - 140

Optical density, not less — 1,8

Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578Dyne/cm,

mN/m36

MD — Machine, longitudinal direction T — Metallized side TD — Transverse direction UT — Untreated, non metallized film side GOST — Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

20

METALLIZED FILMS

Biaxplen HMPLB.M

DESCRIPTION:Metallized heatsealable BOPP film with low sealing threshold and standard coefficient of friction, with barrier properties, for printing and lamination.

B Aluminum layer with increased thickness

C Treated modified layer for high adhesion to aluminum


E Heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• More thick coating of aluminium is firmly bound to the film• high barrier properties to oxygen and water vapor;• low threshold for heat sealing, high adhesion of aluminum, good mechanical properties;• permanent standard coefficient of friction;• contains no migratory antiblock and slip additives;• intended for contact with food;• without coating or primer.

APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for the food with long shelf life: cakes, sunflower

seeds, candies, chips and the like;• for vertical VFFS and horizontal HFFS packaging machines;• for cold seal glue frame coating onto UT film side (if necessary).

Properties Methods Unit HMPLB.M

Thickness, ± 5%

BIAXPLEN

mkm 18 20 30 35 40

Density* g/cm3 0,91

Weight, ± 5% g/m2 16,38 18,20 27,30 31,85 36,40

Yield, ± 5% m2/kg 61,05 54,95 36,63 31,40 27,47



N/mm2, MPa130 140

TD 230 250


%220 200

TD 80 70


- 0,10


GOST 18616 ISO 11501 ASTM D1204 %5 4

TD 3 2


N/15 mm 2,0 2,3



Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 36

Water vapour transmission rate at 38 °C, 90% rel.humidi-ty, 24 h, not more

BIAXPLEN — ASTM F 1249 g/m2/24 h 1,0

Oxygen transmission rate at 23 °С, 24 h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24 h 50


22

METALLIZED FILMS

Biaxplen HOHMLB.M

DESCRIPTION:Metallized white pearl microporous heatsealable BOPP film with increased barrier properties for printing and laminations for production of flexible packaging for products with long shelf life.

B Aluminum layer with increased thickness

C Treated modified layer for high adhesion to aluminum

D Oriented polypropylene tie layer

E White Pearl cavitated core layer of orinted polypropylene

F Oriented polypropylene tie layer

G White pearl heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• Metallized side with high adhesion to the film;• low threshold for heat welding, increased barrier properties and stable coefficient

of friction;• contains mineral fillers as calcium carbonate and titanium dioxide;• good protection from UV and sunlight;• intended for contact with food;• pearl side (UT) easily takes an activation, at 200 m/min corona power 4 KW is enough for

proper printing or lamination;• without coating or primer.

APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for both side printing or in center of triplex lamination;• for lamination with solvent based or solventless polyurethane adhesives;• production of flexible packaging with frame cold glue;• manufacture of flexible packaging for products with high shelf life;• manufacture of lid for trays with food, typically in center of triplex;• production of flexible packaging for the bouillon cubes.

Properties Methods Unit HOHMLB.M

Thickness, ± 5%

BIAXPLEN

mkm 30 35 40

Density* g/cm3 0,7

Weight, ± 5% g/m2 21,0 24,5 28,0

Yield, ± 5% m2/kg 47,6 40,8 35,7



N/mm2, MPa70

TD 140


%200

TD 60


-0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Heat sealing strength at 130 °C, 1 bar, 1 sec, not less UT/UT GOST 27319 ISO 527ASTM D 882, ASTM

F 88N/15 mm 2,5

Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °С 105 - 140

Optical density, not less BIAXPLEN — 2,5

Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 36

Water vapour transmission rate at 38 °C, 90% rel.humidity, 24 h, not more

BIAXPLEN — ASTM F 1249 g/m2/24 h 1

Oxygen transmission rate at 23 °С, 24 h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24 h 90

MD — Machine, longitudinal direction T — Metallized side TD — Transverse direction UT — White pearl side, untreated side GOST — Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

24

METALLIZED FILMS

Biaxplen HMIL.M

DESCRIPTION:Metallized heat sealable BOPP film with a low sealing intention temperature, long time surface tension shelf life and standard coefficient of friction for printing and lamination.

B Aluminum layer



E Heat sealable non treated, skin layer with standard coefficient of friction

F

MAIN PROPERTIES:• Excellent adhesion of the aluminum layer;• long time surface tension shelf life;• good optical and barrier properties of the metallized films;• low threshold for welding, high adhesion of aluminum, good mechanical properties;• stable standard coefficient of friction;• contains slip-antiblock additives;• intended for contact with food;• without coatings and primers;• UT side is allowed to accept activation inline on the printing press or laminator

(if necessary).

APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for food products;• packaging for vertical VFFS and horizontal HFFS packaging machines;• for production of fully wrapped labels for bottles;• UT side can be coated by frame cold seal glue.

Properties Methods Unit HMIL.M

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 25 30 35 40

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,20 22,75 27,30 31,85 36,40

Yield, ± 5% m2/kg 73,26 61,05 54,95 43,96 36,63 31,40 27,47



N/mm2, MPa130 140

TD 230 250


%220 200

TD 80 70


- 0,15


GOST 18616 ISO 11501 ASTM D1204 %5 4

TD 3 2


N/15 mm 2,0 2,2 2,3 2,5 2,8



Treatment level, not less** T BIAXPLEN ISO 8296 ASTM D 2578Dyne/cm,

mN/m36

Water vapour transmission rate at 38 °C, 90% rel.humidity, 24 h*

BIAXPLEN — ASTM F 1249 g/m2/24 h 1

Oxygen transmission rate at 23 °С, 0% rel.humidi-ty 24 h*

BIAXPLEN — ASTM D 3985 cm3/m2/24 h 90


26

METALLIZED FILMS

Biaxplen PMD.M

DESCRIPTION:None heat sealable metallized BOPP film for the production of decorative packaging. With increased coefficient of friction. for printing and lamination and for decorative packaging.

B Aluminum layer



E Non heat sealable skin layer with high coefficient of friction, without treatment (by default)

MAIN PROPERTIES:• Standard barrier properties of metallized films; • contains antiblock additives; • mechanical properties are good; • high adhesion of the aluminum layer; • intended for contact with food;• without coating or primer.

APPLICATION:• High quality rotogravure and flexographic solvent based printing; • for lamination with solvent based or solventless polyurethane adhesives; • production of decorative packaging for flowers, gift wrap and etc.; • heat sealing by string is possible;• lamination with films, paper and cardboard;• in case of both side corona treatment:• - lamination as middle of triplex or both side printing;• - cold seal glue coating onto non metalized film side. •

Properties Methods Unit PMD.M

Thickness, ± 5%

BIAXPLEN

mkm 20 25 30 35 40


Weight, ± 5% g/m2 18,2 22,8 27,3 31,9 36,4

Yield, ± 5% m2/kg 54,9 44,0 36,6 31,4 27,5



N/mm2, MPa140

TD 280


%200

TD 70

Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,1

- 0,1

Thermal shrinkage at 120˚C, 5 min, not more

MDGOST 18616 ISO 11501 ASTM D1204 %

4

TD 2

Treatment level, not less ** T BIAXPLEN ISO 8296 ASTM D 2578Dyne/cm,

mN/m36 / 36 ***

Optical density, not less BIAXPLEN — 1,8

MD — Machine, longitudinal direction T — Metallized sideTD — Transverse direction UT — Untreated, non metallized film side GOST — Russian Federation standards* Typical value** Garanteed shelf life of the activation of the metallized side is 30 days from the date of manufacture indicated on roll label*** When the order is placed for both side corona treatment Shelf life of activation for non metallized film side is 6 months

28

METALLIZED FILMS

Biaxplen HMPLA.M

DESCRIPTION:Metallized heatsealable BOPP film with low sealing threshold and standard coefficient of friction, with barrier properties for printing and lamination with glue or hot melt.

B Aluminum layer with increased thickness (T)

C Treated modified layer for aluminum coating, with increased heat resistance


E Heat sealable, non treated skin layer with standard coefficient of friction (UT)

MAIN PROPERTIES:• Thick coating of aluminium;• increased heat resistance for metallized layer; • long time surface tension shelf life; • high barrier properties to oxygen and water vapor; • increased stiffness;• low threshold for heat sealing, high adhesion of aluminum, good mechanical properties;• permanent standard coefficient of friction;• contains no migratory antiblock and slip additives; • intended for contact with food;• without coating or primer.

APPLICATION:• High quality rotogravure and flexographic solvent based printing;• hot melt lanination; • for lamination with solvent based or solventless polyurethane adhesives; • manufacture of flexible packaging for the food with long shelf life: cakes, sunflower

seeds, candies, chips and the like;• for vertical VFFS and horizontal HFFS packaging machines;• for cold seal glue frame coating onto UT film side (if necessary).

Properties Methods Unit HMPLA.M

Thickness, ± 5%

BIAXPLEN

mkm 18 20 30 35 40


Weight, ± 5% g/m2 16,38 18,20 27,30 31,85 36,40

Yield, ± 5% m2/kg 61,05 54,95 36,63 31,40 27,47



N/mm2, MPa130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+ 0,10

- 0,10

Thermal shrinkage at 120˚C, 5 min, not moreMD

GOST 18616 ISO 11501 ASTM D1204 %5 4

TD 3 2

Heat sealing strength at 130°C, 1bar, 1 sec, not less UT/UT GOST 27319 ISO 527


N/15mm 2,0 2,3

Heat sealing range at 1bar, 1sec.* UT / UTBIAXPLEN

°С 105 - 140


Treatment level, not less ** T BIAXPLEN ISO 8296 ASTM D 2578Dyne/cm,

mN/m36

Water vapour transmission rate at 38°C, 90% rel.humidity, 24h, not more BIAXPLEN — ASTM F 1249 g/m2/24h 0,1

Oxygen transmission rate at 23°С, 24h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24h 15

MD — Machine, longitudinal direction T — Metallized sideTD — Transverse direction UT — Untreated, non metallized film side GOST — Russian Federation standards* Typical value** Garanteed shelf life of the activation of the metallized side is 90 days from the date of manufacture indicated on roll label

30

METALLIZED FILMS

Biaxplen PMP.M

DESCRIPTION:Metallized non heat sealable both side treatedBOPP film with standard coefficient of frictionfor both side printing and lamination

B Aluminum layer



E Treated non heat sealable skin layer with standard coefficient of friction

MAIN PROPERTIES:• Both sides (T, UT) activated film;• standard barrier properties of metallized films;• standard coefficient of friction;• mechanical properties and aluminum adhesian are good;• contains no migratory antiblock and slip additives;• intended for contact with food;• without coating or primer.

APPLICATION:• Rotogravure and flexographic solvent based one or both side printing;• for both side lamination with solvent based or solventless polyurethane adhesives;• lamination with films, paper and cardboard, as well as in the center of the triplex

in flexible packaging;• for the production of labels with both side printed design;

Properties Methods Unit PMP.M

Thickness, ± 5%

BIAXPLEN

mkm 20 25 30 35 40


Weight, ± 5% g/m2 18,2 22,8 27,3 31,9 36,4

Yield, ± 5% m2/kg 54,9 44,0 36,6 31,4 27,5



N/mm2, MPa140

TD 250


%200

TD 70

Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3- 0,1

+ 0,1

Heat sealing strength at 130 ˚C, 1bar, 1 sec, not less UT / UT GOST 27319 ISO 527


N/15mm


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Treatment level, not less ** TBIAXPLEN ISO 8296 ASTM D 2578

Dyne/cm, mN/m

36

Treatment level, not less *** UT 38

Optical density, not lessBIAXPLEN

— 2,2

Heat sealing range at 1bar, 1sec.* UT / UT ˚С

Water vapour transmission rate at 38 ˚C, 90% rel.humidity, 24h, not more

BIAXPLEN — ASTM F 1249 g/m2/24h 1

Oxygen transmission rate at 23 ˚C, 24h, not more BIAXPLEN — ASTM D 3985 cm3/m2/24h 100

MD — Machine, longitudinal direction T — Metallized side TD — Transverse direction UT — Non metallized film side GOST — Russian Federation standards* Typical value** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label*** Activation shelf-life for UT activated side is at least for 6 months

32

METALLIZED FILMS

Biaxplen HMHW.M

DESCRIPTION:Metallized BOPP heat sealable film with a very wide range of weldingand a standard coefficient of friction for high speed packaging machines.for high quality rotogravure and flexographic printing.

B Ò

C Aluminum layer

D Treated modified copolymer layer for aluminum adhesion

E Transparent oriented polypropylene core layer

F Heat sealable, non treated skin layer with very low seal intention temperature and standard coefficient of friction

MAIN PROPERTIES:• Good adhesion of the aluminum layer;• good optical and barrier properties;• a very wide range of heat sealing;• sufficiently low coefficient of friction, including the heated surfaces for high-speed

packaging machines;• contains slip-antiblock additives;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality rotogravure and flexographic solvent based printing;• for lamination with solvent based or solventless polyurethane adhesives;• manufacture of flexible packaging for food products;• for high speed vertical VFFS and horizontal HFFS packaging machines;• for applications requiring temperature decrease or increase the speed of heat sealing;• in some cases, instead of using packaging with frame glue cold welding;• not for corona treatment of UT side;• not for cold seal coating for UT side.

Properties Methods Unit HMHW.M

Thickness, ± 5%

BIAXPLEN

mkm 15 20 25 30 35 40


Weight, ± 5% g/m2 13,65 18,20 22,75 27,30 31,85 36,40

Yield, ± 5% m2/kg 73,26 54,95 43,96 36,63 31,40 27,47



N/mm2, MPa

130 140

TD 230 250


%220 200

TD 80 70

Kinetic coefficient of friction UT / UT GOST 27492 ISO 8295ASTM

D 1894— 0,25

+ 0.10

- 0.10



%5 4

TD 3 2

Heat sealing strength at 130 ˚C, 1bar, 1 sec, not less UT / UT GOST 27319 ISO 527

ASTM D 882,

ASTM F 88N/15mm 2,0 2,3 2,5 2,8

Heat sealing range at 1bar, 1sec.* UT / UTBIAXPLEN

˚С 75 - 140


Treatment level, not less ** T BIAXPLEN ISO 8296ASTM

D 2578Dyne/cm,

mN/m36

Water vapour transmission rate at 38 ˚C, 90% rel.humidi-ty, 24h *

BIAXPLEN —ASTM F 1249

g/m2/24h 1

Oxygen transmission rate at 23 ˚C, 0% rel.humidity 24h * BIAXPLEN —ASTM

D 3985cm3/

m2/24h100

MD — Machine, longitudinal direction T — Metallized side TD — Transverse direction UT — Untreated, non metallized film side GOST — Russian Federation standards* Typical value** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

34

NON-FOOD FILMS

Biaxplen PGA

DESCRIPTION:Transparent BOPP film for general purposes for the production of adhesive tapes.

B Glossy, treated, none heat sealable skin layer


D Glossy, non treated (by default), none heat sealable skin layer

MAIN PROPERTIES:• Contains antiblocking additives;• very high optical properties: transparency and gloss;• high mechanical properties;• good flatness of the film;• intended for contact with food (if necessary);• low thermo shrinkage to save print sizes in glue drying process;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• production of adhesive tapes (skotch) with hot melt and water based adhesives;• solvent based and solvent free lamination with polyurethane adhesives (if necessary).

Properties Methods Unit PGA

Thickness, ± 5%

BIAXPLEN

mkm 20 23 25 26 28 32 40

Density* g/cm3 0,91

Weight, ± 5% g/m2 18,20 20,93 22,75 23,66 25,48 29,12 36,40

Yield, ± 5% m2/kg 54,95 47,78 43,96 42,27 39,25 34,34 27,47



N/mm2, MPa150 140

TD 250


%180

TD 70


- 0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


N/15 mm Non heat sealable


Gloss at 45 °, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 90

Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °C None heat sealable

Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578Dyne/cm,

mN/m38**/44 ***

MD — Machine, longitudinal direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards * Typical value ** In case of corona treatment *** In case of flame treatment

36

NON-FOOD FILMS

Biaxplen PGD

DESCRIPTION:Transparent non heat sealable BOPP film for general purposes and decorative packaging.

B Glossy, treated, none heat sealable polypropylene skin layer



MAIN PROPERTIES:• Contains slip-antistatic and antiblocking additives;• very high optical properties: transparency and gloss;• good physical and mechanical properties;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• production of decorative packaging for flowers, gift wrap and etc.;• solvent based and solvent free lamination with polyurethane adhesives (if necessary);• in cases in which the exception of heat sealability is required.

Properties Methods Unit PGD

Thickness, ± 5%

BIAXPLEN

mkm 20 25 30 35 40 48

Density* g/cm3 0,91

Weight, ± 5% g/m2 18,2 22,75 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 54,95 43,96 36,63 31,40 27,47 22,89



N/mm2, MPa140

TD 250


%200

TD 70


- 0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2





Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °C Non heat sealable


mN/m38


38

NON-FOOD FILMS

Biaxplen PGT

DESCRIPTION:Transparent non heat sealable BOPP film for textile packaging, general purposes and decorative overwrapping with high antistatic properties.

B Corona treated, copolymer skin layer

C Transparent biaxially oriented polypropylene with antistatic


MAIN PROPERTIES:• Contains efficient antistatic and antiblocking additives;• corona treated film;• very high optical properties: transparency and gloss;• good physical and mechanical properties;• high antistatic properties;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• for textiles packaging, production of decorative and flowers packagings, gift wrapping

and etc.;• for heat sealing by hot wire or knife (sealing and cutting simultaneously);• solvent based and solvent free lamination with polyurethane adhesives (if necessary);• in cases in which the exception of heat sealability and/or stickiness is required at the

increased temperatures.

Properties Methods Unit PGT

Thickness, ± 5%

BIAXPLEN

mkm 20 25 28 30 35 40

Density* g/cm3 0,91

Weight, ± 5% g/m2 18,20 22,75 25,48 27,30 31,85 36,40

Yield, ± 5% m2/kg 54,95 43,96 39,25 36,63 31,40 27,47



N/mm2, MPa140

TD 250


%200

TD 70


-0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2





Heat sealing range at 1 bar, 1 sec.* UT/UT BIAXPLEN °C Non heat sealable


mN/m38


40

NON-FOOD FILMS

Biaxplen PWA

DESCRIPTION:White none heat sealable opaque BOPP film for general purposes and production of adhesive tapes.

B Glossy, treated, none heat sealable skin layer

C Solid – white opaque oriented polypropylene core layer

D Glossy, non treated (by default), none heat sealable skin layer

MAIN PROPERTIES:• White appearance;• high opacity;• good mechanical properties;• high protection from UV light;• contains antiblocking and mineral filler as titanium dioxide;• does not contain migratory additives;• intended for contact with food (if necessary);• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• production of adhesive tapes (sktoch) with hot melt and water based adhesives;• decorative wrapping or other packaging with protection from UV light;• white appearance allows to exclude white inks from printing or/and exclude white

adhesives;• solvent based and solvent free lamination with polyurethane adhesives (if necessary).

Properties Methods Unit PWA

Thickness, ± 5%

BIAXPLEN

mkm 23 25 28 32

Density* g/cm3 0,96

Weight, ± 5% g/m2 22,08 24,00 26,88 30,72

Yield, ± 5% m2/kg 45,29 41,67 37,20 32,55



N/mm2, MPa120 140

TD 240 250


%200

TD 70

Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,5+ 0,1

- 0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Heat sealing strength at 130 °С, 1 bar, 1 sec UT/UT GOST 27319 ISO 527ASTM F 88; ASTM

D882N/15 mm None heat sealable

Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 45


Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C None heat sealable

Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38 **/42 ***

MD — Machine, longitudinal direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards * Typical value ** In case of corona treatment *** In case of flame treatment

42

MATT FILMS

Biaxplen MGS

DESCRIPTION:One side matt BOPP film for general purposes, for high quality rotogravure and flexographic printing and lamination for flexible packaging and labels.

B Matt not treated side


D Treated modified heat sealable copolymer skin layer

MAIN PROPERTIES:• Matte appearance;• contains slip-antistatic and anti-blocking additives;• good ink adhesion;• good mechanical properties;• low coefficient of friction;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• for production of decorative packaging for flowers, gift wrap and etc.;• for production of fully wrapped labels for bottles;• to make the flexible packaging or labels matte (paper like) appearance.

Properties Methods Unit MGS

Thickness, ± 5%

BIAXPLEN

mkm 15 20 35

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 18,2 31,85

Yield, ± 5% m2/kg 73,26 54,95 31,40



N/mm2, MPa125

TD 240


%220

TD 80


-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


F 88N/15 mm 2,0 2,3 2,5

Haze, not less GOST 15875 ISO 14782 ASTM D 1003 % 70

Gloss at 45 °, not more T BIAXPLEN ISO 2813 ASTM D 2457 % 12


Treatment level, not less T BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38

MD — Machine, longitudinal direction T — Treated glossy side of the film TD — Transverse direction UT — Untreated matt side of the film GOST — Russian Federation standards * Typical value

44

MATT FILMS

Biaxplen MGD

DESCRIPTION:Both side matt film for general purposes, for flexographic printing, for decorative packaging.

B Matt not treated side


D Matt treated side

E

MAIN PROPERTIES:• Both side matte appearance;• contains slip-antistatic additives;• good mechanical properties;• standard coefficient of friction;• intended for contact with food;• without coatings and primers.

APPLICATION:• Solvent based flexographic printing;• for production of decorative packaging for flowers, gift wrap and etc.;• heat sealing by string is possible;• to make the flexible packaging or labels matte (paper like) appearance.

Properties Methods Unit MGD

Thickness, ± 5%

BIAXPLEN

mkm 20 30 35

Density* g/cm3 0,91

Weight, ± 5% g/m2 18,2 27,3 31,85

Yield, ± 5% m2/kg 54,95 36,63 31,40



N/mm2, MPa125

TD 240


%220

TD 80


-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


F 88N/15 mm 2,3 2,4 2,5





MD — Machine, longitudinal direction T — Treated matt side of the film TD — Transverse direction UT — Untreated matt side of the film GOST — Russian Federation standards * Typical value

46

MATT FILMS

Biaxplen MGPL

DESCRIPTION:One side matt heat sealable BOPP film for general purposes, for high quality rotogravure and flexographic printing and lamination for flexible packaging and labels.

B Matt heat sealable, non treated skin layer with low seal intention temperature


D Treated modified heat sealable copolymer skin layer

MAIN PROPERTIES:• Matte appearance;• contains slip-antistatic and antiblocking additives;• wide heat sealing range;• good ink adhesion;• good mechanical properties;• standard coefficient of friction;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• for vertical packaging machine with tamping of the film;• for production of decorative packaging for flowers, gift wrap and etc.;• for production of fully wrapped labels for bottles;• to make the flexible packaging or labels matte (paper like) appearance.

Properties Methods Unit MGPL

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20 35

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,2 31,85

Yield, ± 5% m2/kg 73,26 61,05 54,95 31,40



N/mm2, MPa125

TD 240


%220

TD 80


-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


N/15 mm 2,0 2,3 2,5






48

MATT FILMS

Biaxplen MGR

DESCRIPTION:Matte release BOPP film for high quality rotogravure, flexographic printing and lamination; for the production of flexible packaging with frame cold seal glue.

B Matte not treated release skin layer with low coefficent of friction


D Treated smooth modified copolymer skin layer

MAIN PROPERTIES:• Matte UT side has a release properties to the latex cold seal glue;• low coefficient of friction, including hot surfaces, specially for high speed HFFS

machines;• good ink adhesion;• good mechanical properties;• contains antistatic, slip-antiblocking and release additives;• chemically resistant to oils, fats and chemicals;• intended for contact with food;• without coating or primer.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• for the production of “flow-pack” flexible packaging with frame cold seal glue;• to make the flexible packaging with matte (paper like) appearance;• for vertical VFFS, and mainly for horizontal high speed HFFS packaging machines.

Properties Methods Unit MGR

Thickness, ± 5%

BIAXPLEN

mkm 15 18 20

Density* g/cm3 0,91

Weight, ± 5% g/m2 13,65 16,38 18,2

Yield, ± 5% m2/kg 73,26 61,05 54,95



N/mm2, MPa125

TD 240


%220

TD 80


-0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2





50

OPAQUE FILMS

Biaxplen НOHL

DESCRIPTION:Heat sealable White Pearlised BOPP film with low seal intention temperature and standard coefficint of friction for packaging machines. For high quality rotogravure and flexographic printing and lamination.

B Treated, heatsealable copolymer skin layer

C Transparent oriented polypropylene tie layer

D White Pearl cavitated core layer of oriented polypropylene

E Transparent oriented polypropylene tie layer

F Heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• A wide temperature range of heat sealing;• high opacity and good whiteness;• good protection from UV light;• low density and high yield;• contains slip-antistatic and antiblocking additives;• contains mineral fillers as calcium carbonate and titanium dioxide;• intended for contact with food;• stable standard coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of flexible packaging with frame cold seal adhesives;• for cold seal glue frame coating onto UT film side (if necessary);• packaging of ice cream, chocolate bars, candy, etc. which requires protection from

UV light.

Properties Methods Unit НOHL

Thickness, ± 5%

BIAXPLEN

mkm 30 35 40 45

Density* g/cm3 0,72

Weight, ± 5% g/m2 21,60 25,20 28,80 32,40

Yield, ± 5% m2/kg 46,30 39,68 34,72 30,86



N/mm2, MPa70

TD 140


%200

TD 60


- 0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


D882N/15 mm 2,5

Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 40 35 30


Heat sealing range at 1 bar, 1 sec* UT/UT BIAXPLEN °C 105 - 140



52

OPAQUE FILMS

Biaxplen HWHL

DESCRIPTION:White heat sealable BOPP film with low seal intention temperature and standard coefficint of friction for packaging machines. For high quality rotogravure and flexographic printing and lamination.


C White opaque oriented polypropylene core layer


MAIN PROPERTIES:• A wide range of heat sealing;• completely white appearance, high opacity;• very high protection from UV light;• white appearance allows to exclude white paint using from printing process;• contains slip-antistatic, antiblocking and mineral filler as titanium dioxide;• stable standard coefficient of friction;• good physical and mechanical properties;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of flexible packaging with frame cold seal adhesives;• for cold seal glue frame coating onto UT film side (if necessary);• packaging of ice cream, chocolate bars, candy, etc. which requires protection from

UV light;• for production of fully wrapped labels for bottles in the original form of the film

or in laminate.

Properties Methods Unit HWHL

Thickness, ± 5%

BIAXPLEN

mkm 15 20 30 35

Density* g/cm3 0,96

Weight, ± 5% g/m2 14,40 19,20 28,80 33,60

Yield, ± 5% m2/kg 69,44 52,08 34,72 29,76



N/mm2, MPa110 120

TD 210 220 230


%200

TD 70


- 0,10


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


D882N/15 mm 2,5

Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 60 50 40 35





54

OPAQUE FILMS

Biaxplen НOHW

DESCRIPTION:White Pearlised BOPP film with very wide heatsealing range and standard coefficient of friction for packaging machines.For high quality rotogravure and flexographic printing and lamination.

B Treated, heatsealable copolymer skin layer (T)




F Non treated skin layer, with standard coefficient of friction and very broad heat sealing range (UT)

MAIN PROPERTIES:• A wide range and high speed of heat sealing;• high opacity and good whiteness;• good protection from UV light;• low density and high yield;• contains slip-antistatic and antiblocking additives;• contains mineral fillers as calcium carbonate and titanium dioxide;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for high speed heat sealing 130–250 packs/min. (depends from packaging thickness and

machine);• low sealing temperature in ice-cream packaging process;• for vertical VFFS and high speed horizontal HFFS packaging machines;• packaging of ice cream, chocolate bars, candy, etc. which requires protection from

UV light;• not for the application of the framework cold glue on UT-side.

Properties Methods Unit НOHW

Thickness, ± 5%

BIAXPLEN

mkm 30 35 40 45

Density* g/cm3 0,72

Weight, ± 5% g/m2 21,60 25,20 28,80 32,40

Yield, ± 5% m2/kg 46,30 39,68 34,72 30,86



N/mm2, MPa70

TD 140


%200

TD 60


- 0,10


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


D882N/15 mm 2,5






56

OPAQUE FILMS

Biaxplen НOHG

DESCRIPTION:White Pearlised both side corona treated BOPP film with a standard coefficient of friction for both side printing, lamination and for “flowpack” packaging with cold seal glue coating.

B Corona treated copolymer skin layer (OUT)

C White polypropylene oriented tie layer



F Corona treated, glossy, copolymer skin layer with a standard coefficient of friction (IN)

MAIN PROPERTIES:• High gloss, whiteness and good opacity;• low density and high yield;• contains antistatic and antiblocking additives;• both side corona treated;• OUT side for the main printing and lamination;• IN side for a minor printing, lamination and cold seal glue coating;• without delamination of the foam layer during repeated opening of the packaging;• contains white fillers;• intended for contact with food;• standard coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing onto OUT side;• solvent based and solvent free lamination with polyurethane adhesives within IN, OUT

sides;• for cold seal glue frame coating onto IN film side SIBUR_cat_films_eng.indd;• for lamination in the center of the triplex (if necessary);• for flexible packaging with frame cold seal adhesives of single and multiple opening;• the production of flexible packaging “flowpack” for food;• production of both side printed labels for full round wrapping bottles;• production of self adhesive labels;• packaging of ice cream, chocolate bars, candy, etc.;• as the heat-sealing film is not always suitable.

Properties Methods Unit НOHG

Thickness, ± 5%

BIAXPLEN

mkm 30 35 40 45

Density* g/cm3 0,73

Weight, ± 5% g/m2 21,90 25,55 29,20 32,85

Yield, ± 5% m2/kg 45,66 39,14 34,25 30,44



N/mm2, MPa90

TD 180


%200

TD 70

Coefficient of friction, kinetic IN/IN GOST 27492 ISO 8295 ASTM D 1894 — 0,35+ 0,10

- 0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Heat sealing strength at 130 °С, 1 bar, 1 sec.*IN/IN

GOST 27319 ISO 527ASTM F 88; ASTM

D882N/15 mm 2 3

Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 40 35

Gloss at 45 °, not lessIN

BIAXPLEN ISO 2813 ASTM D 2457 %70

OUT 85

Heat sealing range at 1 bar, 1 sec*IN/IN

BIAXPLEN °C115 - 140

OUT/OUT 125 - 140

Treatment level, not less OUT

BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m38

IN 36

MD — Machine, longitudinal direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards * Typical, background values

58

OPAQUE FILMS

Biaxplen HWHW

DESCRIPTION:White heat sealable BOPP film with low seal intention temperature and standard coefficint of friction for packaging machines. For high quality rotogravure and flexographic printing and lamination.


C White opaque oriented polypropylene core layer


MAIN PROPERTIES:• A wide range of heat sealing;• completely white appearance, high opacity;• very high protection from UV light;• contains slip-antistatic, antiblocking and mineral filler as titanium dioxide;• sufficiently low coefficient of friction, including the heated surfaces for high-speed

packaging machines;• good physical and mechanical properties;• intended for contact with food;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• white appearance allows to exclude white paint using from printing process;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• in some cases, instead of using packaging with frame glue cold welding;• for vertical VFFS and horizontal HFFS packaging machines;• for applications requiring temperature decrease or increase the speed of heat sealing;• packaging of ice cream, chocolate bars, candy, etc. which requires protection from

UV light;• not for corona treatment of UT side and not for cold seal coating for UT side.

Properties Methods Unit HWHW

Thickness, ± 5%

BIAXPLEN

mkm 15 20 30 35

Density* g/cm3 0,96

Weight, ± 5% g/m2 14,40 19,20 28,80 33,60

Yield, ± 5% m2/kg 69,44 52,08 34,72 29,76



N/mm2, MPa110 120

TD 210 230


%200

TD 70


- 0,10


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


D882N/15 mm 2,5

Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 60 50 40 35





60

OPAQUE FILMS

Biaxplen НOHС

DESCRIPTION:Heat sealable white-pearl BOPP film with ultra high yieldand standard coefficient of friction. For high quality rotogravure andflexographic printing and lamination





F Heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• A wide temperature range of heat sealing;• high opacity and good whiteness;• good protection from UV light;• ultra low density and very high yield;• contains slip-antistatic and antiblocking additives;• contains mineral fillers as calcium carbonate and titanium dioxide;• intended for contact with food;• stable standard coefficient of friction;• without coatings and primers.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• solvent based and solvent free lamination with polyurethane adhesives;• manufacture of flexible packaging for food products;• for vertical VFFS and horizontal HFFS packaging machines;• production of flexible packaging with frame cold seal adhesives;• for cold seal glue frame coating onto UT film side (if necessary).• packaging of ice cream, chocolate bars, candy, etc. which requires protection from

UV light;

Properties Methods Unit НOHС

Thickness, ± 5%

BIAXPLEN

mkm 33 35 38 40


Weight, ± 5% g/m2 18,15 19,25 20,90 22,00

Yield, ± 5% m2/kg 55,10 51,95 47,85 45,45



N/mm2, MPa70

TD 140


%200

TD 60


- 0,10


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Heat sealing strength at 130 ˚C, 1bar, 1sec UT / UT GOST 27319 ISO 527ASTM F 88; ASTM D882

N/15mm 2


Gloss at 45˚, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 80

Heat sealing range at 1bar, 1sec * UT / UT BIAXPLEN ˚C


mN/m38

Water vapour transmission rate at 38 ˚C, 90% rel.humidity, 24h, ± 20% *

BIAXPLEN — ASTM F 1249 g/m2/24h 4,3 3,7 3,3 2,9

Oxygen transmission rate at 23 ˚C, 0% rel.humidity 24h, ± 20% * BIAXPLEN — ASTM D 3985 cm3/m2/24h 1770 1515 1325 1180

MD — Machine, longitudinal direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards* Typical value

62

LABEL FILMS

Biaxplen LGBA

DESCRIPTION:Transparent BOPP film for labels and for general applications for bonding by cold and hot melt adhesives when labelling with improved ink adhesion for printing.

B Treated side of modified copolymer skin layer


D Glossy, none treated, none heat sealable polypropylene skin layer with standard coefficient of friction

MAIN PROPERTIES:• Improved ink adhesion;• contains antistatic and slip- antiblocking agents;• excellent optical properties: transparency and gloss;• good mechanical properties;• permanent coefficient of friction;• without coating or primer.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue;• solvent based and solvent free lamination with polyurethane adhesives (if necessary).

Properties Methods Unit LGBA

Thickness, ± 5%

BIAXPLEN

mkm 30 35 40 48

Density* g/cm3 0,91

Weight, ± 5% g/m2 27,30 31,85 36,40 43,68

Yield, ± 5% m2/kg 36,63 31,40 27,47 22,89



N/mm2, MPa140

TD 280


%200

TD 70


- 0,1


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


Gloss at 45 °, not less UT BIAXPLEN ISO 2813 ASTM D 2457 % 90



64

LABEL FILMS

Biaxplen LOBA

DESCRIPTION:White Pearl microporous BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with good gloss and ink adhesion

B Modified copolymer corona treated skin layer

C White opaque oriented polypropylene tie layer


E Oriented polypropylene tie layer

F Glossy non heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• High adhesion of solvent based inks: flexo and rotogravure for direct printing;• both side glossy film;• good opacity and whiteness;• contains slip, antistatic and antiblock additives;• contains mineral fillers such as calcium carbonate and titanium dioxide;• low coefficient of friction, stable in time; • without coating or primer.

APPLICATION:• High quality solvent rotogravure and flexographic direct printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.

Properties Methods Unit LOBA

Thickness, ± 5%

BIAXPLEN

mkm 35 38 47


Weight, ± 5% g/m2 23,80 25,84 31,96

Yield, ± 5% m2/kg 42,02 38,70 31,29


N/mm2, MPa80

TD GOST 14236 ISO 527 ASTM D882 150


GOST 27492 ISO 8295 ASTM D 1894

%200

TD 70

Coefficient of friction, kinetic UT / UT — 0,3+0,10

- 0,10

Thermal shrinkage at 120˚C, 5 min, not moreMD

GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


Gloss at 45°, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85


MD — Machine, longitudinal direction T — Treated side of the filmTD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards* Typical value

66

LABEL FILMS

Biaxplen LOBB

DESCRIPTION:White Pearl microporous glossy BOPP film for fully wrapped labeling of bottlesfor cold and hot melt glue application while labelingwith excellent gloss and high ink adhesion

B Modified copolymer corona treated glossy skin layer

C Oriented polypropylene tie layer



F Glossy non heat sealable, non corona treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• Both side excellent gloss;• high adhesion of solvent based inks: flexo and rotogravure for direct printing;• excellent opacity and whiteness;• with increased yield;• contains slip, antistatic and antiblock additives;• contains mineral fillers such as calcium carbonate and titanium dioxide;• low coefficient of friction, stable in time;• without coating or primer.

APPLICATION:• High quality solvent rotogravure and flexographic printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue;

Properties Methods Unit LOBB

Thickness, ± 5%

BIAXPLEN

mkm 33 35 38 47


Weight, ± 5% g/m2 20,46 21,70 23,56 29,14

Yield, ± 5% m2/kg 48,88 46,08 42,44 34,32



N/mm2, MPa75

TD 145


%190

TD 65

Coefficient of friction, kinetic UT/UT GOST 27492 ISO 8295 ASTM D 1894 — 0,3+0,10

-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Light transmission, not more GOST 15875 ISO 14782 ASTM D 1003 % 30 25

Whiteness index * BIAXPLEN — 78 80

Gloss at 45˚, not less T BIAXPLEN ISO 2813 ASTM D 2457 % 85


mN/m38

MD — Machine direction T — Treated side of the film TD — Transverse direction UT — Untreated side of the film GOST — Russian Federation standards* Typical value

68

LABEL FILMS

Biaxplen LOBC

DESCRIPTION:White Pearlised microporous BOPP film for fully wrapped labeling of bottles for cold and hot melt glue application while labeling with very high yield good gloss and good ink adhesion.

B Modified copolymer corona treated skin layer




F Glossy non heat sealable, non corona treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• Very low density and very high yield;• high adhesion of solvent based inks: flexo and rotogravure for printing;• both side glossy film;• good opacity and whiteness;• contains mineral fillers such as calcium carbonate and titanium dioxide;• contains slip, antistatic and antiblock additives;• low coefficient of friction, stable in time;• without coating or primer.

APPLICATION:• High quality solvent based rotogravure and flexographic printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.

Properties Methods Unit LOBC

Thickness, ± 5%

BIAXPLEN

mkm 38 47

Density* g/cm3 0,60

Weight, ± 5% g/m2 22,80 28,20

Yield, ± 5% m2/kg 43,86 35,46



N/mm2, MPa70

TD 140


%180

TD 60


-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2



Treatment level, not less Т BIAXPLEN ISO 8296 ASTM D 2578 Dyne/cm, mN/m 38


70

LABEL FILMS

Biaxplen LOHM.М

DESCRIPTION:White Pearlised metallized microporous BOPP film for labeling of bottles, for cold and hot melt glue application while labeling.

B High glossy aluminum layer

C Modified layer for aluminum adhesion

D Oriented polypropylene tie layer

E White Pearl cavitated core layer of orinted polypropylene

F Oriented polypropylene tie layer

G Glossy non heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• Very smoth surface and high gloss metallized side;• excellent adhesion of the aluminum layer;• lower density, high opacity and good whiteness;• permanent coefficient of friction and good mechanical properties;• contains an organic dye pearl and non-migratory slip additives;• intended for contact with food;• without coating and primer.

APPLICATION:• High quality solvent based rotogravure and flexographic direct printing;• for production of fully wrapped labels for bottles;• for labeling with cold and hot melt glue.

Properties Methods Unit LOHM.М

Thickness, ± 5%

BIAXPLEN

mkm 35 38

Density* g/cm3 0,71

Weight, ± 5% g/m2 24,85 26,98

Yield, ± 5% m2/kg 40,24 37,06



N/mm2, MPa90

TD 180


%200

TD 70


-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Optical density, not less BIAXPLEN О.D. 1,8

Treatment level, not less** Т BIAXPLEN ISO 8296 ASTM D2578 Dyne/cm, mN/m 36

MD — Machine, longitudinal direction T — Metallized side TD — Transverse direction UT — White pearl, non treated side GOST — Russian Federation standards * Typical value ** Garanteed shelf life of the activation of the metallized side is 15 days from the date of manufacture indicated on roll label

72

LABEL FILMS

Biaxplen LOMB

DESCRIPTION:Matt White Pearlised microporous BOPP film for fully wrapped labeling of bottles.

B Matt white corona treated skin layer




F Glossy non heat sealable, non treated skin layer with standard coefficient of friction

MAIN PROPERTIES:• Matt white, paper appearance;• high adhesion printing;• good opacity and whiteness;• contains slip, antistatic and antiblock additives;• contains mineral fillers such as calcium carbonate and titanium dioxide;• low coefficient of friction, stable in time;• without coating or primer.

APPLICATION:• High quality solvent based printing;• for production of fully wrapped labels of bottles;• for labeling with cold and hot melt glue.

Properties Methods Unit LOMB

Thickness, ± 5%

BIAXPLEN

mkm 35 38 47

Density* g/cm3 0,68

Weight, ± 5% g/m2 23,80 25,84 31,96

Yield, ± 5% m2/kg 42,02 38,70 31,29



N/mm2, MPa80

TD 150


%200

TD 70


-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2





74

LABEL FILMS

Biaxplen LGBL

DESCRIPTION:Transparent BOPP film for the production of transparentself-adhesive labels (SAL)

B Corona treated copolymer skin layer (OUT)


D Corona treated copolymer skin layer (IN)

MAIN PROPERTIES:• Transparent both side corona treated film• OUT side for primer coating and printing• IN side for coating by adhesives• No migratory additives• High adhesion to printing and adhesives• Good optical properties: transparency and gloss• Good mechanical properties• Without coating or primer

APPLICATION:• Production of transparent self adhesive labels (SAL)• Coating by primer and glue• Solvent and UV — based printing

Properties Methods Unit LGBL

Thickness, ± 5%

BIAXPLEN

mkm 40 48 50 58


Weight, ± 5% g/m2 36,40 43,68 45,50 52,78

Yield, ± 5% m2/kg 27,47 22,89 21,98 18,95



N/mm2, MPa140

TD 280


%200

TD 70

Kinetic coefficient of friction * IN / IN GOST 27492 ISO 8295 ASTM D 1894 — 0,5

+ 0,10

- 0,10


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Haze, not more GOST 15875 ISO 14782 ASTM D 1003 % 3,5

Gloss at 45˚, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 %

Treatment level, not lessOUT

BIAXPLEN ISO 8296 ASTM D 2578Dyne/cm,

mN/m

38

IN 36

MD — Machine, longitudinal direction IN — Internal side of the roll TD — Transverse direction OUT — External side of the roll GOST — Russian Federation standards* Typical, background values

76

LABEL FILMS

Biaxplen LWBL

DESCRIPTION:Solid white BOPP filmfor production of self adhesive labels (SAL)

B Сorona treated glossy copolymer skin layer (OUT)

C Polypropylene tie layer

D Solid white core layer of oriented polypropylene

E Polypropylene tie layer

F Corona treated glossy skin layer (IN)

MAIN PROPERTIES:• Both side corona treated solid white film• Excellent whiteness• OUT side for primer coating and printing• IN side for coating by adhesives• No migratory additives• High adhesion to printing and adhesives• Contains mineral filler titanium dioxide• Intended for contact with food• Without primers or coating

APPLICATION:• Production of self adhesive labels (SAL)• Coating by primer and glue• For solvent and UV based printing

Properties Methods Unit LWBL

Thickness, ± 5%

BIAXPLEN

mkm 40 50 60


Weight, ± 5% g/m2 38,40 48,00 57,60

Yield, ± 5% m2/kg 26,04 20,83 17,36



N/mm2, MPa120

TD 230

Elongation at break, not more.MD

%200

TD 70

Coefficient of friction, kinetic * IN / IN GOST 27292 ISO 8295 ASTM D 1894 — 0,50

+0,10

-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


Gloss at 45˚, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 45

Treatment level, not lessOUT


mN/m

38

IN 36

MD — Machine, longitudinal direction IN — Internal side of the roll TD — Transverse direction OUT — External side of the roll GOST — Russian Federation standards* Typical values

78

LABEL FILMS

Biaxplen SOI

DESCRIPTION:White Pearl BOPP film. Synthetic paper.for production of self adhesive labels (SAL)

B Glossy corona treated copolymer skin layer (T)

C Polypropylene tie layer



F Corona treated white matt skin layer (UT)

MAIN PROPERTIES:• White-Pearl both side corona treated film• One side gloss second side matt film• Low density, high opacity and whiteness• No migratory additives• Contains mineral fillers calcium carbonate and titanium dioxide• Intended for contact with food• High adhesion to printing and glue• Without primers or coating

APPLICATION:• Production of self adhesive labels (SAL)• As synthetic paper, if necessary• Coating by primer and glue• For solvent and UV based printing

Properties Methods Unit SOI

Thickness, ± 5%

BIAXPLEN

mkm 50 60 70


Weight, ± 5% g/m2 36,50 43,80 51,10

Yield, ± 5% m2/kg 27,40 22,83 19,57



N/mm2, MPa70

TD 130


%180

TD 60

Coefficient of friction, kinetic * UT / UT GOST 27292 ISO 8295 ASTM D 1894 — 0,50

+0,10

-0,15


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2


Gloss at 45˚, not less TBIAXPLEN ISO 2813 ASTM D 2457 %

50

Gloss at 45˚, not more UT 13

Treatment level, not lessT


mN/m

38

UT 36

MD — Machine direction T — Glossy side TD — Transverse direction UT — Matte side GOST — Russian Federation standards * Typical value

80

LABEL FILMS

Biaxplen SOIL

DESCRIPTION:White Pearl BOPP film for productionof in mould labels (IML)

B Glossy corona treated skin layer (T)

C Oriented polypropylene tie layer



F Corona treated white matt skin layer (UT)

MAIN PROPERTIES:• Special antistatic properties• Low density, high opacity, high yield and high gloss• Both side corona treated film• Glossy side (T) for primer coating and printing• Matte side (UT) for injection moulding with polypropylene• Contains migratory and non-migratory additives• Intended for contact with food• Without primers or coating

APPLICATION:• The basis for the production of in-mold labels (IML)• Printing with solvent and UV based inks• For polypropylene injection moulding• Pre-testing is required before industrial use

Properties Methods Unit SOIL

Thickness, ± 5%

BIAXPLEN

mkm 60 65 68 70


Weight, ± 5% g/m2 33,00 35,75 37,40 38,50

Yield, ± 5% m2/kg 30,30 27,97 26,74 25,97



N/mm2, MPa70

TD 130


%180

TD 60


GOST 18616 ISO 11501 ASTM D1204 %4

TD 2

Light transmission, not more ГОСТ 15875 ISO 14782 ASTM D 1003 % 25

Gloss at 45˚, not lessT

— ISO 2813 ASTM D 2457 %85

UT 13

Treatment level, not lessT

BIAXPLENDyne/cm,

mN/m

38

UT 36

MD — Machine direction T — Glossy side TD — Transverse direction UT — Matte side GOST — Russian Federation standards* Typical value

82

TOBACCO FILMS

Biaxplen TSHL

DESCRIPTION:Thermo shrinkable transparent BOPP film for general purposes with a wide heat sealing range and low coefficient of friction for “rigid” carton pack overwrapping on high speed machines.

B Non treated skin layer (OUT) with a low coefficient of friction and low heat sealingt threshold

C Transparent oriented modified polypropylene

D Non treated skin layer (IN) with a bit higher coefficient of friction and low heat sealing threshold

MAIN PROPERTIES:• Contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• stable low coefficient of friction, including the heated surfaces;• medium shrinkage film;• excellent optical properties;• good physical and mechanical properties and increased stiffness;• intended for contact with food;• without coating.

APPLICATION:• Overwrapping of the “rigid” cardboard packs on the horizontal high speed machines;• for tight carton packs overwrapping due to shrinkability of the film;• wrapping cardboard packs of tea, zephyr, cigarette cardboard blocks, etc.;• mainly for machines with heat tunnel;• also for machines without a heat tunnel in which the shrinkage of the film occurs due

to heating of the weld;• for tight overwrapping of small and medium-sized carton packs.

Properties Methods Unit TSHL

Thickness, ± 5%

BIAXPLEN

mkm 16 18 20

Density* g/cm3 0,91

Weight, ± 5% g/m2 14,56 16,38 18,2

Yield, ± 5% m2/kg 68,68 61,05 54,95



N/mm2, Mpa150

TD 260


%180

TD 65

Kinetic coefficient of frictionIN/IN

GOST 27492 ISO 8295 ASTM D 1894 — 0,30 + 0,05

OUT/OUT 0,25 -0,10

Thermal shrinkage at 120 °C, 5 minMD

GOST 18616 ISO 11501 ASTM D1204 %6,5 - 9,0

TD 6,5 - 9,0

Heat Seal strength at 1 bar, 1 sec, 130 °C, not less IN/OUT GOST 27319 ISO 527ASTM D 882, ASTM

F 88N/15 mm 2,5

Haze, no more GOST 15875 ISO 14782 ASTM D 1003 % 2,5

Gloss at 45 °, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 85

Heat sealing range at 1 bar, 1 sec.* OUT/OUT BIAXPLEN °C 105 - 140

MD — Machine, longitudinal direction of the film IN — Internal film side of the reel TD — Transverse direction of the film OUT — External film side of the reel GOST — Russian Federation standards * Typical value

84

TOBACCO FILMS

Biaxplen TSHD

DESCRIPTION:Transparent heat shrinkable BOPP film with a wide heat sealing range and low coefficient of friction specially designed for cigarette and tea carton packs overwrapping in high speed machines.

B Non treated skin layer (OUT) with very low coefficient of friction and low heat sealingt threshold


D Non treated skin layer (IN) with a bit higher coefficient of friction and low heat sealing threshold

MAIN PROPERTIES:• Scratch and abrasion resistant;• contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• stable low coefficient of friction, including the heated surfaces;• medium shrinkage film;• excellent optical properties;• good physical and mechanical properties and high stiffness;• intended for contact with food;• without coating.

APPLICATION:• For carton cigarette packs overwrapping, including on ultra high speed machines with

speed up to 1000 p/min;• overwrapping of the “rigid” cardboard packs on the horizontal high speed machines;• for tight carton packs overwrapping due to shrinkability of the film;• wrapping cardboard packs of tea, zephyr, cigarette cardboard blocks, etc.;• mainly for machines with heat tunnel;• also for machines without a heat tunnel in which the shrinkage of the film occurs due


Properties Methods Unit TSHD

Thickness, ± 5%

BIAXPLEN

mkm 16 18 20 25

Density* g/cm3 0,91

Weight, ± 5% g/m2 14,56 16,38 18,2 22,75

Yield, ± 5% m2/kg 68,68 61,05 54,95 43,96



N/mm2, MPa140

TD 260


%180

TD 70

Flexural modulus*MD

N/mm2, MPa2700

TD 4500

Kinetic coefficient of frictionIN/IN

GOST 27492 ISO 8295 ASTM D 1894 — 0,20

± 0,05OUT/OUT 0,15

Thermal shrinkage at 120 °C, 5 min*MD

GOST 18616 ISO 11501 ASTM D1204 %

8,5± 1,0

TD 6,5

Thermal shrinkage at 130 °C, 15 min*MD 13

± 2,0TD 13

Heat Seal strength at 1 bar, 1 sec, 130 °C, not less IN/OUT GOST 27319 ISO 527ASTM D 882, ASTM F 88

N/15 mm 2,5


Gloss at 45 °, not less OUT BIAXPLEN ISO 2813 ASTM D 2457 % 85

Heat sealing range at 1 bar, 1 sec.* OUT/OUT BIAXPLEN °C 105 - 140

MD — Machine, longitudinal direction of the film IN — Internal film side of the reel TD — Transverse direction of the film OUT — External film side of the reel GOST — Russian Federation standards * Typical value

86

TOBACCO FILMS

Biaxplen TSHT

DESCRIPTION:Heat shrinkable transparent corona treated BOPP film with a wide heat sealing range and low coefficient of friction designed for printing for cigarette and other carton packs overwrapping in high speed machines.

B Non treated skin layer with very low coefficient of friction and low heat sealing threshold (UT)


D Corona treated skin layer with a higher coefficient of friction and low heat sealing threshold (T)

MAIN PROPERTIES:• Scratch and abrasion resistant;• treated for printing;• contains antistatic and slip-antilock additives;• non symmetric coefficient of friction of the film for packs tight overwrapping;• stable low coefficient of friction, including the heated surfaces;• medium shrinkage film;• excellent optical properties;• good physical and mechanical properties and high stiffness;• intended for contact with food;• without coating or primer;• when the shipment is for the printing, activation is OUT (specify in order);• when the shipment is for the packaging wrapping, activation is IN (specify in order).

APPLICATION:• For carton cigarette packs overwrapping, including on ultra high speed machines with

speed up to 1000 p/min;• for solvent based flexographic and rotogravure printing with special inks;• overwrapping of the “rigid” cardboard packs on the horizontal high speed machines;• for tight carton packs overwrapping due to shrinkability of the film;• wrapping cardboard packs of tea, zephyr, cigarette cardboard blocks, etc.;• mainly for machines with heat tunnel;• also for machines without a heat tunnel in which the shrinkage of the film occurs due


Properties Methods Unit TSHT

Thickness, ± 5%

BIAXPLEN

mkm 16 18 20 25

Density* g/cm3 0,91

Weight, ± 5% g/m2 14,56 16,38 18,2 22,75

Yield, ± 5% m2/kg 68,68 61,05 54,95 43,96



N/mm2, Mpa150

TD 260


%180

TD 70

Flexural modulus*MD

N/mm2, MPa2700

TD 4500

Kinetic coefficient of frictionT/T

GOST 27492 ISO 8295 ASTM D 1894 — 0,25

± 0,05UT/UT 0,15

Thermal shrinkage at 120 °C, 5 min*MD

GOST 18616 ISO 11501 ASTM D1204 %

8,5± 1,0

TD 6,5

Thermal shrinkage at 130 °C, 15 min*MD 12

± 2,0TD 12

Heat Seal strength at 1 bar, 1 sec, 130 °C, not less T/UT GOST 27319 ISO 527ASTM D 882, ASTM F 88

N/15 mm 2,5


Gloss at 45 °, not less UT BIAXPLEN ISO 2813 ASTM D 2457 % 85



MD — Machine, longitudinal direction of the film T — Treated side of the film TD — Transverse direction of the film UT — Untreated side of the film GOST — Russian Federation standards * Typical value

BIAXPLEN LTD16/1 Krzhizhanovskogo st., Moscow Russia 117997 +7 (495) 777 5500

CHIEF OF MARKETING DEPARTMENTMatveev Dmitry +7 (495) 777 5500 ext. 2508 [email protected]

Vinogradova Maria +7 (495) 777 5500 ext. 2631 [email protected]

Mkrtycheva Karina +7 (495) 777 5500 ext. 6811 [email protected]

CUSTOMER SERVICESmirnova Nadezhda +7 (495) 777 5500 ext. 2609 [email protected] [email protected]

CUSTOMER TECHNICAL SUPPORTOlkhovikova Evgeniya +7 (495) 527 9784, ext. 1243 +7 (495) 777 5500, ext. 4549 +7 (985) 217 0473 [email protected]

PRODUCT DEVELOPMENTMaksim Fedorov +7 (495) 527 9784, ext. 1240 +7 (916) 033 2881 [email protected]

SALESIlja Tultschinsky +43 1 370 8000 ext. 61 +43 664 188 1978 [email protected]

Tatyana Mironenko +43 1 370 8000 ext. 819 +43 664 887 392 98 [email protected]

Maxim Nordas +43 1 370 8000 ext. 868 +43 664 88738157 [email protected]

CHIEF OF MULTINATIONAL SALES Natalya Malkova +7 (495) 733 9318 ext. 2604 +7 (916) 531 2732 [email protected]

www.sibur.ru/biaxplen