![Page 1: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/1.jpg)
Dominique Carrouge
Houston
February 2002
• Phase Transformation Group • H. K. D. H. Bhadeshia
• MCAS Technology Group • Dr. P. Woollin
![Page 2: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/2.jpg)
Microstructural Change in HighTemperature Heat-Affected
Zones of Welded
![Page 3: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/3.jpg)
Why this project ?
Super Martensitic SS are :
• Increasingly employed in the Oil & Gas industries
• Cost effective alternative to Duplex SS
Engineered to be :
• High strength, Corrosion resistant, Weldable
But :
• Work on understanding microstructure development in HAZ could improve service properties
![Page 4: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/4.jpg)
Phases in HAZ
• Low carbon martensite (ok) • Retained austenite (ok)• Delta-ferrite (?)
• Can reduce toughness and corrosion resistance !
![Page 5: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/5.jpg)
Aim
• Understand HAZ microstructure• Locate delta-ferrite in HAZ of single-pass and
multi-pass welds• Investigate effect of some welding parameters• Predict ferrite retention
![Page 6: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/6.jpg)
HAZ & Phase diagram
Ae5
Ae4
Ae3
![Page 7: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/7.jpg)
Single-pass weld
• Plate : 5 mm thick• Mechanised TIG process• No filler material• Heat-input : 0.7 kJ/mm
Steel A (UNS S41426) : 0.01 C, 12 Cr, 6.5 Ni, 2.5Mo
![Page 8: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/8.jpg)
Microstructure
• Electrolytic sulphuric acid• Villela’s reagent
![Page 9: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/9.jpg)
Coarse-Grained HAZ
![Page 10: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/10.jpg)
Widmanstätten Austenite
Ferrite
(now martensite)
Amount of ferrite negligible
![Page 11: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/11.jpg)
Dual Phase HAZ
• ~ 20 % ferrite • DPHAZ maximum length : 1 mm
![Page 12: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/12.jpg)
X-ray Mapping of Ferrite
MoMo
CrCr
NiNi
Partitioning during
welding !
![Page 13: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/13.jpg)
Less ferrite with high heat-input
0.7 kJ/mm 0.3 kJ/mm
Slow cooling rate Fast cooling rate
Steel A : 0.01 C, 12 Cr, 6.5 Ni, 2.5Mo
![Page 14: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/14.jpg)
Situation in multi-pass weld
Steel A : 0.01 C, 12 Cr, 6.5 Ni, 2.5Mo
• 12 mm thick pipe
• HI : 0.4 - 1.2 kJ/mm
• 25 Cr Duplex filler wire
• 7 passes TIG + MMA
![Page 15: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/15.jpg)
Ferrite distribution
Root
Cap
Fast cooling rate
Slow cooling rate
![Page 16: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/16.jpg)
Modelling ferrite content
• Physical model need reliable thermodynamic data• MT DATA software has been used• Prediction of equilibrium phase transformation
temperatures and volume fractions
A : 0.01 C, 12 Cr, 6.5 Ni, 2.5Mo
B : 0.01 C, 11 Cr, 1.5 Ni, 0.5 Cu
C : 0.01 C, 12 Cr, 3 Ni
1223oC1255oC1235oC
Ae4
![Page 17: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/17.jpg)
High temperature dilatometry
• Heating rate : 10 K/min
Ae4
![Page 18: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/18.jpg)
Comparison
• Poor agreement• Lack of data in the
database• Physical Modelling
cannot be used
![Page 19: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/19.jpg)
Neural network model
• Non linear regression tool that can be used to make extrapolation and predictions
• Not enough data to create a neural network model due to difficulty to measure ferrite content in Martensitic SS
• But a model has been developed for predicting ferrite retention in Austenitic stainless steels
• For a given composition the Ferrite Number can be estimated
http://www.msm.cam.ac.uk/phase-trans/2001/ferrite.number.html/index.html
![Page 20: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/20.jpg)
To avoid ferrite
Minimum level of Nickel required to minimise ferrite :
![Page 21: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/21.jpg)
To avoid ferrite
Minimum level of Nickel required to minimise ferrite :
![Page 22: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/22.jpg)
To avoid ferrite
Minimum level of Nickel required to minimise ferrite :
![Page 23: Dominique Carrouge Houston February 2002 Phase Transformation Group H. K. D. H. Bhadeshia MCAS Technology Group Dr. P. Woollin](https://reader036.vdocuments.net/reader036/viewer/2022081603/56649d7a5503460f94a5e61d/html5/thumbnails/23.jpg)
Summary &Conclusion• HT-HAZ microstructure has been studied• Volume fraction of ferrite trapped in HAZ are small• Mo containing alloy retain more ferrite
Effects of this ferrite on properties are not well established
But if ferrite content is to be minimised :• Slower cooling rate would reduce ferrite content• Alloy chemical composition could be adjusted
Thank you for your attention