DAY 1 ---------->>>
TOPICS
• INRODUCTION
• HISTORY
• BASICS
1
![Page 2: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/2.jpg)
INRODUCTION:
• Ultrasonic Testing (UT) uses high frequency sound energy to conduct examinations and make measurements.
• Ultrasonic inspection can be used for flaw detection/evaluation, dimensional measurements, material characterization, and more.
2
![Page 3: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/3.jpg)
• The sound energy is introduced and propagates through the materials in the form of waves.
• When there is a discontinuity (such as a crack) in the wave path, part of the energy will be reflected back from the flaw surface.
• The reflected wave signal is transformed into electrical signal by the transducer and is displayed on a screen.
3
![Page 4: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/4.jpg)
See below fig
delamination plate
0 2 4 6 8 10
IP
F
BE
4
![Page 5: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/5.jpg)
Ultrasonic Inspection is a very useful and versatile NDT method.
Some of the advantages of ultrasonic inspection that are often cited include:
• It is sensitive to both surface and subsurface discontinuities.
• The depth of penetration for flaw detection or measurement is superior to other NDT methods.
• Only single-sided access is needed when the pulse-echo technique is used.
5
![Page 6: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/6.jpg)
• It is high accuracy in determining reflector position and estimating size and shape.
• Minimal part preparation required.
• Electronic equipment provides instantaneous results.
• Detailed images can be produced with automated systems.
• It has other uses such as thickness measurements, in addition to flaw detection.
6
![Page 7: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/7.jpg)
As with all NDT methods, ultrasonic inspection also has its limitations, which include:
• Surface must be accessible to transmit ultrasound.
• Skill and training is more extensive than with some other methods.
• It normally requires a coupling medium to promote transfer of sound energy into test specimen.
7
![Page 8: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/8.jpg)
• Materials that are rough, irregular in shape, very small, exceptionally thin or not homogeneous are difficult to inspect.
• Cast iron and other coarse grained materials are difficult to inspect due to low sound transmission and high signal noise.
• Linear defects oriented parallel to the sound beam may go undetected.
• Reference standards are required for both equipment calibration, and characterization of flaws.
8
![Page 9: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/9.jpg)
Applications:
• Ultrasonic inspection is used for quality control and materials inspection in all major industries.
• Ultrasonic inspection is used for finding flaws in production of metallic and composite materials.
• It is used in fabrication of structures such as airframes, piping and pressure vessels, ships, motor vehicles, machinery , jet engines and submarines.
9
![Page 10: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/10.jpg)
• In-service ultrasonic inspection for preventive maintenance is used for detecting the impending failure of rails, rolling-stock axils, mill rolls, mining equipment and nuclear systems.
• And also used for thickness measurement in refinery and chemical pressure vessels
• And many more in medical , rail track inspection, liquid height measurements, material analysis.
• Etc…..
10
![Page 11: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/11.jpg)
HISTORY:
UT is the discovery of Curie the brothers in 1880 that the quartz crystal cut in a certain way produces an electric potential subjected to pressure.
In 1881 Lippmann theorized that the effect might work in reverse.
In 1929 Russian physicist sokolov experimented with the techniques of passing the vibration to metals to find the flaws.
The first flaw detector was made by D O Sproule in 1942.
11
![Page 12: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/12.jpg)
• Prior to World War II, sonar, the technique of sending sound waves through water and observing the returning echoes to characterize submerged objects, inspired early ultrasound investigators to explore ways to apply the concept to medical diagnosis.
• in 1931, obtained a patent for using ultrasonic waves, using two transducers to detect flaws in solids. Firestone (1940) and Simons (1945) developed pulsed ultrasonic testing using a pulse-echo technique.
12
![Page 13: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/13.jpg)
• Shortly after the close of World War II, researchers in Japan began to explore medical diagnostic capabilities of ultrasound. The first ultrasonic instruments used an A-mode presentation with blips on an oscilloscope screen. That was followed by a B-mode presentation with a two dimensional, gray scale imaging.
• Japan was also the first country to apply Doppler ultrasound, an application of ultrasound that detects internal moving objects such as blood coursing through the heart for cardiovascular investigation.
13
![Page 14: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/14.jpg)
BASICS:
WHAT IS ULTRASONIC:
• It is a High frequency Sound.
• We generate the Ultrasonic Sound sound by using piezo electric crystals
14
![Page 15: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/15.jpg)
What is sound, frequency
• Sound is a mechanical vibration (oscillation) of particles in a medium.
• Sound travels in a medium(where particles are present) but not in vacuum.
• Particles are oscillating and comes in contact with another particles and form a wave form.
15
![Page 16: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/16.jpg)
Examples of oscillation
ball on a spring
pendulum rotating earth
16
![Page 17: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/17.jpg)
Oscillation
17
![Page 18: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/18.jpg)
18
![Page 19: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/19.jpg)
In vibratory motion the motion in which a body moves to and fro repeatedly in a fixed interval of time about a fixed point is called mean position. Mean position is also called equilibrium position or zero position.
19
![Page 20: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/20.jpg)
• The deviation of a vibrating or oscillating body from the mean position of oscillation with time is called displacement.
20
![Page 21: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/21.jpg)
gas liquid solid
Atomic structures
• low density
• weak bonding forces
• medium density
• medium bonding forces
• high density
• strong bonding forces
• crystallographic structure
21
![Page 22: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/22.jpg)
Understanding wave propagation:
Spring = elastic bonding force Ball = atom
22
![Page 23: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/23.jpg)
T
distance travelled
23
![Page 24: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/24.jpg)
Frequency:
• Number of oscillations for second
• Its measured in Hertz(Hz)
• 1 OSCILATION 2 OSILATIONS
24
![Page 25: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/25.jpg)
• FREQUENCY
In 1second 1 oscillation so frequency 1 Hz In 1 second 2 oscillation frequency 2 Hz
1sec 1sec> 2cycles=2Hz frequency
1 cycle=1Hz
25
![Page 26: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/26.jpg)
• One vibration in one second is called One Hertz
• Ten vibration in one second is called Ten Hertz
• One thousand vibrations in one second is called One Kilohertz( kHz)
• One million vibrations in one second is called One Megahertz ( MHz)
26
![Page 27: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/27.jpg)
• The distance travelled by a wave at one complete cycle is called wave length.
• Wave length is denoted by lambda(λ).
27
![Page 28: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/28.jpg)
• The minimum time taken to complete one complete vibration is called time period.
• Time period is denoted by ‘T’.
28
![Page 29: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/29.jpg)
• The force which tends the vibrating particles towards its mean position is called restoring force of vibrating particles.
29
![Page 30: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/30.jpg)
DISPLACEMENT(λ)
• VELOCITY = _______________ (mts/sec)
TIME PERIOD(T)
VELOCITY= λ*F
WHERE FREQUENCY (F) = 1/T
• c = λ × f ; λ = c / f = c × T ; f = c / λ
30
![Page 31: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/31.jpg)
Wavelength = Velocity Frequency or = V F If we want to know the wavelength of a 2 Megahertz compression wave traveling through steel, we can use the formulae as we know compression sound speed of sound in steel is, 5920 meters per second. = 5,920 2,000,000 = 2.96 mm
31
![Page 32: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/32.jpg)
DAY 2
TOPICS 1. PROPERTIES OF ULTRASONIC WAVES
2.MODES OF SOUND ENERGY 3.PRINCIPAL OF UT
4.REFLECTION ,TRANMISION , RAREFRACTION , DIFRACTION
5.SNELLS LAW 32
![Page 33: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/33.jpg)
SPECTROM OF SOUND:
Frequency range Hz Description Example
0 - 20 Infrasound Earth quake
20 - 20.000 Audible sound Speech, music
> 20.000 Ultrasound Bat, Quartz crystal
33
![Page 34: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/34.jpg)
34
![Page 35: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/35.jpg)
35
![Page 36: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/36.jpg)
General we are using 0.5 M Hz to 10 M Hz Ultrasonic Frequencies.
In special testing's we go for up to 25 M Hz also(Immersion Testing)
For high thickness, high grain size materials we are using low frequencies bcoz low frequencies travels more distances and less attenuation.
36
![Page 37: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/37.jpg)
• High frequencies are give good sensitivity and resolution
• But these high frequencies are more attenuated due to high grain sizes and more thickness.
• High frequency low frequency
37
![Page 38: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/38.jpg)
Factors Affecting the propagation of ultra sound:
The propagation of ultrasound in a material I depend on the density elastic properties of the material and type of the wave transmitted.
The test material grain size Attenuation( scattering, absorption) Acoustic impedance of the material Characteristic impedance of inclusion Diffraction Lack of homogeneity Anisotropic material
38
![Page 39: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/39.jpg)
Attenuation of Sound Wave
o When sound travels through a medium, its intensity diminishes with distance. In idealized materials, sound pressure (signal amplitude) is only reduced by the spreading of the wave.
o Natural materials, however, all produce an effect which further weakens the sound. This further weakening results from two basic causes,
o which are scattering and absorption.
39
![Page 40: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/40.jpg)
• Scatter:
This is the major cause of attenuation and is the redirection of the sound waves reflecting off grain boundaries, porosity and non-metallic inclusions, etc.,
And becomes more apparent on the inspection when the size of grain become of the wavelength of the search unit being employed.
40
![Page 41: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/41.jpg)
41
![Page 42: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/42.jpg)
• ABSORPTION:- • As the sound travel through a material a small amount of
the energy is used up by the interaction of the particles, as they vibrate, causing friction which is dissipated as heat.
• As the frequency of the sound is increased the attenuation
increases due to more particle vibration and increased sensitivity to small reflectors which is related to the wavelength of the sound.
• Materials such as castings and austenitic stainless steel are
highly attenuative due to their coarse grain structures, etc., • The attenuation factor of material can be measured and is
expressed in db/mm.
42
![Page 43: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/43.jpg)
• Natural attenuation also occurs due to the divergence of the beam in the far zone, i.e. assuming compression probe use, the amplitude of the backwall echo will be halved(-6db) every time the distance from the probe is doubled.
• Materials such as castings and austenitic stainless steel are highly attenuative due to their coarse grain structures, etc.,
• The attenuation factor of material can be measured and is expressed in db/mm. natural attenuation also occurs due to the divergence of the beam in the far zone, i.e. assuming compression probe use, the amplitude of the backwall echo will be halved(-6db) every time the distance from the probe is doubled.
43
![Page 44: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/44.jpg)
44
![Page 45: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/45.jpg)
α=αs+αa
where α is attenuation constant αs scattering constant
αa absorption constant
45
![Page 46: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/46.jpg)
Reflection, Transmission:
46
![Page 47: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/47.jpg)
• Reflection:
How much sound energy coming back while hitting an interface.
• Transmission:
How much energy transmitted from one medium to another medium.
47
![Page 48: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/48.jpg)
Reflection and Transmission Coefficients
• Ultrasonic waves are reflected at boundaries where there is a difference in acoustic impedances (Z) of the materials on each side of the boundary. (See preceding page for more information on acoustic impedance.)
• This difference in Z is commonly referred to as the impedance mismatch. The greater the impedance mismatch, the greater the percentage of energy that will be reflected at the interface or boundary between one medium and another.
48
![Page 49: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/49.jpg)
T= 1-R R= Parentage of reflection coefficient
T= Percentage of Transmission coefficient
Where Z= pV p= Density of material
V=Sound velocity in that material 49
![Page 50: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/50.jpg)
As soon as a sound wave comes to a change in material characteristics e.g. the surface of a workpiece, or an internal inclusion, wave propagation will change too:
50
![Page 51: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/51.jpg)
Behaviour at an interface
Medium 1 Medium 2
Interface
Incoming wave Transmitted wave
Reflected wave
51
![Page 52: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/52.jpg)
Reflection + Transmission: Perspex - Steel
Incoming wave Transmitted wave
Reflected wave
Perspex Steel
1,87
1,0 0,87
52
![Page 53: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/53.jpg)
Reflection + Transmission: Steel - Perspex
0,13
1,0
-0,87
Perspex Steel
Incoming wave Transmitted wave
Reflected wave
53
![Page 54: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/54.jpg)
54
![Page 55: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/55.jpg)
Amplitude of sound transmissions:
• Strong reflection
• Double transmission
• Less reflection
• Single transmission
• Strong reflection with inverted phase
• No transmission
Water - Steel Copper - Steel Steel - Air
55
![Page 56: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/56.jpg)
UT Principle (Acoustic impedance mismatch)
• Acoustic Impedance • Sound travels through materials under the influence
of sound pressure. • Because molecules or atoms of a solid are bound
elastically to one another, the excess pressure results in a wave propagating through the solid.
• The acoustic impedance (Z) of a material is defined as the product of density (p) and acoustic velocity (V) of that material.
Z = pV
56
![Page 57: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/57.jpg)
• Acoustic impedance is important in
• The determination of acoustic transmission and reflection at the boundary of two materials having different acoustic impedance
• The design of ultrasonic transducers.
• Assessing absorption of sound in a medium.
57
![Page 58: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/58.jpg)
TRANSDUCER
MATERIAL DISCONTINIUITY BACK WALL REFLECTION REFLECTION FROM DICONTINUITY
AMPLITUDE
INITIAL PULSE
DISCONTINUITY INDICATION
BACK WALL ECHO
HORIZONTAL SWEEP
PRINCIPLE OF ULTRASONIC TESTING
58
![Page 59: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/59.jpg)
Modes of sound waves: • In solids, sound waves can propagate in four principle
modes that are based on the way the particles oscillate.
• Sound can propagate as longitudinal waves, shear waves, surface waves, and in thin materials as plate waves.
• Longitudinal and shear waves are the two modes of
propagation most widely used in ultrasonic testing
59
![Page 60: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/60.jpg)
Wave Types in Solids Particle Vibrations
Longitudinal Parallel to wave direction
Transverse (Shear) Perpendicular to wave direction
Surface - Rayleigh Elliptical orbit - symmetrical mode
Plate Wave – Lamb Component perpendicular to surface (extensional wave)
Plate Wave – Love Parallel to plane layer, perpendicular to wave direction
Stoneley (Leaky Rayleigh Waves) Wave guided along interface
Sezawa Antisymmetric mode
60
![Page 61: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/61.jpg)
Reflection ,Rarefaction
• When an ultrasound wave passes through an interface between two materials at an oblique angle, and the materials have different indices of refraction, it produces both reflected and refracted waves.
• Refraction takes place at an interface due to the different velocities of the acoustic waves within the two materials.
61
![Page 62: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/62.jpg)
Angle of incidence=angle of reflection
62
![Page 63: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/63.jpg)
Snell law, mode conversion:
• Snell's Law describes the relationship between the angles and the velocities of the waves.
• Snell's law equates the ratio of material velocities V1 and V2 to the ratio of the sine's of incident (Q1) and refraction (Q2) angles, as shown in the following equation.
63
![Page 64: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/64.jpg)
Where:
VL1
is the longitudinal wave velocity in material 1.
VL2
is the longitudinal wave velocity in material 2.
64
![Page 65: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/65.jpg)
Mode Conversion • When sound travels in a solid material, one form of
wave energy can be transformed into another form.
• For example, when a longitudinal waves hits an interface at an angle, some of the energy can cause particle movement in the transverse direction to start a shear (transverse) wave.
• Mode conversion, occurs when a wave encounters an
interface between materials of different acoustic impedance and the incident angle is not normal to the interface.
65
![Page 66: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/66.jpg)
VL = VS = CL = CS
Sin1 Sin3 Sin4 Sin2
TRANSMISSION, REFLECTION & MODE CONVERSION OF
LONGITUDINAL WAVES AT AN INTERFACE
INCIDENT LONGITUDINAL WAVE VELOCITY = VL
REFLECTED LONGITUDINAL WAVE VELOCITY = VL
REFLECTED SHEAR WAVE VELOCITY = VS
TRANSMITTED SHEAR WAVE VELOCITY = CS
4
2
1
1
3
TRANSMITTED LONGITUDINAL WAVE VELOCITY = CL
MEDIUM - 1
MEDIUM - 2
INTERFACE
SNELL’S LAW
66
![Page 67: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/67.jpg)
Where: VL1 is the longitudinal wave velocity in material 1. VL2 is the longitudinal wave velocity in material 2.
VS1 is the shear wave velocity in material 1. VS2 is the shear wave velocity in material 2.
67
![Page 68: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/68.jpg)
68
![Page 69: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/69.jpg)
69
![Page 70: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/70.jpg)
• Diffraction: This occurs when sound waves pass the tip of a narrow
reflector. Some of the sound scatters off tip causing waves in different directions that reinforce or cancel out the original waves. This results in a series of high and low intensity waves radiating out from the tips, gives imperfection of sound bending around the edges of the defect.
70
![Page 71: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/71.jpg)
71
![Page 72: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/72.jpg)
• LONGITUDINAL WAVES:
• In longitudinal waves, the oscillations occur in the longitudinal direction or the direction of wave propagation.
• In compression and dilatational forces are active in these waves.
• They are also called pressure or compression waves. They are also sometimes called density waves because their particle density fluctuates as they move.
72
![Page 73: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/73.jpg)
• Compression waves can be generated in liquids, as well as solids because the energy travels through the atomic structure by a series of compression and expansion (rarefaction) movements.
• These waves are high velocities compare to other waves,
less sensitive and less attenuated. • Compression waves can be generated in liquids, as well as
solids because the energy travels through the atomic structure by a series of compression and expansion (rarefaction) movements.
• These waves are high velocities compare to other waves,
less sensitive and less attenuated. 73
![Page 74: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/74.jpg)
74
![Page 75: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/75.jpg)
Direction of oscillation
Direction of propagation Longitudinal wave
Sound propagation
75
![Page 76: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/76.jpg)
SHEAR WAVES:
• In the transverse or shear wave, the particles oscillate at a right angle or transverse to the direction of propagation.
• shear waves require an acoustically solid material for effective propagation and therefore are not effectively propagated in materials such as liquids or gasses.
• Shear wave are relatively weak when compared to longitudinal waves in fact, shear waves are usually generated in materials using some of the energy from longitudinal waves.
76
![Page 77: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/77.jpg)
Direction of propagation Transverse wave Direction of oscillation
Sound propagation
77
![Page 78: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/78.jpg)
78
![Page 79: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/79.jpg)
79
![Page 80: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/80.jpg)
Surface or Rayleigh waves:
• Surface or Rayleigh waves travel the surface of a relative thick solid material penetrating to a depth of one wavelength.
• The particle movement has an elliptical orbit as shown in the image and animation below.
• Rayleigh waves are useful because they are very sensitive to surface defects and since they will follow the surface around, curves can also be used to inspect areas that other waves might have difficulty reaching.
80
![Page 81: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/81.jpg)
• These waves are high sensitive compare to all other waves.
• These wave velocities are approximately 90% of shear waves in solids.
81
![Page 82: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/82.jpg)
• Surface waves are formed when shear waves refract to 90 degrees.
• Particle vibration is elliptical motion by changing direction at the interface with surface.
• Penetration depth is 1 wave length only.
• Their velocity is approximately 90% of shear waves of that material.
• These are high sensitive .
82
![Page 83: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/83.jpg)
83
![Page 84: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/84.jpg)
• Plate waves can be propagated only in very thin metals.
• Lamb waves are the most commonly used plate waves in NDT.
• Lamb waves are a complex vibrational wave that travels through the entire thickness of a material.
• Propagation of Lamb waves depends on density,
elastic, and material properties of a component, and they are influenced by a great deal by selected frequency and material thickness.
84
![Page 85: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/85.jpg)
With Lamb waves, a number of modes of particle vibration are possible, but the two most common are symmetrical and asymmetrical
85
![Page 86: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/86.jpg)
Typical Sound Velocities (m/sec)
Material Compression Shear
Air 332 N/A
Water 1480 N/A
Steel 5920 3250
Aluminum 6320 3130
Perspex 2730 1430
Copper 4700 2260
Brass 4430 2120
N/A= not applicable i.e. not travelling
86
![Page 87: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/87.jpg)
Direction of oscillation
Air
Water
Steel, long
Steel, trans
330 m/s
1480 m/s
3250 m/s
5920 m/s
87
![Page 88: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/88.jpg)
Day 3
• Topics
• Ultra sonic Sound generation
• Piezo electric materials
• Types of probes
• UT equipment
88
![Page 89: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/89.jpg)
ULTRAONIC SOUND GENERATION:
• Piezo electric crystals generates ultra sonic sound.
• Piezo electric crystals generates ultrasonic sounds when we are giving electrical signal to them.
89
![Page 90: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/90.jpg)
90
![Page 91: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/91.jpg)
91
![Page 92: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/92.jpg)
Natural Artificial Grown Manufactured Ceramics
Quartz Crystals Lithium Sulphate Barium Titanate Lead Zirconate Lead Metaniobate Lead Zirconate Titanate
92
![Page 93: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/93.jpg)
93
![Page 94: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/94.jpg)
94
![Page 95: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/95.jpg)
95
![Page 96: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/96.jpg)
96
![Page 97: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/97.jpg)
Crystal material Advantages Limitations
Quartz Stable ,Good Wear Resistance
Poor piezo electric properties
Lithium Sulphate Best Receiver and Easily Damped
Soluble in water
Barium Titanate Best Transmitter good piezo electric properties and may used as Focused beam
Less critical temperature
Lead Zirconate Good piezo electric properties
Lead Zirconate Titanate Good transmitter and Round properties
Poor silvering
97
![Page 98: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/98.jpg)
• Lead zerconate titanate crystal lattice:
98
![Page 99: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/99.jpg)
Crystal Thickness
Frequency depends on the thickness of the
crystal, according to the formula :
t = v
2f Where t=crystal thickness, v= sound velocity in crystal, f= frequency
99
![Page 100: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/100.jpg)
100
![Page 101: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/101.jpg)
101
![Page 102: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/102.jpg)
102
![Page 103: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/103.jpg)
• The conversion of electrical pulses to mechanical vibrations and the conversion of returned mechanical vibrations back into electrical energy is the basis for ultrasonic testing.
• The active element is the heart of the transducer as it converts the electrical energy to acoustic energy, and vice versa.
• The active element is basically a piece polarized material
103
![Page 104: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/104.jpg)
104
![Page 105: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/105.jpg)
Piezoelectric Effect
Piezoelectrical
Crystal (Quartz)
Battery
+
105
![Page 106: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/106.jpg)
+
The crystal gets thicker, due to a distortion of the crystal lattice
Piezoelectric Effect
106
![Page 107: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/107.jpg)
+
The effect inverses with polarity change
Piezoelectric Effect
107
![Page 108: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/108.jpg)
An alternating voltage generates crystal oscillations at the frequency f
U(f)
Sound wave with
frequency f
Piezoelectric Effect
108
![Page 109: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/109.jpg)
A short voltage pulse generates an oscillation at the crystal‘s resonant
frequency f0
Short pulse
( < 1 µs )
Piezoelectric Effect
109
![Page 110: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/110.jpg)
Reception of ultrasonic waves
A sound wave hitting a piezoelectric crystal, induces crystal vibration
which then causes electrical voltages at the crystal surfaces.
Electrical
energy Piezoelectrical crystal Ultrasonic wave
110
![Page 111: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/111.jpg)
Probe frequency , bandwidth & damping:
• UT probe transmits range of frequencies, this I know as bandwidth.
• For example 5 M Hz
• probe trans mitts 4 t0 6 M Hz
Broad band probes Narrow band probe
Highly damped Low damping
Short pulse length Longer pulse length
Less dead zone More dead zone
Good resolution Poor resolution
Poor penetration Good penetration 111
![Page 112: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/112.jpg)
Near zone, Far zone, Dead zone, Beam divergence
N
Near field Far field
Focus Angle of divergence Crystal Accoustical axis
D0
6
112
![Page 113: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/113.jpg)
113
![Page 114: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/114.jpg)
114
![Page 115: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/115.jpg)
• Since the ultrasound originates from a number of points along the transducer face, the ultrasound intensity along the beam is affected by constructive and destructive wave interference
• These are sometimes also referred to as diffraction effects in the NDT world.
• This wave interference leads to extensive fluctuations in the sound intensity near the source, known as the near field.
115
![Page 116: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/116.jpg)
• Because of acoustic variations within a near field, it can be extremely difficult to accurately evaluate flaws in materials when they are positioned within this area.
• The pressure waves combine to form a relatively
uniform front at the end of the near field. • The area beyond the near field where the ultrasonic
beam is more uniform is called the far field. • In the far field, the beam spreads out in a pattern
originating from the center of the transducer 116
![Page 117: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/117.jpg)
117
![Page 118: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/118.jpg)
Transducer Beam Spread
118
![Page 119: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/119.jpg)
• The energy in the beam does not remain in a cylinder, but instead spread out as it propagates through the material.
• The phenomenon is usually referred to as beam spread but is sometimes also referred to as beam divergence or ultrasonic diffraction.
119
![Page 120: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/120.jpg)
120
![Page 121: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/121.jpg)
Where: θ = Beam divergence angle from centerline to point
where signal is at half strength.
V = Sound velocity in the material. (inch/sec or cm/sec)
a = Radius of the transducer. (inch or cm)
D= Dia of probe=2a
F = Frequency of the transducer. (cycles/second)
Full beam angle Half beam angle (Beam spread) (Beam divergence)
121
![Page 122: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/122.jpg)
Low frequency HIGH FREQUENCY
Long wavelength Short wavelength
More beam spread Less beam spread
Shorter near zone Longer near zone
Better penetration Less penetration
Less attenuation More attenuation
Longer dead zone Shorter dead zone
Less sensitivity Higher sensitivity
122
![Page 123: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/123.jpg)
Transducers:
• The conversion of electrical pulses to mechanical vibrations and the conversion of returned mechanical vibrations back into electrical energy is the basis for ultrasonic testing.
• The active element is the heart of the transducer as it converts the electrical energy to acoustic energy, and vice versa. The active element is basically a piece polarized material
123
![Page 124: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/124.jpg)
124
![Page 125: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/125.jpg)
125
![Page 126: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/126.jpg)
126
![Page 127: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/127.jpg)
127
![Page 128: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/128.jpg)
• Contact transducers are used for direct contact inspections, and are generally hand manipulated.
• They have elements protected in a rugged casing to
withstand sliding contact with a variety of materials. These transducers have an ergonomic design so that they are easy to grip and move along a surface.
• They also often have replaceable wear plates to lengthen
their useful life. • Coupling materials of water, grease, oils, or commercial
materials are used to remove the air gap between the transducer and the component inspected.
128
![Page 129: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/129.jpg)
129
![Page 130: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/130.jpg)
Ultrasonic Probes
socket
crystal
Damping
Delay / protecting face
Electrical matching
Cable
Straight beam probe Angle beam probe TR-probe
130
![Page 131: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/131.jpg)
131
![Page 132: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/132.jpg)
• Delay line transducers provide versatility with a variety of replaceable options.
• Removable delay line, surface conforming membrane, and protective wear cap options can make a single transducer effective for a wide range of applications.
• As the name implies, the primary function of a delay line transducer is to introduce a time delay between the generation of the sound wave and the arrival of any reflected waves.
• This allows the transducer to complete its "sending" function before it starts it "listening" function so that near surface resolution is improved.
132
![Page 133: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/133.jpg)
133
![Page 134: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/134.jpg)
134
![Page 135: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/135.jpg)
135
![Page 136: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/136.jpg)
136
![Page 137: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/137.jpg)
137
![Page 138: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/138.jpg)
Dual element transducers contain two independently operating elements in a single housing. One of the elements transmits and the other receives. Active elements can be chosen for their sending and receiving capabilities providing a transducer with a cleaner signal, and transducers for special applications, such as inspection of course grain material. Dual element transducers are especially well suited for making measurements
138
![Page 139: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/139.jpg)
139
![Page 140: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/140.jpg)
140
![Page 141: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/141.jpg)
141
![Page 142: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/142.jpg)
142
![Page 143: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/143.jpg)
• Angle beam transducers and wedges are typically used to introduce a refracted shear wave into the test material.
• Transducers can be purchased in a variety of fixed angles or in adjustable versions where the user determines the angles of incident and refraction.
• In the fixed angle versions, the angle of refraction that is marked on the transducer is only accurate for a particular material, which is usually steel.
143
![Page 144: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/144.jpg)
144
![Page 145: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/145.jpg)
145
![Page 146: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/146.jpg)
146
![Page 147: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/147.jpg)
147
![Page 148: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/148.jpg)
• The angled sound path allows the sound beam to be reflected from the back wall to improve delectability of flaws in and around welded areas.
• They are also used to generate surface waves for use in detecting defects on the surface of a component
148
![Page 149: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/149.jpg)
149
![Page 150: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/150.jpg)
150
![Page 151: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/151.jpg)
• Normal incidence shear wave transducers are unique because they allow introduction of shear waves directly into a test piece without the use of an angle beam wedge.
• Careful design has enabled manufacturing of transducers with minimal longitudinal wave contamination.
• Paint brush transducers are used to scan wide areas. These long and narrow transducers are made up of an array of small crystals that are carefully matched to minimize variation of performance and maintain uniform sensitivity over the entire area of the transducer.
• Paint brush transducers make it possible to scan a larger area more rapidly for discontinuities.
151
![Page 152: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/152.jpg)
152
![Page 153: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/153.jpg)
153
![Page 154: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/154.jpg)
154
![Page 155: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/155.jpg)
155
![Page 156: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/156.jpg)
156
![Page 157: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/157.jpg)
157
![Page 158: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/158.jpg)
SELECTION OF TEST FREQUENCIES
TEST PARPMETERS RECOMMENDED
FREQUENCY RANGE
CAST IRON & COARSE GRAIN MATERIALS 0.5 MHz
REFINED GRAIN STEELS,
SMALL DISCONTINUITIES,
(BURST,FLAKING,PIPE)
LARGE FORGINGS
2.25 TO 5.0 MHz
SMALL FORGINGS
5.0 - 10.0 MHz
MICROSCOPIC DEFECTS,
FATIGUE CRACKS ETC.
10.0 MHz
158
![Page 159: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/159.jpg)
TYPE OF PROBE SIZE APPLICATION / ADVANTAGE
NORMAL BEAM
PROBE
LARGE DIAMETER USED FOR THICKER SECTION
MAXIMUM BEAM COVERAGE
MINIMUM NUMBER OF SCANNING
PASSES
LOW BEAM SPREAD
SMALL
DIAMETER LESS THICK SECTION
BEAM SPREAD IS MORE
DESIRABLE FOR RANDOMLY
ORIENTED FLAW
D
D
SELECTION OF PROBES
159
![Page 160: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/160.jpg)
Couplant:
• A couplant is a material (usually liquid) that facilitates the transmission of ultrasonic energy from the transducer into the test specimen.
• Couplant is generally necessary because the acoustic impedance mismatch between air and solids, such as the test specimen, is large and, therefore, nearly all of the energy is reflected and very little is transmitted into the test material
160
![Page 161: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/161.jpg)
161
![Page 162: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/162.jpg)
• The couplant displaces the air and makes it possible to get more sound energy into the test specimen so that a usable ultrasonic signal can be obtained.
• In contact ultrasonic testing a thin film of oil, glycerin or water is generally used between the transducer and the test surface.
162
![Page 163: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/163.jpg)
Ultrasonic Flaw Detector:
amplifier
work piece
probe
horizontal
sweep
clock
pulser
IP
BE
screen
163
![Page 164: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/164.jpg)
The pulse generator:- It is also known as clock or timer. It generates electrical signal frequencies. The time base generator:- It is also known as sweep generator. It controls the voltage or charge on the X-plate causing beam on the CRT to sweep across in a linear motion.
164
![Page 165: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/165.jpg)
• The pulse transmitter:- It is also called a pulsar circuit. This circuit burst the electrical energy to activate the probe.
• The receiving amplifier:- This circuit amplifies the incoming electrical signal.
• The attenuator:- It is also called a gain control circuit. It reduces the amplification from the amplifier by controlling the voltage on the Y-plate in CRT , which will control the signal heights
165
![Page 166: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/166.jpg)
CATHODE RAY TUBE(CRT)
• Cathode is an out put device which shows the flaws of the job material.
• Let us see the cross sectional view of CRT.
166
![Page 167: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/167.jpg)
Cathode ray tube : CRT
0 2 4 8 10 6
167
![Page 168: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/168.jpg)
168
![Page 169: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/169.jpg)
169
![Page 170: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/170.jpg)
170
![Page 171: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/171.jpg)
171
![Page 172: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/172.jpg)
172
![Page 173: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/173.jpg)
173
![Page 174: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/174.jpg)
174
![Page 175: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/175.jpg)
Modes of displays:
• Ultrasonic data can be collected and displayed in a number of different formats. The three most common formats are know in the NDT world as
• A-scan
• B-scan
• C-scan
175
![Page 176: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/176.jpg)
A-Scan Presentation • The A-scan presentation displays the amount of received
ultrasonic energy as a function of time.
• The relative amount of received energy is plotted along the vertical axis and elapsed time .
• In the A-scan presentation, relative discontinuity size can be estimated by comparing the signal amplitude obtained from an unknown reflector to that from a known reflector.
• Reflector depth can be determined by the position of the signal on the horizontal sweep
176
![Page 177: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/177.jpg)
B-Scan Presentation
• The B-scan presentations is a profile (cross-sectional)
view of the a test specimen.
• In the B-scan, the time-of-flight (travel time) of the sound energy is displayed along the vertical and the linear position of the transducer is displayed along the horizontal axis.
• From the B-scan, the depth of the reflector and its approximate linear dimensions in the scan direction can be determined.
177
![Page 178: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/178.jpg)
178
![Page 179: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/179.jpg)
C-Scan Presentation
• The C-scan presentation provides a plan-type view of the location and size of test specimen features.
• The plane of the image is parallel to the scan pattern of the transducer.
• C-scan presentations are produced with an automated data acquisition system, such as a computer controlled immersion scanning system.
179
![Page 180: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/180.jpg)
180
![Page 181: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/181.jpg)
181
![Page 182: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/182.jpg)
182
![Page 183: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/183.jpg)
183
![Page 184: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/184.jpg)
184
![Page 185: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/185.jpg)
Cables and Connectors:
• For Ultrasonic testing Coaxial cables are used for connecting transducer and UT flaw detector.
• Because coaxial cables are S/N ratio is good.
185
![Page 186: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/186.jpg)
186
![Page 187: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/187.jpg)
187
![Page 188: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/188.jpg)
DAY 4
• Ultrasonic Testing Techniques
• Calibration blocks
• Weld scan
188
![Page 189: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/189.jpg)
Ultrasonic Testing Techniques:
A. Contact Testing
1.Pulse echo Testing
2.Through Transmission Testing
B. Immersion Testing
C. Through Transmission Testing
D. Air Coupling Testing
189
![Page 190: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/190.jpg)
Contact Testing:
• In Contact Testing the Transducer is on contact with testing object with the help of couplet.
Pulse Echo Testing:
.In which single Transducer is used
.From the reflected echo I to be considered.
.It is mostly used industrial UT technique.
. In which avoid lack of coupulant, which causes improper contact .
190
![Page 191: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/191.jpg)
CONTACT TESTING
SIDE - 1 SIDE - 2
SIDE - 3 SIDE - 4
DOUBLE “V” BUTT JOINT SCANNING FROM ALL FOUR SIDES
ADVANTAGES IT IS PORTABLE. SYSTEM DOES NOT REQUIRE LARGE AMOUNT OF ACCESSORIES
191
![Page 192: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/192.jpg)
0.5 TO 6 MHz COMMONLY USED FREQUENCY FOR CONTACT TESTING 10 TO 25 MHz IMMERSION TESTING
PULSE ECHO METHOD
NORMAL PROBE
ANGLE PROBE
T.R. PROBE
CONTACT TESTING
NORMAL PROBE
ANGLE PROBE
IMMERSION TESTING
AMPLIFIER
TRANSMITTER
RECEIVER
HIGH FREQUENCY GENERATOR
METHODS OF ULTRASONIC TESTING OF MATERIALS
PULSE ECHO METHOD
192
![Page 193: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/193.jpg)
• Depth of defect is possible.
• Near zone and Dead zone are major draw backs in this technique.
• In which from the reflected echo we will estimate depth, size, shape and type of defect.
• For weld scanning angle beams are used in this technique.
193
![Page 194: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/194.jpg)
• Through Transmission technique:
• In which separate Transducer and Receiver is used. • In which both side accessible is important. • Tx, Rx are in same axis. • It mostly used for less thickness plate scanning. • Only normal probes and delay line probes are used. • Depth of defect is not possible. • Initial pulse is not appear, dead zone and near field
effects are eliminated.
194
![Page 195: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/195.jpg)
• CAPABILITY OF TESTING THICKER TEST SPECIMENS
• DEFECTS VERY NEAR TO THE SURFACE CAN BE DETECTED
100% INTENSITY
HIGH FREQUENCY GENERATOR AMPLIFIER
AMPLIFIER
0
INTENSITY METER
TRANSMITTING PROBE RECEIVING PROBE
DISCONTINUITY
25% intensity due to partial energy being received because of the discontinuity
METHODS OF ULTRASONIC TESTING OF MATERIALS
2. THROUGH TRANSMISSION METHOD
INTENSITY OF ULTRASOUND IS MEASURED AFTER IT HAS PASSED THROUGH THE TEST PIECE
ADVANTAGES
LIMITATIONS
• DEFECT LOCATION IS NOT POSSIBLE.
• BOTH SIDES SHOULD BE ACCESSIBLE. 195
![Page 196: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/196.jpg)
AIR COUPLING METHOD
• In this we used air as a couplent
• This method is used when we test heated objects.
196
![Page 197: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/197.jpg)
Straight beam inspection techniques:
Direct contact,
single element probe
Direct contact,
dual element probe Fixed delay
Immersion testing Through transmission
197
![Page 198: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/198.jpg)
Sound reflection at a flaw
Probe
Flaw Sound travel path
Work piece
s
198
![Page 199: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/199.jpg)
Plate testing
delamination plate 0 2 4 6 8 10
IP
F
BE
IP = Initial pulse
F = Flaw
BE = Backwall echo
199
![Page 200: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/200.jpg)
0 2 4 6 8 10
s
s
Wall thickness measurement
Corrosion
200
![Page 201: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/201.jpg)
Through transmission testing
0 2 4 6 8 10
Through transmission signal
1
2
1
2
T
T
R
R
Flaw
201
![Page 202: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/202.jpg)
surface = sound entry
backwall flaw
1 2
water delay
0 2 4 6 8 10 0 2 4 6 8 10
IE IE IP IP
BE BE F
1 2
Immersion testing
202
![Page 203: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/203.jpg)
IMMERSION TESTING METHOD
• In this case near field is minimize in water
• velocity of water
min water path= --------------------- X thickness
velocity of job material
203
![Page 204: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/204.jpg)
• The main disadvantage of this method is shocking problem.
• The main advantage of this method is near field is
minimized.
• In this we use high frequency probes are used around 25 Mhz.
• In this object we can generate all type of incident angles, generally it is used in automatic testing or hydro testing.
204
![Page 205: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/205.jpg)
205
![Page 206: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/206.jpg)
Automated Immersion scanning:
206
![Page 207: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/207.jpg)
207
![Page 208: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/208.jpg)
208
![Page 209: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/209.jpg)
Weld inspection
0 20 40 60 80 100
s
a a'
d
x
a = s sinß
a' = a - x
d' = s cosß
d = 2T - t'
s
Lack of fusion
Work piece with welding
F ß = probe angle s = sound path a = surface distance a‘ = reduced surface distance d‘ = virtual depth d = actual depth T = material thickness
ß
209
![Page 210: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/210.jpg)
210
![Page 211: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/211.jpg)
211
![Page 212: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/212.jpg)
212
![Page 213: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/213.jpg)
213
![Page 214: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/214.jpg)
Shear Wave Propagation
Transmitter / Receiver
No reflected echo
Propagate at same angle through part
Time (distance)
214
![Page 215: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/215.jpg)
Shear Wave Beam Spread
Transmitter / Receiver
215
![Page 216: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/216.jpg)
Reflection
Transmitter / Receiver
Reflected echo
Wave reflected from acoustic interface
Time (distance)
216
![Page 217: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/217.jpg)
Reflection Transmitter / Receiver
Strong reflected echo
217
![Page 218: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/218.jpg)
Reflection Transmitter / Receiver
Scattered reflected echo
218
![Page 219: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/219.jpg)
Reflection Transmitter / Receiver
No reflected echo
219
![Page 220: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/220.jpg)
Raster Scan Transducer moved into and away from weld while being
indexed
Manual or automated (encoded for position)
Slow
220
![Page 221: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/221.jpg)
Line Scan Transducer moved along the weld
Fixed distance from weld
Manual or automated, encoded for position
Fast
221
![Page 222: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/222.jpg)
Different types of probe movement:
222
![Page 223: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/223.jpg)
Calibration Methods • Calibration refers to the act of evaluating and adjusting
the precision and accuracy of measurement equipment. In ultrasonic testing, several forms of calibration must occur
• 1. The electronics of the equipment must be calibrated to assure that they are performing as designed. This operation is usually performed by the equipment manufacturer .
• 2.This user calibration is necessary because most ultrasonic equipment can be reconfigured for use in a large variety of applications.
223
![Page 224: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/224.jpg)
• The user must "calibrate" the system, which includes the equipment settings, the transducer, and the test setup, to validate that the desired level of precision and accuracy are achieved.
• In ultrasonic testing, there is also a need for reference standards. Reference standards are used to establish a general level of consistency in measurements and to help interpret and quantify the information contained in the received signal.
• Reference standards are used to validate that the equipment and the setup provide similar results from one day to the next and that similar results are produced by different systems.
224
![Page 225: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/225.jpg)
• Reference standards also help the inspector to estimate the size of flaws. In a pulse-echo type setup, signal strength depends on both the size of the flaw and the distance between the flaw and the transducer.
• The inspector can use a reference standard with an artificially induced flaw of known size and at approximately the same distance away for the transducer to produce a signal.
• By comparing the signal from the reference standard to that received from the actual flaw, the inspector can estimate the flaw size.
225
![Page 226: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/226.jpg)
SENSITIVITY
CHARACTERISTIC OF ULTRASONIC PROBES
• ABILITY OF THE PROBE TO DETECT SMALLEST DISCONTINUITY
• MEASURED BY THE AMPLITUDE OF ITS RESPONSE TO ENERGY REFLECTED FROM A STANDARD DISCONTINUITY
SAME REFLECTOR, SAME DISTANCE & GAIN SETTING PROBE N0 - 2 IS MORE SENSITIVE
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
FLAT BOTTOM HOLE
PROBE NO. - 1
FLAT BOTTOM HOLE
PROBE NO. - 2
HIGHER THE FREQUENCY, MORE THE SENSITIVITY 226
![Page 227: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/227.jpg)
IIW V1 Block:
1). Material: carbon steel 2). Dimensions: 300mmL*100mmW*25mmT.
3). Application: Used for calibration of shear , longitudinal transducers, verification of shear wedge exit point and refracted angle. Can also be used for resolution and sensitivity checking. Includes a 100mm radius on one end . Also includes a 50mm
diameter and a 1.5mm diameter hole. In accordance with International Institute of Welding and ASTM E164
227
![Page 228: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/228.jpg)
228
![Page 229: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/229.jpg)
229
![Page 230: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/230.jpg)
230
![Page 231: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/231.jpg)
RESOLUTION
ABILITY TO SEPARATE ECHOES FROM TWO OR MORE DISCONTINUITIES LOCATED CLOSE TOGETHER IN DEPTH
HIGHER THE FREQUENCY, BETTER WILL BE RESOLUTION
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
GOOD RESOLUTION POOR RESOLUTION
231
![Page 232: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/232.jpg)
• MINIMUM TWO REFERENCE POINTS ARE NECESSARY
• FIRST REFERENCE ALWAYS CONTROLLED WITH THE HELP OF DELAY CONTROL
KNOB
• SECOND REFERENCE POINT ALWAYS CONTROLLED WITH THE HELP OF RANGE CONTROL
KNOB
IIW “V1” BLOCK
CALIBERATION OF ULTRASONIC EQUIPEMENT
GENERAL RULES
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BACK WALL ECHO (BWE)
232
![Page 233: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/233.jpg)
IIW “V1” BLOCK
CALIBERATION OF ULTRASONIC EQUIPEMENT
RANGE CALIBERATION BY NORMAL PROBE
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BACK WALL ECHO (BWE)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO
1ST BWE 2ND BWE
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BWE
2ND BWE
233
![Page 234: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/234.jpg)
IIW:V-2: OR Miniature Aperture Block
Description: 12.5mm thick, small calibration block
• For on-site checking of miniature shear wave probe index,
time base, beam angle , Sensitivity(1.5 mm)
• Includes a 25mm and 50 mm radius, 1.5mm hole engraved reference mark scales from 35 to 75 degrees.
• In accordance with BS EN 27963:1992, ISO 7963 Cal block No. 2, Fig. 1.
234
![Page 235: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/235.jpg)
235
![Page 236: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/236.jpg)
ASME Angle Beam Calibration Blocks:
• Meet the requirements of ASME Section V, Article 5, Fig. T-542.8.1.1 and contain EDM notches at 10% of nominal wall on both OD and ID oriented longitudinally and transversely.
236
![Page 237: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/237.jpg)
237
![Page 238: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/238.jpg)
AWS Resolution Calibration (RC) Block
238
![Page 239: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/239.jpg)
• The RC Block is used to determine the resolution of angle beam transducers per the requirements of AWS
• Engraved Index markers are provided for 45, 60, and 70 degree refracted angle beams.
239
![Page 240: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/240.jpg)
Step and Tapered Calibration Wedges
240
![Page 241: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/241.jpg)
• Step and tapered calibration wedges come in a large variety of sizes and configurations.
• Step wedges are typically manufactured with four or five steps but custom wedge can be obtained with any number of steps.
• Tapered wedges have a constant taper over the desired thickness range.
241
![Page 242: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/242.jpg)
Distance/Area-Amplitude Blocks
242
![Page 243: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/243.jpg)
• Distance/area amplitude correction blocks typically are purchased as a ten-block set, as shown above.
• Aluminum sets are manufactured per the requirements of ASTM E127 and steel sets per ASTM E428.
• Sets can also be purchased in titanium. Each block contains a single flat-bottomed, plugged hole.
• The hole sizes and metal path distances are as follows:
3/64" at 3"
5/64" at 1/8", 1/4", 1/2", 3/4", 11/2", 3", and 6"
8/64" at 3" and 6" 243
![Page 244: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/244.jpg)
DAY 5
• DAC CURVE • DGS CURVE
• 6dB,20dB DROP METHODS
• DISCONTINUTIES
• Accept and Rejection criteria
244
![Page 245: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/245.jpg)
DAC Curve:
• Acoustic signals from the same reflecting surface will have different amplitudes at different distances from the transducer.
• Distance amplitude correction (DAC) provides a means of establishing a graphic ‘reference level sensitivity’ as a function of sweep distance on the A-scan display.
• The use of DAC allows signals reflected from similar discontinuities to be evaluated where signal attenuation as a function of depth has been correlated.
• Most often DAC will allow for loss in amplitude over material depth (time), graphically on the A-scan display but can also be done electronically by certain instruments
245
![Page 246: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/246.jpg)
246
![Page 247: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/247.jpg)
247
![Page 248: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/248.jpg)
• A distance amplitude correction curve is constructed from the peak amplitude responses from reflectors of equal area at different distances in the same material.
• Reference standards which incorporate side drilled holes (SDH), flat bottom holes (FBH), or notches whereby the reflectors are located at varying depths are commonly used
248
![Page 249: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/249.jpg)
• While drawing DAC 1st echo set to 80% FSH, and note down the gain . Which is Actual gain or Actual dB.
• And trace the next 2 or 3 indications, and make a curve.
• While scanning on job increase gain to(DAC+6dB), which is called as scanning dB.
• If any echo touches DAC curve reduce gain by 6dB, still it is touches then mark as defect at that place.
249
![Page 250: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/250.jpg)
DGS curve:
• DGS – Distance Gain Size is a method of setting sensitivity or assessing the signal from an unknown reflector based on the theoretical response of a flat-bottomed hole reflector perpendicular to the beam axis.
• The DGS system was introduced by Krautkramer in 1958 and is referred to in German as AVG.
• A schematic of a general DGS diagram is shown in the Figure. The Y-axis shows the Gain and X-axis shows the Distance from the probe.
250
![Page 251: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/251.jpg)
251
![Page 252: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/252.jpg)
• In a general DGS diagram the distance is shown in units of Near Field and the scale is logarithmic to cover a wide range. The blue curves plotted show how the amplitudes obtained from different sizes of disc shaped reflector (equivalent to a FBH) decrease as the distance between the probe and the reflector increases.
252
![Page 253: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/253.jpg)
Finding Length of defects:
• Length of defect by 2 techniques.
1. 6dB Drop method
2.20 dB drop method
253
![Page 254: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/254.jpg)
254
![Page 255: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/255.jpg)
255
![Page 256: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/256.jpg)
DISCONTINUTIES
256
![Page 257: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/257.jpg)
DEFECTS IN PLATE MATERIAL
• LAMINATIONS
• INCLUSIONS > LINEAR INCLUSIONS > SCATERED INCLUSIONS
• STRINGERS
• A ROLLING LAP
257
![Page 258: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/258.jpg)
DEFECTS IN WELDS
• ROOT DEFECTS:-
>LACK OF PENETRATION
>LACK OF ROOT FUSION
>ROOT CRACK
>ROOT UNDER CUT
>OVER PENETRATION
>ROOT CONCAVITY
258
![Page 259: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/259.jpg)
DEFECTS IN PLATE MATERIALS
259
![Page 260: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/260.jpg)
LAMINATIONS:
THESE ARE FORMED WHEN A BILLET IS FLATTENED AND SPREAD OUT MAY CAUSES LAMINATION.PIPE AND POROSITY ALSO MAY CAUSES LAMINATION.
260
![Page 261: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/261.jpg)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BWE 2ND BWE
APPLICATIONS OF ULTRASONIC TESTING
TESTING OF LAMINATION IN PLATES
LAMINATION IN THE PLATE PLATE
NO DEFECT
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BWE FROM DEFECT
2ND BWE FROM DEFECT
3RD BWE FROM DEFECT
4TH BWE FROM DEFECT
DEFECT INDICATION
261
![Page 262: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/262.jpg)
APPLICATIONS OF ULTRASONIC TESTING
BOND TESTING
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BWE FROM DEFECT
2ND BWE FROM DEFECT
DEFECT INDICATION
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO FIRST ECHO FROM INTERFACE 1ST BWE
NO DEFECT
DEFECT IN BONDING AT INTERFACE CALLED “DISBONDING”
BEARING CASTING PORTION
BABBIT METAL
INTERFACE
262
![Page 263: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/263.jpg)
APPLICATIONS OF ULTRASONIC TESTING
BOND TESTING
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO 1ST BWE FROM DEFECT
2ND BWE FROM DEFECT
DEFECT INDICATION
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO FIRST ECHO FROM INTERFACE 1ST BWE
NO DEFECT
DEFECT IN BONDING AT INTERFACE CALLED “DISBONDING”
BEARING CASTING PORTION
BABBIT METAL
INTERFACE
263
![Page 264: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/264.jpg)
INCULUSIONS
• LINEAR INCLUSIONS:
264
![Page 265: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/265.jpg)
SCATTERED INCLUSIONS:
265
![Page 266: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/266.jpg)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO
INDICATION FROM SPHERICAL FLAW
BWE
SCREEN PRESENTATION WHEN PROBE IS AT 1 OR 2 OR 3 OR 4
INTERPRETATION OF ULTRASONIC FLAW - ECHO INDICATIONS
SPHERICAL FLAW (POROSITY)
• REFLECT ONLY A SMALL AMOUNT OF SOUND
• ECHO HEIGHT SMALL
• ECHO HEIGHT REMAINS UNCHANGED WHEN ANGLE OF APPROACH IS
CHANGED
1
2
SPHERICALFLAW
3
4
266
![Page 267: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/267.jpg)
STRINGERS:
• These are formed when the non metallic inclusions in the ingot.
The signal response Is like the linear Inclusion signal
In the rolling direction The BWE is still present But the signal can be Maintained along the Defects length
267
![Page 268: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/268.jpg)
A ROLLING LAP:
• This defect occurs in the rolling process.
268
![Page 269: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/269.jpg)
DEFECTS IN WELDS
269
![Page 270: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/270.jpg)
ROOT DEFECTS
• LACK OF PENETRATIN:
• High amplitude corner signals both sides of the weld, rapidly decreasing in amplitude on rotational path.
• Plotting at plate thickness depth, the width of the root gap apart, with no cross over.
270
![Page 271: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/271.jpg)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO
INDICATION FROM CORNER
SCREEN PRESENTATION WHEN PROBE IS AT 1 OR 2
1 2
LACK OF PENETRATION
ANGLE PROBE WELD
WELD TESTING - INTERPRETATION OF ULTRASONIC INDICATIONS
LACK OF PENETRATION
• SHARP ECHO FROM BOTH SIDES OF WELD
• INDICATION REMAINS AT THE SAME POSITION WHEN PROBE IS MOVED ALONG THE LENGTH
271
![Page 272: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/272.jpg)
ROOT CRACK
• It would be normal to expect a high amplitude, multi-faceted reflector probably from both sides of the weld.
• The vertical height of the crack was substantial, a characteristic running signal on the time base would be noted on depth scan with the angle probe.
• The response would raise and fall on rotational or lateral probe moments due to crack irregularity.
272
![Page 273: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/273.jpg)
ROOT CRACK
273
![Page 274: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/274.jpg)
ROOT UNDERCUT
• Depend on how severe the undercut is will determine the type of amplitude received.
• However, associated with the undercut echo will be as signal from the root bead as well.
• If the undercut is only one side of the weld the root bead is examined from the opposite side.
274
![Page 275: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/275.jpg)
ROOT UNDERCUT
275
![Page 276: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/276.jpg)
EXCESS ROOT PENETRATION
• Root bead type signals on both side of the welds are plotting beyond expected beam path length to the bead and crossing over.
• Steeper angle probe(i.e., 38 and 45 degrees), access permitting will give best results.
• It is also called over penetration.
276
![Page 277: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/277.jpg)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO
INDICATION FROM EXCESS PENETRATION
SCREEN PRESENTATION WHEN PROBE IS AT 1 ECHO MAY BE ABSENT WHEN PROBE AT 2 DEPENDING ON SURFACE CONTOUR
WELD TESTING - INTERPRETATION OF ULTRASONIC INDICATIONS
EXCESS PENETRATION
• SHARP ECHO DEPENDS ON SHAPE OF ROOT SURFACE
1 2
EXCESS PENETRATION
ANGLE PROBE WELD
277
![Page 278: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/278.jpg)
ROOT CONCAVITY
• Low amplitude signals on both sides of the weld are plotting short of plate thickness and no cross over.
• If only slight concavity it is likely that it will not be observed ultrasonically.
278
![Page 279: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/279.jpg)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO
INDICATION FROM ROOT CONCAVITY
SCREEN PRESENTATION WHEN PROBE IS AT 1 OR 2
WELD TESTING - INTERPRETATION OF ULTRASONIC INDICATIONS
ROOT CONCAVITY
1 2
ROOT CONCAVITY
ANGLE PROBE WELD
279
![Page 280: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/280.jpg)
DEFECTS IN WELD REGION
• High amplitude signal from “a” on full skip and “c” on half skip.
• Low amplitude signal from “c” and “d”.
A B C D
280
![Page 281: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/281.jpg)
SLAG INCLUSION
• Detectable from all accessible positions and directions due to volumetric nature.
• Signal contains numerous half cycles and have a rounded peak.
• It should be detected with any angle probe.
281
![Page 282: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/282.jpg)
SLAG INCLUSION
282
![Page 283: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/283.jpg)
CLUSTER POROSITY
• Detectable from all accessible positions and directions due to volumetric nature.
• Very low amplitude response due to signal attenuation giving multiple signal with a wide time base.
• It is also called as multiple small inclusions.
283
![Page 284: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/284.jpg)
CLUSTER POROSITY
284
![Page 285: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/285.jpg)
0 2 4 6 8 10
0
2
0
40
6
0
80
1
00
INITIAL ECHO
INDICATION FROM MISMATCH
SCREEN PRESENTATION WHEN PROBE IS AT 2 ECHO MAY BE ABSENT WHEN PROBE AT 1 DEPENDING ON SURFACE CONTOUR
WELD TESTING - INTERPRETATION OF ULTRASONIC INDICATIONS
MISMATCH
• STRONG ECHO INDICATION WHEN SCANNED FROM LOWER SIDE OF THE WELD
• NO INDICATION FROM OTHER SIDE
1 2
MISMATCH
ANGLE PROBE WELD
285
![Page 286: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/286.jpg)
Accept and Rejection criteria:
• According to CODES and STANDARDS we will interpitation the results.
• Codes and standards are intended to enhance the safety of workers and the public
• CODE:
A systematic collection of regulations and rules of procedure or conduct
286
![Page 287: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/287.jpg)
• A standard is a set of "how to" instructions for designers, manufacturers, and/or users of the equipment covered.
• It can run from a few paragraphs to hundreds of pages. Standards are considered voluntary because they serve as guidelines only, without the force of law.
• Organizations such as ASME that develop standards can publish them, and can certify manufacturers
287
![Page 288: 188269428-Asnt-Level-II-UT](https://reader034.vdocuments.net/reader034/viewer/2022042717/55cf99e1550346d0339f9ea1/html5/thumbnails/288.jpg)
• Some of the codes used in NDT
• API 650 Oil and Storage Tanks.
• API 1104 Cross Country or Long Pipe Lines.
• ASME Sec V Preparation of NDT Procedures.
• ASME Sec VIII Div 1&2 Boiler and Pressure Vessels .
• ASME Sec IX Welder Qualification Tests.
• ASME B31.1 Power Piping.
• ASME B31.4 Liquid Transportation system for
hydro carbons.
ASME B31.8 Gas Transmission & piping
system.
AWS D1.1 Structural Welding.
288