IC TECHNOLOGYCHEMICAL VAPOUR
DEPOSITION AND EPITAXIAL LAYER
GROWTH
By:Kritica Sharma
Assistant Professor (ECE)
![Page 2: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/2.jpg)
CONTENTS
2
CVD for deposition of dielectric and polysilicon thick Layer – a simple CVD system
Chemical equilibrium and the law of mass action Introduction to atmospheric CVD of dielectric low pressure CVD of dielectric semiconductor. Epitaxy Vapour Phase Expitaxy Defects in Epitaxial growth Metal Organic Chemical Vapor Deposition Molecular beam epitaxy.
![Page 3: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/3.jpg)
CHEMICAL VAPOUR DEPOSITION Chemical Vapour Deposition (CVD) is a chemical
process used to produce high purity, high performance solid materials.
In a typical CVD process, the substrate is exposed to one or more volatile precursors which react and decompose on the substrate surface to produce the desired deposit.
During this process, volatile by-products are also produced, which are removed by gas flow through the reaction chamber.
![Page 4: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/4.jpg)
STEPS INVOLVED IN CHEMICAL VAPOUR DEPOSITION
Transport of reactants by forced
convection to the
deposition region
Transport of reactants
by diffusion from the main gas stream to
the substrate surface.
Adsorption of
reactants in the wafer
(substrate) surface.
Chemical
decomposition and other
surface reactions
take place.
Desorption of by-
products from the surface
Transport of by-products by diffusion
Transport of by-products by forced
convection away from
the deposition
region.
![Page 5: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/5.jpg)
STEPS INVOLVED IN A CVD PROCESS (SCHEMATIC)
![Page 6: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/6.jpg)
SCHEMATIC DIAGRAM - THE STEPS INVOLVED IN CVD1. Transport of reactants by forced convection to the deposition region. 2. Transport of reactants by diffusion from the main gas stream through the boundary layer to the
wafer surface3. Adsorption of reactants on the wafer surface. 4. Surface processes, including chemical decomposition or reaction, surface migration to
attachment sites (such as atomic-level ledges and kinks), site incorporation, and other surface reactions.
5. Desorption of byproducts from the surface. 6. Transport of byproducts by diffusion through the boundary layer and back to the main gas
stream. 7. Transport of byproducts by forced convection away from the deposition region.
![Page 7: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/7.jpg)
STEPS INVOLVED IN A CVD PROCESS (SCHEMATIC)
![Page 8: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/8.jpg)
STEPS INVOLVED IN A CVD PROCESS (SCHEMATIC)
![Page 9: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/9.jpg)
STEPS INVOLVED IN A CVD PROCESS (LIMITING PROCESSES)1. Gas phase process (mainly diffusion to substrate).2. Surface process (mainly reaction)
![Page 10: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/10.jpg)
CVD KINETIC GROWTH MODEL
We approximate the flux Fl by the linear formula
F1 = hG(CG –CS)
where CG and CS are the concentrations of the SiCI4 (molecules per cubic centimeter) in the bulk of the gas and at the surface, respectively, and hG is the gas-phase mass-transfer coefficient. The flux consumed by the chemical-reaction taking place at the
surface of the growing film F2 is approximated by the formula F2 = kSCS
where kS is the chemical surface-reaction rate constant.In steady state F1 = F2 = F. Using this condition, we get
GS
GS hk
CC/1
![Page 11: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/11.jpg)
CVD KINETIC GROWTH MODEL-IIWe can now express the growth rate of the silicon film by writing
where N1 is the number of silicon atoms incorporated into a unit volume of the film. Its value for silicon is 5.01022 cm-3. Noting that CG = YCT where CT is the total number of molecules per cubic centimeter in the gas, we get the expression for the growth rate,
11 NC
hkhk
NFv G
GS
GS
YNC
hkhk
NFv T
GS
GS
11
The growth rate at a given mole fraction is determined by the smaller of hG or kS. In the limiting cases the growth rate will be given either by
[surface-reaction control]or by [mass-transfer control].
YkNCv ST
1
YkNCv ST
1
![Page 12: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/12.jpg)
CVD GROWTH MODEL – GAS PHASE MASS TRANSFER
The “Stagnant-film” model of gas-phase mass-transfer
SG
GCCDF
1
G
GDh
Boundary layer theory: δ increases with distance in the direction of gas flow (from Newton’s second low).
DG – diffusivity of reactant species - boundary layer thickness
![Page 13: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/13.jpg)
CVD GROWTH MODEL – GAS PHASE MASS TRANSFER
The flow of reactants F is F DG -1
![Page 14: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/14.jpg)
TYPES OF CVD CVD’s are classified into two types on the basis of
Operating Pressure. 1. Atmospheric Pressure CVD 2. Low Pressure CVD Plasma Enhanced CVD Photochemical Vapour Deposition Thermal CVD
![Page 15: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/15.jpg)
CASE 1 : HIGH TEMPERATUREThis process is used to deposit Silicon and compoundfilms or hard metallurgical coatings like TitaniumCarbide and Titanium Nitride. CASE 2 : LOW TEMPERATUREMany insulating film layers such as Silicon dioxide needto be deposited at low temperatures for effectivedeposition.
ATMOSPHERIC PRESSURE CHEMICAL VAPOUR DEPOSITION
![Page 16: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/16.jpg)
Aluminium oxide films are deposited by this method from aluminium trichloride, argon and oxygen gas mixtures at temperatures ranging from 800-1000 degree Celsius
The films have low chlorine content, which continue to decrease with increasing temperature.
Analysis of the film growth rate on the substrates revealed that, the growth takes place only by diffusion from 800 to 950 degree Celsius and only by gas phase reaction at 1000 degree Celsius.
CONTINUED..
![Page 17: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/17.jpg)
CONVEYOR BELT - APCVD
![Page 18: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/18.jpg)
Film thickness uniformity cannot be maintained. Large number of pinhole defects can occur. Wafer (Substrate) throughput is low due to low
deposition rate. The deposits get contaminated very easily since it
takes place at atmospheric pressure. Maintaining stochiometry is extremely difficult.
LIMITATIONS OF APCVD
![Page 19: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/19.jpg)
The deposition of Silicon carbide thin film is performed using low pressure CVD of Dichlorosilane / Acetylene / Hydrogen reaction system.
The Silicon carbide film deposited at three different temperatures has three different properties.
LOW PRESSURE CVD
1023 K AMORPHOUS1073 K MICROCRYSTALLINE1173 K PREFERENTIALLY
ORIENTED
![Page 20: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/20.jpg)
This technique permits either horizontal or vertical loading of the wafers into the furnace and accommodates a large number of wafers for processing.
The process results in the deposition of compounds with excellent purity and uniformity.
However the technique requires higher temperatures and the deposition rate is low.
CONTINUED..
![Page 21: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/21.jpg)
Plasma-enhanced chemical vapor deposition (PECVD) is a process used to deposit thin films from a gas state (vapor) to a solid state on a substrate.
Chemical reactions are involved in the process, which occur after creation of a plasma of the reacting gases.
The plasma is generally created by RF (AC) frequency or DC discharge between two electrodes, the space between which is filled with the reacting gases.
The helping hand of the Plasma helps in increasing the film quality at low temperature and pressure.
PLASMA ENHANCED CVD
![Page 22: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/22.jpg)
PECVD uses electrical energy which is transferred to the gas mixture.
This transforms the gas mixture into reactive radicals, ions, neutral atoms and molecules, and other highly excited species.
These atomic and molecular fragments interact with a substrate and, depending on the nature of these interactions, either etching or deposition processes occur at the substrate.
Some of the desirable properties of PECVD films are good adhesion, low pinhole density and uniformity.
CONTINUED..
![Page 23: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/23.jpg)
SCHEMATIC DIAGRAM OF PECVD
![Page 24: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/24.jpg)
REINBERG TYPE REACTOR (DIRECT): Reactants, by-products, substrates and plasma are in
the same space. Capacitive-coupled Radio Frequency plasma. Rotating substrates are present. DOWNSTREAM REACTOR (INDIRECT): Plasma is generated in a separate chamber and is
pumped into the deposition chamber. Allows better control of purity and film quality when
compared to the Direct type.
REACTORS USED IN PECVD
![Page 25: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/25.jpg)
Al thin films are deposited via photochemical vapour deposition on catalytic layers of Ti, TiO2, and Pd, using dimethyl aluminum hydride.
Deposition is carried out at low gas pressures to induce a surface reaction based on adsorption and subsequent decomposition of adsorbates.
Of these three layers Ti is so effective as a catalyst that the Al films are thermally deposited even at a low substrate temperature of 60°C with a growth rate of 0.5 nm/min.
PHOTOCHEMICAL VAPOUR DEPOSITION
![Page 26: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/26.jpg)
The UV light generated by a deuterium lamp helped increase the growth rates. On the other hand, Al could be deposited on TiO2 layers only under irradiation at a substrate temperature of 120°C It takes several minutes to cover the TiO2 surface with Al and initiate the Al film's growth.
Here, the UV light inhibited the Al growth on the surface, whereas the films are deposited thermally.
X-ray photoelectron spectroscopy showed the formation of a photolytic production of the adsorbate, which acts presumably as a center that inhibits further Al growth.
CONTINUED..
![Page 27: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/27.jpg)
In thermal CVD process, temperatures as high as 2000 degree Celsius is needed to deposit the compounds.
There are two basic types of reactors for thermal CVD.1. Hot wall reactor2. Cold wall reactorA hot wall reactor is an isothermal surface into whichthe substrates are placed. Since the whole chamber isheated, precise temperature control can be achievedby designing the furnace accordingly.
THERMAL CVD
![Page 28: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/28.jpg)
A disadvantage of the hot wall configuration is that deposition occurs on the walls of the chamber as well as on the substrate.
As a consequence, hot wall reactors must be frequently cleaned in order to reduce contamination of substrates.
In a cold wall reactor, only the substrate is heated. The deposition takes place on the area of the highest
temperature, since CVD reactions are generally endothermic.
CONTINUED..
![Page 29: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/29.jpg)
The deposition is only on the substrate in cold wall reactors, and therefore contamination of particles is reduced considerably.
However, hot wall reactors have higher throughput since the designs can easily accommodate multiple wafer (substrate) configurations.
CONTINUED..
![Page 30: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/30.jpg)
Variable shaped surfaces, given reasonable access to the coating powders or gases, such as screw threads, blind holes or channels or recesses, can be coated evenly without build-up on edges.
Versatile –any element or compound can be deposited.
High Purity can be obtained. High Density – nearly 100% of theoretical value. Material Formation well below the melting point Economical in production, since many parts can be
coated at the same time.
ADVANTAGES OF CHEMICAL VAPOUR DEPOSITION
![Page 31: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/31.jpg)
CVD has applications across a wide range of industries such as:
Coatings – Coatings for a variety of applications such as wear resistance, corrosion resistance, high temperature protection, erosion protection and combinations thereof.
Semiconductors and related devices – Integrated circuits, sensors and optoelectronic devices
Dense structural parts – CVD can be used to produce components that are difficult or uneconomical to produce using conventional fabrication techniques. Dense parts produced via CVD are generally thin walled and maybe deposited onto a mandrel or former.
APPLICATIONS OF CHEMICAL VAPOUR DEPOSITION
![Page 32: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/32.jpg)
Optical Fibres – For telecommunications. Composites – Preforms can be infiltrated using CVD
techniques to produce ceramic matrix composites such as carbon-carbon, carbon-silicon carbide and silicon carbide-silicon carbide composites. This process is sometimes called chemical vapour infiltration or CVI.
Powder production – Production of novel powders and fibres
Catalysts Nanomachines
CONTINUED..
![Page 33: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/33.jpg)
![Page 34: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/34.jpg)
Epitaxy: “arranged upon”Definition: Epitaxy means the growth of a single crystal film on
top of a crystalline substrate. For most thin film applications (hard and soft coatings,
optical coatings, protective coatings) it is of little importance.
However, for semiconductor thin film technology it is crucial
EPITAXY
![Page 35: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/35.jpg)
Why Silicon dominates? Abundant, cheap Silicon dioxide is very stable, strong
dielectric and it is easy to grow on thermal process.
Wider band gap, wide operation temperature Unit cell of single crystal silicon
Si
Si
Si
Name Silicon Bond length in singleCrystal Si
2.352 Ao
Symbol Si Density of solid 2.33 gm/cm3
Atomic Number 14 Molar Volume 12.06 cm3
Atomic Weight 28.0855 Velocity of sound 2200 m/s
Discoverer Jons Jacob Berzelius Electrical resistivity 1000,000 µΩcm
Discovered at Sweden Reflectivity 28%
Discovery Year 1824 Melting point 1414oC
Origin of name From Latin Word“silices”
Boiling Point 2900oC
Si
Si
![Page 36: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/36.jpg)
Why Si Epitaxy? To enhance the performance of discrete bipolar transistor. To improve the performance of dynamic random access memory
devices (RAMs).
Advantages of epitaxial wafers over bulk wafers Offers
•means of controlling the doping profile Epitaxial
•layers are generally oxygen and carbon free
![Page 37: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/37.jpg)
Lattice matching in Epitaxial Growth
Lattice structure and lattice constant must match for twomaterials eg. GaAs and AlAs both have zincblende structure
1.43eV
In .53Ga.47 As
0.36eV
5.65 6.06
![Page 38: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/38.jpg)
Gases used inSilane (SiH4) Pyrolysis :
Dichlorosilane (DCS) Tricholorosilane (TCS)Silicon tetrachlorideDisilane
Silicon Epitaxya)
b) c) d) e)f)
SiH4 (H2)SiH2Cl2
SiHCl3
SiCl4
Si2H6
Si + 2H2
Dopant gases –Diborane (B2H6)– Phosphine (PH3)– Arsine (AsH3)
![Page 39: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/39.jpg)
TYPES OF EPITAXY Homoepitaxy – The film and the substrate are the same material. – Often used in Si on Si growth. – Epitaxially grown layers are purer than the substrate
and can be doped independently of it. Heteroepitaxy – Film and substrate are different materials. – Eg: AlAs on GaAs growth – Allows for optoelectronic structures and band gap
engineered devices.
![Page 40: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/40.jpg)
HETEROEPITAXY Trying to grow a layer of a different material on top of
a substrate leads to unmatched lattice parameters. This will cause strained or relaxed growth and can
lead to interfacial defects. Such deviations from normal would lead to changes in
the electronic, optic, thermal and mechanical properties of the films.
![Page 41: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/41.jpg)
LATTICE STRAINS For many applications nearly matched lattices are
desired to minimize defects and increase electron mobility.
As the mismatch gets larger, the film material may strain to accommodate the lattice structure of the substrate. This is the case during the early stages of film formation (pseudomorphic growth) and with materials of the same lattice structure. The Si-Ge system is an example.
If strain accommodation is not possible then dislocation defects at the interface may form leading to relaxed epitaxy and the film returns to its original lattice structure above the interface.
![Page 42: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/42.jpg)
![Page 43: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/43.jpg)
LATTICE MISFITS AND DEFECTS If the lattice mismatch is less than ~9%, the initial
layers of film will grow pseudomorphically. Therefore very thin films strain elastically to have the
same inter-atomic spacing as the substrate. As film thickness increases, the rising strain will
eventually cause a series of misfit dislocations separated by regions of relatively good fit. As such they are equilibrium theories.
There is a critical film thickness, dc, beyond which dislocations are introduced.
![Page 44: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/44.jpg)
DEFECTS GE SI FILM The GeSi/Si system has a large lattice misfit built in
and as such is not an equilibrium system. This results in a large number of dislocations with few
regions of good fit and the theory breaks down. Rippled surfaces and pyramidal tips are typical.
![Page 45: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/45.jpg)
TYPES AND SOURCES OF DEFECTS Defects reduce electron mobility, carrier concentration
and optical efficiency. Current levels in Si are 1-10 defects/cm 2. Defects can propagate from the substrate as a screw
dislocations. Dopants and impurities can cause edge and point
dislocations. Another type of defect is the stacking faults where the
stacking order of successive layers do not follow a specific order.
![Page 46: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/46.jpg)
FORMATION OF MISFIT DISLOCATIONS They generally originate from threading dislocations at
the film-substrate interface. The dislocation pierces through the substrate and the
film. As it grows, it glides and bends in a slip plane. • Above the critical thickness ( dc) the increasing strain
allows a break and the film dislocation separates from the originating defect, leaving behind a stable misfit dislocation.
![Page 47: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/47.jpg)
Types of EpitaxyLiquid phase epitaxy- III-V epitaxial layer GaAs- Refreeze of laser melted siliconMolecular beam epitaxy- Crystalline layer grows in vacuum- 500o CVapor phase epitaxy- It is performed by chemical vapor deposition
(a)
(b)
(c)
(CVD)
- Provides excellent control of thickness, doping andcrystallinity- High temperature (800o C – 1100oC)
![Page 48: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/48.jpg)
Liquid phase epitaxy Growing crystals from
melting point .Melting point of GaAs
a liquid solution below their
is 1238oC whereas a mixtureof GaAs with Ga metal has considerably lowermelting point
Single crystal GaAs layer can be grown fromGa+GaAs melt.
The solution becomes richer in Ga melting point.
and thus lower
Low temperature eliminates many problems ofimpurity introduction.
![Page 49: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/49.jpg)
LIQUID PHASE EPITAXYGrowth of AlGaAs and GaAs layer on GaAs substrate
Wafer held on carbon slider
Moves into a pocket containing melt
Slider moves the substrate to the next chamber.
![Page 50: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/50.jpg)
Molecular beam
Substrate is held in high vacuum
epitaxy (MBE)
10-10in the range torr
in separateComponents along with dopants, are heatedcylindrical cells.
Collimated beams of these escape into directed into the surface of a substrate
the vacuum and are
Sample held at relatively low temperature (600oC for GaAs)Conventional temperature range is 400o C to 800oC Growth rates are in the range of 0.01 to 0.3 µm/min
![Page 51: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/51.jpg)
Equipment
![Page 52: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/52.jpg)
Equipment An ultra high vacuum chamber holding heated substrate. Furnaces holding electronic grade silicon and dopants. Beams of these dopants & EGS directed into the heated wafer. For attaining vacuum level in the 10–10 torr range, material should have a low vapor pressure and low sticking coefficient. Silicon volatized by electron beam heating rather than by
heating in furnace. Buffers & shutters shape and control flux. Resistance heating generates temperature over the range of400oC to 1100oC.
![Page 53: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/53.jpg)
Advantages of MBELow temperature processing (400oC-800oC)Precise control of dopingNo chemical reactions along with high thermal velocities results in properties rapidly changing with sourceA wider choice of dopantsMostly used dopants are Sb, Ga, Al
![Page 54: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/54.jpg)
Vapor phaseepitaxy
Crystallization from vapor phase
Better purity and crystal perfectionOffers great flexibility in the actual fabrication of devices
Epitaxial layers are generally grown on Si substrates by thecontrolled deposition of Si chemical vapor containing atoms if Si
e.g. SiCl4 + 2H2 Si + 4HCl(for deposition as well as for etching)
![Page 55: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/55.jpg)
Vapor Phase EpitaxyusedFour silicon sources have been
Silicon (Si)Silicon tetrachloride (SiCl4) Dichlorosilane (SiH2Cl2) Trichlorosilane (SiHCl3) Silane (SiH4)Four species in a reaction
for growing epitaxial
SiCl4 (gas) + 2H2 (gas) Si (solid) + 4HCl (gas)
at 1200o C were detected
![Page 56: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/56.jpg)
Concentration of species at different
positions along a horizontal reactor
![Page 57: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/57.jpg)
Overall reaction in VPE SiCl4 concentration decreases while the other three
constituents (SiHCl3, SiH2Cl2, HCl) increase
SiCl4 + H2
SiHCl3 + H2
SiH2Cl2 + H2
SiHCl3
SiCl2 + H2
SiHCl3 + HCl ……….. (1)SiH2Cl2 + HCl……….. (2)
SiCl2 + H2 …………(3)
SiCl2 + HCl …………. (4)Si + 2HCl ……………(5)
![Page 58: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/58.jpg)
Equipment
Weight 2000 KgOccupy 2m2 or more of floor space. Quartz reaction chamber withsusceptors
Graphite susceptors for physical supportA coating of silicon carbide (50 to500 µm) applied by CVD process on susceptors.Rf heating coil or tungsten halogen lamps.Radiant heatingWater cooling
![Page 59: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/59.jpg)
A radiant barrel reactor
![Page 60: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/60.jpg)
Three basic reactor configurations
![Page 61: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/61.jpg)
VPE process Hydrogen gas purges of air from the reactor . Reactor is heated to a temperature. After thermal equilibrium, an HCl etch takes place at
1150oC and 1200oC for 3 minutes nominally. Temperature is reduced to growth temperature. Silicon source and dopant flows are turned on. After growth, temperature is reduced by shutting off
power. Hydrogen flow replaced by nitrogen flow. Depending on wafer diameter and reactor type, 10 to 50 wafer
per batch can be formed. Process cycle times are about one hour .
![Page 62: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/62.jpg)
Doping Inentional addition of impurities or dopants to the
crystal to change its electronic properties (varying conductivity of semiconductors)
Doping of 1014 to 1017 atom/cm3
Typically hydrides of atoms are used as the source of
dopants eg. PH3, AsH3 or B2H6 for controlled doping
2AsH3 (gas) 2As (solid) + 3H2 (gas)2As (solid) 2As+ (solid) +
2e-
![Page 63: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/63.jpg)
Doping: Schematic representation ofarsine doping and growth processes
2AsH3 (gas) 2As2As
(solid) + 3H2 (gas)
2As+ (solid) + 2e–(solid)
![Page 64: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/64.jpg)
Doping: Impurity concentration Interaction between doping process & growth process Growth rate influences the amount of dopant incorporated in Si Equilibrium established at low growth rates.
![Page 65: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/65.jpg)
AutodopingOutdiffusion from heavily doped substrate Impurity incorporation from dopant in gas phase Autodoping limits the minimum layer thicknessGeneralized doping profile of an epitaxial layer detailing various regions of autodoping
![Page 66: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/66.jpg)
Minimizing Autodoping
• Fast growth to minimize outdiffusion.• Low temperature deposition reduces boron
autodoping (not As however).
• Seal backside of substrate withpolyoxide.
• Avoid the use of HCl etching.• Reduced pressure epitaxy.
highly doped
![Page 67: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/67.jpg)
Silicon on insulators• Fabrication of devices in small islands of silicon
on an insulating substrate eg. Silicon on Sapphire (Al2O3)
• Substrates have the appropriate thermal expansion match to silicon.
• Epitaxial films grown by CVD (eg. Pyrolysis of silane)
• Junction capacitance is reduced thus improve the high frequency operation of circuits
![Page 68: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/68.jpg)
Silicon on sapphire
SiH4 Si + 2H2 (low temperature)
• Temperature 1000o C – 1050oC• Growth rate 0.5 µm/min• Film thickness 1 µm or less
• Doping range 1014 1016 atoms/cm3to
• High defect density permits only majority carrier devices• Carrier mobility is reduced.
![Page 69: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/69.jpg)
Buried layerThe higher collector series resistance of an integrated transistor can be easily reduced by a process known as “buried layer”
•
![Page 70: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/70.jpg)
Silicon on sapphire devices
![Page 71: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/71.jpg)
Ultraviolet Silicon Detector
![Page 72: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/72.jpg)
APPLICATIONS
The driving force today is the fabrication of advanced electronic and optoelectronic devices.
Transistors (HEMT,HBT):
Microwave devices (IMPATT)
Optoelectronic devices (MQW) laser
![Page 73: Ic technology- chemical vapour deposition and epitaxial layer growth](https://reader036.vdocuments.net/reader036/viewer/2022062523/5872ffce1a28ab8c718b80df/html5/thumbnails/73.jpg)