UNIVERSITÀ DEGLI STUDI DI PADOVA
MSc Environmental Engineering
ICEA Department
Master Thesis
Federica Ruggero
FATE OF BIOPLASTICS IN COMPOSTING
Supervisor
Prof.ssa Ing. Maria Cristina Lavagnolo
A.Y. 2016-2017
Ringrazio i miei docenti
- La Professoressa Maria Cristina Lavagnolo
- Il Professor Paolo Salandin
- Il Professor Michele Modesti
- Il Professor Alberto Pivato
- Il Professor Alessandro Chiumenti
Un ringraziamento speciale a
- Mamma e Papà
- La mia Famiglia
- Annalisa Sandon
- Carlo Boaretti
- Moreno, direttore della mensa Piovego
- Il team di Voltabarozzo
- Elena, Giulia, Fiorella, Arianna, Federico, Jacopo
- Il laboratorio di Geotecnica
- Gli iWaste
- Gli amici di sempre
- I miei cumuli
Un pensiero ai miei nonni, le mie stelle
Federica
“Ogni scelta comporta una rinuncia e chi non sa rinunciare probabilmente non
sceglierà mai niente, facendo scegliere gli altri al suo posto, o farà sempre scelte che
non costano fatica. Le scelte che non costano fatica sono prive d'’amore. L'amore senza
le sue gambe resta nelle parole. Posso risparmiare sulla luce, ma mai sull'amore, perché
non so spegnere tutte le stelle che ho dentro."
M. Bisotti, La luna blu
Index
1. INTRODUCTION ............................................................................................................................ 1
1.1 The beginning ........................................................................................................................ 1
1.2 Introduction to the purpose of the research ........................................................................ 1
1.3 Legend of the acronyms for samples .................................................................................... 3
1.4 The research history .............................................................................................................. 4
2. PRELIMINARY STUDY TO THE RESEARCH ..................................................................................... 7
2.1 Bioplastic: the appearance of an environmentally responsible material ............................. 7
2.1.1 What are bioplastics? ..................................................................................................... 7
2.1.2 Why bioplastics have been introduced on the market? ................................................ 8
2.1.3 The main economic and environmental challenges of bioplastics .............................. 10
2.2 Knowing bioplastics ............................................................................................................. 12
2.2.1 Actual and forecast bioplastics production in Europe and Italy .................................. 12
2.2.2 New frontiers for the use of bioplastics ...................................................................... 15
2.2.3 Characteristics and production of compostable bioplastics ........................................ 17
2.3 Bioplastics in composting .................................................................................................... 21
2.3.1 The composting process: phases, parameters, waste to composting ......................... 21
2.3.2 Bioplastics and composting in scientific papers .......................................................... 24
2.4 Standards for definition of bioplastics compostability ....................................................... 26
2.4.1 Full scale standards ...................................................................................................... 26
2.4.2 Pilot scale standards .................................................................................................... 29
2.4.3 Lab scale standards ...................................................................................................... 32
2.4.4 Certification of compostability .................................................................................... 34
3. MATERIALS AND METHODOLOGIES ........................................................................................... 37
3.1 Composting process ............................................................................................................ 37
3.1.1 Analyses of the composting process parameters ........................................................ 38
3.1.2 Sieving analyses for the granulometric curve .............................................................. 40
3.2 Evaluation of bioplastics disintegration and degradation in composting ........................... 41
3.2.1 Sieving analyses of bioplastics disintegration .............................................................. 42
3.2.2 Bioplastics concentration ............................................................................................. 44
3.2.3 IR analyses of degrading bioplastics spectra ............................................................... 45
3.2.4 Visual analyses of bioplastics changing features ......................................................... 48
3.3 Samples preparation and characterization ......................................................................... 49
3.3.1 Choice of the initial conditions .................................................................................... 49
3.3.2 Choice of the constant values and variables of the tested material ........................... 50
3.3.3 Characterization of the compostable matrix ............................................................... 55
3.3.4 Location of the tests and their mounting .................................................................... 57
4. RESULTS AND DISCUSSION......................................................................................................... 65
4.1 Analyses of the composting process parameters ............................................................... 65
4.1.1 Temperature ................................................................................................................ 65
4.1.2 Weight .......................................................................................................................... 66
4.1.3 Total and volatile solids ............................................................................................... 69
4.1.4 pH ................................................................................................................................. 71
4.1.5 TKN and nitrates........................................................................................................... 71
4.1.6 TOC and inorganic carbon ............................................................................................ 73
4.1.7 C/N ............................................................................................................................... 74
4.1.8 Respirometric Index (RI)............................................................................................... 74
4.2 Sieving analyses for the granulometric curve ..................................................................... 76
4.3 Evaluation of bioplastics disintegration and degradation in composting ........................... 78
4.3.1 Sieving analyses of bioplastics disintegration .............................................................. 78
4.3.2 Bioplastics concentration ............................................................................................. 88
4.3.3 IR analyses of degrading bioplastics spectra ............................................................... 95
4.3.4 Visual analyses of bioplastics changing features ....................................................... 101
5. CONCLUSIONS .......................................................................................................................... 105
REFERENCES ..................................................................................................................................... 109
Bibliography ................................................................................................................................. 109
Sitography .................................................................................................................................... 112
ANNEXES .......................................................................................................................................... 113
I. ANNEX: Composting process parameters ................................................................................ 115
II. ANNEX: Granulometric curves ................................................................................................. 125
III. ANNEX: Bioplastics concentration ........................................................................................... 132
IV. ANNEX: IR analyses .................................................................................................................. 135
LIST OF FIGURES
Figure 1.1-Experimental part of the thesis work - Line 1 .................................................................... 4
Figure 1.2-Experimental part of the thesis work - Line 2 .................................................................... 5
Figure 2.1-Subdivision of bioplastics according with European Bioplastics ........................................ 7
Figure 2.2-Graph of economic model linking demand and supply (www.khanacademy.org) ............ 9
Figure 2.3-Global production of bioplastics in 2016 (www.european-bioplastics.org) .................... 13
Figure 2.4-Biodegradable and non-biodegradable bioplastics production (www.european-
bioplastics.org) ................................................................................................................................... 13
Figure 2.5-Novamont bioplastic bags and food packaging (www.materbi.com) .............................. 15
Figure 2.6-Shopping biobags and bags for the collection of the organic fraction (brand-finder-
italy.info) ............................................................................................................................................ 15
Figure 2.7-Cutlery, ice cream cup and food packaging. From catalogue of Ecozema
(www.ecozema.com) ......................................................................................................................... 16
Figure 2.8-Packaging for egg and packaging for ice cream (www.alcas.it) ....................................... 16
Figure 2.9-Coffee capsules (corriereinnovazione.corriere.it) and packaging film and cups in Mater-
Bi (www.materbi.com) ....................................................................................................................... 16
Figure 2.10-Packagings for drugs and personal care products (www.lameplastgroup.com,
www.vib.be) ....................................................................................................................................... 16
Figure 2.11-Use of bioplastics for stationary items and mulching (www.novamont.com) ............... 17
Figure 2.12-Starch chemical structure ............................................................................................... 18
Figure 2.13-Mater-Bi in granular form. They are made on corn-starch and biodegradable polyesters
(www.novamont.com) ....................................................................................................................... 19
Figure 2.14-transparent granules of PLA (www.solostocks.it) .......................................................... 20
Figure 2.15-Cellulose after delignification (www.hempplastic.com) ................................................ 21
Figure 2.16-Phases of composting (www.researchgate.net) ............................................................ 23
Figure 2.17-Labels certifying compostability (www.materbi.com) ................................................... 34
Figure 2.18-Labels of Vinicotte certifying compostability (www.materbi.com) ............................... 35
Figure 3.1-Manual sorting of bioplastics (F. Ruggero, 2017) ............................................................. 43
Figure 3.2-Starting of sedimentation, mixing, BioPOF after 2 hours of sedimentation (F. Ruggero,
2017) .................................................................................................................................................. 43
Figure 3.3-IR machinery (F. Ruggero, 2017) ...................................................................................... 46
Figure 3.4-Comparison between spectra of four different bioplastic bags distributed in the Italian
markets .............................................................................................................................................. 47
Figure 3.5-Spectra of polymers composing BioP ............................................................................... 48
Figure 3.6-Bioplastics aspect after the removal from composting (F. Ruggero, 2017) ..................... 49
Figure 3.7-Small bioplastics size and big bioplastics size (F. Ruggero, 2017) .................................... 50
Figure 3.8-Composting of organic fraction from separate collection in Italy. (ISPRA, 2015) ............ 51
Figure 3.9-Quantity of municipal solid waste disposed of in composting plants in Italy. (ISPRA, 2015)
............................................................................................................................................................ 51
Figure 3.10-Fractions of waste to composting. (ARPAV 2015) .......................................................... 52
Figure 3.11-30% increase in bioplastics production all over the world. (www.european-
bioplastics.org) ................................................................................................................................... 53
Figure 3.12-Food waste, wood chips, clipping glass and inoculum to compose OFi (F. Ruggero, 2017)
............................................................................................................................................................ 55
Figure 3.13-OFi composition in percentages ..................................................................................... 56
Figure 3.14-Photographs of materials supplied for the experimentation (F. Ruggero, 2017) .......... 57
Figure 3.15-Scheme of the samples od line 1 .................................................................................... 58
Figure 3.16-Working on the sample building (F. Ruggero, 2017) ...................................................... 59
Figure 3.17-Heaps aspect immediately after their building, and coverage for the night (F. Ruggero,
2017) .................................................................................................................................................. 60
Figure 3.18-Heaps on their baskets, on tables inside the container (F. Ruggero, 2017) .................. 60
Figure 3.19-The place for compostable heaps (F. Ruggero, 2017) .................................................... 61
Figure 3.20-Line 2: OF, BioPOF small, BioPOF big (F. Ruggero, 2017) ............................................... 61
Figure 3.21-Scheme of the two lines with the respective heaps ....................................................... 62
Figure 3.22-Line 1 and Line 2 with blanks and heaps containing the tested material (F. Ruggero,
2017) .................................................................................................................................................. 63
Figure 4.1-Comparison between outside temperature and heaps temperature - Line 1 ................. 65
Figure 4.2-Mean temperatures during the phases of composting process ...................................... 66
Figure 4.3-Total weight of composted heaps- Line 1 ........................................................................ 67
Figure 4.4-Total weight of composted heaps- Line 2 ........................................................................ 67
Figure 4.5-Dry weight of composted heaps- Line 1 ........................................................................... 68
Figure 4.6-Dry weight of composted heaps- Line 2 ........................................................................... 69
Figure 4.7-Moisture content - Line 2 ................................................................................................. 70
Figure 4.8-TKN behaviour during the composting process – Line 2 .................................................. 72
Figure 4.9-TOC behaviour during the composting process - Line 2 ................................................... 73
Figure 4.10-RI 4 normalized on volatile solids ................................................................................... 75
Figure 4.11-Sieved fractions 10th day, OF (F. Ruggero, 2017) .......................................................... 76
Figure 4.12-Ssieved fractions 25th day, BioPOF small (F. Ruggero, 2017) ........................................ 76
Figure 4.13 Sieving operation (F. Ruggero, 2017) .............................................................................. 77
Figure 4.14-Granulometric curve example ........................................................................................ 77
Figure 4.15-The main waste components of each granulometric fraction ....................................... 78
Figure 4.16-BioPi small size at the beginning of the test ................................................................... 79
Figure 4.17-BioPi big size at the beginning of the test ...................................................................... 79
Figure 4.18-Histograms of BioP small granulometry – Line 1 ............................................................ 80
Figure 4.19-Histograms of BioP small granulometry – Line 2 ............................................................ 81
Figure 4.20-Histograms of BioP big granulometry – Line 1 ............................................................... 82
Figure 4.21-Histograms of BioP big granulometry – Line 2 ............................................................... 83
Figure 4.22-Model of prevision of bioplastics disintegration ............................................................ 87
Figure 4.23-Bioplastic lumps formed during the composting process .............................................. 90
Figure 4.24-BioP concentration trend during the composting process ............................................ 90
Figure 4.25-Range of BioP small weight during the composting process ......................................... 93
Figure 4.26-MicroBioP concentration during the composting process ............................................. 94
Figure 4.27-comparison between 10th and initial spectra of BioP ................................................... 95
Figure 4.28-PBAT chemical structure ................................................................................................. 96
Figure 4.29-Comparison between 25th and initial spectra of BioP ................................................... 97
Figure 4.30-Comparison between 40th and initial spectra of BioP ................................................... 98
Figure 4.31-Comparison between 55th and initial spectra of BioP ................................................... 99
Figure 4.32-Comparison between spectra of BioP during the composting process ....................... 100
Figure 4.33-Spectrum of a BioP sample submitted to a temperature of 60 °C in the oven ............ 100
Figure 4.34-Photographs of bioplastic samples taken during the composting process (F. Ruggero,
2017) ................................................................................................................................................ 101
Figure 4.35-MicroBioP aspect after 55 days (F. Ruggero, 2017) ..................................................... 102
Figure 4.36-Bioplastics stickiness (F. Ruggero, 2017) ...................................................................... 103
Figure 4.37-Comparison between the internal and the external side of a sticky bioplastic piece . 104
Figure I.1-Outside temperature during the small scale test ............................................................ 115
Figure I.2-Comparison between outside temperature and heaps temperature - Line 2 ................ 115
Figure I.3-Temperature during composting process - Line 1 ........................................................... 116
Figure I.4-Temperature during composting process - Line 2 ........................................................... 116
Figure I.5- Moisture content - Line 2 ............................................................................................... 118
Figure I.6-Volatile solids - Line 1 ...................................................................................................... 119
Figure I.7-Volatile solids - Line 2 ...................................................................................................... 119
Figure I.8-TKN behaviour during the composting process - Line 1 .................................................. 120
Figure I.9-TOC behaviour during the composting process - Line 1 .................................................. 121
Figure I.10-RI 4 normalized on total solids ...................................................................................... 122
Figure I.11--RI 7 normalized on volatile solids ................................................................................. 123
Figure I.12-RI 7 normalized on total solids ...................................................................................... 124
Figure II.1-Granulometric curve OF ................................................................................................. 125
Figure II.2-Granulometric curve OF ................................................................................................. 125
Figure II.3-Granulometric curve BioPOF small ................................................................................. 126
Figure II.4-Granulometric curve BioPOF small ................................................................................. 126
Figure II.5-Granulometric curve BioPOF big .................................................................................... 127
Figure II.6-Granulometric curve BioPOF big .................................................................................... 127
Figure III.1-Graph of weight range of BioP small - Line 1 ................................................................ 132
Figure III.2-Graph of weight range of small BioP - Line 2 ................................................................ 133
Figure III.3-Graph of weight range of big BioP - Line 1 .................................................................... 134
Figure III.4-Graph of weight range of big BioP - Line 2 .................................................................... 134
Figure IV.1-Aspect of bioplastic pieces submitted to IR analysis ..................................................... 135
Figure IV.2-Spectra at the 10th day of the biggest granulometric fractions ................................... 136
Figure IV.3-Spectra at the 10th day of the biggest granulometric fractions ................................... 136
Figure IV.4-Spectra at the 10th day of the smallest granulometric fractions ................................. 137
Figure IV.5-Spectra at the 25th day of the biggest granulometric fractions ................................... 137
Figure IV.6-Spectra at the 25th day of the biggest granulometric fractions ................................... 138
Figure IV.7-Spectra at the 25th day of the smallest granulometric fractions ................................. 138
Figure IV.8-Spectra at the 25th day of the smallest granulometric fractions ................................. 139
Figure IV.9-Spectra at the 40th day of the biggest granulometric fractions ................................... 139
Figure IV.10-Spectra at the 40th day of the biggest granulometric fractions ................................. 140
Figure IV.11-Spectra at the 40th day of the smallest granulometric fractions ............................... 140
Figure IV.12-Spectra at the 55th day of the biggest granulometric fractions ................................. 141
Figure IV.13-Spectra at the 55th day of the smallest granulometric fractions ............................... 141
Figure IV.14-Spectra at the 55th day of the smallest granulometric fractions ............................... 142
LIST OF TABLES
Table 2.1-Compostable bioplastics forecast production in Italy ....................................................... 14
Table 2.2-Parameters to define compost maturity ........................................................................... 24
Table 2.3-Requirements of 14045:2003 for physico-chemical characterization of the biowaste
sample ................................................................................................................................................ 30
Table 2.4-Sieving Scheme from EN 14045:2003 ................................................................................ 31
Table 2.5-Requirements of 14806:2005 for physico-chemical characterization of the waste sample
............................................................................................................................................................ 33
Table 3.1-Timing of the process parameters analyses ...................................................................... 38
Table 3.2-Yearly production of organic waste pro capite in Veneto. ARPAV 2015 ........................... 52
Table 3.3-Proportions between waste to composting and bioplastics produced ............................. 54
Table 3.4-Paramters of the single components of the waste matrix ................................................ 56
Table 3.5-Weighted average of the parameters required by composting standards ....................... 56
Table 3.6-Weight of basket and tray for test storage ........................................................................ 59
Table 4.1-Total weight of heaps during composting process ............................................................ 68
Table 4.2-Dry weight of heaps during composting process .............................................................. 69
Table 4.3-pH ....................................................................................................................................... 71
Table 4.4-TKN in grams ...................................................................................................................... 72
Table 4.5-TOC in grams ...................................................................................................................... 73
Table 4.6-C/N (TOC on TKN) ............................................................................................................... 74
Table 4.7-RI 4 normalized on volatile solids ...................................................................................... 75
Table 4.8-BioPOF small granulometry - Line 1 ................................................................................... 84
Table 4.9-BioPOF small granulometry - Line 2 ................................................................................... 84
Table 4.10-BioPOF big granulometry - Line 1 .................................................................................... 84
Table 4.11-BioPOF big granulometry - Line 2 .................................................................................... 84
Table 4.12-Mean size of bioplastics during the composting process ................................................ 86
Table 4.13-BioP small concentration in BioPOF ................................................................................. 89
Table 4.14-BioP big concentration in BioPOF .................................................................................... 89
Table 4.15-Range of variability in bioplastics weight ........................................................................ 92
Table 4.16-Bioplastics weight variation range in percentage, with respect to the initial value ....... 93
Table I.1-Moisture content .............................................................................................................. 117
Table I.2-Total solids ........................................................................................................................ 117
Table I.3-Volatile solids .................................................................................................................... 118
Table I.4-TKN normalized with total solids ...................................................................................... 120
Table I.5-TOC normalized with TS .................................................................................................... 121
Table I.6-RI 4 normalized on total solids .......................................................................................... 122
Table I.7-RI 7 normalized on volatile solids ..................................................................................... 123
Table I.8-RI 7 normalized on total solids .......................................................................................... 124
Table II.1-Granulometry 10th day OF .............................................................................................. 128
Table II.2-Granulometry 10th BioPOF small .................................................................................... 128
Table II.3-Granulometry 10th day BioPOF big ................................................................................. 128
Table II.4-Granulometry 25th day OF .............................................................................................. 129
Table II.5-Granulometry 25th day BioPOF small .............................................................................. 129
Table II.6-Granulometry 25th BioPOF big ........................................................................................ 129
Table II.7-Granulometry 40th day OF .............................................................................................. 130
Table II.8-Granulometry 40th day BioPOF small .............................................................................. 130
Table II.9-Granulometry 40th day BioPOF big ................................................................................. 130
Table II.10-Granulometry 55th day OF ............................................................................................ 131
Table II.11-Granulometry 55th day BioPOF small ............................................................................ 131
Table II.12-Granulometry 55th day BioPOF big ............................................................................... 131
Table III.1-Weight range of BioP small - Line 1 ................................................................................ 132
Table III.2-Weight range of BioP small - Line 2 ................................................................................ 133
Table III.3-Weight range of BioP big - Line 1 .................................................................................... 133
Table III.4-Weigh range of BioP big - Line 2 ..................................................................................... 134
1
1. INTRODUCTION
1.1 The beginning
The topic of bioplastics degradation in composting was proposed to me as a new research on
which nobody had even worked before. The consequence of working on a new topic is that probably
the most of problems met during the experimental part will be unexpected and they will not have
a previously adopted solution. But I wanted to welcome this challenge for two reasons: on the one
hand, driven by personal motivation to undertake a research path that would have shown me, with
all its difficulties, if in this field I could make my plans for the future. On the other hand, I found that
this research was significant of what an environmental engineer should do with his job. His task is
to continuously wonder if the technologies, the materials, the processes, the innovations used in
our world are compatible with a sustainable development: nowadays ever new products are
immitted on the market, new industrial processes are elaborated to ensure a faster and more
efficient production, new sources of energies are searched and so on, but it is not always proven
that a better solution for the economy, is also a better solution for the environment, the human
health and the sustainable development.
The question on the fate of bioplastics after waste management in the composting process, gave
me the opportunity to enter in this world of environmental engineering, investigating the possible
long-term impact on the environment of a recent material.
1.2 Introduction to the purpose of the research
Bioplastics now form part of the collective imagination, even though they have been in
circulation since 1980s. Production of these materials have been growing; the numbers from
European Bioplastics show that 1.13 million tons of bioplastics were produced in Europe in 2016,
with an increase of 30% forecast by 2021.
The definition of bioplastics includes two features that can be present both simultaneously or one
without the other: biodegradability and originating from renewable resources (European
Bioplastics, 2016). The bioplastics with both characteristics, which are 23.2% of the total amount,
fall into the field of this research.
2
It’s fair to say that the growing production and distribution of bioplastic products is related to the
possibility to satisfy two societal needs: firstly, having a material with features and uses similar to
plastic, which is so widely exploited in everyday life that in Europe it corresponds to 30.4% of the
waste produced (Ispra, 2015). Secondly, the emergent need for sustainability. Bioplastics are an
environmental responsible material (Karana, 2012), with a production chain cleaner than plastics:
starting from the extraction of renewable resources to the return to earth trough waste disposal.
Some commonly used bioplastics are biodegradable and compostable, therefore the
degradation time is much shorter than the hundreds of years required by plastics, and the
certification EN 13432 allows their disposal of in composting plants. Composting is an aerobic
biological treatment where organic waste can be broken down through the living activity of
microorganisms, and it is divided into two phases: the thermophilic and the maturation phases
(Bidlingmaier, 2016). In accordance with the above mentioned standard, the two characteristics
required for bioplastics to be disposed of in a composting plant are described as follows:
biodegradation is the breakdown of an organic chemical compound by microorganisms, while
compostability is a property of a packaging material to be biodegraded in a composting process. To
evaluate this property, the disintegration of the tested material has to be assessed and no more
than 10% of the initial material should fail to pass a 2 mm sieve at the end of the process.
The fate of bioplastics at the end of the composting process may not be a complete
disappearance but disintegration into microscopic pieces, and release on to cultivated fields through
compost in the form of microplastics, which are less than 5 mm in size (Thompson et al., 2009).
Some research in recent years has been aimed at dealing with problems posed by microplastics,
from identification, and enumeration, to extraction and cleaning of aquatic and terrestrial
environments (Horton et al., 2016, Qiu et al., 2016). Microplastics due to their small size, abundance,
attractive colours and similarity with food, are easily bioavailable for the species of the lowest
trophic levels and consequently acccumulable in the food chain (Wright et al., 2013). Furthermore,
bioplastics after composting are sticky; they start to melt due to the high temperatures during the
process and to the increase in moisture after having been in contact with putrescible waste. Sticky
microplastics deriving from disintegration can stay attached to crop foods, soil grains and
vegetation.
The possible release into the environment of bioplastic fragments after composting raises
an issue: bioplastics can be dispersed in soil through the fertilization of fields and reach waterways
with run off during rainfall events, thus being in a new environmental condition that affects their
3
potential to conclude degradation. The result and the timing will vary depending upon the
environment, and in accordance with the varying outside temperature and humidity (Mehdi et al.,
2016).
The object of the research is to investigate the fate of bioplastics during the composting
process, in order to follow their biodegradation and disintegration up to release into the
environment. With the growing use of bioplastics, the research has also developed to evaluate their
effective potential for biodegradability; the analyses carried out mainly at lab scale demonstrated
that bioplastics have different potential according to the polymers of which they are composed
(Tabasi e Ajji, 2015): starch, PLA, PHB, PCL, PBAT. The temperature also has a significant influence;
constant room temperature causes a low degradation (Mohee et al., 2008), while maintaining the
process at the thermophilic phase for a long period can lead to a higher degradation (Balaguer et
al., 2015, Javierre et al., 2015). Since the aim of this research is to obtain results that reflect the real
world, the tests have been carried out on a small scale with the inclusion of some typical variables
of a composting process, such as outside temperature and humidity changes, waste mixture, waste
and bioplastics size.
1.3 Legend of the acronyms for samples
To simplify the names of the components within the tests, some acronyms will be adopted from
now to the end of the research, and each of them identifies the moment of the test, the starting
point and the end, and the matrix with or without bioplastics.
OFi = organic matrix to composting, without bioplastics, at the beginning of the test
BioPi = initial bioplastics
BioPOFi = matrix composed of organic waste and bioplastics
OFf = matrix obtained at the end of composting, without bioplastics. Or simply compost without
bioplastics
BioPf = final bioplastics
BioPOFf = matrix obtained at the end of composting, with final bioplastics. Or simply compost with
bioplastics.
MicroBioP = Micro-Bioplastics, bioplastics smaller than 5 mm
4
1.4 The research history
My master thesis work was composed on three parts: the first two months were dedicated to
the research of methods available to the evaluation of biodegradability and compostability of
bioplastics already applied in laboratory tests by other authors.
The bibliographic study was followed by a personal elaboration of the methods used in the
experimental part of the thesis to reach the purpose of the study.
The next four months involved the preparation of the experimental part and the actuation of it
(Figure 1.1 and 1.2), including the analyses to be carried out on the composting process and those
on bioplastic material.
The last part was the elaboration of the obtained data and the writing of the thesis.
Figure 1.1-Experimental part of the thesis work - Line 1
5
Figure 1.2-Experimental part of the thesis work - Line 2
6
7
2. PRELIMINARY STUDY TO THE RESEARCH
2.1 Bioplastic: the appearance of an environmentally responsible material
2.1.1 What are bioplastics?
Bioplastic materials appeared for the first time on the market at the turn of the years 1980s and
1990s, but the history of this new product is more in the future than in the past: in fact, in
accordance with a study lead by the Hannover University, the production of bioplastics had been
increasing until 2016 of 500%.
Bioplastics, or biopolymers, are an alternative for almost every conventional plastic material and
corresponding application, having similar properties as conventional plastics.
The definition of bioplastic materials coming from the European Bioplastics includes the
consideration of them as an eco-friendly alternative to petrochemical polymers due to the
renewable feedstock used to produce them and to their biodegradability.
Considering both the source, which can be renewable resources or fossil resources, and the final
degradation, made by bacteria or not, biopolymers are subdivided into three groups (Figure 2.1):
- Biobased or partially biobased non-biodegradable plastics such as biobased PE, PP, or PET;
- Plastics that are both biobased and biodegradable, such as PLA and PHA or PBS;
- Plastics that are based on fossil resources and are biodegradable, such as PBAT, PCL, PVA.
Figure 2.1-Subdivision of bioplastics according with European Bioplastics
8
2.1.2 Why bioplastics have been introduced on the market?
Plastic is a material with a widespread use all over the world; in accordance with ISPRA, the
amount of plastic waste corresponds to 30,4 % of the total amount of waste produced by a person
per year in Europe.
Data about waste production in 2013 resulted in a yearly production of 481 kg/ca, therefore plastic
waste was about 150 kg/ca*y.
Due to environmental problems linked with plastic materials, in the last two decades the demand
for solutions to move to a society that has its production based on environmentally responsible
materials has rapidly increased.
Since the 1990s, many companies have moved from the pollution prevention, to the so called green
chemistry as a more fundamental way to achieve sustainability. Green chemistry is a broad term
which refers to a chemical production that aims to reduce environmental and health hazards to
advance sustainability.
The major challenge, as discussed later, is to find ways to integrate sustainable innovations and new
eco-friendly materials into the market.
In fact, industry’s business models include that costumers are interested in buying the new product
emitted on the market, and a central role in linking producers and customers is the awareness and
the knowledge of benefits achieved with the use of bioplastics and environmental problems caused
by plastic materials.
Bioplastics are a clean material which can be used for food packaging without risk of food
contamination by additives, plasticizers or other potentially health hazardous substances present
instead in non-biobased plastics.
Their production chain is cleaner than that of plastics from non-renewable resources: the main
concerns with which plastic must face and that can in part be solved by new biobased materials,
are, during the production phase, the use of non-renewable resources, and, during the disposal
phase, waste generation and emissions into the environment.
Fossil fuel is the non-renewable resource employed for processes of plastic realization, and its
availability is bound to end, so future generations will be obliged to find alternative solutions for
energy production and for all the materials commonly used in everyday life coming from fossil fuel.
Furthermore, from an economic point of view, the price of this non-renewable resources has been
fluctuating in the last years and, once the equilibrium point is overcome, it is bound to increase in
9
accordance with the inverse relationship between the increasing demand and decreasing supply
(Figure 2.2).
So, concerning the raw materials, the use of renewable resources is a strategy to reduce the
dependency on fossil resources and to reduce CO2 emissions.
Figure 2.2-Graph of economic model linking demand and supply (www.khanacademy.org)
Finally, as concerns the use of energy for processes of material production, light-weight, resistance
to corrosion and low temperature processing of bioplastics often result in energy savings.
Concerning plastic waste disposal, because of longevity and widespread use, managing plastic waste
is actually a major problem. Unlike the materials they have replaced, such as glass and metal, the
recycling of plastics has been less successful due to difficulties in identification and sorting and the
presence of various other materials and additives, as fillers and plasticizers.
Plastics are organic materials so they can be potentially incinerated in order to reduce their volume
and produce energy, but if this process is uncontrolled or poorly managed, it can result in hazardous
emissions, such as dioxins from PVC.
So, even if the previously described processes are nowadays used for plastic waste management, a
part of them is also disposed of in landfills, which, due to the increasing waste production, have a
lowering capacity.
Bioplastic materials have much shorter degradation time than the one thousand years of
plastics, and they offer different solutions for management of final waste: one possibility is
recycling, but it is strictly regulated in accordance with some studies of European Bioplastics and
CONAI.
10
In fact, the analyses carried out on bioplastics recycling together with virgin plastics showed that
the they don’t negatively influence the recovery of plastics in an amount less than 10%. Moreover,
bioplastics collected together with virgin plastics that will be led to a recycling plant must not be
contaminated with food scraps.
The second option, widely discussed in this thesis, is composting bioplastics together with organic
and green waste, in accordance with UNI EN 13432.
Using this way, the period necessary for waste disposal is only few months (in accordance with
particularly well defined conditions), reducing both costs for management and time during which
disposal plant is occupied by those waste. Composting leads also to the production of a fertilizer, so
it can be considered as a form a recycling itself.
2.1.3 The main economic and environmental challenges of bioplastics
The question is if it is possible to introduce bioplastics in a new way, so that they will be
perceived as natural and high quality product by society. This paragraph aims to analyse two doubts:
people can like bioplastics as they like plastics? And are they effectively materials coming from
nature and retuning back to nature in a short period?
Over the last decades, plastics have been fundamental for the progression of our man-made
environment. But the appreciation of plastics and how they are received by costumers has changed
over time in different societies; in fact, when they first emerged, they stood for cheapness, low
quality and in-authenticity, and their tactile experience was generally unsatisfactory for people
(Sparke, 1990). They were not brilliant, not heavy and not so hard as porcelain or iron.
However, with parallel improvements of their technical and sensorial qualities and with
breakthrough applications, the value attributed to plastics has drastically increased.
After the establishment of the new status, critiques on environmental impacts and disposal
management stimulated severe reactions on the use of plastics.
It’s also fair to say that, even if bioplastics are not very diffuse on the market and people are not
sure about their properties and application, along the next decades they will supply to the needs of
population, both social and environmental needs.
From the point of view of bioplastics mechanical properties, generally additives are used to improve
resistance and hardness, because the most of these bioplastic materials alone, especially in the food
11
packaging, have brittleness, stiffness, high sensitivity to moisture, high water sensitivity, poor
impact resistance and thermal instability (Balaguer et al., 2015).
Additives used to improve these properties are not always biobased, because this type of market is
nowadays not so developed, but some tests have been carried out to obtain new results in this field.
Obviously, companies have the heavy burden of integrating bioplastics and all biobased materials
linked with bioplastics, as biobased additives, in their traditional boundaries.
It’s not an easy question to face, because the emerging bioplastic sector poses new technical,
business and infrastructure challenges that companies are still learning to address. To develop
bioplastic product lines, chemical companies must attend to changing customer need, markets, and
socio-political conditions together with the organizational, scientific, and marketing challenges of
integrating industrial biotechnologies and agricultural resources into their supply chain in ways that
can maximize existing manufacturing systems and demonstrate ecological value.
Companies need to develop the so called dynamic capabilities, which mean internal processes
creating, replacing and adjusting a business model in response to changing business environments
and new customer needs, in a way that doesn’t imply a high failure risk (Iles and Martin, 2010).
Finally, it must be addressed the annoying question of environmental challenges presented by
bioplastics.
Although biopolymers do not rely on fossil resources as a feedstock, the agricultural, milling, and
production stages consume large amounts of energy, currently mainly derived from fossil fuel
themselves.
There are additional environmental burdens associated with the agricultural stage, such as nitrogen
and phosphorous emissions from fertilizers which result in eutrophication.
Other issues which may be raised concerning agriculture-derived biopolymers are finite land
resources, the resulting competition with food crops, and their vulnerability to crop failure from
flooding or drought. Crank et al. (2005) stated that if biopolymer consumption has a high growth
rate, as forecast, there may be some conflict of interest with bioenergy crops around 2050.
Additionally, Colwill et al (2012) predicted that in the same year all crop and grazing land would not
be sufficient to meet the demand for food, liquid fuels and plastics, resulting in the fact that if grass
and forest land do require clearing to make space for biopolymer feedstock cultivation, the indirect
greenhouse gas emissions associated with this need, may cancel out any carbon savings.
12
But the environmental problem with which this thesis faces, is the possible generation of
microplastics and bioplastics litters after composting process. In fact, if they don’t completely
biodegrade during disposal process, they will be discharged in landscapes together with compost,
resulting in their diffusion into the environment.
2.2 Knowing bioplastics
2.2.1 Actual and forecast bioplastics production in Europe and Italy
Data about production of bioplastics were found from three different sources: European
Bioplastics documents, an article by Assobioplastiche and an article by MaTech.
There is a great difference between them, but a constant question is underlined by all the sources:
the increasing trend in biodegradable bioplastics production, which makes difficulties in giving a
precise prevision for the next years.
In fact, from 2011 to 2016 the production was quintupled, and actually more and more products
usable not only for packaging but also for many different purposes are being launched on the
market.
So, all the data given by the three sources had been considered and evaluated to set the quantity
of bioplastics in the samples to carry out the analyses.
The first information is given by Assobioplastiche, not at European level but at national level:
it is just a prevision. In fact, data are related to 2015, with an estimated production of 0.0545 million
tonnes, increased of 25% with respect to 2014.
The value for 2018 production can be arranged around 0.11 million tonnes, basing this estimation
basically on two points: firstly, the increasing trend of industries to create new and better biobased
materials instead of plastic from non-renewable resources. Secondly, Italy with Mater-Bi produced
by Novamont, is at the forefront in this sector and can be considered one of the major
manufacturers of compostable bioplastics in Europe.
From European Bioplastics, in 2016 the global production of bioplastic was estimated to be
about 4.16 million tonnes, distributed in the regions of the world in accordance with figure 2.3.
In particularly, the production in Europe was about 27.1 % of the total amount, corresponding to
1.13 million tonnes.
13
Figure 2.3-Global production of bioplastics in 2016 (www.european-bioplastics.org)
Furthermore, in the same document it is specified that not all the bioplastics produced are
biodegradable and compostable: as the topic of this study are mainly compostable bioplastics, the
graph with the percentages of biodegradable and non-biodegradable materials is shown in figure
2.4.
Figure 2.4-Biodegradable and non-biodegradable bioplastics production (www.european-bioplastics.org)
Among the 23.2% of biodegradable bioplastics, it’s possible to underline the prevalent production
of starch based materials (10.3%), which is in accordance with the recent appearance and
development on the market of a new starch based bioplastic, called Mater-Bi.
14
To conclude, the quantity of biodegradable bioplastics produced in Europe in accordance with
European Bioplastics agency, is equal to 0.26 million tonnes.
As the analyses on bioplastics are carried out considering Italian waste and bioplastics production,
from the European production it’s possible to reach the Italian production through a simple
proportion.
In Europe, there are about 750 million inhabitants, while in Italy about 60 million: the bioplastic
million tonnes produced in Italy in accordance with the proportion is 0.021.
But, considering also the two points already evaluated in the Assioplastiche previsions for what
concerns Italian production, this quantity could be doubled, reaching 0.050 million tonnes.
Furthermore, another interesting question pointed out by European Bioplastics, is the potential
increase in bioplastics production up to 30% into five years.
Data provided by MaTech are a prevision given in 2013 for 2016, for a production in Europe
of about 5-6 million tonnes of bioplastic materials; considering 25% of them biodegradable, the
quantity to consider for the study could be around 1.5 million tonnes.
With the same proportion use for European Bioplastics prevision, the Italian production can be
arranged around 0.12 million tonnes.
Finally, in table 2.1 are summarized the quantities obtained considering the previsions provided by
these three different bibliographic sources.
Table 2.1-Compostable bioplastics forecast production in Italy
References MaTech Assobioplastiche European Bioplastics
Compostable bioplastics produced
in Europe
5-6*10 6 ton * 0.25 = 1.5*106 ton.
1.23*10 6 ton * 0.232 =
0.26*106 ton
Compostable bioplastics produced
in Italy
1.5∗60
750 = 0.12*10 6 ton 0.11*106 ton
1.5∗60
750 = 0.021*10 6 ton
Million tonnes of compostable
bioplastics in Italy 2016-2018
0.12 0.11 0.050
15
2.2.2 New frontiers for the use of bioplastics
Bioplastics have been initially applied in the packaging sector: bags for the separate collection
of the organic fraction, shopping bags especially in food stores, packaging for food products and
gloves used in the supermarkets to take fruits and vegetables.
In figure 2.5 packaging bags taken from Novamont internet site, while in figure 2.6 some pictures
about other bags made using Mater-Bi.
Figure 2.5-Novamont bioplastic bags and food packaging (www.materbi.com)
Figure 2.6-Shopping biobags and bags for the collection of the organic fraction (brand-finder-italy.info)
These products have spread very quickly on the market for the last five years; in Italy since 21 August
2014 it has been even banned the commercialization of shopping bags non-compliant with UNI EN
13432:2000.
Furthermore, industries of other different products are trying to adapt their production to this new
trend of using bioplastics: innovation with disposable cutlery in PLA, plates and cups for ice cream
made of cellulose of cardboard plus Mater-Bi, packaging for eggs, yogurt, ricotta cheese, capsules
for coffee and finally packaging for soaps, drugs or personal care products (Figures 2.7-2.10).
16
Figure 2.7-Cutlery, ice cream cup and food packaging. From catalogue of Ecozema (www.ecozema.com)
Figure 2.8-Packaging for egg and packaging for ice cream (www.alcas.it)
Figure 2.9-Coffee capsules (corriereinnovazione.corriere.it) and packaging film and cups in Mater-Bi (www.materbi.com)
Figure 2.10-Packagings for drugs and personal care products (www.lameplastgroup.com, www.vib.be)
All these products are part of our everyday life, and if they can be thrown together with food waste
in the organic bin, people will become used to do this. So, the amount of bioplastic intended to the
17
composting plants will sensibly increase in a way directly proportional to the increase of the
availability on the market of these new products.
For the last years, also industries of non-packaging products have been developed pieces of their
commodities using bioplastics: some examples are stationary items, bottoms, glasses, shoes.
They are then applied in agriculture for mulching and in the automotive sector for car interiors
(Figure 2.11).
Figure 2.11-Use of bioplastics for stationary items and mulching (www.novamont.com)
.
The disposal of this industrial products, especially car parts and interiors, is likely to be done in
landfill, or in recycling sectors; so, it’s fair to say that the contribute of these commodities to the
increase of bioplastics for composting will be less than which of domestic packaging products.
2.2.3 Characteristics and production of compostable bioplastics
Among the most diffuse biodegradable bioplastics, they are included: starch based materials,
like Mater-Bi, polyactic acid or polyactide PLA, polyhydroxyalkanoates PHA, cellulose, polybutylene
succinate PBS and polybutylene adipate terephthalate PBAT.
The products mainly present on the market for packaging are made of Mater-Bi, PLA, cellulose pulp
and PHA, so these four types of bioplastics will be discussed in this paragraph to know their physical,
chemical and mechanical properties.
Mater-Bi are a product made on corn-starch and biodegradable polyesters; so, it’s fair to give
a piece of information on the way through which starch is used to produce bioplastics.
Starch is the most abundant and commonly used renewable raw material, its unique chemical and
physical characteristics can be distinguished from all other carbohydrates (Figure 2.12).
18
Figure 2.12-Starch chemical structure
It is obtained from seed, corn, wheat, potato, rice, sweet potato and cassava (Zhang et al., 2005).
Starch is made up of repeating units of glucose and comprised of amylose and amylopectin. Amylose
is a mostly linear glucan, while amylopectin is a very large, highly branched glucan with α,1-6
linkages at the branch points. The ratio of amylose and amylopectin depends on the source and age
of the starch and can also be influenced by the extraction processes.
Starch for bioplastic materials is used as thermoplastic starch (TPS) and starch composites.
Thermoplastic starch can be produced after destructuration of starch in the presence of heat and
plasticizers. Water and glycerol are the most common plasticizers, and water has a bigger effect
than glycerol.
TPS has properties like those of common synthetic thermoplastics and can be processed as a
traditional plastic: however, its sensitivity to moisture and poor mechanical properties limit
packaging applications. Mechanical properties depend also on percentage of amylose and
amylopectin; in fact, TPG with higher amylose content is more ductile.
Polymers derivate from starch are crystalline and can be used themselves or mixed with other
polymers; for example, starch itself is added as a filler for other bioplastics to lower the cost
production, and it has been reported that the addition of starch into biodegradable polymer like
PLA, enhances the biodegradability of polymer composite (Liao and Wu, 2009).
If mixed with glycerol, polyesters and urea, intermolecular hydrogen bonds are reduced and
properties of the product are stabilized.
Mechanical properties of starch are generally comparable to which of PE: they are ease to
manipulate, but sensitive to thermal degradation and they tend to absorb humidity. In fact, starch
interacts with water and degrades through hydrolysis.
Polymers from starch have a not high resistance to oils and solvents, but if mixed with other
biopolymers, this capacity can be improved.
19
As said, Mater-Bi materials, made by Novamont, result from corn-starch and biodegradable
polyesters. They are present on the market since 1990s, and it’s fair to say that its biodegradation
rate is similar to that of cellulose and its mechanical properties close to those of traditional plastics
like polyethylene PE and polystyrene PS, and it has a good resistance to heat, until 80-100°C.
It is also possible to submit these bioplastics to all the processes generally applied to traditional
plastics, as filming to produce bioplastic films and sheets, extrusion to produce woven nets,
thermoforming for rigid containers, vessels, pans, glasses, printing and injection to produce cutlery,
toys, pens and finally expansion that generates loose fillers.
Five types of Mater-Bi are present on the market, four of them are classified as compostable.
Class A: biodegradable non-compostable material, with degradation in liquid medium of among 2
years. Products made from starch and vinylic ethylene alcohol copolymers.
Class Z: biodegradable compostable material, mainly used for manufaturing films and sheets.
Biodegradation within 20-45 days in composting conditions.
The material is made from starch and polycaprolactone PCL in 50% ratio.
Class V: Biodegradable compostable and soluble materials, as sobstitutes for EPS material; it
biodegrades faster than class Z, beacuase starch content is of 85%.
Class Y: biodegradable compostable material for injection molded, rigid and dimensinally stable
product. Made of entirerly natural raw materials, such as starch with cellulose acetate.
Class N: Biodegradable compostable materials, it is made on starch and polybutylene adipate
terephtalate PBAT.
The aspect of Mater-Bi is in granular form, as in figure 2.13.
Figure 2.13-Mater-Bi in granular form. They are made on corn-starch and biodegradable polyesters (www.novamont.com)
PLA is a family of biodegradable thermoplastic polyester made from renewable resources; it
is propose for a commercial use as a substitute fro low density polyethylene LDPE and high density
polyethylene HDPE, polystyrene PS and polyethyleneterephthalate PET.
20
It is produced by conversion of corn, or other carbohydrate sources, into dextrose, followed by
fermentation into lactic acid. After this procedure, through direct polycondensation of lactic acid
monomers or through ring opening polymerization of lactide, PLA pellets are obtained. Three
different stereochemical compositions of lactide can be found and the composition determines the
final properties of the polymer. It has a transparent granular aspect, as in figure 2.14.
The processing possibilities for this bioplastic ranging from injection molding and extrusion over cast
film extrusion to blow molding and thermoforming.
Physical properties of PLA are comparable to PET, especially as for the tensile strength and elastic
modulus; PLA however is a brittle material, with less than 10% elongation at break. Another major
limitation is that it has poor gas barrier properties and low melt strength which creates limitations
during melting processes with temperatures higher than 45-60°C in conditions of high humidity.
The low melting point of this product makes it difficult also the long-term storage.
On the contrary, it has a good resistance to welding and a high HDT, so it gives good performances
for the junction between film and vessel, and for this reason it is widely applied in food packaging.
Figure 2.14-transparent granules of PLA (www.solostocks.it)
The PHAs family are a biodegradable thermoplastic polymers, produced by a wide range of
microorganisms. The polymer is produced in the microbial cells through fermentation process and
then harvested by using solvents such as chloroform, methylene chloride or propylene chloride.
They are known more than one hundred PHA composites but polyhydroxybutyrate PHB is the most
common, and it possesses chemical and physical properties comparable to those of poplypropylene
PP except its brittleness.
The other PHAs are also similar to PP but also to PE while others are elastomeric: therefore, blending
with members of the PHAs family can expand the potential range of applications.
21
Cellulose is the most widely spread natural polymer and is derived by delignification from
wood pulp or cotton linters (Figure 2.15). It is a biodegradable polysaccharide which can be dissolved
in a mixture of sodium hydroxide and carbon disulphide to obtain cellulose xanthate and then recast
into acid solution, as sulfuric acid, to make a cellophane film. Alternatively, cellulose derivate can
be produced by derivatization of cellulose from solvated state, via esterification or etherification of
hydroxyl groups.
Figure 2.15-Cellulose after delignification (www.hempplastic.com)
Cellulose esters like cellulose di and triacetate need addition of additives to produce thermoplastic
materials which can be submitted to injection molding or extrusion. Furthermore, most of cellulosic
materials are water soluble and show excellent film-forming properties, but are too expensive for
bulk use
2.3 Bioplastics in composting
2.3.1 The composting process: phases, parameters, waste to composting
With the D.Lgs 22/97 waste management underwent a turning point: the national and
international legislation about waste are more and more facing toward the consideration of waste
as a resource, a matter that can be recovered or recycled.
In this view the process of composting is a way of waste disposal through which it can be obtained
a final product, compost, reached in humic acids, to be used as fertilizer.
Composting means the process of biological degradation and maturation of organic substances by
a variety of living microorganisms, in aerobic conditions and solid state. At the end of the process
products with a simpler molecular chain, more stable and hygenized, enriched in humus, are
22
obtained, with the emission of CO2 and water; the following is the basic reaction of aerobic
degradation.
C6H12O6 + 6O2 6CO2 + 6H2O + Energy (2870 KJ/mol) + Biomass
Composting is a way of waste disposal suitable for three main reasons: from an environmental point
of view, waste are transformed into a new product, useful in agriculture. Then, if temperatures
during the thermophilic rise to 65-70°C there is an hygienization of the organic waste, and it is a
process energetically autonomous.
It is interesting to specify that composting is one of the three possible aerobic stabilizations of
organic waste: in fact, in aerobic conditions other two processes exist. Mechanical-biological
pretreatment, MBT, and biodrying.
The processes are quite similar: two phases are well defined, the thermophilic phase, that lasts for
about two weeks, and the curing or maturation phase, for a period of 2-3 months.
The preliminary step before starting the process is the shredding of waste to ensure the obtainment
of a suitable size. What changes between composting, MBT and biodrying is mainly the aim for
which the process is chosen and consequently the waste disposed of.
While biodrying and MBT are pretreatments, the first before incineration to increase the calorific
power and the second before landfilling to stabilize organic waste and allow to reach the FSQ in one
generation time, composting is done with purpose to recover a final product.
So, it’s important to pay attention to waste disposed of in a composting plant: they must come only
from separated organic fraction, green waste, or waste water sludge not contaminated. Smaller
powders as waste from street sweeping are not allow to be treat in this way, nor other organic
contaminated waste, because they pollute the matrix and the compost.
The living organisms that carry out the process are bacteria, actinomycetes, fungi and also
worms or beetles. Each microorganism is able to degrade a particular category of materials, and
develops during the process in precise conditions.
Bacteria can be extremely fast-growing, they feel good at high temperature and moisture content,
so they develop during the thermophilic phase, and they degrade the simpler substances as
monosaccharides, starch and proteins.
Actinomycetes stay in the middle of the process, they are identifiable at a naked eye because of the
white colour around the waste lump. Fungi are psychrophilic, can penetrate also the dry matter, are
23
less sensitive to change of conditions and they degrade the most complex substances as lignin and
cellulose, operating mainly during the maturation phase.
Figure 2.16-Phases of composting (www.researchgate.net)
There are some operational controlling parameters in the different moment of the
composting process: before starting, water content, structure, substrate composition and nutrient
content should be defined for waste matrix.
The treatment requires a good level of structure of the substrate, generally ensure by lignin and
green waste. The nutrient content is given by C/N parameter, in accordance with the amount of
carbon and nitrogen available for living organisms, that should be around 20-35 to guarantee the
operativity of bacteria after the lag phase.
Finally the moisture content is fundamental to make the process start; a perfect value is of 50-60%.
Water is necessary for bacteria to implement the hydrolysis, the first step in the biodegradation
process, which breaks the more complex molecular bounds and leads to the production of simpler
compounds.
During the process five parameters must be kept under control to ensure the effective activity of
the living organisms: temperature, water content, oxygen content, the process is aerobic so a
minimum of 20% of oxygen must granted for the aerobic bacteria to live, structure and pH values.
The operations to maintain these parameters suitable are aeration with turning, which allows to
control the rise of temperatures and the fall of oxygen, and moistening.
24
At the end of the process, structure and compost properties are analysed: if the compost is sold it
must respect the requirements of DM 5 February 1998 and in case of Veneto DGRV 766.
To evaluate if a composting process ran out, some parameters should be checked: C/N, self-heating
and oxygen demand and their limit values are reported in table 2.2.
The values in table are a sum of more than one reference, www.venetoagricoltura.org then
docenti.unicam.it for temperature, C/N and moisture, and from Cossu (2016) for respirometric
index.
Table 2.2-Parameters to define compost maturity
Temperature RI4 C/N Moisture
<25°C without high peaks <5 mg O2/g VS < 10-15 < 40-50%
2.3.2 Bioplastics and composting in scientific papers
The behaviour of bioplastics after the composting process has already been studied, in
particularly with the interest for their biodegradation timings and efficacy.
However, analysing the scientific papers about this topic, many different questions have been
discussed, and from the consideration behind the experimental parts, the environmental conditions
for the experiments, the purpose of the tests, some useful information were taken and applied to
implement my personal research.
At this point it’s fair to specify that the most of the researches published in scientific literature are
at a lab scale, just few on a full scale, but none of them were done on a small scale. Thus they
generally referred to European standards, respectively EN 14806 for lab scale and EN 13432 and
14995 for full scale. While for a small scale it doesn’t exist a specific standard that gives information
or improvements on how to carry out the experiments.
So, for the purposes of this research, some suggestions from standards and research methods of
both lab and full scale were observed and considered in the view of a small scale test.
The lab scale experiments studied and analysed were mainly four. Starting from Javierre et al.
(2015), a research which focuses on the different level of degradation for a painted and a normal
bioplastic. In perfect accordance with the correspondent standard, the samples were kept at 58°C
for 90 days, and CO2 emissions were evaluated to define the biodegradation level. At the end of the
25
process bioplastic pieces were dried at 40°C and finally sieved with a 2 mm sieves. A similar
procedure was adopted by Balaguer et al. (2015) to assess the compostability of a nano-reinforced
PLA film. The difficulties in copying these tests is that on a small scale test is not possible to keep
the sample in an oven at 58°C for all the testing period. Furthermore, even if this technique allows
the study of biodegradation in accordance with the standard, the condition of such high
temperature for three months doesn’t correspond to a real composting condition, which is instead
the aim of my research. However from these two papers the two main techniques to evaluate the
biodegradation level were learnt: CO2 emissions and weight losses. To measure CO2 emissions, it is
necessary to operate in a closed environment, as the reactor proposed by the lab scale European
standard, with an opening a tube through which gas is taken out and measured. On the contrary,
weight losses can be simply calculated with the use of a balance, a method that is applicable to a
condition of a small scale with baskets or heaps that can be put in a tank and weighted.
Furthermore, Balaguer observed that after 7 weeks of composting, bioplastics are assimilable to
compost in their aspects and no distinctions can be made between normal and nono-rinforced
bioplastics.
Considering this last observation, in my research a particular paragraph on bioplastic aspects was
written, in order to follow the peculiarities of the tested material also from a visual inspection.
Another interesting research is which of Tabasi and Ajji (2015) on PLA film and PHB degradation:
this was a short-term research, with a tested material size of 5 cm and a ratio between compost and
material of 6:1. The most interesting point of this research was the study of bioplastics aspect
changing in time, through a scanning electron microscope.
To conclude with the small lab scale tests, Mohee (2008) following EN 18455 analysed the
degradation of a Mater-Bi bioplastic for 40 days; from this experiment, resulting in a degradation of
26.9%, it could be extrapolated an important suggestion. In fact the test was carried out at room
temperature for all the time, on a sample of few kilos: as the degradation level was very low, it is
possible to deduce that the main cause is linked with the low temperature, maybe a sign that the
composting process had never started efficiently enough.
On the other hand, the most interesting scientific paper about a full scale research was Rawoteea
et al. (2016), about co-composting of vegetable waste an carbon. At the end of the process, some
sieves were used to define a granulometric curve for both the compostable matrix and the tested
material, an idea which was used in my research to study the disintegration of bioplastics, not only
at the end, but also during the composting process.
26
To conclude with the bibliography about researches on bioplastics, a considerable paper is Emadian
et al. (2016) about the degradation of different types of bioplastics, from PLA, to PHB, to starch
based materials, not only in composting but also in soil, sediments and water matrix.
The main and useful point of this article is that bioplastics degradation in greatly influenced by the
surrounding environment, for example in water bioplastics have a degradability similar to which of
plastics, it means very long, while in soil it depends on the type of soil, the microorganisms which
live there, the climate. Thus, if at the end of the composting process bioplastics are still not
completely degraded and they are released into the environment, external conditions of this new
environment should be considered, accounting that they could be able to stop or slow down
biodegradation.
2.4 Standards for definition of bioplastics compostability
To define if a plastic material is biodegradable and compostable, it must pass through the
approval of European standards.
There is more than one standard on this topic, because one standard is general for plastic materials
and each of the others is specific for the type of material under study, or the environment of
degradation.
2.4.1 Full scale standards
EN 14995:2006
Plastics – Evaluation of compostability – Test scheme and specification.
This standard has not yet been implemented in the European Union or in Italy; in fact, this is the
most general standard about plastic compostability, and it specifies requirements and procedures
to determine the compostability or anaerobic treatability of plastic materials by addressing four
characteristics: biodegradability, disintegration during biological treatment, effect on the biological
treatment process and effect on the quality of the resulting compost.
The main points of interest for this study are biodegradability and disintegration under aerobic
composting.
Aerobic biodegradation tests are discussed at point A.2.2.
27
A.2.2.1 “The period of application for the test specified in the test methods shall be a maximum of
6 months”.
A.2.2.2 “For plastic material the percentage of biodegradation shall be at least 90% in total or 90%
of the maximum degradation of a suitable reference substance after a plateau has been reached for
both plastic material and reference substance”.
Disintegration is discussed at point A.3.
A.3.1 Aerobic composting: “Following submission to the composting process for a maximum of 12
weeks, not more than 10% of the original dry weight of the plastic material shall fail to pass through
a < 2 mm fraction sieve”.
Moreover, the ecotoxic effects of the resulting compost shall be analyse through OECD 208 test with
the modifications describes in the Annex D of the standard.
EN 13432:2000
Packaging – Requirements for packaging recoverable through composting and biodegradation –
Test scheme and evaluation criteria for the final acceptance of packaging.
This standard is specific for plastic packaging materials, and because of this, it is the standard to
which all the compostable shopping bags, food packaging, cutlery and other bioplastics packaging
refer.
It specifies requirements and procedures to determine the compostability or anaerobic treatability
of plastic materials by addressing four characteristics: biodegradability, disintegration during
biological treatment, effect on the biological treatment process and effect on the quality of the
resulting compost. In case of a packaging formed by different components, some of which are
compostable and some other not, the packaging itself as a whole is not compostable.
About this standard it’s fair to underline some interesting points: aerobic biodegradation and
disintegration under aerobic composting are discussed in the same way of EN 14995:2006, at the
same reference point A.2.2 and A.3.1.
Also for ecotoxicity tests the reference is OECD 208 modified.
To determine the other eventual negative effects on the resulting compost, its quality is evaluated
through: volumetric weight, total dry solids, volatile solids, salt content, pH, the presence of total
nitrogen, ammonium nitrogen, phosphorous, magnesium and potassium.
Chemical characteristics of compost are discussed at point A.1.
28
A.1.1 Volatile solids: “Packaging, packaging materials and packaging components shall contain a
minimum of 50% of volatile solids which include largely inert materials”.
A.1.2 Heavy metals and other toxic and hazardous substances, listed in Table A.1 of the Annex. The
element under evaluation are Zn, Cu, Ni, Cd, Pb, Hg, Cr, Mo, Se, As, F.
The last point to underlain is the granulometry of material before test starting, discussed in Annex
D, point D.1.3: “The shredding of used packaging with machinery and procedures, commonly used
in composting plants, shall not be disturbed and should lead to particle sizes of less than 10 cm in
the longest dimension, suitable for the composting process”.
EN 14855:1999
Determination of the ultimate aerobic biodegradability and disintegration of plastic materials
under controlled composting conditions — Method by analysis of evolved carbon dioxide.
It exists a new version of this standard, EN 14855:2004, but the requirements and proposed tests
are the same of the previous one. “This International Standard specifies a method for the
determination of the ultimate aerobic biodegradability of plastics, based on organic compounds,
under controlled composting conditions by measurement of the amount of carbon dioxide evolved
and the degree of disintegration of the plastic at the end of the test. This method is designed to
simulate typical aerobic composting conditions for the organic fraction of solid mixed municipal
waste. The test material is exposed to an inoculum which is derived from compost. The composting
takes place in an environment wherein temperature, aeration and humidity are closely monitored
and controlled. The test method is designed to yield the percentage conversion of the carbon in the
test material to evolved carbon dioxide as well as the rate of conversion”.
This standard is the first reference standard to evaluate the biodegradability of a test material: in
fact, EN 19455 and EN 13432 are both based on it as for the procedure for biodegradability
evaluation.
At point 8 of the standard, the procedure is exposed, starting from the preparation: the test is
carried out with an inoculum, deionized water, test material and a reference material.
Well aerated compost from a properly operating aerobic composting plant shall be used as the
inoculum; a mixture of 1 part of inoculum with 5 parts of deionized water is prepared, and finally
tested material is added.
29
The evaluation of its biodegradation level is done by measuring carbon dioxide emissions, and the
result must be compared with a reference material of which biodegradability was already
ascertained.
This standard is no more use as reference by companies to define their product as compostable,
and the main reason is linked with the affirmation at point 10 validity of test.
“The test is considered as valid if the degree of biodegradation of the reference material is more
than 70 % after 45 days”.
Due to this definition, it seems that even if the material succeeds in this test, its compostability is in
a level inferior with respect to a material succeeded in test of standard EN 13432:2000, which
requires 90% biodegradation in 6 months.
2.4.2 Pilot scale standards
EN 14045:2003
Packaging – Evaluation of the disintegration of packaging materials in practical oriented tests
under defining composting conditions.
“This European Standard is used to evaluate the disintegration of packaging materials in a pilot-scale
aerobic composting test under defined conditions. Other methods should be used to measure the
biodegradability of the packaging materials. Packaging materials are mixed with biowaste and
spontaneously composted for 12 weeks in practical oriented composting conditions. At the end of
the composting cycle the disintegration is measured by sieving of the compost and the calculation
of a mass balance. The influence of the tested sample on the quality of the compost can be studied
by using the compost obtained at the end of the composting process for further measurements such
as chemical analyses and ecotoxicity tests.
Additionally, this method can be used for visual perception and photographic documentation of the
disintegration of packaging materials and for evaluating the effect of their addition on the
composting process”.
Since this is the specific standard used to demonstrate the compostability of packaging materials in
the precise conditions analysed in this thesis, few worlds will be spent to describe the main points
and requirements specified in the standard.
30
The principle of the standard is exposed at point 4: the test duration is established to be 12 weeks,
with a continuous monitoring of temperature, pH, moisture content and gas composition.
At the end of the composting process, the mixture of compost and test material is sieved over 2 mm
and 10 mm to evaluate disintegration of packaging material after sieving.
If possible, the standard requires a mass balance based on dry and wet weight. The compost
obtained shall be used for further measurements such as chemical analyses and ecotoxicity tests.
The procedure of the test is specified at point 6: to simplify the discussion of this point, in table 2.3
are reported all the information exposed in the standard about the biowaste sample composition
and physico-chemical characterization.
Table 2.3-Requirements of 14045:2003 for physico-chemical characterization of the biowaste sample
Physico-chemical characteristic Reference value from 14045:2003
Sample wet weight 60 kg
Biowaste dimension < 50 mm
C/N 20-30
Moisture content >50%
Volatile solids >50%
pH >5
Temperature <75°
>60° for at least 1week
>40° for at least 4 consecutive weeks
Some types of biowaste are suggested to be added to sample to reach a good structure: fresh mixed
fruit and vegetable waste, rabbit feed, matured compost, urea, bulking agent as woodchips or bark.
At point 6.1.1.2 is specified that the dimensions of the test material shall be reduced to 10 x 10 cm.
At point 6.1.3.2 is defined the sieving procedure through which is finally defined the disintegration
of the test material.
31
Table 2.4-Sieving Scheme from EN 14045:2003
Compost
(at end of pilot scale test)
Analyses
Sieving > 10 mm Particles > 10 mm:
Segregation and determination of the dry mass of residual test material
Fraction < 10 mm 10 mm > Particles > 0 mm:
Gently mixed: separation of a part of the compost for chemical analysis
Option: Ecotoxicity testing
Sieving > 2 mm 10 mm > Particles > 2 mm:
Segregation and determination of the dry mass of test material
Fraction < 2 mm Use for optional analysis
At point 6.1.3.3 some visual observations are optionally proposed. In particularly: “A visual
assessment of the criteria described below is carried out at the beginning of the test and also during
the entire trial period whenever the test material is turned.
- Initially distribution of particle size of remaining packaging particles;
- signs of microbial colonisation of the packaging (fungal hyphae, bacterial growth) to be
described and photographed.
At least 10 packaging particles shall be selected with the intention to provide an impression of all
visible degradation phenomena, ranging from little decomposition to severe degradation of the
packaging particles. The selected particles shall be carefully cleaned with water and evaluated
visually for the following criteria:
- consistency and thickness of the material;
- discolouring;
- erosion of the material (holes, tunnels, etc.) and signs of local disintegration;
- ease of discovery”.
At point 6.2.3.1 are discussed all the analyses to carry out on the resulting compost to evaluate its
quality.
“The characteristics of the compost obtained in the presence of the test material shall be compared
to the results for the biowaste control bins. The wet weight of the total compost before sieving shall
be exactly determined.
32
A homogeneous sample of the < 10 mm fraction shall be analysed for dry matter, volatile solids, pH,
NH4-N, NOx-N, Kj-N content, Volatile Fatty Acids (VFA) and maturity. The results of these analyses
are used to describe the quality of the compost produced. If applicable the < 10 mm fraction shall
also be used for further ecotoxicity testing”.
To conclude, at point 7 it is presented the formula for the calculation of disintegration in %:
𝐷 =𝑚1 ∗ 𝑅 ∗ 𝑚2
𝑚2 ∗ 𝑅∗ 100 (1)
m1 = dry weight of test substance input
m2 = dry weight of retrievable test substance > 2 mm
R = 𝑐𝑜𝑚𝑝𝑜𝑠𝑡 𝑠𝑐𝑟𝑒𝑒𝑛𝑒𝑑
𝑡𝑜𝑡𝑎𝑙 𝑐𝑜𝑚𝑝𝑜𝑠𝑡 (w/ w)
2.4.3 Lab scale standards
EN 14806:2005
Packaging – Preliminary evaluation of the disintegration of packaging materials under simulated
composting conditions in a laboratory scale test.
First, it is necessary to underline that even if a test on a plastic material succeeds in this test, it must
also succeed in full scale tests to obtain the certification of compostable material.
“This laboratory scale test method using synthetic waste aims at simulating the environmental
conditions found in industrial composting plants. Packaging materials exposed to this environment
can be preliminary assessed for disintegrability. A negative result does not necessarily mean that
the test material is not disintegrating under industrial composting conditions. This test does not
replace the acceptance disintegration test as specified in EN 14045, in accordance with EN 13432”.
So generally, this standard is used for demonstrative laboratory analyses.
Some information given in this standard will be reported, because a part of them will be used in the
experimental part of this thesis work.
At point 5 there is a description of synthetic solid waste for the analysed sample, with its physico-
chemical characteristics, summarized in table 2.5. Furthermore, synthetic waste suitable for the test
and their percentages in the sample are suggested.
33
Table 2.5-Requirements of 14806:2005 for physico-chemical characterization of the waste sample
Physico-chemical characteristic Reference value from 14806:2005
Sample wet weight 1 kg
C/N 20-30
Moisture content >55%
pH >5
Temperature 58°±2°, and after 30 days it can decrease until a 21°
Another important point of the standard is point 6, where the reactor suitable for the test is
described: “The composting reactor is a box made with a suitable inert material which does not
affect the composting process, having preferably the following dimensions: 30 cm × 20 cm × 10 cm
(l, w, h). In the sequences the container chosen shall not vary more than 5 % in dimensions. The box
shall be provided with a lid assuring a tight closing to avoid an excessive evaporation. Additionally,
the closing between box and lid may be sealed with an adhesive tape. In the middle of the two 20
cm wide sides, a hole of 5 mm in diameter shall be applied at a height of about 6,5 cm from the
bottom. The two holes provide gas exchange between the inner atmosphere and the outside
environment”.
While at point 7 the dimensions for the test materials are specified: 25 x 25 mm if the thickness of
the material is > 5 mm, and 15 x 15 mm if the thickness is < 5 mm.
The termination of the test and the final calculation of its degradation is described at point 10.
The compost is sieved through 2 mm sieve, and the smaller fraction is cleaned from the compost,
washed by dipping in water and finally dried in an oven until a constant mass, as it was done initially
before the test.
The disintegration in 100% is expressed through the formula:
𝐷 = 𝑀𝑖 − 𝑀𝑟
𝑀𝑖∗ 100 (2)
Mi = is the initial dry mass of the test material
Mr = is the mass of the dry residues recovered by sieving.
34
2.4.4 Certification of compostability
Once a plastic product has succeeded in the tests required by standards, producer company can
ask for the certification of compostability.
It consists on a label which is drawn on the packaging material, near the name of the standard.
The commonly known labels of compostability can be released if the product meets the
requirements of EN 13432:2003.
Label of CIC (Consorzio Italiano dei Compostatori) cerifies that a product is objectively eligible to
composting, and when composted in an industrial facility no plastic residues will be left behind to
destroy the value of the finished compost.
Label of Biodegradable Products Institute (BPI) certifies products as compostable, which means they
will biodegrade quickly, completely and safely, when composted in well-run municipal and
commercial facilities and that no plastic residues will be left behind to destroy the value of the
finished compost. This certification does not guarantee the products will biodegrade completely in
a backyard compost or that they will biodegrade in the ocean.
Then European Bioplastics offers the seedling label, which certifies that the product will biodegrade
completely in a well-run industrial compost facility, but not necessarily in a backyard compost or in
the environment.
DIN-Geprüft Biobased has a label which indicates a product is certified to contain a certain
percentage of biobased material. The percentage is indicated on the label. This label does not tell
you that the product is biodegradable.
In figure 2.17 the labels of CIC, BPI, European Bioplastics and DIN.
Figure 2.17-Labels certifying compostability (www.materbi.com)
Vinicotte has developed different labels, each of them specified a particular condition under which
the bioplastic material can degraded in composting.
35
- OK compost certifies the product will biodegrade completely in an industrial compost facility.
However, it does not guarantee that the product will break down in a home compost system;
- OK compost HOME certifies the product will biodegrade completely in a home compost
system;
- OK biodegradable SOIL certifies the product will biodegrade completely in the soil without
harming the environment. No composting system necessary.
Figure 2.18-Labels of Vinicotte certifying compostability (www.materbi.com)
36
37
3. MATERIALS AND METHODOLOGIES
The experimental part of thesis involved two parallel fields: the composting process, developed
on a small scale, comprehensive of all the analyses carried out to study the evolution of the process,
and the methods applied to follow the degradation and the disintegration of bioplastics within the
composted matrix.
The decision to carry out the test on a small scale was linked with the necessity to have more than
one replicate for a statistical definition of the results, in addition to the purpose to simulate a real
composting plant, with the two main phases, the thermophilic and the maturation.
In particularly, as the aim was not to have the results only at the end of the process, but to follow
the different steps and the evolution of bioplastics fate in composting, there were established five
points of analysis, to study in parallel the composting process and the bioplastics degradation and
disintegration.
The five timing of analysis were the 1st day, then the day correspondent to the end of the
thermophilic phase, two points during the maturation phase and the last at the end of the process.
The test lasted for 55 days, in accordance with the purpose of simulating the period of activity of a
composting plant, and with the effective possibility to do this in a small scale; it was observed that
after two months the values typical of a good compost were obtained, and it was reached a size of
the heap, consequently to the weight lost and the samples taken, no more useful to simulate a real
process.
In this chapter the material and methodologies applied to the composting process and to
the evolution of bioplastics in the process itself are explained; moreover, the preparation of the
sample and the characterization of the waste matrix used are explicated.
3.1 Composting process
The composting process were studied during its different phases: in this paragraph the methods
for the analyses of the process parameters, and the use of sieving analyses to follow the changing
granulometry of the composted matrix are described in order to show the evolution of the process
in time.
38
To carry out the analyses during the composting process, no more than 2 kg from the heaps were
taken each time, to ensure the maintenance of a good mass of the heaps for the proceeding of the
composting.
3.1.1 Analyses of the composting process parameters
The main parameters monitored from the beginning to the end of the process were:
temperature, total and volatile solids, pH, moisture content, C/N, respirometric index.
It was established a program of research for the timing of the analyses, as show in table 2.1.
Table 3.1-Timing of the process parameters analyses
Parameter Daily Weekly
analyses
Sampling days Initial
Temperature x x
Weight lost x
Moisture x x x
Total solids x x x
Volatile solids x x x
pH x x
TOC x x
TKN x x
Nitrates x x
C/N x x
RI x x
The analyses carried out for these parameters are briefly exposed below.
- Temperature: the monitoring of the temperature was done through two thermometers able
to provide a value between -50 °C and up to 200 °C, one thermometer with a probe of 10
cm, for the upper part and the sides of the heaps, and the other, to measure the bottom of
the heaps, of 20 cm.
Temperatures were taken at least daily, but during the thermophilic phase it was measured
up to four times a day, because the heap was subjected to possible high increases, to which
it followed an immediate mixing, and to a decrease due to the outside temperature. In this
case it was provided a cover on the heap for the coldest hours of the day, to avoid a too
great decrease of temperature. Furthermore, once the thermophilic phase was finished, the
39
mixing of the heaps was done no more once a day, but twice a week, to supply also water to
the heaps and maintain a god moisture content.
- Outside temperature: the monitoring of the temperature includes also the monitoring of the
external climate, in order to find a possible connection between the changes within the
heap. It was monitored through an outside probe, measuring also the humidity, positioned
within the box in which the experiments were carried out.
- Total weight: the total weight was monitored through the use of a balance precise up to 30
kg. The heaps were dismantled, put within a basket and weight. Then they were recomposed
in their original configuration.
- Dry weight: the dry weight, used especially to carry out the analyses that require a
normalization on the total solids, was measured removing the water content from the total
weight. Water content was previously analysed drying the sample in oven at 105 °C, in
accordance with the procedure for the evaluation of the total solids, as described in the
specific voice.
- Total solids and moisture content: the moisture content was daily monitored to a probe
generally used in agriculture for the humidity of soil, but as the heap was small the
measurements obtained with this simple probe was not precise, moreover they vary greatly
in accordance with the materials of the composted heaps in which the probe was infixed.
So the most suitable way to obtain a significant value for humidity and total solids was to
take a sample of few grams generally one in the upper part of the heap and another on the
bottom, and to dry it in the oven at 105 °C for 24h.
𝑊105 °𝐶 − 𝑊𝑐𝑟𝑢𝑐𝑖𝑏𝑙𝑒
𝑊𝑟𝑎𝑤∗ 100 = 𝑇𝑆 (%) (3)
- Volatile solids: they were calculated in accordance with the equation:
𝑊105 °𝐶 − 𝑊550 °𝐶
𝑊105 °𝐶 − 𝑊𝑐𝑟𝑢𝑐𝑖𝑏𝑙𝑒∗ 100 = 𝑉𝑆 (%) (4)
- pH: the evaluation of pH was done through a cession of the solid material in distilled water,
with a proportion 1/10, and the measurement was done on the liquid sample.
40
- TKN: the analyses for the TKN, Total Kjeldhal Nitrogen, comprehensive of organic nitrogen
and free and saline ammonia (FSA), were implemented by steam extraction at high pH (with
the required dose of ammonia, 60 ml for all my samples) and condensation with boric acid
(30 ml). Then there was a further titration by using H2SO4.
The obtained results were in concentration of g TKN/ Kg TS, so to obtain the real trend of
TKN decrease within the heaps, this value was multiplied by the dry weight.
- Nitrates: the nitrates were analysed with the UV analyser, after the cession of the solid
samples in distilled water.
- TOC: the analyses of TOC were done through an oxidation by a combination of heat and
oxygen, ultraviolet radiation and chemical oxidants. The inorganic carbon was also measured
through this method, but with the CO2 was then evaluated directly by an infrared analyser,
allowing to obtain the results of the organic carbon.
As for the TKN, the result directly obtained was a concentration, so multiplying by the dry
weight it was obtained the bulk of organic carbon.
- C/N: this number represented the ratio between total carbon (organic and inorganic) and
total nitrogen (TKN and nitrates), available for the bacteria active during the composting
process. They required a minimum ratio of 20, up to a maximum of 35, in accordance with
the Liebig law: in fact, bacteria require both nitrogen and carbon (also a small amount of
phosphorous) to allow the internal metabolic processes active in feeding. If the value is less
than 20, it means that carbon is not enough, while for a value higher than 35 there is an
amount of carbon not compensated by the right amount of nitrogen so that bacteria cannot
supply the energy required for survival.
- Respirometric index: the respirometric index is the parameter which identifies the
consumption of oxygen by living organisms active in the composting process: the result of
test is normalized for a moisture content of 50% so it is a potential respirometric index.
This index can be done for four or seven days: in the analyses carried out for this research
both the RI were developed.
3.1.2 Sieving analyses for the granulometric curve
The granulometric curve of the composted matrixes was drawn starting from the sieving
analyses of a sample of less than 2 kg of each heap.
41
The purpose of this analysis is not directly related with the composting process monitoring, but with
the necessity to divide the size of bioplastic pieces, and the only way to reach this result was
previously to sieve the composted matrix and then to manually remove the bioplastics, as explained
in details it the dedicated paragraph. Furthermore, the separation into different granulometries
allows the evaluation of the main component of each withheld sample.
Six sieves were used to describe the granulometric curve of each sample during the composting
process: The used sieves are, in accordance with ASTM: 3/4, 3/8, 5/16, 3.5, 8, 14, which corresponds
to 20 mm, 10 mm, 8 mm, 5.60 mm, 2.38 mm, 1.40 mm.
This range of sieve highlights law limits, 10 mm and 2 mm, and it allows to comprehend different
scales of values, from a sieve just smaller than the starting dimensions, up to much smaller sieves,
under the limit posed for microplastics identification, which is 5 mm.
3.2 Evaluation of bioplastics disintegration and degradation in composting
The purpose of my thesis work consists, as said, in defining the behaviour of bioplastics in
composting, because, as the most common and used way of bioplastics disposal, it must ensure the
disappearance of potentially polluting materials before the use of compost in agriculture.
Compost in fact is mainly used as fertilizer, if it is a compost coming from waste of good quality,
without heavy metals, powder from street sweeping, or toxicants, so all the components present in
compost are discharged in field, soil and water due to run-off.
This is the reason why the research has the aim to evaluate the level of disintegration and
degradation of bioplastics in composting process, providing an answer to the question of which is
the fate of bioplastics during and at the end of this waste treatment process.
Disintegration and degradation were separately studied through a series of four analyses: sieving
analyses on bioplastic pieces to differentiate them in accordance with the size, showing the trend
of size along time. Then the concentration of each single fraction and on the total sample was
calculated with the ratio between weight of bioplastics and the weight of the sample.
The study of the concentration involved not only the disintegration, it was just calculated using the
data collected with the sieving and sorting analyses, but also the evolution of the influence of the
bioplastics amount in the composted matrix.
42
Biodegradation of the tested material was analysed through the infrared, making a comparison
between the spectra at the beginning of the process and during the timing of sampling, up to the
last sampling at the of the process.
Through the changes in the bioplastic spectra it was observed the evolution of the material during
the phases of the process, and knowing the type of bounds associated to the ranges of the
wavelengths it was just possible to follow the passage from a polymer with high concentration of
complex bounds to a polymer with a higher concentration of single and generally simpler bounds at
the end of the composting process.
The last type of analyses, which showed directly the interventions of the process on the material
surface and features, was the visual inspection of the removed bioplastic samples.
On these samples were also carried out TS analyses to define the moisture content of the bioplastics
during the process in comparison with the beginning, and some of these pieces were accurately
cleaned to measure the effect of dirt on the total weight of the pieces, used in the definition of the
sieved fractions.
3.2.1 Sieving analyses of bioplastics disintegration
A crucial point of this research is to find if bioplastics effectively disappeared from composted
matrix or if they are still present but in a smaller size than at the beginning of the composting
process. Through the sieving of a sample the composted matrix during the phases of composting, it
could be possible to divide also bioplastics in accordance with their different granulometries.
To obtain a subdivision of bioplastic samples in accordance with their size, a previous operation to
separate the pieces of tested materials from the other components of the composted matrix was
necessary.
The operation of the removal of bioplastics from the rest of the composted matrix was quite long
due to the difficulties to find a solution different from a manual sorting.
In fact, as described well in the next paragraphs, there are more troubles that influence the removal
of bioplastics; firstly their stickiness that keep them attached to wood chips and composted grains,
and also they stick each other, secondly this lumps of bioplastics have a density similar to which of
grains and wood chips so sedimentation is not always applicable.
43
When it occurred that bioplastics formed lumps with other components, they were manually taken
off and divided from the lump.
It’s also fair to say that with the manual sorting of bioplastics in the smaller fractions of the sieves
the identification of them into the compost is unlikely on a naked eye.
So, the manual sorting was used until the fraction withheld by sieve 5.60 mm, while for last two
fractions it was used firstly manual sorting and secondly sedimentation with water to ensure a total
removal of the pieces.
Sedimentation was applied in a bowl with a proportion of 100 g of matrix /2 l of water, in a squared
bowl. After the discharge of water within the bowl, a quickly mixing of the solution encouraged the
separation of the components of the composted matrix in low and high dense; the solution was left
in the bowl for 2 hours and at the end of the process the swimming pieces were removed with a
strainer to recognize among them the bioplastics thanks to their aspect and colour.
At the end of the sorting, each bioplastic fraction was weighted with a precision balance and
conserved for the further analyses on biodegradation.
In figures 3.1 and 3.2 there are some photographs taken during the manual sorting of bioplastics
and the sedimentation.
Figure 3.1-Manual sorting of bioplastics (F. Ruggero, 2017)
Figure 3.2-Starting of sedimentation, mixing, BioPOF after 2 hours of sedimentation (F. Ruggero, 2017)
44
The manual sorting of bioplastic pieces from each sieve allowed then the subdivision of the
tested material within six categories in accordance with their sizes; the smallest passing fraction,
less than 1.40 mm, was too fine to allow the finding and the separation of bioplastic pieces, as they
had an aspect and a density so similar to that of the compost that nor identification nor
sedimentation were possible.
A direct comparison between the categories of size during the timing of sampling along the
composting process would have shown the behaviour of disintegration and the consequent creation
of the micro-fraction of bioplastics.
3.2.2 Bioplastics concentration
The second type of analyses carried out during the composting process was done exploiting the
data collected with the sieving. It was possible through these data to calculate the concentration of
bioplastics within the sample.
At the beginning, it was defined the initial concentration: it was determined from data of bioplastics
quantity in the real composting processes, considering also a future increase in their production, as
previously described, and it can be calculated through this formula:
𝐵𝑖𝑜𝑃 𝐶𝑜𝑛𝑐𝑒𝑛𝑡𝑟𝑎𝑡𝑖𝑜𝑛 =𝐵𝑖𝑜𝑃𝑖 (𝑔)
𝐵𝑖𝑜𝑃𝑂𝐹𝑖 (𝑔) (5)
Where BioP identified the bioplastics within the samples, and BioPOF the compostable matrix
including bioplastics.
Then, with the data of the sieving analyses, the concentration was also calculated at the four chosen
times during the composting process: it was calculated, using the following equations, the
concentration of each withheld fraction, the concentration of the total sample, and of the
microfractions smaller than 5.60 mm.
𝐵𝑖𝑜𝑃 𝐶𝑜𝑛𝑐𝑒𝑛𝑡𝑟𝑎𝑡𝑖𝑜𝑛 =𝐵𝑖𝑜𝑃 (𝑔)
𝐵𝑖𝑜𝑃𝑂𝐹 (𝑔) (6)
𝑀𝑖𝑐𝑟𝑜𝐵𝑖𝑜𝑃 𝐶𝑜𝑛𝑐𝑒𝑛𝑡𝑟𝑎𝑡𝑖𝑜𝑛 =𝐵𝑖𝑜𝑃 < 5.60 𝑚𝑚(𝑔)
𝐵𝑖𝑜𝑃𝑂𝐹 < 5.60 𝑚𝑚 (𝑔) (7)
45
The purpose of this second analysis was to follow the progression of the concentration trend during
the process, underlining the differences between each phase and between the initial value and the
value at the end of the 55th day.
Furthermore, from the experimental data of the concentration obtained from the collected
samples, a more general development was elaborated: the aim was to define the final percentage
of weight of bioplastics with respect to the initial weight in each kilo of compostable matrix.
To obtain this result, the following equation was applied:
𝐵𝑖𝑜𝑃 𝑐𝑜𝑛𝑐𝑒𝑛𝑡𝑟𝑎𝑡𝑖𝑜𝑛 (𝑔 𝐵𝑖𝑜𝑃
𝑔 𝐵𝑖𝑜𝑃𝑂𝐹) ∗ 𝐵𝑖𝑜𝑃𝑂𝐹 𝑤𝑒𝑖𝑔ℎ𝑡 (𝑔) = 𝐵𝑖𝑜𝑃 𝑤𝑒𝑖𝑔ℎ𝑡 (𝑔) (8)
Where BioP concentration is the value of the total concentration of BioP in each sample taken from
the heaps at the times of analyses, obtained experimentally.
In this way, applying the concentration found for the samples to a general vision where the weight
is no more that of the sample but that of the heap, it is possible to obtain the weight of BioP in the
heap, or in 1 kg of matrix.
At this point, a further step consisted on defining all the possible variables involved in the weight
of the BioP during the treatment, because it was observed that they had some features, so different
from the initial ones, that they could contribute to weather the real weight of the plastic piece.
So, taking into account points, defined when the test had been already carried out, it was defined a
ranging value of decrease with respect to the observed weight, to attest the real weight of
bioplastics.
3.2.3 IR analyses of degrading bioplastics spectra
The study of biodegradability of bioplastics was done with the method of the infrared analyses:
this method allowed to follow the changes in the spectrum of the tested material during the process,
providing a new solution in the evaluation of the biodegradation, generally done through the
monitoring of CO2 emissions or of the weight losses.
46
Infrared analysis allows to know the spectrum of the tested material: in the spectrum, each of the
peaks represent a bound, leading to the possibility to identify the main polymers of which the
material is composed.
Figure 3.3-IR machinery (F. Ruggero, 2017)
Through this analysis the changes in the spectrum of bioplastics had been followed during the
composting process, so that there could be identified those bounds which firstly were broken.
An important point of this method involves the fact that no literature of biodegraded bioplastics
spectra was present before my analyses: as a consequence the analyses were not used to make a
direct comparison between the spectra obtained and some reference spectra, but they were used
to make a comparison among the obtained spectra in the times of sampling.
IR spectroscopy means the absorption of IR radiation, which is the part of the
electromagnetic spectrum with wavelength between visible < 0.7 micron and microwaves > 1 mm.
The wavelength used in organic chemistry is 2.5-25 micron, it corresponds to 4000-400 cm-1.
The IR absorption bands have two characteristics: frequency and magnitude. The former is signed
in the horizontal axis at it corresponds to the absorbed IR wave numbers. It depends on the
constancy of the bound strength, coming from the bound order, and on the mass of the involved
atoms. The latter corresponds simply to the amount of IR, and it is visible in the spectrum through
the peaks. It depends on the variation of the dipolar momentum after a vibration.
The IR analysis was done as first step to identify if the spectrum of the different bioplastic
bags was the same or not, in order to decide if keep the material as a variable or as a constant during
the test.
47
The results, showed in figure 3.4, highlighted that all the four tested biobags were made of the same
polymers. The main reason to which this result can be related is that the material used for bags
come from the same industry and is then modelled by each agency for bags production.
The analysis was carried out also on the laces for bags closure, because they have a different colour
form the rest of the material, but the resulted spectrum was the same.
Figure 3.4-Comparison between spectra of four different bioplastic bags distributed in the Italian markets
Once this point was clarified, the identification of the polymers composing the material was done
through a comparison with spectra already present in literature and in scientific registers of the
laboratory.
Knowing first of all that these biobags are made on Mater-Bi, all the classes of Mater-Bi were studied
and the spectra of the polymers used for their production were found in literature.
The most probable composition was a polymer with corn starch and PBAT, typical of Mater-Bi class
N. In figure 3.5 the three spectra are compared: in the spectrum of BioP it’s possible to identify the
main peaks of the two polymers.
Between 4000-2500 cm-1 the peaks represent single bounds, as C-H and O-H, from 2500-2000 cm-1
the triple bounds, not present in this bioplastic, between 2500-2000 cm-1 the peaks are typical of
48
the double bounds, then the smallest values of wavelenght correspond to other bounds, for
example which of C=O with a glucosidic ring. It’s also fair to say that the same type of molecular
bound can have different arrangements, in accordance with the different wavelenght.
Figure 3.5-Spectra of polymers composing BioP
3.2.4 Visual analyses of bioplastics changing features
The visual analyses are proposed by the standards regulating the full scale tests on bioplastics:
they allow the study of the surface aspect of bioplastic pieces during the phases of the composting
process. In particularly, the visual inspection to evaluate the presence of holes, lateral erosion, dirty,
and to show the differencies in pieces sizes in time.
Furthermore, observing the evolution of the aspect of bioplastics, it will be possible to define when
is the turing point after which the pieces of the tested material become assimilable to compost for
their size, colour, smell and features.
The second important analysis, linked with a visible and direct change of bioplastics features,
involves the study of the physical and mechanical properties of the material, underlaing the
differences between the beginning and the phases of the composting process.
49
An example of how this method will proceed in parallel with the other analyses is in figure
3.6, where, after the manual sorting of bioplastics, some photographs were taken to immortalize
the changes of aspects.
Figure 3.6-Bioplastics aspect after the removal from composting (F. Ruggero, 2017)
3.3 Samples preparation and characterization
To start the research, the main decisions involved in the preparation of the samples, were:
quantity of bioplastics inside tests, their initial sizes, quantity of waste matrix to be composted,
numbers of replicated and the location.
3.3.1 Choice of the initial conditions
A relevant point to match in this small scale test, is the number of variables that could be
involved in the disintegration and biodegradation of bioplastics: the initial quantity of bioplastics
thrown away in the waste matrix, the size of bioplastic pieces, their thickness and composition, the
different products made on bioplastics, the environmental conditions and the composition and
quality of waste matrix.
Furthermore, before starting with the test, another consideration was done to choose the number
of samples, and it concerns the management of the experiments. Analyses of weight, temperature,
moisture content, acidity and oxygen are monitored once or twice a day, and mixing is done almost
every day during the first phase, and twice a week during the maturation.
Considering all the possible variables, it was decided for this research to use as main variable the
different sizes of bioplastics within the waste matrix, and the other as constants.
50
In fact, in the composting plants when bags with organic waste arrive, the first steps consist on bag
opening and shredding, until dimensions from 1/2 cm to 7 cm.
In accordance with a not evenly performed shredding, two sizes were chosen: small size, from 1 to
3 cm, and big size from 4 to 7 cm.
The shredding was done manually with scissors, so the pieces are not homogeneous in length and
width (Figure 3.7).
Figure 3.7-Small bioplastics size and big bioplastics size (F. Ruggero, 2017)
The pieces were accuratley divided because bioplastics have the tendency to remain attach each
other when they stay in contact, but to start the test in a way as similar as possible to the real
conditions of a composting plant they were separated, as the pieces of a biobag for waste collection.
This tendency to remain attach is called stickiness, and the evolution of this characteristics will be
accurately followed during the composting process, as it could be an element involved in bioplastics
degradation.
3.3.2 Choice of the constant values and variables of the tested material
It’s fair to discuss also about the constants of the research: quantity of bioplastics in the sample,
reference product, which is a bag for organic waste collection, and the typology of bag.
The first thing to underline is that the field of this research is a sector in continuous developments;
consequently, the idea is not to focus on the actual situation, but to adjust it in the prospective of
an expected increase of bioplastics use into the next five to ten years.
51
Made this clear, it’s possible to proceed with the explanation of the constant value chosen for
quantity of bioplastics in the samples.
To evaluate the initial concentration of bioplastics inside the waste matrix to be composted, data
from Rapporto Rifiuti Urbani 2015, ISPRA and from ARPAV were used.
Two representative graphs taken from ISPRA report are shown: the former in figure 3.8 with waste
disposed of in composting plants, coming from separate collection of organic fraction, the latter in
figure 3.9 with all the waste arriving at the composting plants, included green waste and sludges
from waste water treatment plants.
Figure 3.8-Composting of organic fraction from separate collection in Italy. (ISPRA, 2015)
Figure 3.9-Quantity of municipal solid waste disposed of in composting plants in Italy. (ISPRA, 2015)
52
In figure 3.10 it is represented the partition of the different fractions arriving at a composting plant
on average in Italy.
Figure 3.10-Fractions of waste to composting. (ARPAV 2015)
The waste mainly responsible of the discharge of bioplastics in composting plants are those coming
from houses separate collection of the organic fraction, since putrescible waste are thrown in bins
inside a bag, and this bag is made on bioplastics.
Furthermore, with the emerging use of bioplastic cutlery and packaging, also these products will be
thrown away together with organic fraction.
Another important data available concerns the yearly organic waste production pro capite in
Veneto; table 3.2 is built in accordance with ARPAV, 2015.
Table 3.2-Yearly production of organic waste pro capite in Veneto. ARPAV 2015
Year Kg/inh/y Increase
2015 140 -1.4 %
2014 142 +5.8 %
2013 134 +3 %
2012 130 +3.8 %
2011 126 -1.7%
53
Many biobags for organic waste collection are available on the market, with different dimensions:
10 litres, 15 litres or 30 litres. And different weights, variable between 6 grams and 14 grams
depending on the bag size.
Some Italian composting plants provide bags for waste collection, so that all the waste conferred to
the plant have the same bag, but generally people are free to use compostable bags bought in the
supermarket.
So, it’s not easy to give a statistical for the grams of bags per kilo of waste: to reach a final estimation,
some considerations were met.
Firstly, it was made a proportion between the amount of waste disposed of in composting plants,
from ISPRA data, and the production of compostable bioplastics from European Bioplastics data, as
expressed in table 3.3.
The variables are on the one hand the bioplastic production in Italy, equal to 0,021 if the precise
proportion between European population and Italian population is done, and equal to 0,050 in
accordance with a little bit difference in bioplastics production all over the Europe, with Italy as a
greater producer than other countries, as explained in paragraph 2.2.
On the other hand, it was taken into account also the forecast increase in bioplastic production and
in waste collected and disposed in composting.
From European Bioplastics 30% was estimated as the increase in bioplastics production, shown in
figure 3.11, while 3% is a mean value of increasing waste to composting over the last ten years
present in the ISPRA report.
Figure 3.11-30% increase in bioplastics production all over the world. (www.european-bioplastics.org)
54
Table 3.3-Proportions between waste to composting and bioplastics produced
Waste to
composting
(million tons)
Bioplastics production
(million tons)
Proportion: waste to composting/ bioplastics
Data of 2015/2016 5,3 0,021 252/1
Data of 2015/2016 5,3 0,050 106/1
Data forecast for 2018 5,3 + 3 % 0,021 + 30 % 200/1
Data forecast for 2018 5,3 + 3 % 0,050 + 30 % 84/1
It’s fair to consider that not all the bioplastics produced will be led to composting plants after their
used, so the values in the proportions should be adjusted a little bit.
Secondly, knowing the capacity of a biobag and the amount of organic waste produced pro capite a
day, an estimation of biobags grams per kilo of organic waste was done: few variables must be
considered, as the number of householders, the fact that sometimes the bag are not completely
filled before having thrown in the bins, the collection system, the period of the year, because in
summer organic fraction is collected generally every days to avoid bad smells, and so for small
families bags could be half full.
To conclude, the production of bioplastic waste is about 5,5 g every 1 kg of putrescible collected.
Adjusting this value with a future forecast increase of 30% in bioplastic products thrown away
together with organic fraction, the amount is of 7 g per kilo.
The second constant consists on the bioplastic product to use as tested material: just because the
main bioplastic product used is biobag for organic waste collection, a bag was taken as tested
materials.
Bioplastics bags present on the market are almost all composed on Mater-Bi; the chosen bag is
produced in Veneto, and has a high number of certifications: CIC, Vinicotte OK compost, Mater-Bi
Novamont license and obviously, it is according with EN UNI 13432.
As explained in the paragraph 3.2.3, the decision to take constant the typology of tested
material was supported by an infrared analysis of biobags spectrum. It defined that the analysed
biobags, all bought in supermarkets, have the same spectrum, it means the same composition, so it
was feasible to use only one type of bag.
55
3.3.3 Characterization of the compostable matrix
Waste used to simulate real matrix of composting plants are four, with the exclusion of waste
representative of sludge from waste water treatment plants.
For the putrescible kitchen waste, without paper from handkerchiefs and napkins, were taken from
university canteen: it was provided with a machinery which shreds the food scraps in pieces of about
1 cm with a moisture content varying from 60 to 80%.
Green waste was simulated using clipping grass and wood chips; the adding of grass adjusted the
nutrients contents, while wood chips increased the structure of the composting matrix and
decreased the moisture content until a suitable level.
Finally, a percentage of manure enriched in bacteria were added as inoculum (Figure 3.12).
Figure 3.12-Food waste, wood chips, clipping glass and inoculum to compose OFi (F. Ruggero, 2017)
To verify the initial mixture of waste composing OF complied with the requirements of waste
to composting, the analyses of the main parameters were carried out on the single components of
the matrix and a mean value of them was elaborated with a weighted average.
56
Table 3.4-Paramters of the single components of the waste matrix
OFi composition Percentages% Quantity Kg Moisture % VS% TKN g/kg TS TOC g/kg C/N pH
Kitchen waste 53 2,65 80 96,4 29,5 493 17 7,4
Clipping grass 3 0,15 50 46,9 11,7 311 27 5,5
Wood chips 33 1,65 25 96,9 7,2 511 71 6,4
Manure 11 0,55 18 63,8 34,5 348 10 5,6
The main requirements are the value of moisture, volatile solids and C/N, so their weighted average
is elaborated in the following table, with the purpose to show that they are suitable for the
composting process, in accordance with the standards. In fact moisture content and VS are higher
than 50%, C/N is in the required range 20-35, and pH higher than 5.
Table 3.5-Weighted average of the parameters required by composting standards
OF Initial conditions
Parameter Moisture % VS% C/N pH OF weighted average 54 91 34 6
Required values (EN 13432) > 40-50 > 50 20-35 > 5
When these values had been analysed in the initial matrix with all the components mixed
together, they were found to be a little bit different, especially the C/N; the observation is linked
with some considerations, as the points of sampling, the effect of the mixing, the predominance of
a component on the others.
Figure 3.13-OFi composition in percentages
53%
3%
33%
11%
OFi composition
kitchen waste
clipping grass
wood chips
inoculum
57
3.3.4 Location of the tests and their mounting
The location for the storage of the samples was a box, with internal temperature in accordance
with the external one; for the hot climate in summer an air conditioner was installed inside the
container to maintain the temperature around 25 -30 °C.
The initial idea for this research was to compose small baskets with 5 kg of waste each, in
order to disassemble all of them in different established timings to carry out analyses on the
composting process and on bioplastics.
Three blanks for the first line, five samples with small bioplastics size for the second and five samples
with big bioplastics size for the third line.
The three blanks were useful to compare the final quality of compost without and with tested
material, and to evaluate the differences in weight losses between them along the process.
It was considered that in number of three they can be representative of a statistical, and if along
the process it was considered worthwhile to destroy one of them to carry out some deeper analyses
on composting parameters and granulometry, other two blanks would be continued until the end
of the experiments.
For the two lines with bioplastics, five replicates were prepared, in accordance with the necessity
to have four samples to be analysed along the process (Figure 3.15).
To hold the composting waste, baskets with holes generally used for fruits and vegetables
were kept; holes are necessary to allow exchange of oxygen and exit of water, but to avoid the
passage of the smallest fractions of the matrix, the basket was internally lined with a mosquito net,
firm seals with clips. At the bottom of the basket a tray was displaced in other to collect water and
allow the weighting of water losses during the process (Figure 3.14)
Figure 3.14-Photographs of materials supplied for the experimentation (F. Ruggero, 2017)
58
Figure 3.15-Scheme of the samples od line 1
59
To have the precise weight of waste along the process and daily weight of water, in table 3.6
the weights of basket and tray for each test are reported.
Table 3.6-Weight of basket and tray for test storage
Sample name Basket weight with nets and clips (kg) Tray weight (kg)
OF 1 0,478 0,509
OF 2 0,484 0,482
OF 3 0,582 0,508
BioPOF 1 small 0,475 0,506
BioPOF 2 small 0,681 0,509
BioPOF 3 small 0,652 0,480
BioPOF 4 small 0,553 0,483
BioPOF 5 small 0,492 0,484
BioPOF 1 big 0,660 0,509
BioPOF 2 big 0,477 0,482
BioPOF 3 big 0,531 0,483
BioPOF 4 big 0,761 0,481
BioPOF 5 big 0,701 0,509
The heaps of waste to be composted were prepared by mixing together the amount of the
different components previously discussed in blanks, and adding the shredded bioplastics for the
samples with tested material.
To be sure that the established proportions were perfectly respected in the samples, each matrix
was individually prepared, mixed and disposed in the respective basket, after ensuring the total
weight was equal to 5 kg for blanks and to 5,035 kg for the two lines of BioPOF (Figure 3.16).
Figure 3.16-Working on the sample building (F. Ruggero, 2017)
60
The resulting aspect of the heaps immediately after their building is shown in figure 3.17; each
component is easily distinguishable from the others, and the shape of the sample can be maintained
as a heap thanks to the presence of wood chips that ensure a good structure of the matrix.
For the first days, the baskets were partially covered with a bag; this was done only during the night,
because the experiments began at the end of march and, with a minimum temperature in the night
between 5 and 10 °C.
So, the coverage allows the temperature inside the heaps to increase and the process to start,
avoiding a high influence coming from the external cold.
Air could enter from the sides of the basket, as the photograph shows, so that oxygen level remained
suitable for the advancement of composting process.
To conclude, all the samples were aligned on tables inside the container, finally ready to start their
composting process (Figure 3.18).
Figure 3.17-Heaps aspect immediately after their building, and coverage for the night (F. Ruggero, 2017)
Figure 3.18-Heaps on their baskets, on tables inside the container (F. Ruggero, 2017)
61
Having followed the composting process during the thermophilic phase, it was noticed that
such small heaps of waste were not able to retain the heat; so, being in a period between winter
and spring, during the night the temperatures decreased both in the box and in the heaps.
Problems like this are possible when it is carried out a research in a new field, without a bibliography
to support the experimental part: the solution thought to overcome the problem was firstly to join
the baskets of each sub-lines at the end of the thermophilic phase, creating three bigger heaps.
Secondly to start with a new line directly with three heaps of 25 kg each, one for the blank, the other
two with the tested material in the two defined different sizes. The same bioplastic material was
used and the initial composition of waste compostable matrix was the same of the previous tests.
The heaps were located in the box, a nylon cloth was put on the floor in order to retain the leaching
water, and edges were made with tubes to keep separate the heaps and avoid mixing of their
materials during the operations of turning, weighting, sampling and water adding (Figure 3.19).
In figure 3.20, the photographs of the heaps just composed: bioplastics are visible even if their
colour is similar to which of the waste.
Figure 3.19-The place for compostable heaps (F. Ruggero, 2017)
Figure 3.20-Line 2: OF, BioPOF small, BioPOF big (F. Ruggero, 2017)
62
From this point to end of the research, the two lines are called Line 1, started from the
baskets jointed into three heaps after the thermophilic phase, and Line 2, started directly from the
heaps of 25 kg.
In figure 3.21 is reported the scheme of the two lines with the respective blank (OF), matrix with
small size bioplastics (BioPOF small) and matrix with big size bioplastics (BioPOF big), while in figure
3.22 the three just composed heaps of Line 2 on the right and the three heaps of Line 1 at the end
of the thermophilic phase on the left.
It was already visible the difference in the process development even if the two lines had been
started only with ten days of distance.
Figure 3.21-Scheme of the two lines with the respective heaps
63
Figure 3.22-Line 1 and Line 2 with blanks and heaps containing the tested material (F. Ruggero, 2017)
64
65
4. RESULTS AND DISCUSSION
4.1 Analyses of the composting process parameters
The parameters analysed during the composting process are reported in this paragraph to follow
the evolution of the composted matrix in time, up to the results which defined the end of the
process, in accordance with the required standard values.
The graphs and tables are in part reported in the Annex I: composting process parameters.
4.1.1 Temperature
During the period of experimentation, the outside temperature had a great variability, and the
thermophilic phase of the two lines coincided with two different climatic conditions: for the Line 1
at the end of march the outside temperature was around 10 up to 20 °C, feeling the influence of
night and rainy days, while for the Line 2 the external conditions were more favourable, with a
higher constancy of temperature around 25 °C.
Figure 4.1 shows a comparison between the outside temperature and the heap temperatures for
Line 1: in the Annex I the graphs with also the comparison between temperatures of the three heaps
of each lines, even if their values are significantly similar one to the others.
Figure 4.1-Comparison between outside temperature and heaps temperature - Line 1
0,0
10,0
20,0
30,0
40,0
50,0
60,0
1 3 5 7 9 11 13 15 17 19 21 23 25 27 29 31 33 35 37 39 41 43 45 47 49 51 53
Tem
per
atu
re (
°C)
Time (d)
Temperatures comparison - Line 1
Mean T Outside T
66
It results then interesting the graph built in figure 4.2 which representing the different
phases of the two lines with the respective changing temperatures; making an average between the
main steps of temperature values during the process, four phases could be identified. Starting from
the lag phase, very brief due to the small mass of the compostable heap, then the thermophilic
phase of nine days, the cooling phase of eleven days, followed by the maturation phase of one
month. This last phase presented an increase of temperature from the 47th day to the end, and it
was clearly linked to the outside increase of temperature. In fact, as the lower temperature of
thermophilic phase in Line 1 than in Line 2 was linked with the outside lower temperature, also the
influence of a hot climate was able to influence in the opposite way the increase of temperature
within the heap.
This influence from outside was mainly reliable with the small mass of the heap which was not a
good buffer between inside conditions and outside climate.
Figure 4.2-Mean temperatures during the phases of composting process
4.1.2 Weight
The weight losses were monitored every day during the thermophilic phase of the Line 1,
when the samples were located in the baskets. Then, after the composition of the six heaps, the
weight was monitored in the timings of sampling for the analyses.
67
In fact, to weight the heaps, they were dismantled and put within a big basket to be weighted in a
balance precise up to the grams, able to weight no more than 30 kg.
Each heap was then rebuilt in the typical pyramidic shape.
The total weight of the heaps is shown in figures 4.3 and 4.4, for the two lines, and
summarized in table 4.1.
Figure 4.3-Total weight of composted heaps- Line 1
Figure 4.4-Total weight of composted heaps- Line 2
0
10
20
30
40
50
60
70
80
90
100
OF BioPOF small BioPOF big
Wei
ght
of
the
hea
p (
%)
Weight during the composting process - Line 1
1st day 10th day 25th day 40th day 55th day
0
10
20
30
40
50
60
70
80
90
100
OF BioPOF small BioPOF big
Wei
ght
of
the
hea
p (
%)
Weight during the composting process - Line 2
1st day 10th day 26th day 40th day 55th day
68
Table 4.1-Total weight of heaps during composting process
Line 1 Weight % Line 2 Weight % OF BioPOF small BioPOF big OF BioPOF small BioPOF big
1st 100 100 100 100 100 100 10th 61 59 59 65 66 65 25th 39 40 43 36 37 37 40th 30 30 35 35 36 33 55th 28 29 28 29 31 30
As the histograms elaborated for each phase of the process show, the weight decreased in
fifty-five days from 100% to 30%, in accordance with the general values reliable to a real composting
process.
In particularly it is fair to observe that the main weight losses were between the 1st and the 10th day,
so during the thermophilic phase, and between 10th and 25th, the cooling phase.
During the maturation phase there was a weight stabilization, consequently also to the stabilization
of the moisture content.
In the monitoring of the weight, the sampling and the water adding were taken into account for the
elaboration of the mass balance.
In table 4.2 and in figures 4.5 and 4.6 it is represented the dry weight during the days of the
sampling.
Figure 4.5-Dry weight of composted heaps- Line 1
0
5
10
15
20
25
30
35
40
45
50
OF BioPOF small BioPOF big
Wei
ght
of
the
hea
p (
%)
Dry weight during the composting process - Line 1
1st day 10th day 25th day 40th day 55th day
69
Figure 4.6-Dry weight of composted heaps- Line 2
Table 4.2-Dry weight of heaps during composting process
Line 1 Dry weight % Line 2 Dry weight % OF BioPOF small BioPOF big OF BioPOF small BioPOF big
1 43,5 43,3 43,2 44 44 43 10 34 33 33 36 33 36 25 24 25 25 22 23 22 40 17 17 20 19 19 18 55 16 17 16 15 16 15
4.1.3 Total and volatile solids
Since to apply this procedure a sampling was necessary, it was done during the thermophilic
phase once every two days and during the maturation once a week, in order to keep under control
the water content within the heap and to maintain it constant up to 55%, adding water, when it
decreased.
The water was added with a watering can for flowers, to distribute the water in all the points of the
heap, and then mixed to ensure an equalization of the moisture content.
The graph here reported is the moisture for Line 2, but the tables and the graph of total solids and
moisture for Line 1 are reported in Annex I.
0
5
10
15
20
25
30
35
40
45
50
OF BioPOF small BioPOF big
Wei
ght
of
the
hea
p (
%)
Dry weight during the composting process - Line 2
1st day 10th day 25th day 40th day 55th day
70
Figure 4.7-Moisture content - Line 2
The decreasing peak from the 10th to the 25th day was linked with the initial try to not supply a
manual intervention on the heaps, to leave them making their own pathway during the cooling
phase and observe if the degradation activity was still intense or not.
Because the water content had fallen down to 40%, it was necessary to supply water: at this point
the process showed an increase also in temperature, it meant that the activity of degradation of the
organic substance was not finished at all and the conditions suitable for the living organisms should
be maintained for all the process.
Furthermore, it was noticed that the degradation of bioplastics still proceeded even when water
was not supplied, so the try to leave the process without manual intervention gave the information
that bioplastics are degraded by those microorganisms, as fungi, which are less sensitive to internal
conditions of the heap.
The results of the volatile solids are reported in Annex I, even if they didn’t show a great
variation in time, especially due to the presence of wood chips which need more time to be
degraded and it is so reach in carbon content that it contributed to increase the value of all the
samples taken along time.
0
10
20
30
40
50
60
1st 10th 25th 40th 55th
Mo
istu
re (
%)
Moisture content - Line 2
OF BioPOF s BioPOF b
71
4.1.4 pH
In accordance with the composting process, the pH of the samples taken never went under 5, it
meant that no anaerobic processes of fermentation had happened and the process remained
aerobic at all.
In fact, through the mixing, the supply of oxygen above 20% was ensured: it’s possible to observe
that around the 40th day there was an increase of the values around 8, but at the end of the process
the pH was stabilizing around the neutral value of 7,5 as required for a mature compost.
Table 4.3-pH
pH
Line 1
1st 10th 25th 40th 55th
OF 5,48 7,17 7,45 7,86 7,61 BioPOF s 5,23 6,32 7,56 7,92 7,71 BioPOF b 5,51 6,44 7,23 7,91 7,54
Mean 5,4 6,6 7,4 7,9 7,6
Line 2
1st 10th 25th 40th 55th
OF 5,53 7,07 7,42 7,97 7,5 BioPOF s 5,22 7,13 7,31 7,92 7,77 BioPOF b 5,37 7,03 7,42 7,78 7,75
Mean 5,4 7,1 7,4 7,9 7,7
4.1.5 TKN and nitrates
The results of TKN analyses drew a behaviour which was not uniform nor constant at all, but it’s
important to keep in mind that the experiment, even if was done on a small scale, could have some
differences in the results due to the different points of sampling, so it was possible that for OF it
existed a decrease instead of a constant increase between 25th and 40th days.
However, having started from values of about 250 g per heap, the losses were of 100 g, showing a
consumption of nitrogen by microorganisms that mainly needed it, in accordance with the Liebig
law, for their metabolic processes.
The results are reported in table 4.4 and graph 4.8 for Line 2.
72
Table 4.4-TKN in grams
TKN g
Line 1
1st 10th 25th 40th 55th
OF 116 112 120 64 77 BioPOF s 219 207 158 84 134 BioPOF b 235 205 163 122 138
Mean 190 175 147 90 116
Line 2
1st 10th 25th 40th 55th
OF 222 230 140 130 120 BioPOF s 247 223 186 156 136 BioPOF b 170 228 173 141 130
Mean 213 227 167 142 129
Figure 4.8-TKN behaviour during the composting process – Line 2
As for the nitrates, in all the analysed samples they were less than 10 mg/Kg TS, with the
exception for:
- OF Line 2 55th = 23,6 mg/Kg TS
- BioPOF Line 1 55th = 15,4 mg/Kg TS
It means that there contribute to C/N is negligible.
0
50
100
150
200
250
300
1st 10th 25th 40th 55th
TKN
(g)
TKN (g) - Line 2
OF BioPOF small BioPOF big
73
4.1.6 TOC and inorganic carbon
The graph 4.9, reported here only for Line 2, shows the decrease of total organic carbon, linked
with the consumption of the organic substance by the microorganisms: the final amount of carbon
present in the heaps was still high because, as valid for the volatile solids, it corresponded to the
presence of wood chips which require a longer time to be attacked and degraded by fungi, during
the maturation phase.
Table 4.5-TOC in grams
TOC g
Line 1
1st 10th 25th 40th 55th
OF 3334 2346 1566 1093 1022 BioPOF s 5553 3839 2682 1858 1613 BioPOF b 5594 3818 2590 2182 1669
Mean 4827 3334 2279 1711 1435
Line 2
1st 10th 25th 40th 55th
OF 5658 4260 2562 2159 1967 BioPOF s 5689 3867 2660 2156 1571 BioPOF b 5436 4133 2477 1967 1560
Mean 5594 4087 2566 2094 1699
Figure 4.9-TOC behaviour during the composting process - Line 2
0
1000
2000
3000
4000
5000
6000
1st 10th 25th 40th 55th
TOC
(g)
TOC (g) - Line 2
OF BioPOF small BioPOF big
74
Moreover, the analyses on the inorganic carbon resulted less than 1 g/kg TS, it means that
the parameter is negligible with respect to TOC.
4.1.7 C/N
In table 4.6 they are reported all the values of C/N along the process of composting: as
specified in the previous paragraphs, inorganic carbon and nitrates have a negligible contribute in
the total amount.
Table 4.6-C/N (TOC on TKN)
C/N
Line 1
1st 10th 25th 40th 55th
OF 29 21 13 17 13 BioPOF s 25 19 17 22 12 BioPOF b 24 19 16 18 12
Mean 26 19 15 19 13
Line 2
1st 10th 25th 40th 55th
OF 25 19 18 17 13 BioPOF s 23 17 14 14 11 BioPOF b 32 18 14 14 12
Mean 26,8 18,0 15,6 14,8 12
The initial experimental values enter in the range required by the Liebig law, allowing the process
to start: they were less than the C/N equal to 34 found with the weighted average of the single
fractions of the waste matrix, but they still remained in the necessary range.
Finally, the values obtained at the 55th day of the process, respected the standards for a mature
compost, being in a range 11-13, suggesting a positive result for the process with the consumption
of the organic matter by microorganisms.
4.1.8 Respirometric Index (RI)
In table 4.7 there are reported the values for all the days of sampling, including the 1st, to show
the evolution of the respiration within the composted matrix.
75
It is generally valid that for a fresh waste the RI4 = 70-80 mg O2/g VS, while for a mature compost RI4
< 5 mg O2/g VS (Cossu, 2016). In the case of these samples the RI was done not only for 4 days but
also for 7 days; all the numbers are exposed in the Annex I.
The graph and the table with the results of RI4 show that the final values, even if a little bit higher
for the Line 2 than the Line 1, are below the required value for a mature compost, defining that the
phase of activity of the microorganisms is almost finished.
Table 4.7-RI 4 normalized on volatile solids
RI4 mgO2/g VS
Line 1
1st 10th 25th 40th 55th
OF 52,3 38,7 38,2 26,4 1,3 BioPOF s 51,9 39,1 41,0 33,3 3,4 BioPOF b 49,8 36,5 43,7 30,2 5,3
Mean 51,3 38,1 41,0 30,0 3,4
Line 2
1st 10th 25th 40th 55th
OF 49,5 33,9 27,1 13,1 8,6 BioPOF s 50,0 34,8 35,4 22,1 6,6 BioPOF b 53,2 27,9 32,1 16,2 8,4
Mean 50,9 32,2 31,5 17,1 7,9
Figure 4.10-RI 4 normalized on volatile solids
0,0
10,0
20,0
30,0
40,0
50,0
60,0
1st 10th 25th 40th 55th
RI 4
(m
g O
2/g
VS)
RI 4 (mg O2/ g VS)
Line 1 Line 2
76
4.2 Sieving analyses for the granulometric curve
After each sieving, the passing fractions and the withheld fractions were weighted, and from the
withheld the further sieving could start. In figures 4.11 and 4.12 are shown the seven bowls with
the withheld (except for the last one which contains the passing at 14 sieve) fractions, respectively
for a blank and for a BioPOF small.
Figure 4.11-Sieved fractions 10th day, OF (F. Ruggero, 2017)
Figure 4.12-Ssieved fractions 25th day, BioPOF small (F. Ruggero, 2017)
In figure 4.13 the manual sieving operation is captured, with also a focus on one of a single witheld
fraction.
77
Figure 4.13 Sieving operation (F. Ruggero, 2017)
After sieving the samples through the six sieves, a granulometric curve was drawn with the
passing fractions.
In this way it was possible to have a clear vision of the changing in time of the fractions, making a
comparison between the analysed points.
The graph and the table with weight and percentages are reported in Annex II, while in figure 4.14
it is drawn the granulometric curve of BioPOF small, Line 1, to show the difference among the
composting phases.
Figure 4.14-Granulometric curve example
It’s fair to say that not a significant variation of seizes occurred in time; for the smallest
fractions there was an increase between 10 and 15% of passing materials. So the fractions to be
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
of
pas
sin
g %
Granulometry (mm)
BioPOF small granulometric curve - Line 1
10th day
25th day
40th day
55th day
78
considered as compost, those smallest than 10 mm, reached in total an 80% of the total matrix,
where the material smaller than 5.60 mm was about the half.
To give an idea of the different composted waste present in each fraction after sieving, in figure
4.15 is reported a graph with the material mainly found in the different ranges of seizes of the
samples.
Figure 4.15-The main waste components of each granulometric fraction
4.3 Evaluation of bioplastics disintegration and degradation in composting
4.3.1 Sieving analyses of bioplastics disintegration
The results of sieving analyses are reported in this paragraph for all the four timings of
sampling and for both small and big BioP of the two lines: in fact the purpose is to show on the one
hand the behaviour of bioplastics disintegration during the phases of the process, describing an
eventual linear or not linear trend of disintegration, and on the other hand the comparison between
the results of the two lines to define if this trend is constant within all the samples or if it exists a
substantial difference among big and small BioPOF and among the lines.
The results are reported in tables from 4.8 to 4.11, referring both to the weight of bioplastics sample
taken off from each witheld fraction, and to the correspondent percentage, to avoid having the
79
influence of the difference in the initial weight of the samples taken, from a maximum of 2.5 kg for
the 10th of Line 1 to a minimum of 0.5 kg in the last timings of sample, as not to remove too much
bulk from the ever-smaller heaps.
Then in the histograms elaborated from these data, the values are reported only in percentage, in
figures 4.18 – 4.21. All the results are divided into four sections, to show the comparison in time
between the four points sampled: BioPOF small Line 1, BioPOF small Line 2, BioPOF big Line 1,
BioPOF big Line 2.
Furthermore, in graphs 4.16 and 4.17 there are drawn the size of bioplastics at the beginning of the
test, considering that the samples were equally distributed among the sizes of the two ranges, small
BioP and big BioP.
Figure 4.16-BioPi small size at the beginning of the test
Figure 4.17-BioPi big size at the beginning of the test
0
20
40
60
80
100
30 20 10 0
Per
cen
tage
of
Bio
Pi (
%)
Size (mm)
BioPi small initial size
BioPi small
0
20
40
60
80
100
70 60 50 40
Per
cen
tage
of
Bio
Pi (
%)
Size (mm)
BioPi big initial size
BioPi big
80
Figure 4.18-Histograms of BioP small granulometry – Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 10th day - Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 25th day - Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 40th day - Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 55th day - Line 1
81
Figure 4.19-Histograms of BioP small granulometry – Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withhheld BioP small 10th day - Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 25th day - Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 40th day
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP small 55th day
82
Figure 4.20-Histograms of BioP big granulometry – Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 10th day - Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 25th day - Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 40th day - Line 1
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 55th day - Line 1
83
Figure 4.21-Histograms of BioP big granulometry – Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 10th day - Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 25th day - Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 40th day - Line 2
0
20
40
60
80
100
20,00 10,00 8,00 5,60 2,38 1,40
Per
cen
tage
%
Withheld BioP big 55th day - Line 2
84
Table 4.8-BioPOF small granulometry - Line 1
BioPOF small withheld - Line 1
10th day 25h day 40th day 55th day
Sieve Granulometry (g) (%) (g) (%) (g) (%) (g) (%)
3/4 20 0,883 3 1,337 5 0,206 3 0 0
3/8 10 22,462 66 13,867 52 2,6781 33 2,8168 26
5/16 8 5,969 17 5,357 20 2,4321 30 2,0169 19
3,5 5,6 2,765 8 4,140 16 1,8094 22 2,4682 23
8 2,38 2,052 6 1,685 6 1,0202 12 3,1427 29
14 1,4 0,000 0 0,057 0 0,0724 1 0,2106 2
Table 4.9-BioPOF small granulometry - Line 2
BioPOF small withheld - Line 2
10th day 265h day 40th day 55th day
Sieve Granulometry (g) (%) (g) (%) (g) (%) (g) (%)
3/4 20 3,612 14 1,494 7 0,137 1 0,0012 0
3/8 10 16,323 65 12,003 53 6,462 44 2,4152 23
5/16 8 3,797 15 5,392 24 4,987 34 2,675 25
3,5 5,6 1,138 5 3,078 13 1,934 13 2,5431 24
8 2,38 0,350 1 0,761 3 1,248 8 2,9155 27
14 1,4 0,000 0 0,074 0 0,029 0 0,184 2
Table 4.10-BioPOF big granulometry - Line 1
BioPOF big withheld - Line 1
10th day 265h day 40th day 55th day
Sieve Granulometry (g) (%) (g) (%) (g) (%) (g) (%)
3/4 20 9,603 25 7,340 20 1,0914 16 0,1792 3
3/8 10 24,985 66 27,474 73 3,1363 45 3,1464 44
5/16 8 2,453 6 2,489 7 2,2545 32 2,5702 36
3,5 5,6 0,636 2 0,191 1 0,3534 5 0,809 11
8 2,38 0,076 0 0,029 0 0,1839 3 0,3972 6
14 1,4 0,000 0 0,000 0 0,002 0 0,0108 0
Table 4.11-BioPOF big granulometry - Line 2
BioPOF big withheld - Line 2
10th day 25th day 40th day 55th day
Sieve Granulometry (g) (%) (g) (%) (g) (%) (g) (%)
3/4 20 10,480 50 13,373 36 5,010 21 0,3012 4
3/8 10 10,334 49 22,764 61 12,732 53 2,8764 42
5/16 8 0,177 1 0,540 1 3,733 16 2,4253 35
3,5 5,6 0,001 0 0,271 1 2,235 9 1,004 15
8 2,38 0,016 0 0,285 1 0,328 1 0,2996 4
14 1,4 0,000 0 0,000 0 0,023 0 0,0098 0
85
From the direct observation of the data collected three considerations can be done about
the development and the trend of the disintegration process of bioplastics.
It’s fair to notice that it exists a uniform trend between small BioP of Line 1 and small BioP of Line
2, as for big BioP of the two lines; so the process of disintegration has a common behaviour
independently on the heap.
However, the data of the 10th day for big BioP are quite different as for the sieves 10 and 20 mm;
observing that this difference disappear in the later graphs, it can be associated firstly to the
sampling of few grams in a big heap, and secondly to the less linear behaviour of the thermophilic
phase with respect to the maturation phase.
The second consideration is about the difference which occurs among the small and big size: in fact
it is noticeable from the percentages that the small BioP became microplastics just since the 25th
day, with an average percentage between the two lines of 20%, up to 55% at the 55th day.
Meanwhile, as for the big BioP, the sieving analyses of the 25th day showed a percentage of
MicroBioP less than 1%, increasing up to 20% at the 55th day.
Thus, as supposed in the initial hypotheses of the research, it exists a creation of microplastics during
the composting process of BioP, which, in accordance with the size at the beginning of the
treatment, leads to having after a certain point more micro than normal bioplastics.
In the sieving analyses required by the standards, the sample after twelve weeks is passed
through a sieve of 2 mm to demonstrate that the weight of bioplastics bigger than this fraction is
less than 10%. But, as seen from the data collected in the experimental part of the thesis, this
observation is not sufficient to demonstrate the disappearance of the bioplastics during the
composting process, just only their disintegration.
In order to have a possible prevision of the time needed by the bioplastics of the small scale
experiment of this thesis to become finest than 2 mm and finally disappear, it was built a model that
exploits the linearity of the cooling and the maturation phase.
Starting from the values obtained in tables 4.8-4.11, it was done a weighted average between the
sizes of bioplastics in each timing of sampling, and it was found the mean size of each day of
sampling for the four heaps. In table 4.12 there are reported all these values.
It was also evaluated the percentage of size reduction with respect to the previous day of sampling.
The aim was to demonstrate that it subsisted a substantial difference in the trend of size reduction
between the phases of the composting process.
86
The equations to obtain the mean size of the bioplastics are:
𝛴(𝑆𝑖𝑒𝑣𝑒 (𝑚𝑚) ∗ 𝑊𝑖𝑡ℎℎ𝑒𝑙𝑑 𝐵𝑖𝑜𝑃 (%)) = 𝑀𝑒𝑎𝑛𝑠 𝑠𝑖𝑧𝑒 𝑜𝑓 𝐵𝑖𝑜𝑃 𝑑𝑎𝑦 𝑥, 𝐿𝑖𝑛𝑒 𝑦 (𝑚𝑚) (9)
𝑀𝑒𝑎𝑛 𝑠𝑖𝑧𝑒 𝐿𝑖𝑛𝑒 1 + 𝑀𝑒𝑎𝑛 𝑠𝑖𝑧𝑒 𝐿𝑖𝑛𝑒 2
2= 𝑀𝑒𝑎𝑛 𝑠𝑖𝑧𝑒 𝑜𝑓 𝐵𝑖𝑜𝑃 𝑑𝑎𝑦 𝑥 (𝑚𝑚) (10)
The equation for the evaluation of size reduction is written as follows:
𝑑(𝑖 + 1)
𝑑(𝑖)∗ 100 = % 𝑠𝑖𝑧𝑒 𝑟𝑒𝑑𝑢𝑐𝑡𝑖𝑜𝑛 (11)
Table 4.12-Mean size of bioplastics during the composting process
Mean size mm % Size reduction
Day BioP small BioP big BioP small BioP big
1st 20,00 50,00 50 73
10th 9,96 13,64 9 7
25th 9,11 12,66 13 14
40th 7,93 10,87 22 20
55th 6,21 8,67 29 28
From the values reported in the table it’s fair to notice that during the thermophilic phase
the percentage of size reduction is much higher than between the values obtained during the
cooling and the maturation phase; thus, in order to elaborate a general model (Figure 4.22) able to
give information about the time needed for the bioplastics to disappear, the first ten days and so
the first percentage value of reduction was not considering in the experimental data used to
implement the forecast tendency line of the model because they would have greatly altered the
final results.
Furthermore, the thermophilic phase was closed after ten days, and all the proceeding of the
composting after the 55th day was a maturation phase, so having the same trend and behaviour of
the last forty-five days.
87
Figure 4.22-Model of prevision of bioplastics disintegration
y = -1,1156x + 21,116y = -0,0829x + 10,996
R² = 0,9758
y = -4,5956x + 59,596
y = -0,1111x + 15,064R² = 0,9748
0
10
20
30
40
50
60
0 20 40 60 80 100 120
Bio
P s
ize
(mm
)
Time (days)
Bioplastic disintegration during the phases of the composting process
Thermophilic phase BioP small Maturation phase BioP small Thermophilic phase BioP big
Maturation phase BioP big Lineare (Thermophilic phase BioP small) Lineare (Maturation phase BioP small)
Lineare (Thermophilic phase BioP big) Lineare (Maturation phase BioP big)
88
This model presents a fundamental positive aspect; the advantage involves the square error
obtained from both the lines, so near to 1 that it shows basically a model of almost a perfect
linearity. Thus, following the model it is possible to affirm that after 115 they would be finer than 2
mm.
It means four months, or better 16.5 weeks, to become finer than 2 mm as required by standards.
On a small scale, starting from 25 kg, it is not possible to proceed with the collection of further data
after the 55th day because the heap would become too small to allow the taking of other samples
without compromising the total bulk of the heap and consequently the possibility for the
composting process to follow a natural evolution similar to the real composting plants.
An eventual variable not verifiable through this small scale test concerns the possibility of a
slowdown in the trend of disintegration when the bioplastic pieces become smaller and smaller
after the 55th day.
The hypothesis of this variable arose from the observation of the two lines of the graph; in fact the
bioplastics started with a bigger size have a disintegration velocity higher than which of bioplastics
starting from the smaller size.
To conclude with the elaboration of the results of this analysis of the disintegration, it’s fair
to underline again the discrepancy between the thermophilic and the maturation phase in their
effect on the reduction of bioplastics size.
With the further analyses, it will be analysed if the same situation can be observed also for
disintegration or if this trend is valid only for the disintegration.
4.3.2 Bioplastics concentration
The values of concentration found for each sample during the analyses are reported in tables
4.13 and 4.14: they have been subdivided in accordance with the respective line and the heap of
origin, small or big BioPOF.
In the tables below, not only the values of concentration of each single fraction are reported,
but also the values of the total amount of BioP within the heap, and of the microplastics less than
5.60 mm.
89
Table 4.13-BioP small concentration in BioPOF
BioPOF small - Line 1 BioPOF small - Line 2
Sieve Granulometry 10th day 25th day 40th day 55th day 10th day 25th day 40th day 55th day
3/4 20,00 0,008 0,014 0,009 0,000 0,027 0,015 0,011 0,000
3/8 10,00 0,029 0,034 0,041 0,018 0,031 0,028 0,035 0,016
5/16 8,00 0,023 0,023 0,043 0,023 0,014 0,021 0,051 0,031
3,5 5,60 0,010 0,014 0,029 0,022 0,004 0,009 0,016 0,023
8 2,38 0,002 0,002 0,005 0,007 0,001 0,001 0,003 0,007
14 1,40 0,000 0,000 0,002 0,002 0,000 0,001 0,000 0,002
Total BioP ≤ 20,00 0,017 0,015 0,016 0,011 0,013 0,015 0,015 0,011
MicroBioP ≤ 5,60 0,0015 0,0018 0,0037 0,0055 0,0005 0,0010 0,0023 0,0050
Table 4.14-BioP big concentration in BioPOF
BioPOF big - Line 1 BioPOF big - Line 2
Sieve Granulometry 10th day 25th day 40th day 55th day 10th day 26th day 40th day 55th day
3/4 20,00 0,055 0,061 0,091 0,014 0,070 0,095 0,010 0,017
3/8 10,00 0,047 0,056 0,039 0,020 0,018 0,048 0,073 0,020
5/16 8,00 0,010 0,010 0,040 0,020 0,001 0,002 0,036 0,022
3,5 5,60 0,001 0,001 0,004 0,005 0,000 0,001 0,012 0,007
8 2,38 0,000 0,000 0,001 0,001 0,000 0,000 0,001 0,001
14 1,40 0,000 0,000 0,000 0,000 0,000 0,000 0,000 0,000
Total BioP ≤ 20,00 0,019 0,019 0,014 0,007 0,011 0,019 0,012 0,007
MicroBioP ≤ 5,60 0,0001 0,0000 0,0007 0,0008 0,0000 0,0004 0,0007 0,0006
It’s fair to immediately notice the increase of concentration from the beginning of the process to
the times of sampling.
Three main reasons that can justify this increase are described as follows:
1. During the composting process the mass of the heaps decreases; if bioplastics don’t have
the same weight decreasing evolution, it will be present the same mass of bioplastics in a
heap lighter than at the beginning of the process.
2. The moisture content of bioplastics increases during the composting process; it means that
also their total weight increases. In fact, for having been in contact with putrescible moist
waste, bioplastics, which at the beginning of the process had a moisture content of 2%,
became moister up to 5-9%.
90
3. Bioplastic pieces tend to remain attached one to each other, in this way it’s possible to have
few lumps of bioplastics into the heap that increases bioplastics concentration in certain
points of the BioPOF. Sampling the heap for the analyses it could be possible to take also
one or more of this lumps (Figure 4.23).
Figure 4.23-Bioplastic lumps formed during the composting process
Figure 4.24 shows the variation of the total concentrations along the process: it represents a not
uniform increase up to the 25th day, and a later trend of decrease up to the 55th day when the
concentration returned near to the initial one.
Figure 4.24-BioP concentration trend during the composting process
As typical of the polluting substances, even if they potentially represent a risk for the environment
or human health, the effective contamination is a consequence of the amount of the pollutant
discharged, of its concentration in the matrix, of the duration and the time of pollution, of the space
0
0,002
0,004
0,006
0,008
0,01
0,012
0,014
0,016
0,018
0,02
1st 10th 25th 40th 55thCo
nce
ntr
atio
n B
ioP
(g
Bio
P/g
Bio
PO
F)
Time (d)
BioP concentration
BioP small - Line 1 BioP big - Line 1 BioP small - Line 2 BioP big - Line 2
91
and the matrix where they are discharged. So, not all the pollutants are effectively contaminants, it
depends mainly from the contour conditions.
Bioplastics is not considered a pollutant, but they could be if their presence in compost compromises
field fertilizations and crops or plants growth. The state of fact coming from the experimental
observation of a not constant trend in the concentration behaviour during the process, should be a
suggestion for a further implementation of ecotoxicological tests which would verify the potential
contamination of field through fertilization with a compost with different bioplastics concentration.
A further deduction was made having observed the concentration of bioplastics in
composting samples taken; starting from the experimental data of bioplastics concentration and
weight of the heaps (Table 4.1), which change along the process, it was found the amount in grams
of bioplastics in 1 kg of composted matrix.
Observing the numbers obtained with equation 8, reported in the fourth column of the tables in the
Annex III, it’s noticeable that the grams of bioplastics in the sample often increased, an occurrence
which is physically impossible.
The causes of this occurrence has to be found in the possible variables involved in the weighing of
bioplastic pieces. The first two variables had been already anticipated: firstly the increase of
moisture content in bioplastics ranging from 5 to 9%, secondly the increase of weight due to
impurities and dirt on pieces surfaces. The range of moisture increase was empirically evaluated
through total solids analysis in the oven at 105 °C, and the percentage of weight increase due to dirt
was defined through experimental data obtained with the difference of weight before and after a
cleaning operation of the bioplastic pieces.
In particularly, the operation was carried out on samples of five pieces, taken from different size
categories, different days of analyses and different heaps of the lines: these samples were weighted
as preliminary step, then each piece was cleaned using spatulas, hard brushes and tweezers for the
removal of the attached pieces of other materials. This manual operation required ten to twenty
minutes per pieces, and it was concluded with the weighting of the samples, gaining the percentage
of dirt.
The average of the percentages obtained from the samples was substantially different between days
10th and 25th and days 40th and 55th, because the bioplastics sampled in the last two timings where
dirtier than the previous ones. So the two ranges of percentage are 10-20% and 20-30%.
The last point to take into account is the distribution of bioplastic pieces inside the sample; in fact,
even if during the composition of the compostable heaps, the tested material was equally
92
distributed among the other components of waste, turning, mixing, weighting of heaps and the
composting process itself, may have changed the distribution. The consequence is that, when
sampling the heap for the granulometric analysis, it exists a range of probability that the initial
bioplastic concentration in the chosen is 10% higher or lower than 0,007.
A percentage of 10% was chosen in accordance with the small scale of the experiment which limited
the alteration of the initial pieces’ distribution in the sample, and considering that attention was
paid in taking samples as homogeneous as possible.
If the test was carried out on a full scale, this range should probably be expanded, while, working
with smaller baskets where all the initial matrix is used as sample and analysed, this variable is equal
to zero because it is exactly known the initial concentration of the sample itself.
In table 4.15 these variables are summarized, defining a minimum and a maximum value for each
variable.
Table 4.15-Range of variability in bioplastics weight
Variable Max % Min %
Moisture content + 9 + 5
Sampling + 10 -10
Dirt + 20/30 + 10/20
At this point it was made the sum of the minimum and the maximum parameters: to the values
obtained directly from the bioplastics concentration and the samples weight with equation 8, it was
subtracted from a minimum of 15-25% to a maximum of 39-49%, obtaining the values in table 4.16
and in graph 4.25.
The graph is reported only for bioplastics small of Line 2, but all the tables with calculations and the
graphs with ranges of weight variability are in Annex III.
93
Table 4.16-Bioplastics weight variation range in percentage, with respect to the initial value
BioP small % BioP big %
Line 1 Line 2 Line 1 Line 2
1st 100 100 100 100
10th 87-122 75-104 98-136 62-87
25th 52-73 48-67 71-99 61-85
40th 35-51 39-58 36-53 29-42
55th 23-34 25-37 14-21 15-23
Figure 4.25-Range of BioP small weight during the composting process
Both numerically and graphically it is observed a decrease in weight during the process: it was
excluded a completely disappearance of a certain amount of the tested material because through
the granulometric study of disintegration it was clearly pointed out that the trend of size decrease
didn’t move fast towards the smallest fractions. So, it is not due to disintegration up to
microparticles that the weight decreases, but due to a process of biodegradation that leads to a
simplification of bioplastics and to the transformation of a part of organic material into CO2 emitted
in the air and into water.
Linking now the values obtained from this model with the values obtained from the
disintegration model, it is noticeable that even if during the thermophilic phase the trend of
disintegration was faster than during the maturation phase, the weight losses don’t follow the same
trend: the direct conclusion is that the effect of temperature leads to a disintegration of bioplastic
0 1 2 3 4 5 6 7 8
1st
10th
25th
40th
55th
Weight (g)
BioP small weight range - Line 2
variability min variability max
94
pieces, but the thermophilic bacteria are not as able as the fungi, actinomycetes and mesophilic
bacteria to contribute to the biodegradation of bioplastics.
The next IR analyses will confirm this observation, showing that it is during the maturation phase
that, as the weight losses already demonstrated, the most of the degradation occurred.
The last consideration that closes this paragraph about bioplastics concentration involves a
comment about microplastics.
At the beginning of the research it was supposed that the composting process leads to a progressive
disintegration of the tested material up to 5 mm, it means up to microplastics. With the
experimental data gotten during the tests, it was demonstrated that the concentration of
microplastics in the composted matrix tended to increase along the process (Figure 4.26).
From this observation it’s fair to deduce that compost discharged in the environment could
effectively be reached in micro-bioplastics, with the important unknown of how much time these
pieces need to completely disappear, as already discussed in paragraph 4.3.1.
Figure 4.26-MicroBioP concentration during the composting process
0
0,001
0,002
0,003
0,004
0,005
0,006
1st 10th 25th 40th 55th
Co
nc.
Mic
roB
ioP
(g/
g B
ioP
OF)
Time (d)
MicroBioP concentration
BioP small - Line 1 BioP big - Line 1
BioP small - Line 2 BioP big - Line 2
95
4.3.3 IR analyses of degrading bioplastics spectra
The evolution of the spectrum along time was used to identify if a biodegradation occurred in
the material: so, IR analyses were done on bioplastic samples taken from BioPOF during the sieving
analyses of the 10th, 25th, 40th and 55th days.
A multitude of samples were submitted to the analyses to observe if among the pieces of the same
day there were a similarity, and some of these spectra are reported in Annex IV.
In this paragraph the comparisons between the spectrum of bioplastics at the beginning of the
process and during the composting are reported in the same graph for each period of analysis, just
to permit a visible comparison and a direct association between the explanation given and the
spectra drawn.
It starts from the 10th day, in figure 4.27, and proceeds with samples of 25th, 40th and 55th
day, with the comparison of the spectrum of the 1st day and of two pieces of the sampling day, one
from a fine fraction and one from a big fraction.
Figure 4.27-comparison between 10th and initial spectra of BioP
96
Some considerations can be done observing the comparison between these spectra.
It is present an increase of the first peak, around 2919 cm-1, even if it is necessary to notice that the
increase of the absorbance is just of less than 0,015. It means that, with respect to the next spectra,
here it didn’t occur a great change.
However, the reason for the increase of the bounds in this wavelength, which includes single
bounds, is to be found in the breaking of the most complex bounds into simpler one, so for example
from double to single. In fact the first action of bacteria on a complex polymer is the hydrolysis, to
make it more available: the complex molecules are broken into simpler ones.
It can be observed also the rise of new peaks in the range 1650-1500 cm-1, which corresponds mainly
to the bound C=O. Considering that the increase of a peak represents an increase in the
concentration of the correspondent bound, a reason for these peaks can be found it the breaking
of the longest chains, but maintaining inside the new smaller chains this group, while other
components are removed; as a consequence the concentration of the C=O bound increases in the
broken molecule.
As the chemical structure of the PBAT composing Mater-Bi class N is mainly composed on C=O and
single bounds within its chain (Figure 4.28), the increasing concentration of the peaks in the
correspondent wavelengths confirms that it exists a degradation of the molecule in simpler
molecules, up to reach the final formation of CO2 and water.
Figure 4.28-PBAT chemical structure
It’s fair to underline that the spectra of the samples taken from the 10th day are quite similar to
each other (Annex IV for the figures), showing that even if there are pieces disintegrated more than
others, the biodegradation at the 10th day has the same trend in all the analysed sampled.
The same IR analyses were carried out on samples of the 25th day, in figure 4.29.
97
Figure 4.29-Comparison between 25th and initial spectra of BioP
From the analyses of these spectra it was observed that for few samples, in particularly big BioP
larger than 2 cm and for small BioP larger than 1 cm, the peaks are equal to the initial spectrum, just
no signs of biodegradation.
For the sample of small BioP, withheld by the sieve of 1 cm, two peaks of 2919 and 2848 cm-1 have
an evident increase of concentration. Furthermore, the peak of 1710 cm-1 decreases in favour of the
rise of peaks in the range from 1600 to 1400 cm-1, and from 1300 cm-1 the absorbance of the initial
peaks shows a decrease in the spectra of the 25th day.
A new peak in the wavelength of the single bounds appeared for the sample of big BioP withheld by
sieve 5.60 mm, confirming the hypothesis of the breaking of the more complex molecules in simpler
ones.
More than the IR analyses on the samples of the 10th day, it was done now also an IR analyses on
the smallest, withheld by the sieve 2.38 mm: the spectra were quite disturbed due to the dirty
surface of the sample, but it was still possible to see the main peaks.
Passing now to the spectra elaborated with IR analyses on the samples of the 40th day, in
figure 4.30 compared with the spectrum of the 1st day, it’s noticeable how the trend of increase of
the peaks in the wavelength between 1600 and 1000 cm-1 was still constant, while in all the analysed
98
samples the peaks of 2919 and 2848 cm-1 were disappeared in favour of an increase of the peaks of
wavelength from 3300 to 2750 cm-1, representative of the simplest bounds of the polymer.
Figure 4.30-Comparison between 40th and initial spectra of BioP
The last IR analyses on the samples of the 55th day didn’t present a significant difference with
respect to the previous ones, defining that the main points of bioplastics degradation are the
increase of single bound and of C=O bounds.
99
Figure 4.31-Comparison between 55th and initial spectra of BioP
The spectra of one sample taken for each day of analyses are put together in the graph in figure
4.32 to show the evolution from the beginning to the end of the period of the test.
From this graph it is noticeable how the spectrum of the 1st day in reality is very similar to the initial
spectrum of the virgin bioplastic: while during the maturation phase it is evident the evolution of
the spectra toward the simplest bounds and the creation of C=O peaks: this conclusion is in
accordance with what was already observed in the analyses of the concentration.
During the thermophilic phase the prevalent action is that of the temperature, which leads to a
disintegration of the bioplastics; however, in this phase the degradation observed is almost
negligible, as seen in the change of the spectrum and of the weight, so the thermophilic bacteria
are supposed not to be suitable in biodegrading this material.
On the contrary, the maturation phase is suitable for the growth of bacteria and fungi able to
biodegrade bioplastics, even if the disintegration during this period has a clear and strong slowdown
with respect to the thermophilic phase, confirming the hypothesis that is the action of the
temperature that has a great influence in this process.
100
Figure 4.32-Comparison between spectra of BioP during the composting process
To conclude with this third type of analysis, it was also done an IR on a piece of bioplastic submitted
for 2 days in the oven to a temperature of 60 °C, simulating the thermophilic phase of the
composting process; the purpose was to define the effect of temperature on the changes in the
peaks, but it was observed that, with the exception for a small increase in the concentration of all
the peaks, the shape of the spectrum is unchanged.
Figure 4.33-Spectrum of a BioP sample submitted to a temperature of 60 °C in the oven
101
4.3.4 Visual analyses of bioplastics changing features
To carry out a visual inspection of the surface of bioplastic pieces, some photographs of the
samples were taken during the timing of the analyses, and in figure below they are reported: it was
immortalized one sample for each withheld fraction, at the four days of the analyses.
Figure 4.34-Photographs of bioplastic samples taken during the composting process (F. Ruggero, 2017)
Having a complete view of the aspects of bioplastics removed from the composted matrix, some
considerations involving the changes observed can be done.
The samples taken from the first two samplings are cleaner than the older ones, and it is noticeable
a change of the colour of the smallest fractions from white to yellow-orange.
The pieces prenset a curling especially of the exyernal borders, together with an evident erosions of
the sides, sign that bacteria have attaked the material in these parts.
102
Few holes are present in the pieces, and they are probable related to the probes used to take
temperature and humidity, or because they were pierced by twigs and wood chips during the
mixings.
Moreover, the aspect of the bioplastics, in particularly the smallest ones, become ever more similar
to compost for colour, consistency and sizes.
In figure 4.35 it was focused the aspect of the microplastics prelevated from the samples of the 55th
day, to show how much difficult it was their identification due to the color and the dirt around them,
even if it is surely not feasible to say that they are no more plastics.
Figure 4.35-MicroBioP aspect after 55 days (F. Ruggero, 2017)
Another observation concernign the aspects and the characteristics of bioplastic after having
stayed in the composting process is linked with their stickiness. In fact, pieces of biobag tend to
remain attached to all the other components of the composted matrix, from wood chips to
degrading food waste.
This characteristic is developed exspecially during the thermophilic phase of composting, due to
theramal abiotic degradation, which is one of the possible degradation forms that take place for
bioplastics.
103
Thermal degradation of thermoplastic polymers is not always possible during the composting
process, beacuase it depends on the melting temperature of the polymer; for bioplastics made on
Mater-Bi tm is equal to 64°C (Lucas et al., 2008), allowing the partial melting of the tested material
during the first week of the process when temperatures rose between 55 and 60°C.
Bioplastics stickiness can cause troubles not only during the degradation process but also after the
release of compost in the environment. First of all, if during composting bioplastic pieces remain
attached each others or to other components of the matrix, this decreases the specific surface
avialiable for bacteria both in the piece of bioplastic and in th piece of food or wood. Secondly the
release of some glue or other pastes after melting could discourage biodegradation or make matrix
less appetizing.
Morevore, when released in the environment in form of compost and used as fertilezer for food
crops or vegetables cultivation, small bioplastic pieces with some residues of stickiness after the
composting process may remain attach to the food growing in the fertilized field, or to the soil.
As a consequence it may be ingested with food, not only by animals such as insects or birds, but also
by people who eat those products.
Figure 4.36-Bioplastics stickiness (F. Ruggero, 2017)
To conclude with the analysis of the stickiness and confirm that it is an element of disturbance in
the process of biodegradation, it was done an IR on a piece of bioplastic which was folded; it was
found that the spectrum of the external part, which stayed in contact with the compostable matrix
and was submitted to the action of bacteria, showed a higher degradation than the internal part. In
fact, this spectrum is almost equal to the spectrum of the initial BioP, demonstrating that when
these bioplastic pieces remain attached one to the other or to other components of the BioPOF
104
their surface is not attachable by microorganism, thus biodegradation is not able to start or it is
stopped (Figure 4.37).
Figure 4.37-Comparison between the internal and the external side of a sticky bioplastic piece
105
5. CONCLUSIONS
The results of the research should be evaluated on two sides: the composting process carried
out on a small scale and the analyses obtained on the tested material.
As for the composting process, the most of the conclusions are positive: it passed through the typical
thermophilic phase of this treatment, even if it lasted a little bit less than in the real composting
plants, and during the maturation phase it was observed the growing of actinomycetes and fungi,
which are the main organisms acting on bioplastics degradation.
Furthermore, the analyses carried out on the samples, taken during the phases of the process and
at the end of the period of the research, showed a positive match with the requirements for a good
quality compost. The results for the C/N, the moisture content, the pH, the final temperature and
the respirometric index corresponded to the values generally achieved at the end of the full scale
composting process, confirming that the small scale tests for this type of process are completely
feasible.
The two aspects that revealed a possible improvement for a future development of the research are
on the one hand the initial mixture of waste, and on the other hand the initial conditions in which
the heap should be put.
As for the mixture, the amount of wood chips included in the mixture was too high, fact that was
demonstrating by the final results obtained in the analyses of TOC and volatile solids: in fact the
lignin of the wood chips is the last element to be degraded by fungi, so that in two months its
degradation is still not completed.
It’s also true that an amount of wood is required within the mixture destined to a composting
process because the matrix of waste needs a good level of structure, so for a possible further
implementation the suggestion earnt from this experience is to put within the waste wood twigs
and small branches of a size big enough to be removed with a sieve of 20-10 mm, as happens in the
real plants.
The second point involves the initial conditions to be preserved: in fact, as the small heap make
difficulties in keeping heat and cold, and moisture content, due to the few bulk, it should be helped
through maintaining it in an environment without excessive thermal swings.
Focusing now the attention on the results obtained about the disintegration and the
degradation of bioplastics, four conclusions can be taken at the end of the two months of the test.
106
Firstly, it was observed that the higher disintegration activity was done during the thermophilic
phase, with a percentage of size decrease of 50-70% with respect to the initial dimensions. However,
the IR analyses carried out on bioplastic pieces after ten days of composting showed a not significant
change in the spectrum, linked with a not substantial biodegradation activity by the thermophilic
bacteria.
On the contrary, during the maturation phase it occurred a slowdown in the disintegration trend,
but the IR analyses, especially on the 40th and 55th days, resulted in a change of the spectrum
recallable to the degradation activity carried out by fungi and actinomycetes during the cooling and
the maturation phase.
To conclude with this first consideration, it’s fair to say that the effect of the temperature leads to
a disintegration of the material, thanks to the fact that the reached temperature is almost equal to
the melting temperature of the bioplastics. Meanwhile, it can be said that the major action of
biodegradation occurs during the maturation phase, by mesophilic and psychrophilic bacteria, and
fungi.
In addition to this, the same analyses carried out on the disintegration, revealed that the time
required theoretically to achieve a size less than 2 mm is equal to four, up to four and half, months,
thus more than the three months of the European standards used as reference, and a little bit more
than the time generally reserved for the composting process in the real plants.
The third conclusive information achieved with this research involves the fact that having observed
the number of bioplastic pieces within the samples taken during the process, it didn’t decrease a lot
among the samples of the different timings, even if the weight decrease and the spectra confirmed
the effective degradation of these bioplastics.
So the hypothesis is that the action of microorganisms is mainly on the thickness of these materials,
including that if a thicker material was used and disposed in composting plants, maybe its
degradation and disintegration time would not be the same of the biobags, and it could have a
slowdown which would lead to an increase in the time required for its disposing.
The research developed with this thesis work gave the possibility to explore a new field, and to
observe that other implementations of this project could be done, in order to define a more general
vision of the biodegradation and disintegration of bioplastic products.
In particularly the suggestions for some further implementations could involve an ecotoxicology
study carried out to evaluate if it exists a level of bioplastics concentration in compost that could be
polluting for plants growth and worms’ life.
107
The second interesting implementation could be a microbiologic study of those microorganisms
active during the composting process for bioplastics degradation: thus, it would carry out a confirm
of the action of fungi and actinomycetes as the main microorganism able to biodegrade bioplastics,
developed during the cooling and the maturation phase of the process.
Another interesting point that could be evolved in a further study is that involving the
disintegration and degradation model: in fact, firstly the analyses carried out on biobag can be
expanded also to the new products proposed on the market, such as cutlery and coffee capsules,
and secondly also the variable of quantity could be taken into account to obtain a model with a
more general evolution of the process.
At the conclusion of my thesis work I would like to get a glance on the fieldwork of the new
materials, processes, technologies and products immitted on the markets in these last decades.
Often the focus of the producers is on the birth of the products from the cradle of the industries: so
the attention is posed on the use of renewable resources, both for materials and energies, in the
use of less amount of water, in the reduction of the emissions during the process, in accordance
with the LCA at the basis of the production.
It’s also true, though, that the same responsibility is not felt at all in the disposing of the products
after their life, thing that would be an important part of a LCA study when a new creation is proposed
on the market.
The sensitization to the environment should be extended from the cradle to the grove in the life of
a product, and the research around the development of a new product should be done before the
immision on the market not only to obtain a more sustainable substance at the beginning of its
production chain, but also to leave at the end of the chain a waste with a clear, suitable and
economically and environmentally sustainable way of disposal.
In this view, from the cradle to the grove, the generations of this century will be able to manage in
a sustainable way the beginning of the production chain, as far as the end of the same chain, and
whenever they will leave to the future generations the disposal of their long-life products, they will
have already found a safe and sustainable treatment for the waste management of these products,
in accordance with the view of the sustainable development.
108
109
REFERENCES
Bibliography
ARPAV. Il recupero della frazione organica in Veneto, anno 2015. Dicembre 2016.
Balaguer et al., Compostability assessment of nano-reinforced poly(lactic acid) films. Waste
Management 48 (2016), 143-155. Elsevier, 2016
Bastioli 1997, Properties and application of Mater Bi starch-based materials. Elsevier 1997
Borchani et al., Biocomposites of Alfa fibres dispersed in the Mater Bi type bioplastic:
Morphology, mechanical and thermal properties. Composites: Part A 78 (2015). 371-379. Elsevier,
2015.
Byun and Kim, Bioplastics for food packaging: chemistry and physics. Chapter 14. Elsevier, 2014
Corradini, C., Carvalho, A.J.F., Antonio, A., Jose, A.M. and Luiz, H.C. 2007. Preparation and
characterization of thermoplastic starch/zein blends. Materials Research 10 (3). 227-23
Colwill J. A. et al, 2012. Bio-plastics in the context of competing demands on agricultural land in
2050. International Journal of Sustainable Engineering, volume 5, 2012 - Issue 1: Polymers in
Sustainable Engineering.
Crank M. et al., Techno-economic feasibility of large-scale production of bio-based polymers in
Europe. European Commission, European Science and Technology Observatory, Insitute for
Prospective Technological Studies. EUR 22103 EN, 2005
Cossu R., Aerobic stabilization of biodegradable waste. Course of waste management, 2016.
Direttiva 94/62/CE sugli imballaggi e i rifiuti di imballaggio
EN 13432:2000 Packaging – Requirements for packaging recoverable through composting and
biodegradation-Test scheme and evaluation criteria for the final acceptance of packaging.
EN 14045:2003 Packaging – Evaluation of the disintegration of packaging materials in practical
oriented tests under defined composting conditions.
EN 14995:2006 Plastics – Evaluation of compostability – Test scheme and specifications.
EN 14855:1999 Determination of the ultimate aerobic biodegradability and disintegration of
plastic materials under controlled composting conditions — Method by analysis of evolved carbon
dioxide.
110
EN 14806:2005 Packaging – Preliminary evaluation of the disintegration of packaging materials
under simulated composting conditions in a laboratory scale test.
Horton et al., Microplastics in freshwater and terrestrial environments: Evaluating the current
understanding to identify the knowledge gaps and future research priorities. Science of the Total
Environment (2017). Elsevier, 2017
Iles and Martin, Expanding bioplastics production: sustainable business innovation in the
chemical industry. Journal of Cleaner Production 45 (2013), 38-49. Elsevier, 2013.
ISPRA, 2015. Rapporto rifiuti urbani.
Javierre et al., Study of the biodisintegration on a painted bioplastic material waste. MATERIALE
PLASTICE 52 (2015).
Karana, Characterization of natural and high-quality materials to improve perception of bio-
plastics. Journal of Cleaner Production 37 (2012), 316-325. Elsevier, 2013.
Liao and Wu. Preparation and characterization of ternary blends composed of polylactide,
poly(ɛ-caprolactone) and starch. Materials Science and Engineering: A, volume 515, Issues 1–2, 25
July 2009, Pages 207-214. Elsevier , 2009.
Lopez et al., Processing and properties of biodegradable composites based on Mater Bi and
hamp core fibres. Resources, Conservation and Recycling 59 (2012), 38-42. Elsevier 2011
MaTech, Ottobre 2013. PST Galileo. Il mercato delle bioplastiche, Esempi di nuovi prodotti e
applicazioni.
Mehdi Emadian et al., Biodegradation of bioplastics in natural environments. Waste
Management 59 (2017), 526-536. Elsevier, 2017
Mohee et al., Biodegradability of biodegradable/degradable plastic materials under aerobic and
anaerobic conditions. Waste Management 28 (2008) 1624–1629. Elsevier, 2008.
Nizzetto et al., Are agricultural soils dumps for microplastics of urban origin? Environmental
Science and Technology, 2016.
Pagga, Biodegradability and compostability of polymeric materials in the context of the
European packaging. Polymer Degradation and Stability 59 (1998) 371-376. Elsevier, 1998.
Peelman et al., Application of bioplastics for food packaging. Trends in Food Science &
Technology 32 (2013) 128-141. Elsevier, 2013
Qiu et al., Extraction, enumeration and identification methods for monitoring microplastics in
the environment. Estuarine, Coastal and Shelf Science 176 (2016) 102-109. Elsevier, 2016
111
Steinmetz et al., Plastic mulching in agriculture. Trading short-term agronomic benefits for long-
term soil degradation? Science of the Total Environment 550 (2016) 690–705. Elsevier, 2016
Sparke, P., 1990. The Plastics Age: From Modernity to Post-Modernity. B.A.S Printers, England.
Tabasi and Ajji, Selective degradation of biodegradable blends in simulated laboratory
composting. Polymer Degradation and Stability 120 (2015) 435-442. Elsevier, 2016
Thompson et al., Plastics, the environment and human health: current consensus and future
trend. Philosophical transaction of the royal society (2009) 1, 1-14
Underwood et al., Some problems and practicalities in design and interpretation of samples of
microplastic waste. Analytical methods (2017) 9, 1332.
Vilpoux and Averous, Technology, use and potentialities of Latin American starchy tubers.
Chapter 18, starch-based plastic. 2008
Wright et al., The physical impacts of microplastics on marine organisms: A review.
Environmental pollution (2013), 1-10. Elsevier, 2013
Yates and Barlow, Life cycle assessments of biodegradable, commercial biopolymers – A critical
review. Resources, Conservation and Recycling 78 (2013), 54-66. Elsevier 2012
Zhang, P., Whistler, R. L., BeMiller, J. N., & Hamaker, B. R. (2005). Banana starch: production,
physicochemical properties, and digestibility-a review. Carbohydrate Polymers, 59, 443–458
112
Sitography
www.khanacademy.org
www.european-bioplastics.org
www.materbi.com
brand-finder-italy.info
www.ecozema.com
www.alcas.it
corriereinnovazione.corriere.it
www.lameplastgroup.com
www.vib.be
www.novamont.com
www.solostocks.it
www.hempplastic.com
www.researchgate.net
www.docenti.unicam.it
www.venetoagricoltura.org
ANNEXES
115
I. ANNEX: Composting process parameters
In the Annex I there are reported graphs and tables with all the data collected during the
analyses of the composted matrix: the order of the analyses reported is the same of chapter 4.1.
Figure I.1-Outside temperature during the small scale test
Figure I.2-Comparison between outside temperature and heaps temperature - Line 2
0
5
10
15
20
25
30
35
40
Tem
per
atu
re (
°C)
Outside temperatures
0
10
20
30
40
50
60
70
1 3 5 7 9 11 13 15 17 19 21 23 25 27 29 31 33 35 37 39 41 43 45 47 49 51 53
Tem
per
atu
re (
°C)
Time (d)
Temperatures comparison - Line 2
Outside T Mean T
116
Figure I.3-Temperature during composting process - Line 1
Figure I.4-Temperature during composting process - Line 2
0
10
20
30
40
50
60
1 3 5 7 9 11 13 15 17 19 21 23 25 27 29 31 33 35 37 39 41 43 45 47 49 51 53 55
Tem
per
atu
re (
°C)
Time (d)
Temperature - Line 1
OF BioPOF small BioPOF big
0
10
20
30
40
50
60
70
1 3 5 7 9 11 13 15 17 19 21 23 25 27 29 31 33 35 37 39 41 43 45 47 49 51 53 55
Tem
per
atu
re (
°C)
Time (d)
Temperature - Line 2
OF BioPOF small BioPOF big
117
Table I.1-Moisture content
MOISTURE %
Line 1
1st 10th 25th 40th 55th
OF 56,5 44,5 37,9 43,9 41,9 BioPOF s 56,7 43,3 36,9 44,7 43,1 BioPOF b 56,8 44,1 37,6 44,2 41,7
Mean 56,7 44,0 37,5 44,3 42,2
Line 2
1st 10th 25th 40th 55th
OF 55,8 44,1 39,7 46 41,4 BioPOF s 55,9 43,5 37,9 47 41,5 BioPOF b 56,6 44,1 40,1 45,7 41,6
Mean 56,1 43,9 39,2 46,2 41,5
Table I.2-Total solids
TOTAL SOLIDS %
Line 1
1st 10th 25th 40th 55th
OF 43,5 55,5 62,1 56,1 58,1 BioPOF s 43,3 56,7 63,1 55,3 56,9 BioPOF b 43,2 55,9 62,4 55,8 58,3
Mean 43,3 56,0 62,5 55,7 57,8
Line 2
1st 10th 25th 40th 55th
OF 44,2 55,9 60,3 54 58,6 58,5 BioPOF s 44,1 56,5 62,1 53
BioPOF b 43,4 55,9 59,9 54,3 58,4
Mean 43,9 56,1 60,8 53,8 58,5
118
Figure I.5- Moisture content - Line 2
Table I.3-Volatile solids
VOLATILE SOLIDS %
Line 1
1st 10th 25th 40th 55th
OF 90,7 89,8 89 87 85,5 BioPOF s 90,1 89,9 89,3 87,2 85,7 BioPOF b 90,2 89,9 88,9 87,1 85
Mean 90,3 89,9 89,1 87,1 85,4
Line 2
1st 10th 25th 40th 55th
OF 90,7 88,8 88,1 87,9 80,8 BioPOF s 90,2 88,9 88,7 88,4 81,9 BioPOF b 90,5 89,1 88,3 87,8 82,1
Mean 90,5 88,9 88,4 88,0 81,6
0
10
20
30
40
50
60
1st 10th 25th 40th 55th
Mo
istu
re (
%)
Moisture - Line 1
OF BioPOF s BioPOF b
119
Figure I.6-Volatile solids - Line 1
Figure I.7-Volatile solids - Line 2
82
83
84
85
86
87
88
89
90
91
92
1st 10th 25th 40th 55th
Vo
lati
le s
olid
s (%
)
Volatile solids - Line 1
OF BioPOF s BioPOF b
74
76
78
80
82
84
86
88
90
92
1st 10th 25th 40th 55th
Vo
lati
le s
olid
s (%
)
Volatile solids - Line 2
OF BioPOF s BioPOF b
120
Table I.4-TKN normalized with total solids
Figure I.8-TKN behaviour during the composting process - Line 1
0
50
100
150
200
250
1st 10th 25th 40th 55th
TKN
(g)
TKN (g) - Line 1
OF BioPOF small BioPOF big
TKN g/kg TS
Line 1
1st 10th 25th 40th 55th
OF 17,8 22 32,9 25,4 31,5 BioPOF s 20,2 24,7 25,1 20,3 32,4 BioPOF b 21,8 24,9 26,1 24,9 33,7
Mean 19,9 23,9 28,0 23,5 32,5
Line 2
1st 10th 25th 40th 55th
OF 20,1 25,3 25,8 27,5 31,9 BioPOF s 22,4 26,7 32,4 32,8 34,1 BioPOF b 15,7 25,1 31,3 31,4 34,6
Mean 19,4 25,7 29,8 30,6 33,5
121
Table I.5-TOC normalized with TS
TOC g/kg TS
Line 1
1st 10th 25th 40th 55th
OF 511 462 431 433 385 BioPOF s 513 459 425 448 413 BioPOF b 518 463 415 447 418
Mean 514,0 461,3 423,7 442,7 405,3
Line 2
1st 10th 25th 40th 55th
OF 512 469 472 456 419 BioPOF s 516 464 463 452 390 BioPOF b 501 455 447 439 409
Mean 509,7 462,7 460,7 449,0 406,0
Figure I.9-TOC behaviour during the composting process - Line 1
0
1000
2000
3000
4000
5000
6000
1st 10th 25th 40th 55th
TOC
(g)
TOC (g) - Line 1
OF BioPOF small BioPOF big
122
Table I.6-RI 4 normalized on total solids
RI4 mgO2/g TS
Line 1
1st 10th 25th 40th 55th
OF 110,3 60,8 44,8 41,3 2,7 BioPOF s 112,5 62,7 49,3 52,2 7,0 BioPOF b 109,8 58,5 51,8 47,2 9,2
Mean 110,9 60,7 48,6 46,9 6,3
Line 2
1st 10th 25th 40th 55th
OF 108,1 63,8 46,6 21,5 18,1 BioPOF s 107,1 65,3 51,5 36,7 13,9 BioPOF b 111,2 64,2 52,2 26,4 17,6
Mean 108,8 64,4 50,1 28,2 16,5
Figure I.10-RI 4 normalized on total solids
0,0
20,0
40,0
60,0
80,0
100,0
120,0
1st 10th 25th 40th 55th
RI 4
mg
O2
/g T
S
RI 4 (mg O2/ g TS)
Line 1 Line 2
123
Table I.7-RI 7 normalized on volatile solids
IR7 mgO2/g VS
Line 1
1st 10th 25th 40th 55th
OF 81,5 68,7 57,7 42,9 4,02 BioPOF s 81,9 69,1 65,5 45,9 5,98 BioPOF b 84,8 75,5 69,5 50,6 9,4
Mean 82,7 71,1 64,2 46,5 6,5
Line 2
1st 10th 25th 40th 55th
OF 82,5 58,5 51,2 23,9 22,74 BioPOF s 80,9 53,1 56,4 42,1 17,53 BioPOF b 83,6 58,2 56,1 27,2 21,75
Mean 82,3 56,6 54,6 31,1 20,7
Figure I.11--RI 7 normalized on volatile solids
0,0
10,0
20,0
30,0
40,0
50,0
60,0
70,0
80,0
90,0
1st 10th 25th 40th 55th
RI 7
mg
O2
/g V
S
RI 7 (mg O2/ g VS)
Line 1 Line 2
124
Table I.8-RI 7 normalized on total solids
RI7 mgO2/g TS
Line 1
1st 10th 25th 40th 55th
OF 161,3 83,3 68,3 67,2 5,94 BioPOF s 168,5 79,5 78,7 71,8 8,84 BioPOF b 164,5 95,4 82,5 79,4 13,51
Mean 164,8 86,1 76,5 72,8 9,4
Line 2
1st 10th 25th 40th 55th
OF 167,1 77,4 74,2 38,5 31,71 BioPOF s 164,1 84,2 80,1 69,78 24,45 BioPOF b 166,2 78,2 82,1 44,36 30,34
Mean 165,8 79,9 78,8 50,9 28,8
Figure I.12-RI 7 normalized on total solids
0,0
20,0
40,0
60,0
80,0
100,0
120,0
140,0
160,0
180,0
1st 10th 25th 40th 55th
RI 7
mg
O2
/g T
S
RI 7 (mg O2/ g TS)
Line 1 Line 2
125
II. ANNEX: Granulometric curves
Graphs and tables of granulometric analyses are reported as a reference for paragraph 4.2.
The granulometric curve is done on the passing fractions and follows the disintegration of the
composted matrix during the process.
Each graph is accompanied by the reference table with all the data in weight and percentages.
Figure II.1-Granulometric curve OF
Figure II.2-Granulometric curve OF
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
of
pas
sin
g %
Granulometry (mm)
OF granulometric curve - Line 1
25th day
40th day
55th day
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
s %
Granulometry (mm)
OF granulometric curve - Line 2
10th day
25th day
40th day
55th day
126
Figure II.3-Granulometric curve BioPOF small
Figure II.4-Granulometric curve BioPOF small
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
of
pas
sin
g %
Granulometry (mm)
BioPOF small granulometric curve - Line 1
10th day
25th day
40th day
55th day
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
s %
Granulometry (mm)
BioPOF small granulometric curve - Line 2
10th day
25th day
40th day
55th day
127
Figure II.5-Granulometric curve BioPOF big
Figure II.6-Granulometric curve BioPOF big
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
of
pas
sin
g %
Granulometry (mm)
BioPOF big granulometric curve - Line 1
10th day
25th day
40th day
55th day
0
10
20
30
40
50
60
70
80
90
100
0 2 4 6 8 10 12 14 16 18 20
Per
cen
tage
of
pas
sin
g %
Granulometry (mm)
BioPOF big granulometric curve - Line 2
10th day
25th day
40th day
55th day
128
Analyses on the 10th day
For OF the analyses were carried only on Line 2, because blanks of Line 1 are in a smaller
amount and it was decided to keep them for the further sampling.
Table II.1-Granulometry 10th day OF
OF - Line 2
Sieve Granulometry Passing Kg %Passing Withheld Kg %Withheld
¾ 20,00 1,889 95 0,107 5
3/8 10,00 1,456 73 0,418 21
5/16 8,00 1,149 58 0,304 15
3,5 5,60 0,831 42 0,306 15
8 2,38 0,159 8 0,668 33
14 1,40 0,048 2 0,112 6
Table II.2-Granulometry 10th BioPOF small
BioPOF small - Line 1 BioPOF small - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 2,77 96 0,11 4 1,86 93 0,133 7 3/8 10,00 1,964 68 0,786 27 1,325 66 0,529 27
5/16 8,00 1,659 58 0,263 9 1,051 53 0,266 13 3,5 5,60 1,372 48 0,272 9 0,723 36 0,323 16 8 2,38 0,283 10 1,082 38 0,134 7 0,582 29
14 1,40 0,104 4 0,178 6 0,032 2 0,1 5
Table II.3-Granulometry 10th day BioPOF big
BioPOF big - Line 1 BioPOF big - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 2,679 94 0,174 6 1,844 92 0,150 8
3/8 10,00 2,118 74 0,536 19 1,266 63 0,567 28
5/16 8,00 1,847 65 0,237 8 1,015 51 0,248 12
3,5 5,60 1,357 48 0,478 17 0,663 33 0,347 17
8 2,38 0,258 9 1,081 38 0,14 7 0,520 26
14 1,40 0,097 3 0,158 6 0,042 2 0,097 5
129
Analyses on the 25th day
Table II.4-Granulometry 25th day OF
OF - Line 1 OF - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld %Withheld
Passing %Passing
Withheld %Withheld
Kg Kg Kg
3/4 20 0,97 97 0,03 3 1,851 93 0,13 7
3/8 10 0,753 75 0,215 22 1,385 70 0,458 23
5/16 8 0,605 61 0,145 15 1,079 54 0,306 15
3,5 5,6 0,448 45 0,148 15 0,781 39 0,297 15
8 2,38 0,113 11 0,334 33 0,176 9 0,6 30
14 1,4 0,047 5 0,065 7 0,073 4 0,102 5
Table II.5-Granulometry 25th day BioPOF small
BioPOF small - Line 1 BioPOF small - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 1,901 95 0,094 5 1,887 95 0,103 5
3/8 10,00 1,493 75 0,404 20 1,451 73 0,433 22
5/16 8,00 1,254 63 0,236 12 1,184 59 0,256 13
3,5 5,60 0,958 48 0,292 15 0,850 43 0,334 17
8 2,38 0,243 12 0,71 36 0,185 9 0,659 33
14 1,40 0,097 5 0,145 7 0,072 4 0,109 5
Table II.6-Granulometry 25th BioPOF big
BioPOF big - Line 1 BioPOF big - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 1,878 94 0,121 6 1,847 93 0,141 7
3/8 10,00 1,381 69 0,495 25 1,364 69 0,474 24
5/16 8,00 1,13 57 0,247 12 1,057 53 0,305 15
3,5 5,60 0,802 40 0,328 16 0,802 40 0,248 12
8 2,38 0,175 9 0,624 31 0,182 9 0,618 31
14 1,40 0,067 3 0,107 5 0,079 4 0,103 5
130
Analyses on the 40th day
Table II.7-Granulometry 40th day OF
OF - Line 1 OF - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 0,483 97 0,014 3 0,983 99 0,013 1
3/8 10,00 0,383 77 0,097 20 0,801 80 0,178 18
5/16 8,00 0,324 65 0,058 12 0,694 70 0,105 11
3,5 5,60 0,228 46 0,093 19 0,542 54 0,152 15
8 2,38 0,075 15 0,153 31 0,150 15 0,391 39
14 1,40 0,022 4 0,053 11 0,068 7 0,079 8
Table II.8-Granulometry 40th day BioPOF small
BioPOF small - Line 1 BioPOF small - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 0,481 95 0,023 5 0,977 99 0,012 1
3/8 10,00 0,416 83 0,065 13 0,785 79 0,184 19
5/16 8,00 0,357 71 0,056 11 0,680 69 0,097 10
3,5 5,60 0,294 58 0,063 13 0,547 55 0,124 13
8 2,38 0,07 14 0,221 44 0,137 14 0,409 41
14 1,40 0,024 5 0,046 9 0,053 5 0,084 8
Table II.9-Granulometry 40th day BioPOF big
BioPOF big - Line 1 BioPOF big - Line 2
Sieve Granulometry Passing
Kg %Passing
Withheld Kg
%Withheld Passing
Kg %Passing
Withheld Kg
%Withheld
3/4 20,00 0,488 98 0,012 2 0,979 98 0,019 2
3/8 10,00 0,405 81 0,080 16 0,800 80 0,174 17
5/16 8,00 0,349 70 0,056 11 0,691 69 0,104 10
3,5 5,60 0,248 50 0,087 17 0,497 50 0,193 19
8 2,38 0,058 12 0,188 38 0,132 13 0,358 36
14 1,40 0,017 3 0,038 8 0,046 5 0,073 7
131
Analyses on the 55th day
Table II.10-Granulometry 55th day OF
OF - Line 1 OF - Line 2
Sieve Granulometry Passing Kg %Passing Withheld
Kg %Withheld
Passing Kg
%Passing Withheld
Kg %Withheld
3/4 20,00 0,975 98 0,025 3 0,951 96 0,044 4
3/8 10,00 0,789 79 0,171 17 0,755 76 0,182 18
5/16 8,00 0,674 67 0,103 10 0,683 69 0,062 6
3,5 5,60 0,545 55 0,124 12 0,561 56 0,113 11
8 2,38 0,123 12 0,414 41 0,115 12 0,446 45
14 1,40 0,037 4 0,085 9 0,043 4 0,069 7
Table II.11-Granulometry 55th day BioPOF small
BioPOF small - Line 1 BioPOF small - Line 2
Sieve Granulometry Passing Kg %Passing Withheld
Kg %Withheld
Passing Kg
%Passing Withheld
Kg %Withheld
3/4 20,00 0,985 99 0,013 1 0,962 97 0,033 3
3/8 10,00 0,83 83 0,153 15 0,804 81 0,151 15
5/16 8,00 0,74 74 0,086 9 0,714 72 0,079 9
3,5 5,60 0,614 62 0,111 11 0,613 62 0,101 10
8 2,38 0,165 17 0,434 43 0,182 18 0,428 43
14 1,40 0,046 5 0,108 11 0,056 6 0,118 12
Table II.12-Granulometry 55th day BioPOF big
BioPOF big - Line 1 BioPOF big - Line 2
Sieve Granulometry Passing Kg %Passing Withheld
Kg %Withheld
Passing Kg
%Passing Withheld
Kg %Withheld
3/4 20,00 0,985 99 0,013 1 0,969 98 0,018 2
3/8 10,00 0,818 82 0,160 16 0,821 83 0,141 14
5/16 8,00 0,688 69 0,126 13 0,703 71 0,112 11
3,5 5,60 0,535 54 0,151 15 0,545 55 0,153 16
8 2,38 0,14 14 0,394 39 0,131 13 0,410 42
14 1,40 0,039 4 0,101 10 0,045 5 0,085 9
132
III. ANNEX: Bioplastics concentration
Annex III contains the tables and the graphs referring to the analyses on concentration of
bioplastics in the composted matrix. It includes the results to which it is made reference in
paragraph 4.3.2.
Table III.1-Weight range of BioP small - Line 1
Line 1 - BioP small
Weight (%) Weight (g) Conc. BioP BioP (g/1 kg) Variability min (g) Variability max (g)
1st 100 1000 0,007 7 7 7
10th 59 590 0,017 10,03 8,5 6,1
25th 40 400 0,015 6 5,1 3,7
40th 30 300 0,016 4,8 3,6 2,4
55th 29 290 0,011 3,19 2,4 1,6
Figure III.1-Graph of weight range of BioP small - Line 1
0 1 2 3 4 5 6 7 8 9
1st
10th
25th
40th
55th
Weight (g)
BioP small weight range - Line 1
variability min variability max
133
Table III.2-Weight range of BioP small - Line 2
Line 2 - BioP small
Weight (%) Weight (g) Conc. BioP BioP (g/1 kg) Variability min (g) Variability max (g)
1st 100 1000 0,007 7 7 7
10th 66 660 0,013 8,58 7,3 5,2
25th 37 370 0,015 5,55 4,7 3,4
40th 36 360 0,015 5,4 4,1 2,8
55th 31 310 0,011 3,41 2,6 1,7
Figure III.2-Graph of weight range of small BioP - Line 2
Table III.3-Weight range of BioP big - Line 1
Line 1 - BioP big
Weight % Weight (g) Conc. BioP BioP (g/1 kg) Variability min (g) Variability max (g)
1st 100 1000 0,007 7 7 7
10th 59 590 0,019 11,21 9,5 6,8
25th 43 430 0,019 8,17 6,9 5,0
40th 35 350 0,014 4,9 3,7 2,5
55th 28 280 0,007 1,96 1,5 1,0
0 1 2 3 4 5 6 7 8
1st
10th
25th
40th
55th
Weight (g)
BioP small weight range - Line 2
variability min variability max
134
Figure III.3-Graph of weight range of big BioP - Line 1
Table III.4-Weigh range of BioP big - Line 2
Line 2 - BioP big
Weight (%) Weight (g) Conc. BioP BioP (g/1 kg) Variability min (g) Variability max (g)
1st 100 1000 0,007 7 7 7
10th 65 650 0,011 7,15 6,1 4,4
25th 37 370 0,019 7,03 6,0 4,3
40th 33 330 0,012 3,96 3,0 2,0
55th 30 300 0,007 2,1 1,6 1,1
Figure III.4-Graph of weight range of big BioP - Line 2
0 1 2 3 4 5 6 7 8 9
1st
10th
25th
40th
55th
Weight (g)
BioP big weight range - Line 1
variability min variability max
0 1 2 3 4 5 6 7 8 9
1st
10th
25th
40th
55th
Weight (g)
BioP big weight range - Line 2
variability min variability max
135
IV. ANNEX: IR analyses
In the Annex IV the spectra of some samples of bioplastics taken during the composting process
are reported, introduced with the panoramic photograph of the samples submitted to the analysis.
It is referred to paragraph 4.3.3.
Figure IV.1-Aspect of bioplastic pieces submitted to IR analysis
136
Figure IV.2-Spectra at the 10th day of the biggest granulometric fractions
Figure IV.3-Spectra at the 10th day of the biggest granulometric fractions
137
Figure IV.4-Spectra at the 10th day of the smallest granulometric fractions
Figure IV.5-Spectra at the 25th day of the biggest granulometric fractions
138
Figure IV.6-Spectra at the 25th day of the biggest granulometric fractions
Figure IV.7-Spectra at the 25th day of the smallest granulometric fractions
139
Figure IV.8-Spectra at the 25th day of the smallest granulometric fractions
Figure IV.9-Spectra at the 40th day of the biggest granulometric fractions
140
Figure IV.10-Spectra at the 40th day of the biggest granulometric fractions
Figure IV.11-Spectra at the 40th day of the smallest granulometric fractions
141
Figure IV.12-Spectra at the 55th day of the biggest granulometric fractions
Figure IV.13-Spectra at the 55th day of the smallest granulometric fractions
142
Figure IV.14-Spectra at the 55th day of the smallest granulometric fractions
143