TECHNICAL DATA(ETFE FILM structures)
Jul 2017
ASAHI GLASS Co., LTD.
ContentsⅠ. Fluon® ETFE FILM introduction 3
1. What is Fluon® ETFE FILM ?2. Advantage of Fluon® ETFE FILM
Ⅱ. Grades & Properties 4
Ⅲ. Mechanical Properties 61. Stress - Strain curve2. Creep data3. Ball - drop test (against Hail)
Ⅳ. Optical Properties 81. Light Transmittance chart by wave length
(Comparison with other materials)2. Light Transmittance chart by wave length(by each grade)3. Light Transmittance chart by wave length(by printed part)4. Optical properties of each grade5. Optical properties of glass (for reference only)
Ⅴ. Thermal Properties 101. Thermal Properties (U-Value)2. Thermal properties of glass (for reference only)3. Thermal Properties (G-Value/SC)
Ⅵ. Acoustic Properties (Acoustic Loss in Transmission) 12
Ⅶ. Weatherability 131. Change in tensile strength and elongation with accelerated weathering test2. Change in light transmittance with accelerated weathering test3. Printed film : Retention ratio of reflectance of silver ink after S.W.M test4. Color film : Optical properties of colored film after S.W.M. test
Ⅷ. Combustion Properties 151. Fire proof test2. Combustion test data
Ⅸ. Chemical Properties 15
Ⅹ. Grades & Size 16
XI . Print Patterns 17
Jul 2017 2
Ⅰ. Fluon® ETFE FILM introduction
1. What is Fluon® ETFE FILM ?
It is high-performance film,
developed and produced by AGC
with its own [Fluon ETFE] resin.
It shows the excellent features,
and is used in various applications.
AGC’s advantage is to develop and
produce both resins and films.
And AGC has 30 years history of ETFE film.
Ethylene-TetraFluoroEthylene copolymer
C
H
H F
C C C
H
H
F
F
F
nm
2. Advantage of Fluon® ETFE FILM
Weatherability
Chemical resistance
Heat resistance
Mechanical property
Non-flammability
(DIN B-1)
Anti-stick property
(Antifouling)
Anti-condensation
can be added
Light transmittance
Electric property
Light can be controlled
by wave length range
3Jul 2017
Ⅱ. Grades & Properties
Item Test Method Unit
Grade
Transparent Matted(Diffused light)
100NJ 150NJ 200NJ 250NJ 300NJ 150HJ 200HJ 250HJ
MaterialThickness
DIN-53370ISO-459
μm 100±5 150±8 200±10 250±13 300±15 150±8 200±10 250±13
mil 4±0.2 6±0.3 8±0.4 10±0.5 20±0.6 6±0.3 8±0.4 10±0.5
Mass per unit area
ISO-2286-2 g/m2 175±9 262±13 350±17 437±22 525±26 262±13 350±17 437±22
Specific Gravity
ASTM D792
- 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3
Tensile Strength at Break
DIN-EN-ISO-527-3
MPa 50 min. 50 min. 50 min. 50 min. 50 min. 45 min. 45 min. 45 min.
ASTM D638
MPa 50 min. 50 min. 50 min. 50 min. 50 min. 45 min. 45 min. 45 min.
psi 7250 min. 7250 min. 7250 min. 7250 min. 7250 min. 6525 min. 6525 min. 6525 min.
Tensile Strain
at Break
DIN-EN-ISO-527-3
% 350 min. 350 min. 350 min. 350 min. 350 min. 300 min. 300 min. 300 min.
ASTM D638 % 350 min. 350 min. 350 min. 350 min. 350 min. 300 min. 300 min. 300 min.
Tensile Strength
at 10% Strain
DIN-EN-ISO-527-3
MPa 18 min. 18 min. 18 min. 18 min. 18 min. 17 min. 17 min. 17 min.
ASTM D882
MPa 18 min. 18 min. 18 min. 18 min. 18 min. 17 min. 17 min. 17 min.
psi 2610 min. 2610 mm. 2610 mm. 2610 mm. 2610 mm. 2460 mm. 2460 mm. 2460 mm.
Tear Strength
DIN-EN-1875-3
N/mm 400 min. 400 min. 400 min. 400 min. 400 min. 360 min. 360 min. 360 min.
ASTM D1004 N/mm 140 min. 140 min. 140 min. 140min. 140 min. 140 min. 140min. 140 min.
Dimensional Change
on heating
150 ℃,10 minutes
% -1±5 -1±5 -1±5 -1±5 -1±5 -1±5 -1±5 -1±5
Light Transmittance
DIN-EN-410 % 91min. 91 min. 90 min. 89 min. 88 min. 91 min. 90 min. 88 min.
ASTM D1003 % 91min. 91 min. 90 min. 89 min. 88 min. 91 min. 90 min. 88 min.
Oxygen index ASTM D2863 % 32 32 32 32 32 32 32 32
4
Jul 2017
Item Test Method Unit
Grade
UV cut Blue White Silver printed Film
200UVC 250UVC 200TB 250TB 200WT 250WT 200NJ 250NJ
MaterialThickness
DIN-53370ISO-459
μm 200±10 250±13 200±10 250±13 200±10 250±13 200±10 250±13
mil 8±0.4 10±0.5 8±0.4 10±0.5 8±0.4 10±0.5 8±0.4 10±0.5
Mass per unit area
ISO-2286-2 g/m2 350±17 437±22 350±17 437±22 350±17 437±22 350±17 437±22
Specific Gravity
ASTM D792
- 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3 1.75±3
TensileStrength at Break
DIN-EN-ISO-527-3
Mpa 50 min. 50 min. 50 min. 50 min. 50 min. 50 min. 50 min. 50 min.
ASTM D638
MPa 50 min. 50 min. 50 min. 50 min. 50 min. 50 min. 50 min. 50 min.
psi 7250 min. 7250 min. 7250 min. 7250 min. 7250 min. 7250 min. 7250 min. 7250 min.
Tensile Strain
at Break
DIN-EN-ISO-527-3
% 350 min. 350 min. 350 min. 350 min. 350 min. 350 min. 350 min. 350 min.
ASTM D638 % 350 min. 350 min. 350 min. 350 min. 350 min. 350 min. 350 min. 350 min.
Tensile Strength
at 10% Strain
DIN-EN-ISO-527-3
MPa 18 min. 18 min. 18 min. 18 min. 16 min. 16 min. 18 min. 18 min.
ASTM D882
MPa 18 min. 18 min. 18 min. 18 min. 16 min 16 min 18 min. 18 min.
psi 2610 min. 2610 min. 2610 min. 2610 min. 2320 min. 2320 min. 2610 min. 2610 min.
Tear Strength
DIN-EN-1875-3
N/mm 400 min. 400 min. 400 min. 400 min. 400 min. 400 min. 400 min. 400 min.
ASTM D1004 N/mm 140 min. 140 min 140 min. 140 min 140 min. 140 min 140 min. 140 min
Dimensional Change
on heating
150 ℃,10 minutes
% -1±5 -1±5 -1±5 -1±5 -1±5 -1±5 -1±5 -1±5
Light Transmittance
DIN-EN-410 %10>
(300nm)9>
(300nm)80min. 78min.
35 min.(550nm)
30 min.(550nm)
- -
ASTM D1003 %10>
(300nm)9>
(300nm)80min. 78min.
35 min.(550nm)
30 min.(550nm)
- -
Oxygen index ASTM D2863 % 32 32 32 32 32 32 32 32
5
Jul 2017
Ⅲ. Mechanical Properties1. Stress-Strain curve
〔Test Condition〕
・Sample Piece: 250NJ(AGC standard dumbbell)
・Testing Speed;200mm/min
2. Creep data
〔Test Condition〕・Temperature:Room Temp.(24~25℃)・Sample Piece:200NJ(Strip Shape:10mmwidth×70mm length)・Gauge length:50mm 6Jul 2017
3. Ball-drop test (against Hail)
227±2g
Steel BallHeigh
t for B
reak
Film
Test Board
300mm
300mm
[Test Method]
Holder Frame
7
Jul 2017
Ⅳ. Optical Properties(1)
1.Light Transmittance chart by wave length(Comparison with other materials)
0
10
20
30
40
50
60
70
80
90
100
300 500 700 900 1100 1300 1500 1700 1900 2100 2300 2500
Light Transmittance (%)
Wave length(nm)
200NJ
200UVC
200WT
UV
near infrared raysVisible light
2. Light Transmittance chart by wave length(by each grade)
3.Light Transmittance and reflection ( printed area)
0
10
20
30
40
50
60
70
80
90
100
300 600 900 1200 1500 1800 2100 2400
Tra
nsm
itta
nce
・R
efle
ctio
n(
%)
Wave Length ( nm )
Standard Silver ink:Transmittance
Standard Silver ink:Reflection
High reflection Silver
ink:Transmittance
High reflection Silver
ink:Reflection
8
Light is incident from the non printed surface
Jul 2017
4. Optical properties of each grade
5. Optical properties of glass(for reference only)
Thickness Visible Light (%) Solar Light (%) UV
Transmission
(%)(mm) Reflection Transmission Reflection Transmission
Flat
Glass
FL-3 3 8.2 90.2 7.8 85.8 71.1
FL-6 6 7.8 88.9 7.2 80.2 61.4
Heat Ray
Reflection
Glass
(A) 6 41.9 9.2 34.8 7.2 4.0
(B) 6 19.1 36.6 15.5 29.3 17.9
(C) 6 32.2 63.1 21.6 63.0 34.8
GradeThickness Visible Light (%) Solar Light (%) UV Light (%)
(μm) Reflection Transmittance Reflection Transmittance Reflection Transmittance
Transparent
100NJ 100 6 94 5 95 10 90
150NJ 150 6 93 6 94 12 88
200NJ 200 7 92 6 93 15 85
250NJ 250 8 91 7 93 18 82
300NJ 300 9 89 7 91 20 78
Matted (Diffused)
150HJ 150 9 93 7 93 14 87
200HJ 200 9 92 8 92 15 85
250HJ 250 10 91 8 91 17 83
White200WT 200 59 40 48 50 7 1
250WT 250 63 36 52 46 7 0.3
UV Cut200UVC 200 9 88 8 89 7 35
250UVC 250 10 86 8 88 7 27
Blue200TB 200 7 83 7 89 16 79
250TB 250 8 81 8 87 19 74
Standard Silver inkPrinted
250NJPrinted Area
250 47 32 47 32 46 30
High reflectionSilver inkPrinted
250NJPrinted Area
250 57 17 58 17 55 17
9
Jul 2017
Ⅴ. Thermal Properties
1. Thermal Properties U-Value
2. Thermal Properties of glass (for reference only)
Thickness
(mm)
U Value(Coefficient of Heat Transmission)
W/(m2・K) {kcal/(m2h℃)} Btu/h-ft2℉
Flat
Glass
FL-3 3 6.0 5.1 1.06
FL-6 6 5.9 5.0 1.04
Heat Ray
Reflection
Glass
(A) 6 4.7 4.0 0.83
(B) 6 5.3 4.6 0.93
(C) 6 5.9 5.0 1.04
Grade Thickness(μm)
U Value(Coefficient of Heat Transmission)
W/(m2・K) {kcal/(m2h℃)} Btu/h-ft2℉
Transparent
100NJ 100 6.6 5.7 1.16
150NJ 150 6.5 5.6 1.14
200NJ 200 6.4 5.5 1.13
250NJ 250 6.3 5.4 1.11
300NJ 300 6.2 5.3 1.09
Matted (Diffused)
150HJ 150 6.4 5.5 1.13
200HJ 200 6.3 5.4 1.11
250HJ 250 6.2 5.3 1.09
White200WT 200 6.4 5.5 1.13
250WT 250 6.3 5.4 1.11
UV Cut200UVC 200 6.4 5.5 1.13
250UVC 250 6.3 5.4 1.11
Blue200TB 200 6.4 5.5 1.13
250TB 250 6.3 5.4 1.11
10Jul 2017
3. Thermal Properties G-Value/SC
Type Grade
TotalThickness
(μm)
G-Value(SHGC/
Solar Heat Gain Coefficient)
SC(Shading Coefficient)
Transparent
100NJ 100 0.95 1.08
150NJ 150 0.94 1.07
200NJ 200 0.94 1.06
250NJ 250 0.93 1.06
300NJ 300 0.91 1.04
White200WT 200 0.51 0.57
250WT 250 0.47 0.53
Blue200TB 200 0.90 1.03
250TB 250 0.89 1.01
Silver Printed
P46D16200
0.68 0.77
P63D04 0.59 0.67
P46D16
250
0.68 0.77
P63D04 0.59 0.67
P80N04 0.47 0.54
P90X13 0.41 0.47
H46D16 0.62 0.70
H63D04 0.50 0.57
H80N04 0.38 0.44
H90X13 0.32 0.36
H96X34 0.22 0.24
Silver printed + Transparent (2Layers Cushion)
P46D16
250/250
0.62 0.70
P63D04 0.55 0.62
P80N04 0.42 0.48
H90X13 0.26 0.30
11
Ink code P (Standard silver) or H (High reflection silver ). 46,63,80,90,96 are printed area %.
Jul 2017
D: circle dot. N:nega dot . X: hexagon dot. 16,04,13,34 are dot size.
Ⅵ. Acoustic Properties(Acoustic Loss in Transmission)
0
2
4
6
8
10
12
14
16
18
20
22
24
26
28
30
32
34
10
0
12
5
16
0
20
0
25
0
31
5
40
0
50
0
63
0
80
0
10
00
12
50
16
00
20
00
25
00
31
50
40
00
50
00
(dB)
(Hz)
200NJ (Ave. 7.0dB)
100NJ (Ave. 4.6dB)
200NJ+(Air:200mm)+200NJ (Ave. 9.9dB)
200NJ+(Air:100mm)+100NJ+(Air:100mm)+200NJ (Ave.11.8dB)
12
Jul 2017
10.0
20.0
30.0
40.0
50.0
60.0
70.0
80.0
90.0
100.0
0 2000 4000 6000 8000 10000 12000 14000 16000 18000
Ligh
t tr
ansm
itta
nce(%
)
SWM exposure time(hr)
2. Change in light transmittancewith accelerated weathering test
[S.W.M Test Condition]・Name:Sunshine Weather-meter (S.W.M.)
・Sample piece:Fluon ETFE Film 50μm
・Light source:Sunshine carbon arcRadiation intensity . 78.5W/m2 (300 - 400nm) 255W/m2 (300 - 700nm)S.W.M. 10,000 hours = UV 3132MJ /m2 = 10.4 years (Japan & Florida)
・Black Panel temp.:63℃
・Cycle:48min.Light exposure/12min.Light exposure + Water (60minutes=1 Cycle)
Ⅶ. Weatherability
1.Change in tensile strength and elongation with accelerated weathering test
10
20
30
40
50
60
70
80
90
100
0 2000 4000 6000 8000 10000 12000 14000 16000 18000
Ret
enti
on(%)
SWM exposure time(hr)
Strength
Elongation
13Jul 2017
Printed film : Retention ratio of reflectance of silver ink after S.W.M test
Jul 201715
S.W.M. Test hours
thickness (μm)
haze(%)transmittance(%) reflectance(%) color change
△E*(reflectance)visible solar visible solar
initial 252 91.7 34.3 44.4 64.6 52.0 -
5002H 91.8 34.2 44.6 63.8 51.3 0.5
10035H 91.7 34.2 44.6 63.7 51.3 0.5
S.W.M. Test hours
thickness (μm)
haze(%)transmittance(%) reflectance(%) color change
△E*(transmittance)visible solar visible solar
initial 210 27.2 83.0 88.4 6.9 7.2 -
5034H 26.3 83.5 88.8 6.8 7.2 0.4
10127H 26.1 83.5 88.8 6.8 7.1 0.4
200TB200TB
Color film : Optical properties of colored film after S.W.M. test
250WT250WT
Single layer
Ⅷ. Combustion Properties
Item
Test con
ditio
ns
Weight of specimen (g) 0.05Temperature (℃) 750
Combustion time (min.) 10.5Supporting gas for combustion Air
Flow rate (liter/min.) 0.5 / 1.5Container Platinum (no hole)Electrode Platinum
Detected
su
bstan
ces
Hydrogen Fluoride (mg/g : specimen)570
(equivalent to 87% of the fluoro content)Soot (mg/g : specimen) 80
Aromatic fluoro compoundLow molecular fluoro hydro carbon
Less than 0.1ppm in total(Density in 5 liter of the initial combustion gas)
Carbon monoxide (mg/g : specimen) 25Carbon dioxide (mg/g : specimen) 1200
1. Fire proof test
2. Combustion test data
Test Standard ClassJIS A1322 Class1 (Flame Proof)
UL94150~245μm NJ , all color, printed VTM-0
250NJ~500μm NJ& all color, printed V-0DIN 4102 Class B-1DIN EN 13501-1 B‐s1,d0Oxygen IndexJIS K 7201-2 (ISO4589-2)
29.1%(Nonflammable in the normal air)
NFPA701 Method 2 PASSASTM E84 Class AASTM E108 Class AASTM E662 PASS
15
Ⅸ. Chemical PropertiesChemical
Temp.(℃) Days
Retention (%)
Elong. Wt. Gain
Conc. Hydrochloric acid 35% 100 10 100 0.0
Sulfuric acid 78% 121 10 100 0.1
98% 121 10 100 0.0
Nitric acid 25% 100 14 100 -
60% 120 10 100 0.7
70% 60 60 100 -
Sodium Hydroxide 10% 120 10 97 0
50% 120 10 100 -0.3
Ammonium Hydroxide 15% 66 7 98 0.1
Chlorine 90 10 94 -
Bromine 60 7 100 0.1
Carbon disulfide 100 30 98 1.0
Water 100 7 100 0
Jul 2017
16
Ⅹ. Grades & SizeGrade
Thickness(μm)
Width(mm)
Length(m/Roll)
Surface condition
Covering Ratio (%)
Dot size(mm)
Remarks
Transparent
100NJ 100
1600
500
Glossy - - -
150NJ 150 333
200NJ 200 250
250NJ 250 200
300NJ 300 170
Matted
150HJ 150
1600
333One side matted
- - -200HJ 200 250
250HJ 250 200
Color
200TB 200
1600
250
Glossy
- - Blue250TB 250 200
200WT 200 250- - White
250WT 250 200
Printed
P46D16,H46D16200
1580 - Printed
46 16Silver dot print
(large)250
P63D04,H63D04200
63 4Silver dot print
(small)250
P80N04,H80N04200
80 4 negaSilver dot print
(small nega)250
P90X13,H90H13 250 90 13Hexagon dot
(small)
P96X34,H96H34 250 96 34Hexagon dot
(large)
P80N04,H80N044mm negative dot (80%)
XI. Print PatternsP: Standard silver ink H:High Reflection silver ink
Jul 2017
P63D04,H63D044mm dot (63%)
P46D16,H46D1616mm dot (46%)
P90X13,H90X1313mm Hexagon dot (90%)
P96X34,H96X3434mm Hexagon dot (96%)
17
Light, thermal characteristics of printed film
・The above is a standard print pattern of AGC. Other printing patterns are also available as options.
・There are also over-coated products with improved weather resistance. Its characteristics are the same as those of standard silver ink.
・This is a measured value, not a guaranteed value.
Base film 250NJ
ink Standard silver
Print pattern name P46D16 P63D04 P80N04 P90X13 P96X34
print area(%) 46 63 80 90 96
Figure
Pattern character16mm
circle dot
4mm
circle dot
4mm circle
nega dot
middle
hexagon
large
hexagon
Transmittance of visible 64 54 42 35 23
Reflectance of visible (non printed side) 26 32 40 44 53
Reflectance of visible (printed side) 27 34 42 46 54
Transmittance of solar 65 55 42 36 23
Reflectance of solar (non printed side) 26 32 41 45 54
Reflectance of solar (printed side) 27 34 42 47 56
Transmittance of UV 58 49 38 33 21
Reflectance of UV (printed side) 31 36 45 49 51
Reflectance of UV (non printed side) 24 32 48 52 54
SHGC 0.68 0.59 0.47 0.41 0.30
SC 0.77 0.67 0.54 0.47 0.34
Base film 250NJ
ink High reflection silver
Print pattern name H46D16 H63D04 H80N04 H90X13 H96X34
print area(%) 46 63 80 90 96
Figure
Pattern character16mm
circle dot
4mm
circle dot
4mm circle
nega dot
middle
hexagon
large
hexagon
Transmittance of visible 57 45 32 25 14
Reflectance of visible (non printed side) 31 39 47 52 58
Reflectance of visible (printed side) 32 41 50 55 60
Transmittance of solar 58 45 33 25 13
Reflectance of solar (non printed side) 31 39 48 53 59
Reflectance of solar (printed side) 32 41 50 56 61
Transmittance of UV 52 41 30 24 12
Reflectance of UV (printed side) 35 41 48 52 57
Reflectance of UV (non printed side) 38 46 54 58 59
SHGC 0.62 0.50 0.38 0.32 0.22
SC 0.70 0.57 0.44 0.36 0.24
Jul 2017
Notice
1. The statements and data given in this publication are believed to be accurate. They are presented without any
guarantee and warranty, express or implied. Statements or suggestions regarding the use of these products
are made without representation or warranty that any such use is free of patent infringement and are not
recommendations to infringe any patent. The user should not assume that all safety measures are indicated.
2. Please refer to the MSDS (Material Safety Data Sheet) for safety and details.
3. This product is not designed for use in the implantation of the human body or medical applications that come
in contact with body fluid or body tissues, ASAHI GLASS CO., LTD. Carries out no test as to the fitness of the
product for any medical applications.
4. The contents are subject to change without prior notice.
ASAHI GLASS CO., LTD.
AGC Chemicals,
Multi-Functional Films Business Group
1-5-1 Marunouchi Chiyoda-ku, Tokyo 100-8405 JAPAN
Phone +81-3-3218-5438
Facsimile +81-3-3218-7857
URL http://www.agc.co.jp (Asahi Glass Co., Ltd. HP)
http://www.fluon.jp (Fluon HP)
AGC Chemicals Trading (Shanghai) Co., Ltd.
2701-2705, Metro Plaza,No555 Lou Shan Guan Road, Shanghai, China,
Post Code : 200051
Phone +86-21-63862211
Facsimile +86-21-63865377
AGC Chemicals Trading (Shanghai) Co., Ltd. Guangzhou Branch
2217, No.233 Tian He Bei Road,Tian He District,Guangzhou,China
Post Code:510613
Phone +86-20-38772977
Facsimile +86-20-38773442
AGC Chemicals Americas, Inc.
55 East Uwchlan Ave. Suite 201, Exton, PA 19341, USA
Phone +1-610-423-4300
Facsimile +1-610-423-4301
AGC GREEN-TECH CO.,LTD.
3-5-8 Iwamoto-cho Chiyoda-ku,Tokyo 101-0032 Japan
Phone +81-3-5833-5451
Facsimile +81-3-5833-5457
AGC Asia Pacific Pte. Ltd.
460 Alexandra Road #30-02, PSA Building Singapore 119963
Phone +65-6273-5656
Facsimile +65-6276-8783
AGC Chemicals Europe Commercial Centre
World Trade Center, Zuidplein 80, H-Tower
1077 XV Amsterdam, The Netherlands
Phone +31-20-8804179
Facsimile +31-20-8804188