fundamentals of metal forming processes

23
1 Plastic Deformation of Metals and Related Properties 1.1 INTRODUCTION Metal forming is the backbone of modern manufacturing industry besides being a major industry in itself. Throughout the world hundreds of million tons of metals go through metal forming processes every year. As much as 15–20% of GDP of industrialized nations comes from metal forming industry. Besides, it fulfils a social cause by providing job opportunities to millions of workers. Metal forming industry, in general, is a bulk producer of semi-finished and finished goods and this is one reason that it is viable to undertake large scale research and development projects because even a small saving per ton adds up to huge sums. In metal forming processes, the product shapes are produced by plastic deformation. Hence it is important to know the plastic flow properties of metals and alloys for optimizing the processes. Also the resulting component properties depend upon the intensity and the conditions of plastic deformation during forming. Many forming processes produce raw materials for other processes which in turn produce finished or semi-finished products. For example, steel plants produce sheet metal which is used by automobile industry to manufacture components of automobiles and their bodies. In fact sheet metal is used by a number of manufacturers for producing a large variety of household and industrial products. Similarly billets produced by steel plants are used by re-rolling mills for rolling into products like angles, channels, bars etc. Bars may be further used for manufacturing forgings, wires, bright bars and machined products. Similarly the manufacturers of rivets, screws, bolts and nuts buy wire from wire manufacturers and process them further. Therefore, the producers of semi-finished materials such as sheet metal, bar stock and wires, etc. have to consider that they produce such properties in their products which are required by down stream industry engaged in further processing of these products. For example, deep drawability of sheet metal increases with increase in anisotropy ratio (see Section 1.9), therefore, rolling parameters such as finishing temperature, cold reduction etc, are adjusted to produce higher anisotropy ratio in the sheet metal which is to be used for deep drawing. The properties of metals and alloys are highly influenced by their microstructure which may be modified or altered by alloying elements, by heating or heat treatment or by plastic deformation. For example, metals and alloys may be hardened by plastic deformation. It would, therefore, be helpful if we look at metals at the micro level. 1

Upload: vinayak-bhustalimath

Post on 09-Feb-2016

499 views

Category:

Documents


8 download

DESCRIPTION

metal forming

TRANSCRIPT

Page 1: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 1

1

Plastic Deformation of Metals and Related Properties

1.1 INTRODUCTION Metal forming is the backbone of modern manufacturing industry besides being a major

industry in itself. Throughout the world hundreds of million tons of metals go through metal forming processes every year. As much as 15–20% of GDP of industrialized nations comes from metal forming industry. Besides, it fulfils a social cause by providing job opportunities to millions of workers. Metal forming industry, in general, is a bulk producer of semi-finished and finished goods and this is one reason that it is viable to undertake large scale research and development projects because even a small saving per ton adds up to huge sums.

In metal forming processes, the product shapes are produced by plastic deformation. Hence it is important to know the plastic flow properties of metals and alloys for optimizing the processes. Also the resulting component properties depend upon the intensity and the conditions of plastic deformation during forming.

Many forming processes produce raw materials for other processes which in turn produce finished or semi-finished products. For example, steel plants produce sheet metal which is used by automobile industry to manufacture components of automobiles and their bodies. In fact sheet metal is used by a number of manufacturers for producing a large variety of household and industrial products. Similarly billets produced by steel plants are used by re-rolling mills for rolling into products like angles, channels, bars etc. Bars may be further used for manufacturing forgings, wires, bright bars and machined products. Similarly the manufacturers of rivets, screws, bolts and nuts buy wire from wire manufacturers and process them further. Therefore, the producers of semi-finished materials such as sheet metal, bar stock and wires, etc. have to consider that they produce such properties in their products which are required by down stream industry engaged in further processing of these products. For example, deep drawability of sheet metal increases with increase in anisotropy ratio (see Section 1.9), therefore, rolling parameters such as finishing temperature, cold reduction etc, are adjusted to produce higher anisotropy ratio in the sheet metal which is to be used for deep drawing.

The properties of metals and alloys are highly influenced by their microstructure which may be modified or altered by alloying elements, by heating or heat treatment or by plastic deformation. For example, metals and alloys may be hardened by plastic deformation. It would, therefore, be helpful if we look at metals at the micro level.

1

Page 2: Fundamentals of Metal Forming Processes

2 Fundamentals of Metal Forming Processes

1.2 BASIC STRUCTURE OF METALS AND ALLOYS 1.2.1 Grain Structure

The microstructure of solid metallic bodies consists of grains. Grains consist of unit cells in which atoms are arranged in a particular order. The cell structure repeats itself throughout the volume of the grain (Fig. 1.1). That is why the grains are also called crystallites. The structure is called lattice in which atoms are placed at lattice points. In metals, generally there is only one atom at a lattice point. There are many types of structures of unit cells for different materials, however, metals generally possess one of the following three cell structures.

(i) Body centered cubic structure (BCC). (ii) Face centered cubic structure (FCC).

(iii) Hexagonal closed packed structure (HCP). The three cell structures are illustrated in Fig. 1.2. Some metals such as iron (Fe), cobalt

(Co), titanium (Ti), etc. change their cell structure at different temperatures.

Grain boundaries Atoms

Fig. 1.1. Grain structure

Body Centered Cubic Structure: The structure consists of one atom at each of the eight corners of a cubical element and one atom at the center of the cube in Fig. 1.2(a). Metals with this structure are chromium (Cr), hafnium (Hf) at temperatures greater than 1975oC, iron (Fe) except at temperatures 911oC to 1392oC, molybdenum (Mo), niobium (Nb), tantalum (Ta), titanium (Ti) at temperatures greater than 882°C and tungsten (W), etc.

(a) BCC (b) FCC (c) HCP Fig. 1.2. Cell structures of metals

Page 3: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 3

(c) Grain boundary(b) Edge dislocation(a) Vacancy

Grain boundary

Face Centered Cubic Structure: In this structure there is an atom at each of the eight corners of the cubical element and there is an atom in the middle of each face of the cube as shown in Fig. 1.2(b). Metals with this structure are aluminum (Al), cobalt at temperature greater than 1120°C, copper (Cu), gold (Au), iron (Fe) between temperatures 911°C–1392°C, lead (Pb), nickel (Ni), silver (Ag), platinum (Pt), etc.

Hexagonal Closed Packed Structure: In this cell structure there is an atom at each corner of a hexagonal prismatic element, besides, there are three atoms symmetrically placed between the two end faces as shown in Fig. 1.2(c) and one atom each at center of the flat end faces. Metals with this structure are beryllium (Be), cobalt at temperatures less than 1120°C, magnesium (Mg), zinc (Zn), titanium (Ti) at temperatures less than 882°C, etc.

1.2.2 Lattice Defects Ideally there should not be any defect in lattice structure, however, imperfections and

defects may occur due to alloying elements, plastic deformation, grain boundaries, etc. The lattice structure generally contains following types of defects which are illustrated in Fig. 1.3.

(i) Point defects or imperfections. (ii) Line defects which are also called dislocations. (iii) Surface defects—grain boundaries.

Point defects are caused by various reasons such as (i) absence of an atom from a lattice point, (ii) an atom getting to a site which is not a lattice point, (iii) an atom of a different element (alloy) substituting an atom of parent metal, etc. Point defects disturb the natural arrangement of atoms in its vicinity and consequently atoms surrounding the point defect are either stretched apart or are pushed too close. This gives rise to additional pull or push among the atoms.

Fig. 1.3. Imperfections in lattice structure

The type and concentration of these imperfections or defects greatly influence the properties of metals and alloys. The defects may also be induced or controlled by alloying, heat treatment or plastic deformation in order to obtain a change in the mechanical properties.

Line defects or dislocations are important for plastic deformations. The following two types of dislocations are observed.

Page 4: Fundamentals of Metal Forming Processes

4 Fundamentals of Metal Forming Processes

Shear force

Shear force

Shear force

(i) Edge dislocations. (ii) Screw dislocations.

These are illustrated (Fig. 1.4). The figure also shows how these defects travel through the lattice when subjected to shear forces. The dislocations travel from one layer of atoms to another as the shear stresses increase. Slipping of all the atoms simultaneously would take enormous forces which is not explained by much lower yield strength of metals. A dislocation may be obstructed in its movement by atoms of alloying elements or point defects, by stationary dislocations and grain boundaries or by other defects. More force is then required to overcome the obstruction. Sometimes, the ends of a dislocation may get pinned down, in such a case, increase in applied shear force results in curving of the line defect (Fig. 1.5). With further increase in stress the dislocation may get curved inward, ultimately transforming into a ring dislocation and a new dislocation at the initial points. Thus this becomes a source of production of dislocations. Plastic deformation creates a large number of dislocations. Higher the dislocation density in the material, higher is the resistance to movement of dislocations and hence higher forces are required for plastic deformation. This explains the increase in strength during plastic deformation, which is called strain hardening or work hardening.

Fig. 1.4. Dislocations and their movement

Page 5: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 5

Final state = Initial dislocation +a circular dislocation

Initial dislocation

Force

Fig. 1.5. Generation of dislocation

Surface defects are the irregular arrangement of atoms at the grain boundaries. In a grain the atoms are arranged in particular order, however, the directions of the arrangement are different in neighbouring grains. The boundaries are irregularly shaped with the effect that at some places atoms are too far apart while at other places they are too close than the normal distance, thus giving rise to tensile and compressive forces. These defects also cause restriction to movement of dislocations. In a structure with small grains the dislocations can move only a small distance before encountering an obstacle, i.e. grain boundary. Therefore, a metal is stronger when it has small grains structure than when it has a large grain structure.

1.3 FORMING PROPERTIES OF METALS AND ALLOYS Most of the metal forming processes require a combination of material properties for

their successful operation. For example, for deep drawing of sheet metal, one of the requirements is that the material should be ductile. However, lead is quite ductile at room temperature but lead sheet is not that suitable for drawing into cups in the way steel cups are drawn. The material properties which are of importance for metal forming are listed below.

1. Yield strength/flow stress. 2. Ductility. 3. Strain hardening. 4. Strain rate sensitivity. 5. Effect of temperature on yield strength and ductility. 6. Effect of hydrostatic pressure on yield strength and ductility. 7. Instability and fracture strength.

1.4 TESTING FOR YIELD STRENGTH / FLOW STRESS 1.4.1 Tensile Test

For determination of yield strength or flow stress, one or more of the following three basic tests are conducted.

(i) Tension test. (ii) Compression test. (iii) Torsion test.

Page 6: Fundamentals of Metal Forming Processes

6 Fundamentals of Metal Forming Processes

Most of us are quite conversant with the simple tension test which is the most common and is conducted to determine the yield strength, ultimate tensile strength, percent elongation and fracture strength of metals. Figures 1.6 and 1.7 show typical stress-strain curves obtained in tension tests on two different alloys. Figure 1.6 is obtained for a low carbon steel or mild steel test specimen and Fig. 1.7 is obtained for an aluminium alloy test specimen. In these two diagrams the stress and strain are defined as given below.

Stress = Force/Original area of cross-section of specimen. Strain = Change in length/original length of specimen.

In case of mild steel, for loading up to point A (Fig. 1.6), there is a straight line or linear relationship between stress and strain. That is why the point A is also called proportional limit. Thereafter, the relationship between stress and strain is nonlinear up to a point B which is very near to A. Also up to the point B the deformations are largely elastic and on unloading the specimen regains the original dimensions. But beyond the point B the metal yields, it suffers plastic deformation. This is indicated by a sudden bend in the curve. Most of the strain after this point is plastic strain which is not recovered on unloading. The value of stress at B is called upper yield strength and point B is called upper yield point.

Upper yield

Lower yield

Proportional limit

DC

A

B

UTS

Fracture points

Strain dI/I

Str

ess

Ultimate tensile strength

E

F

Fig. 1.6. A typical stress-strain curve for mild steel

With further increase in strain (beyond B) the stress may fall a bit to a lower level at C (Fig. 1.6). This is due to formation of Lüder bands. With increase in tension, localized plastic flow takes place in a narrow band with boundary planes inclined at a certain angle with the axis of test specimen. Consequently the load falls a bit. However, due to strain hardening of the material in the band, the load again increases till another Lüder band appears in the test piece.

Page 7: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 7

Strain = I/I�

Yield point at 0.002 strain offsetIntersection of tangents to elastic and plastic curves

B

A

F

Fracture point

0.002

O

Str

ess

=lo

ad/o

rigin

alare

aofc/s

This goes on till the whole specimen is full of Lüder bands. Thus between the points C and D the stress is oscillating between two narrow limits. This occurs in alloys having interstitial solid solution structure like low carbon steels. The stress at the point C is called lower yield strength.

However with further increase in strain beyond the point D, when the test piece is full of Lüder bands, the load or stress again starts increasing. The distinction between the two yields may disappear with strain hardening and only a small kink may remain on the stress strain curve. Some authors prefer to take stress value at C as the flow stress at the yield point, however, the data given in material standards generally refers to upper yield point.

After the point D the stress-strain curve moves upwards, however, with further deformation, its slope gradually decreases to zero at the point E which is the highest point on the curve. After E the curve goes down. Before the point E, increase in strain increases the load on the specimen due to strain hardening. Even after the point E, the strain hardening is still there but at some point the area of cross section of the test piece starts decreasing much faster and a neck formation starts, with the result, the force that the test piece can bear decreases continuously with further deformation resulting in an unstable condition. After some elongation in the neck, the specimen fractures at the point F. Since we have defined stress as force divided by original area of cross section the stress value thus calculated also decreases after E, however, if we take true stress, as explained below, it will be much higher.

The stress at the point E is known as ultimate tensile strength. At point E the actual area of cross section is smaller than the original area of cross-section. In order to obtain realistic values of material strength, we must plot true stress-true strain curve which is discussed in the next section.

Most of the nonferrous metals and alloys do not show the sudden bend or kink in their stress strain curve like the one we get for low carbon steel as described above. Instead there is a gradual transition from elastic to plastic state (Fig. 1.7). In such cases, the yield strength may be taken at the point of intersection of tangents to elastic and plastic lines [9].

Fig. 1.7. A typical stress-strain curve for aluminum

Page 8: Fundamentals of Metal Forming Processes

8 Fundamentals of Metal Forming Processes

However the change from elastic to plastic state is very gradual, the point of intersection is rather ambiguous. Different values may be obtained if tangents are drawn at different points. Therefore, an offset yield point is obtained at a strain of 0.002 (0.2%). A straight line is drawn parallel to initial portion of stress-strain curve at the strain value of 0.002 and the point where it intersects the stress-strain curve is taken as yield point.

1.4.2 True Stress-True Strain

The curves of Figs. 1.6 and 1.7 are drawn with the stress defined as load divided by original area of cross-section and the longitudinal strain is defined as δl/l0, where l0 is the original length of test specimen. The curves would look very much different if we use true stress on ordinate and true strain on abscissa. The true stress and true strain are defined below.

True stress = Force applied on the specimenCurrent area of cross-section

(1.1)

For true strain, let us take that a specimen of length l is elongated by ‘δ l’. The differential strain dε becomes

dε = ll

δ (1.2)

The true strain in the specimen which has been elongated from the initial length l0 to final length l is obtained by integrating the above equation.

True strain ε = 0

l

l

ll∫

δ = 0log ( / )e l l (1.3)

The expression for true strain may also be written as below.

0log ( / )e l l = loge ( 1 + δ l /l0)

= loge ( 1 + E ) (1.4) where

E is the engineering strain = δl/l0 (1.5)

For accurate calculations, the true stress-true strain curve for the metal should be drawn to determine the yield strength. Figure 1.6 redrawn on true stress-true strain axes would look like the one shown in Fig. 1.8. Also there are standard specifications for the shape and dimensions of test specimen, which should be adapted in order to obtain meaningful results. Besides, in all above type of tests the following factors should also be noted.

(i) Temperature at which the test is conducted. (ii) The strain rate during the test. (iii) Accuracy of load measuring instrument. (iv) Accuracy of instrument which measures elongation.

Page 9: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 9

True strain = (I/I )o

Tru

estr

ess

=lo

ad

/cu

rre

nt

are

ao

fc/s

F

B

Fig. 1.8. True stress-true strain curve for tensile test

Example 1.1 A mild steel rectangular specimen of length 100 mm is extended to 120 mm. Neglecting

the elastic deformation and taking that material is isotropic, determine the true strains in length, width and thickness directions. Solution

Let εl , εw , and εt be the true strains in length, width and thickness directions respectively.

True strain along the length εl = ln (120/100) = 0.1823 Also, in plastic deformation the change in volume is zero. Therefore,

εl + εw + εt = 0 Since material is isotropic εw = εt

Hence εw = εt = – εl /2 = − 0.09115 The three strains are 0.1823, – 0.09115 and – 0.09115. Example 1.2

Determine the true strains in length, width and thickness directions of a sheet metal test specimen if it is elongated to 130 % of its original length. The anisotropy ratio εw /εt = 1.5. Also determine the per cent decrease in area of cross-section. Solution

The longitudinal strain ε l = loge (130/100) = 0.2623 From incompressibility condition εl + εw + εt = 0

and also we are given that εw /εt = 1.5

Page 10: Fundamentals of Metal Forming Processes

10 Fundamentals of Metal Forming Processes

Therefore, εt = − 0.2623/2.5 = − 0.1049

and εw = − 0.1573

Let ‘a’ be area of cross-section and ‘l’ the length. The volume V of the specimen is given by,

V = a.l The differential change in the volume is given as,

dV = a.dl + l.da

In plastic deformations the volume does not change. Hence, dV = 0, and hence da/a = – dl / l

∴ Change in area of cross-section = – 30 %

1.5 FACTORS THAT AFFECT THE YIELD STRENGTH In metal forming, particularly in hot forming many metallurgical processes may take

place concurrently. These include strain hardening, recovery, re-crystallization, etc. All these factors affect the yield strength. Therefore, it is important to know the extent of effect of each of these factors. The yield strength of a metal or alloy is affected by following factors.

(i) Strain hardening. (ii) Strain rate.

(iii) Temperature of metal and microstructure. (iv) Hydrostatic pressure.

1.5.1 Strain Hardening

To understand the effect of strain hardening let us again consider the tension test curve shown below in Fig. 1.9.

In this figure the test piece is loaded beyond the yield point up to a point P. The test piece is then unloaded. The elastic deformation recovers via the unloading curve PR which is more or less parallel to AO. It is generally taken that there is no change in Young’s modulus during plastic deformation. The line PR depicts elastic recovery. Out of the total strain OS corresponding to the point P, the part RS is the elastic recovery. The part OR which is not recovered is the plastic strain suffered by the test specimen. Now if we reload the same test piece, it nearly follows the line RP. There is, however, some deviation due to hysteresis which is very small, and the yielding now occurs at the point P. Further loading of the test piece beyond P gives the same stress-strain curve as we would have obtained if there were no unloading. This shows that after suffering a plastic strain represented by OR, the yield strength of metal has increased from point B to point P (or σo1 to σo2). This is called strain hardening or work hardening.

Page 11: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 11

�ot

B

P

OR

Q�oc

StrainStr

ess

Fig. 1.9. Strain hardening effect

Fig. 1.10. Bauschinger effect

Bauschinger Effect: Now consider another experiment for which the test curve is shown in Fig. 1.10. In this test, the specimen has been loaded in tension up to a point P beyond the yield point B ( yield strength = σot), then unloaded to point R and again loaded in reverse direction, i.e. compressed. In compression the test piece yields at the point Q where yield strength is equal to σoc which is smaller in magnitude than σot. This shows that the yield strength in compression has decreased due to the previous plastic strain in tension. Similarly the yield strength in tension

E

FP

B

A�o1

�o2

StrainR SO

Str

ess

Page 12: Fundamentals of Metal Forming Processes

12 Fundamentals of Metal Forming Processes

would decrease with previous compressive plastic strain. This is known as Bauschinger Effect (BE).

In fact due to plastic strain the material develops anisotropy. Its properties are no longer the same in different directions. Bauschinger Effect (BE) is observed in many metals and alloys.

BE may be reduced by thermal treatment. Complete removal is possible only by re-crystallization of strained material. However, it may be reduced by stress aging which is a process of heating the material to a certain temperature while it is subjected to suitable value of stress. By this process BE may be reduced at a low temperatures (less than 200°C).

1.5.2 Strain Hardening Index n For the sake of simplification in analysis it is taken that there are two factors in strain

hardening. One is isotropic strain hardening, in which the strain hardening effect is same in all directions, i.e. yield strength increases equally in all the directions. The second is kinematic strain hardening in which the yield strength does not increase in magnitude but whole of the yield diagram shifts (see Chapter 4) in the direction of plastic strain thus showing Bauschinger effect. Metals exhibit both these effects together, however, for sake of simplicity isotropic strain hardening is generally adapted in various analyses of metal forming problems. Some expressions developed for the flow stress ( σf ) by different researchers are as follows. σf = σ0 (ε )n (1.6a)

σf = σ0 ( B + ε )n (1.6b) σf = σ0 ( 1 + Bε )n (1.6c) σf = σ0 + B[ 1 – exp (–Cε ) ]n (1.6d) where σ0, B, n and C are material parameters. The ‘n’ is called strain hardening index or exponent, ε is true strain. Equations (1.6a to 1.6c) are generally used for small strains, while Eqn. (1.6d) is used for large strains for alloys which show a decreasing rate of work hardening or exhibit work hardening saturation. Determination of n

One of the methods to determine n for Eqn. (1.6a) is given below. Let V be the volume, a the area of cross section and l the length of the specimen, then V = a . l Differentiating the above we get

dV = l.da + a.dl (1.7) In plastic deformations the change in volume (dV) is zero. Hence from Eqn. (1.7) we get

dε = dl/l = – da /a (1.7a) and ε = ln l/l0 = − ln a/a0 = ln a0 /a The force ‘F ’ on the specimen at point E (Fig. 1.6) = σ . a Since at E the force F is maximum, we can write the following

dFdε

= 0

Page 13: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 13

dad

σε

+ a . ddσε

= 0 (1.8)

From Eqn. (1.7a) we get a = – da / dε

Substitution of this in Eqn. (1.8) gives the following relation at E.

dd

=σσε

We take that isotropic strain hardening occurs according to Eqn. (1.6a). Substitution of this in the above equation gives the following.

σ0 εun = σ0 n. εu

n–1 where εu

is the strain at the point E (Fig. 1.6). From the above equation we get the value of strain hardening exponent n as

n = εu. (1.9)

Equation (1.9) gives a method of determining the exponent n. Even for other strain hardening rules there is close relationship between n and εu. The data obtained by Narayanasamy and Sowerby [21] on three steels (Table 1.1), shows that n is nearly equal to the true strain at maximum strength. According to them these steel conform to hardening law σf = K (ε0 + ε )n. Example 1.3

For a strain hardening material obeying the law nA εσ = show that

66n = /ddσ σε ε

Solution

By differentiating the equation nA εσ = we get, ddσε

= A n 1−nε

From the initial equation we have A = nεσ / . Substituting this value of A in above equation and by simplification we get

n = /ddσ σε ε

Table 1.1: Relationship between εu and n [21] Material Yield strength K ε 0 n Strain at max. ( MPa) (MPa) strength

AKDQ steel 178.9 528.9 0.007 0.265 0.27 Dual Phase steel 497.9 1037.7 0.002 0.17 0.18 304 Stainless steel 353.02 1754.8 0.054 0.6 0.58

Page 14: Fundamentals of Metal Forming Processes

14 Fundamentals of Metal Forming Processes

In fact many researchers have determined the values of n for different materials. For the sake of comparison, the values of strain hardening exponent n obtained by a few researchers are given below.

Table 1.2: Values of σ 0, B and n in the Eqn. (1.6c) [ 9 ]

Material σ0 (MPa) B n

SAE 1020 (cold rolled) 514 68 0.067

SAE 1020 (annealed) 232 58 0.294

6061-T-6 (Al. Alloy cold rolled) 252 42 0.149

6061-T-6 (annealed) 43 50 0.204

Example 1.4

Determine the percent increase in yield strength of annealed aluminum bar if it is elongated from 200 mm to 250 mm. Take strain hardening data from Table 1.2. Solution Refer to Table 1.2, the yield strength of annealed aluminum is given by,

σf = 43 ( 1 + 50 ε ) 0.204

The longitudinal strain ε = ln (250 /200) = 0.2231 The new yield strength of specimen = σf = 43 [1 + 50× 0.223]0.204 = 71.57 Mpa Similarly yield strength at zero plastic strain = 43 ∴ Increase in the yield strength = 66.44%

You-Min Huang et al., [19 ] have given the following data for low carbon steel, copper and aluminum.

Table 1.3: Flow stress of low carbon steel, Cu and Al [ ref.19]

Material Yield strength kgf/mm2 Flow Stress in kgf/mm2

Steel (Low) Carbon 19.4 σf = 80.394(0.0151 + ε)0.33944

Copper 15.8 σf = 100.067(0.009 + ε)0.39179

Aluminum 2.2 σf = 15.0356(0.01 + ε)0.41628

where ε is the effective plastic strain.

Page 15: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 15

Example 1.5

A cylindrical test specimen of diameter 10 mm and gauge length 50 mm is extended to 65 mm. Determine the true strain. Neglect the elastic deformation. If the ultimate strength occurs at a force of 25000 N and at an extension of 70 mm, determine the strain hardening exponent n and ultimate strength of the material. Solution

The true strain at 65 mm extension is given by ε = ln 65/50 = 0.2623 The true strain at extension of 70 mm = ln 70/50 = 0.3364 ∴ Value of n = 0.3364 and also ε = ln (l/l0) = ln (a0/a) Therefore, the area of cross section at the maximum force is given by

a = a0 / (e0.3364 ) = π × 10 × 10 / (4 × 1.3999) = 56.104 mm2 True ultimate strength is = 25000/56.104 = 445.60 N/mm2

Ultimate tensile strength as given in standard tables is related to original area of cross section. For the above case, UTM is calculated below.

UTM = 25000 × 4 / (π × 10 × 10 ) = 318.31 N/mm2

Work Done During Plastic Deformation Let a bar of area of cross-section ‘a’ and length ‘l0’, be elongated to length l . The work

(W ) done during elongation is given by

W = ∫l

l0

area of cross-section × stress ×δl

Here we neglect the elastic strain and let the yield strength during plastic deformation be given by,

σf = σ0 εn

Substitution of this in the above equation results in

W = ∫l

l0

area × σ0 εn ×δ l

Or

W = ∫l

l0

area ×l0 ×σ0 εn ×δ l /l0

Now the volume of body = area × l0 and it remains constant during plastic deformation and δl/l0 = dε. Therefore, W may be written as,

Page 16: Fundamentals of Metal Forming Processes

16 Fundamentals of Metal Forming Processes

0

0nW Volume d= ∫

ε

ε

σ ε ε

1 10 0( )

1

n n

W Volumen

+ +⎡ ⎤−= ⎢ ⎥+⎣ ⎦

σ ε ε (1.10)

For the other strain hardening laws discussed above, the expressions for work done may be obtained similarly. Thus if the strain hardening law is σf = A (B + C ε ) n the amount of work done for plastic strain 0 to ε becomes

W = 1 1( )( 1)

n nVolume A B C ABC n

+ +⎡ ⎤+ −⎣ ⎦+ε (1.11)

Example 1.6 The yield strength of brass is give by σf = 300 (1 +15 ε ) 0.3 MPa. A bar of this material

having area of cross-section 200 mm2 and length 200 mm is extended to 250 mm. Determine the value of the yield strength of the material of bar after extension. Also determine the work done during the elongation.

Solution The true longitudinal plastic strain = εl = ln (250/200) = 0.223

∴ σf = 300 ( 1 + 15 × 0.223 )0.3 = 466.14 MPa

Refer to Eqn. (1.11). Here A = 300, B = 1, C = 15 , n = 0.3 and hence,

W = [ ] 1.3200 200 300 (1 15 0.223) 115 1.3

× ⎡ ⎤+ × −⎣ ⎦× ×1/1000 Nm

= 3539.255 Nm.

1.5.3 Effect of Strain Rate Another factor that increases load on forming equipment is the rate at which the forming

process is carried out. At higher rates of strain the flow stress of material increases leading to higher loads on the equipment. The effect of strain rate on yield strength for an alloy is illustrated in Fig. 1.11.

The factors described above influence the forming processes to varying degrees depending upon the temperatures at which the processes are carried out. If a forming process is carried out at a temperature less than the re-crystallization temperature and at a slow rate, such a case may be taken as an isothermal process, i.e. the effect of temperature change during the process may be neglected and we may consider only the effect of strain hardening.

Page 17: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 17

1000

800

600

400

200

0

0 0.1 0.2 0.3 0.4

Strain

Str

ess

(Mpa)

�� = 8000 s–1

�� = 1 s–1

Fig. 1.11. Effect of strain rate on yield strength When a forming process is carried out in hot state the re-crystallization is also present

along with strain hardening and strain rate effect. The strain hardening may be nullified by re-crystallization. Therefore, in hot working we may only consider the effect of temperature and strain rate on the yield strength of metal. The effect of strain rate may be written as given below.

σf = σ0 (ε ) m (1.12) where σf is the flow stress, ε is the plastic strain rate, m and σ0 are material parameters. Since the effects of strain rate and strain hardening may vary at different temperatures, this presents a major problem of testing each metal and alloy at different temperatures, at different strain rates and to different extents of strain. The problem of testing becomes more difficult because most of the work done on the metal body for plastic deformation reappears as heat and raises the temperature of the test specimen. At low strain rates the flow stress increases with increase in strain rate. At higher strain rates it still increases but at a slower rate because of the softening effect due to temperature rise in the material. Stout and Follanshee [16] have determined the following expression for strain rate sensitivity in stainless steel 304L at strain rates of the order of 103 s–1 and above.

σf = σb + β ε (1.13) where σb = 668 M Pa and β = 0.0066 ± 0.0025 M Pa-s

1.5.4 Effect of Temperature Recovery and Re-crystallization

Figure 1.12(a) shows initial structure of an undeformed metal piece. Figure 1.12(b) shows the structure after it has been compressed along its height. The grains get elongated in the direction normal to the direction of applied force, i.e. in the lateral direction. The material gets strain hardened, i.e. its yield strength, UTM and hardness increase while ductility decreases. As explained in Section 1.2, the strain hardening occurs because the dislocation density increases due to cold deformation. With increase in temperature the movement of dislocations gets easier and

Page 18: Fundamentals of Metal Forming Processes

18 Fundamentals of Metal Forming Processes

they readjust due to stresses locked in the lattice. Some dislocations having opposite sign may annihilate each other. This is called recovery process in which the residual stresses are reduced, however, the enhanced properties due to cold working are only little affected.

Now if the compressed metal piece is heated to certain higher temperature (0.4 to 0.6. Tmelt.), new grains will start emerging at the boundaries of old grains and at sites of other defects. If this temperature is maintained for some time the new grains will grow to cover the entire structure. This is called primary re-crystallization. Re-crystallization removes the strain hardening effect and hence reduces strength but increases ductility. However, the process does not stop there. Some grains start growing at the expense of other grains till the complete structure is covered by bigger grains. This is called secondary re-crystallization and grain growth.

(a) Initial structure (b) After compression (c) Start of crystallization

(e) Grain growth (d) After recrystallization

New grains

Heat

Fig. 1.12. Re-crystallization

The mechanical properties like yield strength depend upon the grain size. The relationship between grain size and flow stress is given by the Hall-Petch formula (Eqn. 1.14).

σf = σ0 + λ d−1/2 (1.14) where σf is the flow stress of material, d is the average grain size and σ0 and λ are material parameters. The parameters σ0 and λ are not absolute constants but are functions of strain, strain rate and temperature.

During hot working the processes of strain hardening and subsequent stress relieving/ recovery and re-crystallization may occur depending upon the temperature and strain. It has been found that in ferrous alloys at 780°C a three stage softening may take place after hot deformation to a certain minimum true strain which may vary between 0.08 to 0.15.

Several attempts have been made to determine single expression for yield strength, which includes the effect of strain, strain rate, temperature, grain size and re-crystallization. Bonnavand, Bramley and Mynores [22] have employed the following formulation for the effect of these factors for calculations related to backward extrusion process.

Page 19: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 19

)(exp)()1(3

2 TKm

mn βεεσ −−

= (1.15)

where K is material constant in stress units, ε = equivalent strain, n = strain hardening exponent, m = strain-rate-effect exponent, T = temperature (Kelvin) and β = material parameter. Values of these parameters for some metals are given in Table 1.4.

Table 1.4: [ref.22]

Material K(MPa) n m β (k–1)

AISI 1035 5404 0.059 0.126 3.1×10–3

AISI 1045 7260 0.326 0.11 2.9 ×10–3

AISI 3524 3524 0.233 0.082 2.4 ×10–3 AISI 410 1883 0.134 0.103 2.4 ×10–3

1.5.4.1 Hot Forming, Cold Forming and Warm Forming

Metal forming processes may be carried out in hot as well as in cold state. Temperature of re-crystallization is the boundary between the two.

Hot forming or hot working is defined as forming at temperatures above the re-crystallization temperature of the metal. In fact the actual temperatures are much higher than the re-crystallization temperature. High temperatures reduce the flow stress of metals, which results in low deforming forces.

Cold forming or cold working refers to forming at temperatures below the re-crystallization temperature of the metal. The strain hardening during the process improves the mechanical properties of the product. Also close dimensional tolerances can be obtained in cold forming.

Fo

rce

Elongation

At 1250° C

At 1000° C

At 500° C

Stress-strain curve of MSat room temperature

Fig. 1.13. Effect of temperature on the yield strength

Page 20: Fundamentals of Metal Forming Processes

20 Fundamentals of Metal Forming Processes

Advantages of hot forming (i) At high temperatures, the metals become soft, its yield strength decreases (Fig. 1.13)

and hence low forces are required for forming. This reduces the cost of equipment needed for the process.

(ii) Metals are more ductile at higher temperatures and their formability in hot state is higher than in cold state. Therefore, large deformations may be given in hot working.

(iii) The casting defects in ingots like internal shrinkage cavities (not those in contact with atmosphere) and blow holes get welded during hot working. The structure becomes more homogeneous resulting in better mechanical properties.

(iv) Due to low flow stresses at high temperatures, very large components may be made by plastic deformation.

Disadvantages of hot working (i) The products have low surface quality due to oxidation of surface layer. (ii) The components formed have low dimensional accuracy. (iii) There is little improvement in mechanical properties. (iv) The forming tools also get heated up due to contact with hot metal and wear of tools is

rapid. Advantages of cold forming

(i) Good surface finish of the product. (ii) High dimensional accuracy. (iii) Superior mechanical properties, e.g. hardness and strength increase due to strain

hardening. (iv) Strain hardening may eliminate the surface hardening heat treatment required in some

components such as cold rolled gears. (v) The material develops anisotropy which may be used to advantage in subsequent

forming processes. For instance, the anisotropy developed in cold rolled sheet metal helps in getting deeper draws.

Disadvantages of cold forming (i) High loads on the equipment require it to have high strength and rigidity. This

increases the cost of machines. (ii) With strain hardening the material becomes less ductile.

Warm Forming: Of recent, ‘warm forming’ has come to be used in order to gain the advantages of hot as well as cold forming, though to a lesser extent. Warm forming is carried out at a temperature higher than room temperature but lower than the re-crystallization temperature. Since yield strength decreases with increase in temperature, the load on the equipment in warm forming is lower than in cold forming. Also the temperatures are not that high that the surface layer damage can occur. Therefore, the advantages of cold forming are achieved, that is, better surface quality, better dimensional accuracy and better mechanical properties than in hot forming.

Page 21: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 21

1700

1600

1500

1400

0 200 400 600 800 1000

Lower yield in tension

Compression yield strength0.2 % offset

0.1 % offset

Tru

estr

ess

MN

/m2

Hydrostatic pressure MN/m2

Because of reduced forces, the tools wear is less and the equipment is also less expensive. Temperatures for warm forming should be chosen such that the ductility of metal is high at that temperature.

In a forming process, metal blank has to come in contact with dies or tools which are generally massive compared to the metal blank being processed and hence there is considerable heat transfer from work piece to the tools in hot forming. This makes the temperature of metal blank itself non uniform, i.e. reduces temperatures near contact zones.

The testing also becomes more complicated because of phase changes in metals and alloys due to temperature and strain. It is difficult to have a clear cut relationship between yield strength, temperature, strain and strain rate because of complex behavior of metals, however, there are quite a few attempts to empirically describe the yield strength of certain metals as a function of these variables in specific temperature ranges. 1.5.5 Effect of Hydrostatic Pressure

Hydrostatic pressure may affect the following properties of metals and hence their formability.

(i) Ductility. (ii) Yield strength or flow stress.

(iii) Strain hardening index and strain rate index. Experiments of Bridgeman [3] have shown that hydrostatic pressure does not lead to

plastic deformation. However, hydrostatic pressure increases the ductility and formability of metals and alloys. The phenomenon of increased ductility with hydrostatic pressure is also called pressure induced ductility.

Fig. 1.14. Effect of hydrostatic pressure on yield strength of quenched and tempered

AISI 4330 steel [11]

Even brittle materials may be plastically deformed under suitable hydrostatic pressures. Materials in which the plastic deformation leads to change in volume, the yield strength may be affected by hydrostatic pressure. Spitzig et al. [11] have shown that yield strength of quenched and tempered AISI 4310 and 4330 steels is affected by hydrostatic pressure.

Figure 1.14 shows the effect of hydrostatic pressure on the yield strength of 4330 steel. Both the steels show increase in volume during plastic deformation as well as increase in yield

Page 22: Fundamentals of Metal Forming Processes

22 Fundamentals of Metal Forming Processes

strength under hydrostatic pressure. Very few researchers have attempted to determine the effect of hydrostatic pressure on strain hardening and strain rate effect indices. According to Spitzig et al., [11], there is no effect of hydrostatic pressure on the strain hardening index (n).

These steel also show a constant difference in the values of yield strength in tension and in compression. The yield strength in compression is higher than that in tension and the difference between the two yield strengths is not affected by hydrostatic pressure.

1.6 DUCTILITY AND FORMABILITY Ductility is an essential property of material for its formability. However, ductility is not

some thing like absolute constant for a metal or alloy under all conditions. In fact, it gets modified by the process parameters that is why the same material may show different formability in different forming processes.

Ductility is measured by the strain suffered by the material before fracture. In a tensile test it may be measured by percent elongation in engineering terms, or by logarithmic strain at the fracture point. In compression test similar measures may be used. In torsion test it is measured by the strain suffered by outer layer of material of test bar before fracture.

The tensile tests show low ductility because of neck formation and consequently the negative hydrostatic pressure in the neck region promotes crack initiation and propagation. This problem is not there in compression and torsion tests which show higher ductility for the same material. Many researchers have preferred torsion test for measurement of ductility while the strength properties are related to those measured in tensile test.

1.6.1 Factors that Affect Ductility of Metals As already mentioned above ductility is affected by intrinsic factors like composition,

grain size, cell structure etc., as well as by external factors like hydrostatic pressure, temperature, plastic deformation already suffered etc. Some important observations about ductility are given below. (i) Metals with FCC and BCC crystal structure show higher ductility at high temperatures

compared to those with HCP crystal structure. (ii) Grain size has significant influence on ductility. Many alloys show super-plastic behavior

when grain size is very small of the order of few microns. (iii) Steels with higher oxygen content show low ductility. (iv) In some alloys impurities even in very small percentages have significant effect on

ductility. Ductility of carbon steels containing sulfur impurity as small as 0.018%, drastically decreases ductility at around 1040°C. This can however be remedied if Mn content is high. In fact the ratio Mn/S is the factor which can alter ductility of carbon steels at 1040°C. With the value of this ratio at 2 the percent elongation is only 12–15% at 1040°C while with ratio of 14 it is 110 per cent.

(v) Temperature is a major factor that influences ductility and hence formability. In general it increases ductility, however, ductility may decrease at certain temperatures due to phase transformation and micro-structural changes brought about by increase in temperature. Figure 1.15 shows the effect of temperature on ductility of stainless steel. It has low ductility at 1050°C and maximum at 1350°C. Therefore it has a very narrow hot working range [12].

Page 23: Fundamentals of Metal Forming Processes

Plastic Deformation of Metals and Related Properties 23

900 1100 1300 1500

Temperature°C

20

40

60

80

Strain rate 400s–1

Strain rate 500s–1

Re

du

ca

tio

nin

dia

me

ter

pe

rce

nt

Fig. 1.15. Ductility of stainless steel at high temperatures [12]

(vi) Hydrostatic pressure increases ductility. This observation was first made by Bridgeman [3]. In torsion tests the length of specimen decreases with increase in torsion. If the specimen is subjected to an axial compressive stress in torsion test it shows higher ductility than when there is no axial stress. If a tensile axial stress is applied the ductility decreases still further.

(vii) The temperatures for optimum ductility are also affected by concentration of alloying element. Figure 1.16 shows the temperatures for optimum ductility for different concentration of carbon in plain carbon steels [12].

(viii) Duplex microstructures generally lead to lower ductility [12]. For example, low carbon steel when tested in (α + γ ) range shows lower ductility.

(ix) Strain rate also influences ductility. Tests done in tension have shown that increase in strain rate increases the elongation in uniform deformation region and decreases the same in the neck region. For obtaining the effect of strain rate the observed values must be corrected for change in temperature, because, at high strain rates there is considerable increase in temperature of material which increases ductility. More work is needed to establish a conclusive effect of strain rate on ductility.

1300

1200

1100

1000

0 0.20.2 0.4 0.6 0.8 1.0 1.2

Carbon content %

Te

mp

era

ture

°C

Temperature foroptimum ductility

Fig. 1.16. Temperatures for optimum ductility for plain carbon steels [12]