Gas Metal ArcWelding Practice:
Jobs 22-J1J23
(Plate)
Chapter 22
-
7/27/2019 GMAW WELDING
2/152
22 - 2
Objectives
1. Describe GMAW operating variables
2. Describe GMAW weld defects
3. Describe GMAW safe operation
4. Describe and demonstrate proper care, use, and
troubleshooting of equipment
5. Describe and demonstrate welding techniques
6. Make various groove and fillet welds with the
various modes of metal transfer with both solid and
metal cored electrodes
-
7/27/2019 GMAW WELDING
3/152
22 - 3
Operating Variables ThatAffect Weld Formation
Factors that affect operation of arc and weld
deposit
Sound welding of good appearance resultswhen variables in balance
Necessary to become familiar with all variables
-
7/27/2019 GMAW WELDING
4/152
22 - 4
Direct Current ElectrodePositive (DCEP)
Generally used for gas metal arc welding
Provides maximum heat input into work allowing relatively
deep penetration to take place
Assists in removal of oxides from plate Low current values produce globular transfer of metal from
electrode
On carbon steel shielding gas must contain minimum
of 80% argon
Ferrous metals need addition of 2 to 5% oxygen to gas
mixture
-
7/27/2019 GMAW WELDING
5/152
22 - 5
Gas Metal Arc DCEP Welding:Wire Positive, Work Negative
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
6/152
22 - 6
Direct Current ElectrodeNegative (DCEN)
Limited use in welding of thin gauge materials
Greatest amount of heat occurs at electrode tip
Wire meltoff rate great deal faster than DCEP Penetration also less than with DCEP
Arc not stable at end of filler wire
Corrected by use of shielding gas mixture of 5%oxygen added to argon
Meltoff rate reduced so benefit cancelled
-
7/27/2019 GMAW WELDING
7/15222 - 7
Gas Metal Arc DCEN Welding:Wire Negative, Work Positive
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
8/15222 - 8
Alternating Current
Seldom used in gas metal arc welding
Arc unstable because of current reversal
Combination of both DCEN and DCEPpolarity, rate of metal transfer and depth of
penetration falls between those polarities
Found some use for welding of aluminum
-
7/27/2019 GMAW WELDING
9/15222 - 9
Shielding Gas
Argon and helium first used for gas metal arc
Continue to be basic gases
Argon used more than helium on ferrous metalsto keep spatter at minimum
Also heavier than air so good weld coverage
Oxygen or carbon dioxide added to pure gases
to improve arc stability, minimize undercut,reduce porosity, and improve appearance ofweld
-
7/27/2019 GMAW WELDING
10/152
22 - 10
Shielding Gas
Helium added to argon to increase penetration
Hydrogen and nitrogen used for only limited
number of special applications Carbon dioxide has following advantages:
Low cost
High density, resulting in low flow rates
Less burn-back problems because of its shorter arc
characteristics
-
7/27/2019 GMAW WELDING
11/152
22 - 11
Specific Metal Recommendations
Aluminum alloys: argon
Magnesium and aluminum alloys: 75 percent
helium, 25 percent argon Stainless steels: argon plus oxygen
Magnesium: argon
Deoxidized copper: 75 percent helium, 25percent argon preferred
Low alloy steel: argon, plus 2 percent oxygen
-
7/27/2019 GMAW WELDING
12/152
22 - 12
Specific Metal Recommendations
Mild steel: 15 percent argon, 25 percent carbon
dioxide (dip transfer); 100 percent CO2may
also be used with deoxidized wire
Nickel, Monel, and Inconel: argon
Titanium: argon
Silicon bronze: argon
Aluminum bronze: argon
-
7/27/2019 GMAW WELDING
13/152
22 - 13
Joint Preparation
Joint design should provide for mosteconomical use of filler metal
Correct design for job depends on:
Type of material being weldedThickness of material
Position of welding
Welding process
Final results desiredType and size of filler wire
Welding technique
-
7/27/2019 GMAW WELDING
14/152
22 - 14
Joint Preparation
Arc in gas metal arc welding more penetrating
and narrower than arc in shielded metal arc
welding therefore, smaller root openings may
be used for groove welds
Change in joint design increase speed of welding
100% penetration may be secured in " plate
in square butt joint welded from both sides
-
7/27/2019 GMAW WELDING
15/152
22 - 15
Joint Preparation
No root face recommended for 60 single- ordouble-V butt joints
Root opening should range from 0 to 3/32"
Double-V joints may have wider root openingsthan single-V
Plates thicker than 1 inch should have
U-groove preparationRequire less weld metal; root face thickness shouldbe less than 3/32" and root spacing 1/32 and 3/32"
-
7/27/2019 GMAW WELDING
16/152
22 - 16
V-Groove, Butt JointComparison
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
17/152
22 - 17
Joint Preparation
Multipass welding easier since absence of slag
ensures easier cleaning
For fillet welds deposit smaller weld beads onsurface of material
Certain types of joints backed up to prevent
weld from projecting through back side
Blocks, strips and bars of copper, steel or ceramics
-
7/27/2019 GMAW WELDING
18/152
22 - 18
Comparison of Penetration in aFillet Weld
Carbon dioxide shieldedMAG weld versus coated
electrode weld.
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
19/152
22 - 19
Electrode Diameter
Influences size of weld bead, depth of penetration, andspeed of welding
General rule
For same current, arc becomes more penetrating aselectrode diameter decreases and deposition rate increases
To get maximum deposition rate at given currentdensity, use smallest wire possible consistent with
acceptable weld profile Wire 0.045" and larger provide lower deposition rate
and deposit wider beads than small wires
-
7/27/2019 GMAW WELDING
20/152
22 - 20
Electrode Diameter
Filler wires should be same composition as materialsbeing welded
Position of welding may affect size of electrode
Welding thin material Wires with diameters: 0.023/0.025, 0.030, 0.035"
Medium thick materials Wires with diameters: 0.045" or 1/16"
Heavy materials Wire with diameter: 1/8"
Small diameters recommended for vertical andoverhead positions
-
7/27/2019 GMAW WELDING
21/152
22 - 21
Electrode Extension
Length of filler wire that extends pas contact tube
Area where preheating of filler wire occurs
Also called the stickout
Controls dimensions of weld bead since length ofextension affect burnoff rate
Exerts influence on penetration through its effect onwelding current As extension length increased, preheating of wire increases
and current reduced which in turn decreases amount ofpenetration into work
Stickout distance may vary from 1/8 to 1 1/4"
-
7/27/2019 GMAW WELDING
22/152
22 - 22
Electrode Extension
Short electrode extensions (1/81/2 inch) used forshort circuit mode of transfer, generally with smallerdiameter electrodes (0.0230.045 inches)
Stainless steel favors shorter electrode extension
because of its higher resistivity (1/81/4 inch) Longer and larger diameter electrode extensions used for
spray arcs (1/211/4 inches)
Excessive long arcs with active gases reduce the
mechanical properties in weld Various alloys being burned out as metal transferred across
longer arc
-
7/27/2019 GMAW WELDING
23/152
22 - 23
Electrode Extension
Tests indicated that when electrode extensionincreased from 3/16 to 5/8 inch, welding current thendrops approximately 60 amperes
Current reduced because of change in amount of
preheating that takes place in wire As electrode extension increased, preheating of wire increases
Thus less welding current required from power source at agiven feed rate
Because of self-regulating characteristics of constant voltagepower source, welding current decreased
As welding current decreased, depth of penetration alsodecreases
N l f A B
-
7/27/2019 GMAW WELDING
24/152
22 - 24
Nomenclature of Area BetweenNozzle and Workpiece
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
25/152
22 - 25
Position of the Gun
Expressed by two angles: travel and work
Bead shape changed by changing direction of wire asgoes into joint in line of travel
Gun Angle Can be compared to angle of electrode in shielded metal arc
welding
Drag technique results in high narrow bead with deeper
penetration (10 drag angle) As drag angle reduced, bead height decreases, width
increases
Increased travel speeds characteristic of push technique
-
7/27/2019 GMAW WELDING
26/152
22 - 26
Travel and Work Gun Angles
Axis of Weld
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
27/152
22 - 27
Travel and Work Gun Angles
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Travel Angle
(T.A.)
Axis of Weld
(Drag) Travel Direction
(Push) Travel Direction
Work Angle(W.A.)
-
7/27/2019 GMAW WELDING
28/152
22 - 28
Drag and Push Gun angles
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
29/152
22 - 29
Work Angle
Position of wire to joint in plane perpendicularto line of travel
Filler weld joints: work angle normally half of
included angle between plates forming joint
Butt welds: work angle normally 90 to surfaceof plate being joined
Utilizes natural arc force to push weld metalagainst vertical surface to prevent undercut andprovide good bead contour
-
7/27/2019 GMAW WELDING
30/152
22 - 30
Work and Gun Angles
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
31/152
22 - 31
Arc Length
Constant voltage welding machine used for gas metalarc welding provides for self-adjustment of arc length
Arc length shortened, arc voltage reduced
Arc length lengthened, arc voltage increased No change in wire-feed speed occurs
Corrected by automatic increase or decrease ofburnoff rate of filler wire
Welder has complete control of welding current andarc length by setting wire-feed speed on wire feederand voltage on welding machine
-
7/27/2019 GMAW WELDING
32/152
22 - 32
Arc Voltage
Decided effect upon penetration, bead height,and bead width
Chief function to stabilize welding arc and
provide smooth, spatter-free weld bead
Higher or lower causes arc to become unstable
Higher: produces wider, flatter bead and increases
possibility of porosity and increases spatter andincreases undercut in fillet welds
Lower: causes bead to be high and narrow
-
7/27/2019 GMAW WELDING
33/152
22 - 33
Arc Voltage
High arc voltages result in globular transfer
Spatter prone and reduces deposition efficiency
Has sharp crackling sound when proper arcvoltage for short circuit transfer
Spray arc have hissing sound
Not set to control penetration Better control of weld profile and arc stability
R l ti hi f A L th t
-
7/27/2019 GMAW WELDING
34/152
22 - 34
Relationship of Arc Length toWeld Bead Width
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
High VoltageLow Voltage
Arc Length
Arc Length
Electrode
Electrode
-
7/27/2019 GMAW WELDING
35/152
22 - 35
Penetration Comparisons
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Arc voltage too high
for travel speed.
Arc voltage too slow
for travel speed
Proper arc voltage
for speed
-
7/27/2019 GMAW WELDING
36/152
22 - 36
Wire-Feed Speed
Fixed relationship between rate of filler wire burn offand welding current
Electrode wire-feed speed determines welding current
Current set by wire-feed speed control on wire feeder Excessive speed, welding machine cannot put out
enough current to melt wire fast enough
Stubbing or roping of wire occurs
Causes convex weld beads and poor appearance Decrease in speed results in less electrode being melted
Generallyhigh setting of filler wire speed rate resultsin short arc, slow speed in long arc
-
7/27/2019 GMAW WELDING
37/152
22 - 37
Effect of Wire-Feed Speeds
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
38/152
22 - 38
Welding Current
Determines amount of current delivered at arc
Often related to current density
Amperage per square inch of cross-sectional area
of electrode At given amperage, current density of electrode 0.035"
in diameter higher than of electrode 0.045" in diameter
Area of current-carrying sheath of metal coredelectrode more complex to calculate
Current densities much higher with metal coredelectrodes than solid wire
-
7/27/2019 GMAW WELDING
39/152
22 - 39
Welding Current
If going to maintain given amperage and switch from
solid wire to metal core, either jump one wire
diameter size and keep wire-feed speed same or keep
same wire size and increase wire-feed speed Each type and size of electrode has minimum and
maximum current density
Best working range lies between
Direct relationship between welding current and
penetration
Welding current increases, penetration increases
-
7/27/2019 GMAW WELDING
40/152
22 - 40
Welding Current
Table 22-3 gives comparative current ranges and otherparameters for welding carbon steel, stainless steel,and aluminum
Increases in current will increase bead height andwidth (voltage must also be increased)
Too high
Possibility of electrode burn-back into tube, arc unstable
and gas shielding disturbed, spatter Too low
Arc unstable, poor fusion, electrode becomes red hot, arcmay be extinguished, less penetration
-
7/27/2019 GMAW WELDING
41/152
22 - 41
Travel Speed
Has decided effect on penetration, bead size, andappearance
At given current density, slower travel speeds provide
proportionally larger weld beads and more heat inputin base metal per unit length of weld
Too slow, unusual weld buildup occurs
Progressively increased travel speeds have opposite
effects Less weld metal deposited with lower heat input per unit
length of weld
Produces narrower weld bead and lower contour
-
7/27/2019 GMAW WELDING
42/152
22 - 42
Travel Speed
Excessively fast speeds causes undercut
Influenced by thickness of metal being welded,
joint design, cleanliness, joint fitup, and
welding position
If increased, necessary to increase wire-feed
speed, which increases current and burnoff rate
Too low produces overlap of base metal and
even burn-through on this material
-
7/27/2019 GMAW WELDING
43/152
22 - 43
Arc Position
Arc must be on
leading edge of
weld pool to
assure penetrationand fusion.
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
44/152
22 - 44
Optimum Travel Speed
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
-
7/27/2019 GMAW WELDING
45/152
22 - 45
Summary of Operating Variables
Height and width of bead depend on adjustment ofthese variables
Joint preparation
Gas flow rate
Voltage
Speed of travel
Arc length
Polarity
Variables adjusted on basis of type of material beingwelded, thickness of material, position of welding,deposition rate required, and final weld specifications
Gun angle
Size and type of filler wire
Electrode extension
Characteristics of the shieldinggas
Wire-feed speed (current)
-
7/27/2019 GMAW WELDING
46/152
22 - 46
Summary of Operating Variables
Welding current and travel speed have similar
effect on both bead height and width
Each variable increases or decreases both bead
height and width at same time
Arc voltage
As arc voltage increases, bead height decreases and
bead width increases, flattening bead
Affects shape and size of bead
-
7/27/2019 GMAW WELDING
47/152
22 - 47
Weld Defects
Defects found in welds made by gas metal arcprocess similar to those in other welding
Causes and corrective action entirely different
Incomplete penetrationResult of too little heat input in weld area
Correct by increasing wire-feed speed and reducing
electrode extension to obtain maximum current forparticular wire-feed setting
Also causes by improper welding techniques
-
7/27/2019 GMAW WELDING
48/152
22 - 48
Excessive Penetration
Usually causes excessive melt-through
Result of too much heat in weld area
Reducing wire-feed speed to obtain lower amperage orincreasing speed of travel
Another cause is improper joint design
Root opening too wide or root face too small
Correct by checking position of welding and root face andopening
Remedied during welding by increasing electrodeextension distance and weaving gun
-
7/27/2019 GMAW WELDING
49/152
22 - 49
Whiskers
Short lengths of electrode wire sticking through
weld on root side of joint
Caused by pushing electrode wire past leading
edge of weld pool
Can be prevented by
Reducing wire-feed speed
Increasing electrode extension distance
Weaving gun
-
7/27/2019 GMAW WELDING
50/152
22 - 50
Voids
Referred to as wagon tracks because of resemblancein radiographs to ruts in dirt road
May be continuous along both sides of weld
Found in multipass welding Underneath pass has bead with large contour or bead with
too much convexity or undercut
Next bead does not completely fill void between previouspass and plate
Prevent by making sure edges of all passes filled in soundercut cannot take place and arc melts previous
bead and fuses into sides of joint
-
7/27/2019 GMAW WELDING
51/152
22 - 51
Incomplete Fusion
Also referred to as overlap
Result of improper gun handling, low heat and
improper speed of travel
To prevent:
Direct arc so it covers all areas of joint
Keep electrode at leading edge of pool
Reduce size of pool as necessary by adjusting travel speed
Check current values carefully; keep short electrode
extension
-
7/27/2019 GMAW WELDING
52/152
22 - 52
Porosity
Most common defect in welds
Exists on face of weld readily detected
Below surface must be determined byradiograph ultrasonic or other testing methods
Causes of most porosity are contamination byatmosphere, change in physical qualities of
filler wire, and improper welding technique Also caused by entrapment of gas evolved
during weld metal solidification
-
7/27/2019 GMAW WELDING
53/152
22 - 53
Causes of Porosity
Travel so fast that part or all of shielding gaslost, and atmospheric contamination occurs
Shielding gas flow rate too low so gas does not
fully displace all air in arc area
Shielding gas flow rate too high drawing airinto arc area and causing turbulence
Shielding gases must be of right type for metalbeing welded
Shielding gases must be pure and dry
-
7/27/2019 GMAW WELDING
54/152
22 - 54
Causes of Porosity
Gas shield may be blown away by wind or
drafts
May be defects in gas system
Excessive voltage for arc required can cause
loss of its deoxidizers and alloying elements
Foreign material such as oil, dirt, rust, grease,and paint on wire or material to be welded
Improper welding techniques are used
-
7/27/2019 GMAW WELDING
55/152
-
7/27/2019 GMAW WELDING
56/152
22 - 56
Other Defects
Weld cracking
Comes from compositional problems, poor joint design, andpoor welding technique
Prevent by making sure filler metal has composition
suitable for base metal and providing for expansion andcontraction forces during welding
Irregular weld shape
Include too wide, too narrow, excessively convex or
concave surface and those with coarse, irregular ripples Caused by poor gun manipulation, too fast or too slow
speed of gun travel, too high or too low current, improperarc voltage, improper shielding gas, improper extension
-
7/27/2019 GMAW WELDING
57/152
22 - 57
Undercutting
Cutting away of base material along toes of weld
May be present in cover pass weld bead or inmultipass welding
Condition usually result of high current, high voltage,excessive travel speed, low wire-feed speed, poor guntechnique, improper gas shielding, or wrong fillerwire
To correct, move welding gun from side to side injoint, and hesitate at each side before returning toopposite side
-
7/27/2019 GMAW WELDING
58/152
22 - 58
Safe Practices
Safety most important consideration to both
worker and employer
Welding no more dangerous than other
industrial operations
Safety precautions and protective equipment
required for MIG/MAG process essentially
same as for any other electric welding process
-
7/27/2019 GMAW WELDING
59/152
22 - 59
Eye, Face, and Body Protection
Welding helmets and protective clothing
necessary
Radiant energy produced by gas-shielded
process 5 to 30 times more intense than
produced by shielded metal arc welding
Lowest intensities produced by gas tungsten arc
Highest by gas metal arc
Argon produces greater intensities than helium
-
7/27/2019 GMAW WELDING
60/152
22 - 60
Clothing Regulations
Standard arc welding helmets with lenses ranging inshade from no. 6 for work using up to 30 amperes tono. 14 for work using more than 400 amperes should
be worn
Arc should never be viewed with the naked eye whenstanding closer than 20 feet
Skin should be covered completely to prevent burnsand other damage from ultraviolet light
Back of the head and neck should be protected fromreflected radiation
Gloves should always be worn
l hi l i
-
7/27/2019 GMAW WELDING
61/152
22 - 61
Clothing Regulations
Shirts should be dark in color to reduce
reflections
Have tight collar and long sleeves
Leather, wool and aluminum-coated cloth can
withstand action of radiant energy reasonably welld
dli f G C li d
-
7/27/2019 GMAW WELDING
62/152
22 - 62
Handling of Gas Cylinders
Stored cylinders should be in protected area
away from fire, cold, and grease and away
from general shop activity
Cylinders must be secured to equipment to
prevent their being knocked over
Proper regulators and flowmeters must be used
with each special type of cylinder
H dli f G C li d
-
7/27/2019 GMAW WELDING
63/152
22 - 63
Handling of Gas Cylinders
Cylinders should not be dropped, used as
rollers, lifted with magnets, connected into
electric circuit, or handled in any other way
that might damage cylinder or regulator
When cylinders empty, should be stored in
upright position with valve closed
V il i
-
7/27/2019 GMAW WELDING
64/152
22 - 64
Ventilation
Ozone generated in small quantities, generallybelow allowable limits of concentration
Nitrogen dioxide also present around area of
arc in quantities below allowable limits Carbon dioxide shielding may create hazard
from carbon monoxide and carbon dioxide if
welders head in path of the fumes or ifwelding done in confined space
Special ventilation should be provided
V il i
-
7/27/2019 GMAW WELDING
65/152
22 - 65
Ventilation
Eye, nose, and throat irritation can be produced when
welding near such degreasers as carbon tetrachloride,
trichlorethylene, and perchloroethylene
Break down into phosgene under action of powerful raysfrom arc
Locate degreasing operations far away from welding
activities
Much of welding smoke and fumes can be engineeredout of GMAW arc by use of higher argon percent and
pulse-spray mode of transfer
V il i
-
7/27/2019 GMAW WELDING
66/152
22 - 66
Ventilation
During welding, certain metals emit toxicfumes that may cause respiratory irritation andstomach upsetMost common toxic metal vapors given off by
welding of lead, cadmium, copper, zinc, andberyllium
Fumes can be controlled by general ventilation,local exhaust ventilation, or respiratory protective
equipment Welding guns can be purchased with smoke
extractor capability
El i l S f
-
7/27/2019 GMAW WELDING
67/152
22 - 67
Electrical Safety
Hazard less than that with shielded meal arc
process
Open circuit voltage considerably less
Electrical maintenance should be done only by
qualified person
NEVER worked on in electrical HOT condition
Wi F d S f t
-
7/27/2019 GMAW WELDING
68/152
22 - 68
Wire-Feeder Safety
Turn power off when aligning and adjustingdrive rolls
Avoid pinch points when working near drive
rolls Remember force being applied to wire
sufficient to push it through your hand or other
body parts Never let exposed wire come in contact with or
be pointed at your body
Fi S f t
-
7/27/2019 GMAW WELDING
69/152
22 - 69
Fire Safety
Welding should not be done near areas whereflammable materials or explosive fumes present
Paint spray or dipping operations should not belocated close to any welding operation
Combustible material should not be used for floors,walls, welding tables, or in immediate vicinity ofwelding operation
When welding on containers that have previouslycontained combustible materials, special precautionsshould be taken
Use hot work permit as required
C d U f E i t
-
7/27/2019 GMAW WELDING
70/152
22 - 70
Care and Use of Equipment
Do not push gun into arc like an electrode
Wire feeder pushes wire into arc
Either push or drag travel angle can be used
If possible, welding should be done in flat weldingposition to take advantage of increased penetrationand deposition rate characteristic of the MIG/MAG
process
Small fillets and butt welds should be positioned soarc can run slightly downhill
Equipment has to be kept clean, in proper adjustment,and in good mechanical condition
D d P h M th d
-
7/27/2019 GMAW WELDING
71/152
22 - 71
Drag and Push Methods
Produces large wide beads Produces flatter bead shape
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
C f N l
-
7/27/2019 GMAW WELDING
72/152
22 - 72
Care of Nozzles
Keep the gun nozzle, contact tube, and wire-feeding system clean to eliminate wire-feedingstoppages
Nozzle is natural spatter collector If spatter builds up thick enough, it can actually
bridge gap and electrically connectinsulated nozzle to contact tube
To remove spatter, use soft, blunttool for prying
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
C f N l
-
7/27/2019 GMAW WELDING
73/152
22 - 73
Care of Nozzles
Spatter almost falls out by itself if nozzle kept
clean, shiny and smooth
Antispatter compound may be applied to gun
nozzle and contact tube end
Do not clean by tapping or pounding on solid
object
Bends gun nozzles, damages threads and high
temperature insulation in nozzle can break
C f C t t T b
-
7/27/2019 GMAW WELDING
74/152
22 - 74
Care of Contact Tubes
Transfers welding current to electrode wire
Hole has to be big enough to allow wire with slight
cast to pass through easily
Wire wears hole to oval shape Wire slides more easily, but transfer of current not as good
and arcing in tub results
Spatter flies up into bore and wire slows down because of
friction
Must be replace; secure tightly in gun and check
periodically for tightness
C f Wi F d C bl
-
7/27/2019 GMAW WELDING
75/152
22 - 75
Care of Wire-Feed Cables
Wire-feed conduit flexible steel tube that does
not stretch
Main source of friction in wire-feed system
Should be kept clean and straight as possible
Clean with dry compressed air
Lubricate with dry powdered graphite reduces
friction
Clean every time spool or coil changes
Bird Nesting
-
7/27/2019 GMAW WELDING
76/152
22 - 76
Bird Nesting
Wire coils sideways between wire-feed cable
and drive rolls
Prevent by accurate alignment of wire-feed
cable inlet guide
Aligned exactly with rollers so wire does not have
to make reverse bend
Notch in drive rolls must be in perfect alignment toprovide smooth passage for wire
Cleanliness of Base Metal
-
7/27/2019 GMAW WELDING
77/152
22 - 77
Cleanliness of Base Metal
Clean area thoroughly before welding
Remove all rust, scale, burned edges and
chemical coatings
Gas producers
Porosity is result
Intense heat of arc burns away some of the
contaminants
Arc Blow
-
7/27/2019 GMAW WELDING
78/152
22 - 78
Arc Blow
Arc blown to one side or other by condition of pull
and counter-pull as magnetic field is distorted
Ionized gases carrying arc from end of electrode wire to
work act as flexible conductor with magnetic field around it When placed in location such as corner of joint or end of
plate, magnetic field distorted and pulls in another direction
Magnetic field tries to return to state of equilibrium
Does not occur with a.c. welding arcs Forces exerted by magnetic field reversed 120 times per
second thus keeping magnetic field in equilibrium
Connecting Work to Minimize
-
7/27/2019 GMAW WELDING
79/152
22 - 79
gArc Blow
Suggestions to shorten trial-and-error process
to correct or minimize arc blow
Attach work lead or leads directly on
workpiece if possible
Connect both ends of long, narrow weldments
Use electrical conductors of proper length
Weld away from work connection
Connecting Work to Minimize
-
7/27/2019 GMAW WELDING
80/152
22 - 80
gArc Blow
On parts that rotate, use rotating workconnection or allow work cable to wind up nomore than one or two turns
In making longitudinal welds on cylinders, usetwo work connectionsone on each side of theseam as close as possible to point of starting
If multiple work connections necessary, makesure cables are same size and length and haveidentical terminals
Connecting Work to Minimize
-
7/27/2019 GMAW WELDING
81/152
22 - 81
Arc Blow
On multiple-head installations, all heads shouldweld in same direction and away from workconnection
Use individual work circuits on multiple-headinstallations
Do not place two or more arcs close to one
another on weldments that are prone tomagnetic disturbance with one arc such astubes or tanks requiring longitudinal seams
Setting Up Equipment
-
7/27/2019 GMAW WELDING
82/152
22 - 82
Setting Up Equipment
Constant voltage d.c. power source
Wire-feeding mechanism with controls and spooled orreeled filler wire mounted on fixture
Gas-shielding system consisting of one or more
cylinders of compressed gas, pressure-reducingcylinder regulator, flowmeter assembly
Combination gas, water, wire, and cable controlassembly and welding gun of correct type and size
Connecting hoses and cables, work lead, and clamp Face helmet, gloves, sleeves (if necessary), and
assortment of hand tools
Assumed Safety Precautions
-
7/27/2019 GMAW WELDING
83/152
22 - 83
Assumed Safety Precautions
Welding equipment installed properly
Welding machine in dry location, and no water
on floor of welding booth
Welding booth lighted and ventilated properly
All connections tight, and all hoses and leads
arranged so they cannot be burned or damaged
Gas cylinders securely fastened so they cannot
fall over and not part of electrical circuit
Starting Procedure
-
7/27/2019 GMAW WELDING
84/152
22 - 84
Starting Procedure
1. Check power cable connections; connect guncable to proper welding terminal on weldingmachine and work cable end connected to
proper terminal on welding machine2. Start welding machine by pressing onbutton
or, in case of engine drive, start engine
3. Turn on wire-feed unit
4. Check gas-shielding supply system
5. Check water flow if gun water cooled
Starting Procedure
-
7/27/2019 GMAW WELDING
85/152
22 - 85
Starting Procedure
5. Set wire-feed speed control for type and size of fillerwire and for job
6. Voltage rheostat should be set to conform to typeand thickness of material being welded, diameter offiller wire, the type of shielding gas, and type of arc
7. Adjust for proper electrode extension beyondcontact tube
8. To start arc, touch end of electrode wire to properplace on weld joint, usually just ahead of weld bead,with current shut off; lower helmet and press guntrigger on torch
Shutting Down the Equipment
-
7/27/2019 GMAW WELDING
86/152
22 - 86
Shutting Down the Equipment
1. Stop welding and release gun trigger
2. Return feed speed to zero position
3. Close gas outlet valve in top of gas cylinder
4. Squeeze welding gun trigger, hold it down,and bleed gas lines
5. Close gas flowmeter valve until finger-tight
6. Shut off welding machine and wire feeder
7. Hang up welding gun and cable assembly
Starting the Weld
-
7/27/2019 GMAW WELDING
87/152
22 - 87
Starting the Weld
Running start
Arc started at beginning of weld
Electrode end put in contact with base metal
Trigger on torch pressed Tends to be too cold at beginning of weld
Scratch start
Arc struck approximately 1 inch ahead of beginning of weld
Arc quickly moved back to starting point of weld, direction
of travel reversed, and weld started
Arc may also be struck outside of weld area on starting tab
Finishing the Weld
-
7/27/2019 GMAW WELDING
88/152
22 - 88
Finishing the Weld
Arc should be manipulated to reduce penetration
depth and weld pool size when completing weld bead
Decreases final shrinkage area
Reduction accomplished by rapidly increasing speed ofwelding for approximately 1 to 2 inches of weld length
Trigger released, stopping wire feed and interrupting
welding current
Gun trigger can be turned on and off several times atend of weld to fill crater
Gun Angle
-
7/27/2019 GMAW WELDING
89/152
22 - 89
Gun Angle
Push angle of 5to 15generally employed whenwelding in flat position
Take care push angle not changed as end of weldapproached
Work angle equal on all sides when welding uniformthicknesses
Welding in horizontal position, point gun upwardslightly
Thick-to-thin joints, direct arc toward heavier section
Slight drag angle may help when welding thinsections
Control of Arc
-
7/27/2019 GMAW WELDING
90/152
22 - 90
Control of Arc
Arc voltage controls penetration, bead contour,
and such defects as undercutting, porosity and
weld discontinuities
Arc should be occasionally noisy for most
applications of spray arcs
Process and Equipment Problems
-
7/27/2019 GMAW WELDING
91/152
22 - 91
Process and Equipment Problems
Study tables 22-6 which lists problems with
MIG/MAG short arc process and their
correction
Table 22-7 lists problems with MIG/MAG
process and equipment, their causes, and
possible remedies
Practice Jobs
-
7/27/2019 GMAW WELDING
92/152
22 - 92
Practice Jobs
Practice gas metal arc welding on mild steel,
aluminum, and stainless steel
Specifications given in Job Outline in order
assigned by instructor
Beyond these job, practice other forms of joints
in all positions
Use various types and sizes of filler wire and
different shielding gases
Precautions to Observe WhenDoing Practice Jobs
-
7/27/2019 GMAW WELDING
93/152
22 - 93
Doing Practice Jobs
Avoid excessive current values
Check your welding speed
Make sure that gas flow adequate
Keep wire centered in gas pattern and in center ofjoint; make sure correct electrode angle maintained atall times
Select proper filler wire for material being welded andfor such situations as rust, scale, and excessive oxygen
When welding from both sides of plate, be sure rootpass on first side deeply penetrated by root pass onsecond side
MIG/MAG Welding ofC b St l
-
7/27/2019 GMAW WELDING
94/152
22 - 94
Carbon Steel
Bulk of all welding done on carbon steel
MIG/MAG welding on increase
Welders find it relatively easy to master
Consistently produces sound welds at high rate of
speed
Groove Welds:J b 22 J1 d J2
-
7/27/2019 GMAW WELDING
95/152
22 - 95
Jobs 22-J1 and J2
Plate up to 1/8" thick may be butt welded with
square edges with root opening of 0 to 1/16"
Heavier plate, 3/16 and 1/4 inch may be
welded without beveling edges if 1/16 to 3/32"
opening provided
Bead should be wider than root spacing for
proper fusion
Two passes, one from each side usually needed
Groove Welds:J b 22 J1 d J2
-
7/27/2019 GMAW WELDING
96/152
22 - 96
Jobs 22-J1 and J2
For code welding, plate thicknesses from 3/16to 1" should be beveled60 single- or double-V without root face
recommended
Root opening of 0 to 1/16" should be maintainedWider root openings may be provided for double-V
joints
Single-V grooves backing pass from reverse side
generally required Less distortion when welding from both sides
of joint
Groove Welds:J b 22 J1 d J2
-
7/27/2019 GMAW WELDING
97/152
22 - 97
Jobs 22-J1 and J2
Open root joint should be run using short
circuit or pulse spray for ferrous metals
Practice 3G using both uphill and downhill
techniques
U-grooves used on plate thicker than 1 inch
Root spacing between 1/32 and 3/32" maintained
Root face of 3/32" or less to assure penetration
Requires less filler metal than V groove butt joint
Groove Welds:J b 22 J1 d J2
-
7/27/2019 GMAW WELDING
98/152
22 - 98
Jobs 22-J1 and J2
Argon-oxygen mixture containing 1-5% oxygen
recommended for spray arc welding
Oxygen improves flow of weld metal and reduces tendency
to undercut
Argon with 10% CO2sometimes used
Carbon dioxide at 100% used by arc not true spray arc
Popular for MAG small wire welding
Short arc welding of carbon steel uses mixture of 75%
argon and 25% carbon dioxide
Fillet Welds: Jobs 22-J3-J10
-
7/27/2019 GMAW WELDING
99/152
22 - 99
Fillet Welds: Jobs 22 J3 J10
Used in T-joints, lap joints, and corner joints
Deposit rate and rate of travel high with deep
penetration
Permits smaller fillet welds than with stick electrodewelding
Position of nozzle and speed of welding important
Welding may be single pass or multipass Multipass may be done with stringer or weave beads
Each pass must be cleaned carefully
Inspection and Testing
-
7/27/2019 GMAW WELDING
100/152
22 - 100
Inspection and Testing
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Outside corner joint in steel plate welded with gas metalarc welding process in the flat position.
Penetration through back side of corner joint welded
in the flat position.
Inspection and Testing
-
7/27/2019 GMAW WELDING
101/152
22 - 101
Inspection and Testing
Fillet weld on lap joint in steel platewelded with gas metal arc welding
process in 2F position.
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Fillet weld on lap joint in steel plate weldedwith gas metal arc welding process in 3F
position, downhill. Note porosity caused
by poor gas shielding.
Inspection and Testing
-
7/27/2019 GMAW WELDING
102/152
22 - 102
Inspection and Testing
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Fillet weld on T-joint welded
in the 2F position with thegas metal arc welding
process in steel plate.
Penetration through back side of a
V-groove butt joint weldedin the 1G position.
The first (root) pass of a V-groove
butt joint welded in the 1G positionwith the gas metal arc welding
process in steel plate.
Fillet and Groove Welding Combination Project:
Job Qualification Test 1
-
7/27/2019 GMAW WELDING
103/152
22 - 103
Job Qualification Test 1
Purpose
Ability to read print
Develop bill of materials
Thermally cut
Fit components together
Tack and weld carbon steel project
Follow instructions found in Fig. 22-26
Fillet and Groove Welding Combination Project:
Job Qualification Test 1
-
7/27/2019 GMAW WELDING
104/152
22 - 104
Job Qualification Test 1
Inspection and testing (visual inspection only) Shall be no cracks or incomplete fusion
Shall be no incomplete joint penetration in groove weldsexcept as permitted for partial joint penetration groove
welds
Undercut shall not exceed lesser of 10% of base metalthickness or 1/32 inch
Frequency of porosity shall not exceed one in each 4 inches
of weld length, and maximum diameter shall not exceed3/32 inch
Welds shall be free from overlap
Only minimal weld spatter shall be accepted
Fillet and Groove Welding Combination
P j t J b Q lifi ti T t2
-
7/27/2019 GMAW WELDING
105/152
22 - 105
Project: Job Qualification Test2
Purpose
Ability to read print
Develop bill of materials
Thermally cut
Fit components together
Tack and weld carbon steel project
Use spray arc mode of metal transfer
Note on Fig. 22-27
Fillet and Groove Welding Combination
Project: Job Qualification Test2
-
7/27/2019 GMAW WELDING
106/152
22 - 106
Project: Job Qualification Test2
Inspection and testing (visual inspection only) Shall be no cracks or incomplete fusion
Shall be no incomplete joint penetration in groove weldsexcept as permitted for partial joint penetration groove
welds
Undercut shall not exceed lesser of 10% of base metalthickness or 1/32 inch
Frequency of porosity shall not exceed one in each 4 inchesof weld length, and the maximum diameter shall not exceed3/32 inch
Welds shall be free from overlap
Only minimal weld spatter shall be accepted
Groove Weld Project: JobQualification Test 3
-
7/27/2019 GMAW WELDING
107/152
22 - 107
Qualification Test 3
Project
Ability to read print
Fit components together
Tack and weld carbon steel unlimited thickness test
plate
Using spray arc mode of metal transfer
Instructions in notes in Fig. 22-28
Inspection and Testing
-
7/27/2019 GMAW WELDING
108/152
22 - 108
p g
After tacking, have it inspected
After complete welding, use visual inspectionand cut specimens for bend testing
Use side bend test procedures and check: Testing criteria:
No cracks or incomplete fusion
No incomplete joint penetration in groove weldsexcept as permitted for partial joint penetrationgroove welds
Inspection and Testing
-
7/27/2019 GMAW WELDING
109/152
22 - 109
p g
Testing criteria (cont.):
Undercut shall not exceed lesser of 10 percent of
base metal thickness or 1/32 inch
Frequency of porosity shall not exceed one in each4 inches of weld length and maximum diameter
shall not exceed 3/32 inch
Welds shall be free from overlap
Only minimal weld spatter shall be accepted
Side Bend Acceptance Criteria as Measured
on Convex Surface of Bend Specimen
-
7/27/2019 GMAW WELDING
110/152
22 - 110
on Convex Surface of Bend Specimen
No single indication shall exceed 1/8 inch measured in
any direction on surface
Sum of greatest dimensions of all indications on
surface, which exceed 1/32 inch, but are less than orequal to 1/8 inch, shall not exceed 3/8 inch
Cracks occurring at corner of specimens shall not be
considered unless there definite evidence that they
result from slag inclusions or other internaldiscontinuities
MIG Welding of Aluminum
-
7/27/2019 GMAW WELDING
111/152
22 - 111
g
Readily joined by welding, brazing, soldering,adhesive bonding, and mechanical fastening
Lightweight
Alloyed readily with many other metals
Highly ductile and retains ductility at subzerotemperatures
High resistance to corrosion, no colored salts, not toxic
Good electrical and thermal conductivity High reflectivity to both heat and light
Nonsparking and nonmagnetic
MIG Welding of Aluminum
-
7/27/2019 GMAW WELDING
112/152
22 - 112
g
Easy to fabricate
May be given wide variety of mechanical,electrochemical, chemical and paint finishes
Needs high heat input for fusion welding Aluminum and its alloys rapidly develop oxide
film when exposed to air (melting point 3600F)
Must be removed during welding Removed by fluxes, action of arc in inert gas
atmosphere or mechanical and chemical means
MIG Welding of Aluminum
-
7/27/2019 GMAW WELDING
113/152
22 - 113
g
MIG and TIG replaced stick electrode
welding for aluminum and its alloys
Small percentage still using stick electrodes
Type of joint and position of welding
determines process to used on thicknesses
1/8 inch and under
Factors that Make Gas Metal Arc Welding
Desirable Joining Process for Aluminum
-
7/27/2019 GMAW WELDING
114/152
22 - 114
Desirable Joining Process for Aluminum
Cleaning time reduced because there no flux on
weld
Absence of slag in weld pool eliminates
possibility of entrapment
Weld pool highly visible due to absence of
smoke and fumes
Welding can be done in all positions
Joint Preparation
-
7/27/2019 GMAW WELDING
115/152
22 - 115
p
Designed like those for steel
Narrower joint spacing and lower welding currentsused
Foreign substances must be removed
Wiped off or removed by vapor degreasing
Oxide film removed by chemical and mechanical cleaningmethods
Weld as soon as possible before oxide film has chanceto form again
Sheared edges can also cause poor quality welds
Shielding Gas
-
7/27/2019 GMAW WELDING
116/152
22 - 116
g
Argon preferred for welding aluminum platethicknesses up to 1 inch
Plate thicknesses 1-2 inches may use: Pure argon, mixture of 50% argon and 50% helium, or
mixture of 75% argon and 25% helium Helium provides high heat and argon excellent cleaningaction
Plate thicknesses from 2-3 inches Mixture of 50% argon and 50% helium or 25% argon and
75% helium Plate thicknesses greater than 3 inches
Mixture of 25% argon and 75% helium
Spray Arc Welding
-
7/27/2019 GMAW WELDING
117/152
22 - 117
p y g
Weld metal deposited continuously
More arc energy and greater heat provided for melting
filler wire and base material
Helium, helium-argon mixtures and argon used asshielding gases
Choice dependent upon type of material, thickness and
welding position
Welding can be done in all positions
GMAW-P very effective when welding aluminum
Out-of-Position Welding
-
7/27/2019 GMAW WELDING
118/152
22 - 118
g
Horizontal position
Care must be taken to penetrate to root of joint
when welding butt joints and T-joints
Overheating in any one area causes sagging,undercutting or melt-through to back of joint
Weld metal should be directed against upper plate
In multipass welding, be sure fusion betweenpasses
Horizontal Position
-
7/27/2019 GMAW WELDING
119/152
22 - 119
Welding T-joint in aluminum
plate in 2F position
Welding V-groove butt joint
in aluminum plate in 2G position.
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Out-Of-Position Welding
-
7/27/2019 GMAW WELDING
120/152
22 - 120
Vertical position
Travel-up technique on fillet and groove welds
Do not use too high welding current nor deposit too large
weld bead
Slight side-to-side motion helpful
Overhead position
No problem with fillet and groove welds
Welding current and travel speed lower than flat position Gas flow rate higher because gas has tendency to leave area
Somewhat awkwardassume relaxed position as possible
Out-Of-Position Welding
-
7/27/2019 GMAW WELDING
121/152
22 - 121Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Welding V-groove butt joint in
aluminum plate in 3G position, uphill.
Welding T-joint in aluminum
plate in 3F position, uphill.
Butt Joints: Jobs 22-J11 and J12
-
7/27/2019 GMAW WELDING
122/152
22 - 122
Easy to design Require minimum of base material
Perform better under fatigue loading
Require accurate alignment and edge preparation Usually necessary to bevel edge on thicknesses of "
or more to permit root pass penetration
On heavier plate, chipping back side and welding back side
with one pass Sections with different thicknesses should be beveled before
welding
Lap Joints: Job 22-J13
-
7/27/2019 GMAW WELDING
123/152
22 - 123
More widely used on aluminum alloys than on
other materials
Use double-welded, single-lap joints in
thicknesses of aluminum up to "
Require no edge preparation
Easy to fit
Require less jigging than butt joints
T-Joints: Jobs 22-J14-J16
-
7/27/2019 GMAW WELDING
124/152
22 - 124
Seldom require edge preparation on material " orless in thickness
Fully penetrated if weld fused into root of joint
Easily fitted and normally require no back chipping Jigging usually quite simple
Better to put small continuous fillet weld on each side
of joint rather than one large weld on one side
Continuous fillet welding recommended over
intermittent welding for longer fatigue life
Edge and Corner Joints
-
7/27/2019 GMAW WELDING
125/152
22 - 125
Economical from standpoint of preparation,
base metal used, and welding requirements
Harder to fit up
Prone to fatigue failure
Edges do not require preparation
Inspection and Testing
-
7/27/2019 GMAW WELDING
126/152
22 - 126
Inspect carefully for defects
Use same inspection and testing procedures
used previously
Look for surface defects
High quality welds in aluminum can be
produced only if proper welding conditions and
good cleaning procedures been established and
maintained
Effect of Current onAluminum Welds
-
7/27/2019 GMAW WELDING
127/152
22 - 127
Aluminum Welds
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Aluminum weld bead
made with current
too high
Aluminum weld bead
made with current
too low
Aluminum weld bead
made with
correct current
Kaiser Aluminum & Chemical Corporation Kaiser Aluminum & Chemical Corporation Kaiser Aluminum & Chemical Corporation
Main Causes of Cracking inAluminum Welds
-
7/27/2019 GMAW WELDING
128/152
22 - 128
Aluminum Welds
Generally in crater or longitudinal form Crater cracks
Cause: arc broken sharply and leaves crater
Cure: manipulate gun properly Longitudinal cracks caused by
Incorrect weld metal composition
Improper welding procedureHigh stresses imposed during welding by poor joint
design or poor jigging
Main Causes of Porosity inAluminum Welds
-
7/27/2019 GMAW WELDING
129/152
22 - 129
u u We ds
Hydrogen in the weld area
Moisture, oil, grease, or heavy oxides in the weld area
Improper voltage or arc length
Improper or erratic wire feed
Contaminated filler wire (Use as large a diameter as
possible and GMAW-P if lower heat is needed.)
Leaky gun Contaminated or insufficient shielding gas
Major Causes of Incomplete Fusion of
Weld Metal with Base Metal
-
7/27/2019 GMAW WELDING
130/152
22 - 130
Weld Metal with Base Metal
Incomplete removal of oxide film beforewelding
Unsatisfactory cleaning between passes
Insufficient bevel or back chipping
Improper amperage (WFS) or voltage
Causes of Inadequate Penetration at Root
of Weld and Into Side Walls of Joint
-
7/27/2019 GMAW WELDING
131/152
22 - 131
Low welding current (WFS)
Improper filler metal size
Improper joint preparation
Too fast travel speeds for the selected wire-
feed speed
Causes of Metallic and Nonmetallic
Inclusions in Aluminum Welds
-
7/27/2019 GMAW WELDING
132/152
22 - 132
Inclusions in Aluminum Welds
Copper inclusions caused by burn-back ofelectrode to contact tube
Metallic inclusions from cleaning weld with
wire brush which leaves bristles in weld
Nonmetallic inclusions from poor cleaning of
base metal
Always use push gun travel angle whenwelding aluminum
Groove Weld Project:Job Qualification Test 4
-
7/27/2019 GMAW WELDING
133/152
22 - 133
Q
PurposeAbility to read print
Fit components together
TackWeld aluminum test plates
Using spray arc mode of metal transfer
Inspection and testing
Visual inspection
Perform side bend tests
-
7/27/2019 GMAW WELDING
134/152
22 - 134Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Performance Qualification
Test GMAW Spray Transfer, Aluminum
3G and 4G Positions
AWS SENSE
Shown only to illustrate what a qualification test would
look like. Follow it and inspect and test as listed in text.
MAG Welding of StainlessSteel
-
7/27/2019 GMAW WELDING
135/152
22 - 135
Heat and corrosion resistant alloyAlways contains high percentage of chromium in
addition to nickel and manganese
Excellent strength-to-weight ratios Many alloys possess high degree of ductility
Widely used in products such as tubing, piping,kitchen equipment, ball bearings
Supplied in sheets, strip, plate, shapes, tubing,pipe and wire extrusions
MAG Welding of StainlessSteel
-
7/27/2019 GMAW WELDING
136/152
22 - 136
Lower rate of thermal conductivity than carbon steel Heat retained in weld zone longer
Thermal expansion greater than carbon steel Causes greater shrinkage stresses and warpage
Has tendency to undercut All standard forms of joints used in fabrications
Copper backing bars necessary for welding sectionsup to 1/16" thick
No air must be permitted to reach underside of weldwhile weld pool solidifying (air weakens it) If no backing bar, argon should be used as purge gas shield
Advantages of MAG WeldingStainless Steel
-
7/27/2019 GMAW WELDING
137/152
22 - 137
Absence of slag-forming flux reduces cleaningtime and makes it possible to observe weldpool
Continuous wire feed permits uninterruptedwelding
MAG lends itself to automation
Welding may be performed with short-circuiting, spray, or pulsed spray modes oftransfer
Spray Arc Welding
-
7/27/2019 GMAW WELDING
138/152
22 - 138
Electrode diameters as large as 3/32" can be used forstainless steel 1/16" wire used with high current to create spray arc
transfer of metal
DCEP used for most stainless-steel welding
Most common gas: mixture of Ar and 1 to 2% O Recommended for single-pass welding
Push travel angle should be employed on plate "thick or more
Gun should be moved back and forth in direction oftravel and slightly from side to side
Short Arc Welding (GMAW-S)
-
7/27/2019 GMAW WELDING
139/152
22 - 139
Requires low current ranging form 20 to 175 amperes;low voltage of 12 to 20 volts, small diameter wires
Metal transfer occurs when filler wire short circuits
with base metal Ideally suited for most stainless-steel welding on
thicknesses from 16 gauge to 1/16"
Also for first pass in which fitup is poor or copper
backing unsuitable Very desirable in vertical and overhead positions for
first pass
Short Arc Welding (GMAW-S)
-
7/27/2019 GMAW WELDING
140/152
22 - 140
For stainless steel in light gauges, triplemixture of gas gives good arc stability and
excellent coalescence
90% helium, 7 % argon and 2 % carbon dioxideProduces small heat-affected zone that eliminates
undercutting and reduces distortion
Does not lower corrosion resistanceFlow rates must be increased because of lower
density of helium
Pulse Spray Arc (GMAW-P)
-
7/27/2019 GMAW WELDING
141/152
22 - 141
Can be done with lower current levels andhigher wire-feed speeds
Can be used on all thickness ranges
Spray-type gas: 1 and 2% oxygen withremainder being argon most common
Weld more fluid and flows well because arc onall the time
Spatter reduced on thin base metals ascompared to short-circuiting mode of transfer
Hot Cracking
-
7/27/2019 GMAW WELDING
142/152
22 - 142
Tendency of some stainless steels
More welding passes needed
Stringer beads recommended instead of weave
Reduce contraction stresses and cooling more rapid
Can reduce when welding sections 1 inch or
thicker by preheating to 500F
Also reduce by GMAW-S or P welding
Stainless-Steel Sensitization
-
7/27/2019 GMAW WELDING
143/152
22 - 143
Carbide precipitation Sensitizing chromium out of individual grains of austenitic
types of stainless steel
Occurs most readily in 1,200F heat range
To reduce situation
Use GMAW process with its rapid speed and high
deposition rate
Use stabilized and low carbon grades of stainless steel Using proper filler metals such as ER308L which is low in
carbon
Inspection and Testing:Jobs 22-J17-J23
-
7/27/2019 GMAW WELDING
144/152
22 - 144
Inspect each weld carefully for defects
Fillet weld on lap joint in 3/8" stainless-steel plate weldedin the 1F position with the gas metal arc welding process.
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Inspection and Testing:Jobs 22-J17-J23
-
7/27/2019 GMAW WELDING
145/152
22 - 145
Fillet weld on T-joint in 3/8" stainless-steel platewelded in 1F position with gas metal arc welding process.
Fillet weld on T-joint in 3/8" stainless-steel plate
welded in 2F position with gas metal arc welding process.
Copyright The McGraw-Hill Companies, Inc. Permission required for reproduction or display.
Copper and Its Alloys
-
7/27/2019 GMAW WELDING
146/152
22 - 146
May be welded successfully by gas metal arc process Electrolytic copper can be joined by using special
techniques, but weldability not good
Various grades of deoxidized copper readily weldable
with MIG process Deoxidized filler wires necessary
Filler wires of approximately matching chemistryused
Argon preferred shielding gas for material 1" andthinner Flow of 50 cubic feet per hour sufficient
Heavier material uses 65% and 35% argon
Copper and Its Alloys
-
7/27/2019 GMAW WELDING
147/152
22 - 147
Joint design like any other metalSteel backup necessary for sheets 1/8" or thinner
Welding currents on high side required
Preheat not required when welding " or less Always provide good ventilation when welding
copper and its alloys
Beryllium-copper alloy dangerous
Copper and Its Alloys
-
7/27/2019 GMAW WELDING
148/152
22 - 148
GMAW-BVariation of GMAW process where B indicates
brazing or just MIG brazing
Uses silicon-bronze type electrode with inertshielding with Argon 100% most common
Main application for coated carbon steel sheet
metal (light gauge)
Zinc coating applied for corrosion resistance
Base metal not melted (hence brazing operation)
Nickel and Nickel-CopperAlloys
-
7/27/2019 GMAW WELDING
149/152
22 - 149
Can be welded using gas metal arc process Remove all foreign material in vicinity since
susceptible to severe embrittlement andcracking when come in contact with foreign
materials Argon generally preferable for welding up to
about 3/8 inch in thicknessAbove that thickness, argon-helium mixtures
usually more desirable
Joint preparation like other metals
Magnesium
-
7/27/2019 GMAW WELDING
150/152
22 - 150
Silvery white metal, two-thirds weight of aluminumand one-quarter weight of steel
Melting point of 1,204F
Strength-to-weight ratio high when compared to steel
Welding techniques like aluminum
Rate of expansion greater
Care taken that surface clean before welding
Arc characteristics of helium and argon withmagnesium different than with other metals
Argon recommended in most cases
Titanium
-
7/27/2019 GMAW WELDING
151/152
22 - 151
Bright white metal that burns in air
Only element that burns in nitrogen
Melting point of about 3,500F
Most important compound titanium dioxide
Used extensively in welding electrode coatings
Used as stabilizer in stainless steel
Zirconium
-
7/27/2019 GMAW WELDING
152/152
Bright gray metal
Melting point above 4,500F
Very hard and brittle and readily scratches
glass
Used in hard-facing materials
Often alloyed with iron and aluminum
Argon or helium-argon mixtures used for gas