/INSPECTION CERTIFICATE DATE :2014-03-24 1PAGE :CERTIFICATE NO. :BYYF1157

260-100, FUNOO, KAINAN, JAPANWAKAYAMA WORKS (KAINAN)

NIPPON STEEL & SUMITOMO METAL CORPORATION

HEAD OF DEPARTMENT

WE HEREBY CERTIFY THAT THE MATERIAL DESCRIBED HEREIN HAS BEEN MADE IN ACCORDANCE WITH THE RULES OF THE CONTRACT.

QUALITY ASSURANCE DEPARTMENT317517K14<An Important Message To Our Customers>

This certification is intended only for products listed. Modification to or unauthorized use of this certification

INTERTEK INDUSTRY SERVICES JAPAN LIMITED

8

is strictly prohibited. Offences may be regarded as forgery of documents and be subject to criminal prosecution.If you have any questions on this certification, you can contact us by facsimile or e-mail as shown below;Fax. No. : +81-3-6867-4926 E-mail:[email protected]

CUSTOMER :STATOIL ASA

ORDER NO. :RFP-201311138(13-MSCT-10-071633)

SHIPPER :SUMITOMO CORPORATION 057 KEN 4186/2 3P1XS049601

COMMODITY :SEAMLESS STEEL TUBING WITH VAM TOP HC

STANDARD :ISO GROUP2 GR.L80-TYPE 1

SPECIFICATION :TSP-3183R7 DEC.4,2013, TSP-2368R7, TSP-2369R5

MILL WORK NO. :BYYF1157 O.D.:7inch W.T.:29.00lb/ft LENGTH:MIN.10973mm MAX.12192mm

QUANTITY:535pcs. TOTAL LENGTH:6405.46m MASS:276460kg

HEAT NO. :J3L2A86 J3LB677 J3LC743 J4L1765 J4L1772 J4L1B50

PRODUCTS PCS. :16 50 2 5 10 452

HEAT TREATMENT :QUENCHED & TEMPERED

CHEMICAL COMPOSITION(%)

C Si Mn P S Cu Cr Ni Mo Ti B Al

*1 *2 *2 *2 *2 *2

SPEC. MIN. R - - - - - - 80 - - - - -

　　　MAX. R 43 45 190 20 10 35 120 25 - - 2 -

HEAT NO.

J3L2A86 L 24 23 75 13 4 2 95 3 1 30 1 45

P 25 23 73 12 4 1 93 3 1 30 1 41

P 25 23 74 11 4 1 93 3 1 30 1 41

J3LB677 L 25 25 79 13 4 2 96 3 1 30 1 35

P 26 25 77 12 3 1 94 3 2 29 1 32

P 26 25 78 12 3 1 94 3 2 29 1 32

J3LC743 L 26 21 78 11 5 3 95 3 1 32 1 30

P 26 21 77 10 4 2 94 3 1 31 1 26

P 26 21 76 10 4 2 94 3 1 31 1 26

J4L1765 L 26 23 77 9 4 2 94 2 1 27 1 33

P 27 25 76 8 3 2 92 2 1 27 1 29

P 26 25 76 7 4 2 93 2 2 27 1 31

J4L1772 L 25 23 77 9 5 3 95 2 1 32 1 50

P 26 24 78 8 4 2 94 3 1 31 1 46

P 26 24 76 9 4 2 94 2 1 31 1 47

J4L1B50 L 25 25 79 9 5 2 96 3 1 29 1 38

P 25 26 77 9 5 2 94 3 1 28 1 36

P 25 26 77 9 5 2 94 3 1 28 1 35

*1 R:LADLE & PRODUCT ANALYSIS L:LADLE ANALYSIS P:PRODUCT ANALYSIS *2:X1000 OTHER:X100

TENSILE TEST

YS YS TS TS EL

*1 *2 *3 *3 *3 *3 %

SPEC. MIN. HEAT- L B M 552 P 80.0 M 655 P 95.0 17

　　　MAX. LOT NO. L B M 655 P 95.0 M - P - -

HEAT NO.

J3L2A86 707 L B M 589 P 85.4 M 714 P 103.6 31

707 L B M 594 P 86.2 M 712 P 103.3 31

NO.




HEAD OF DEPARTMENT





8


TENSILE TEST

YS YS TS TS EL

*1 *2 *3 *3 *3 *3 %

SPEC. MIN. HEAT- L B M 552 P 80.0 M 655 P 95.0 17

　　　MAX. LOT NO. L B M 655 P 95.0 M - P - -

HEAT NO.

J3LB677 710 L B M 604 P 87.6 M 723 P 104.9 31

710 L B M 595 P 86.3 M 716 P 103.8 31

J3LC743 706 L B M 603 P 87.5 M 713 P 103.4 31

706 L B M 598 P 86.7 M 713 P 103.4 29

J4L1765 709 L B M 585 P 84.8 M 710 P 103.0 31

709 L B M 599 P 86.9 M 718 P 104.1 33

J4L1772 708 L B M 599 P 86.9 M 718 P 104.1 30

708 L B M 603 P 87.5 M 715 P 103.7 31

J4L1B50 701 L B M 590 P 85.6 M 720 P 104.4 32

701 L B M 612 P 88.8 M 733 P 106.3 30

702 L B M 608 P 88.2 M 730 P 105.9 30

702 L B M 610 P 88.5 M 729 P 105.7 30

703 L B M 596 P 86.4 M 723 P 104.9 30

703 L B M 607 P 88.0 M 728 P 105.6 30

704 L B M 592 P 85.9 M 716 P 103.8 31

704 L B M 600 P 87.0 M 725 P 105.2 32

705 L B M 596 P 86.4 M 721 P 104.6 32

705 L B M 604 P 87.6 M 719 P 104.3 31

TYPE OF SPECIMEN:STRIP 25.4mm(1in.) WIDTH *1 SAMPLING DIRECTION L:LONGITUDINAL *2 SAMPLING POSITION B:BASE METAL

*3 UNIT M:MPa P:ksi GAUGE LENGTH:50.8mm(2.0in.) KIND OF YS:0.5% EXTENSION UNDER LOAD

IMPACT TEST(-10.0ﾟC +14.0ﾟF 2mm V-Notch 10X7.50)

*1 *2 *3 *4 *4*3 AVG AVG

SPEC. MIN. HEAT- L B E J *5 F E 48 *5 35 32/48 24/35

　　　MAX. LOT NO. L B E J F E - - -/- -/-

[1] [2] [3] [1] [2] [3]

HEAT NO.

J3L2A86 707 L B E J 189 182 176 F E 182 139 134 130 134

J3LB677 710 L B E J 172 177 184 F E 178 127 131 136 131

J3LC743 706 L B E J 185 164 174 F E 174 136 121 128 128

J4L1765 709 L B E J 162 167 172 F E 167 119 123 127 123

J4L1772 708 L B E J 168 177 166 F E 170 124 131 122 126

J4L1B50 701 L B E J 147 153 149 F E 150 108 113 110 110

702 L B E J 172 163 200 F E 178 127 120 148 132

703 L B E J 158 155 155 F E 156 117 114 114 115

704 L B E J 152 151 162 F E 155 112 111 119 114

705 L B E J 164 169 176 F E 170 121 125 130 125

NO.




HEAD OF DEPARTMENT





8


IMPACT TEST(-10.0ﾟC +14.0ﾟF 2mm V-Notch 10X7.50)

*1 *2 *3 *4 AVG

SPEC. MIN. HEAT- L B S % *6 - -

　　　MAX. LOT NO. L B S % - -

[1] [2] [3]

HEAT NO.

J3L2A86 707 L B S % 100 100 100 100

J3LB677 710 L B S % 100 100 100 100

J3LC743 706 L B S % 100 100 100 100

J4L1765 709 L B S % 100 100 100 100

J4L1772 708 L B S % 100 100 100 100

J4L1B50 701 L B S % 100 100 100 100

702 L B S % 100 100 100 100

703 L B S % 100 100 100 100

704 L B S % 100 100 100 100

705 L B S % 100 100 100 100

[1] [2] [3]: SPECIMEN NO.

ABSORBED ENERGY *5:VALUE OF ONE PIECE/EACH VALUE OF TWO PIECES AVG:AVERAGE VALUE OF ONE SET(3 PIECES)

SHEAR AREA *6:VALUE OF ONE PIECE AVG:AVERAGE VALUE OF ONE SET(3 PIECES)

*1 SAMPLING DIRECTION L:LONGITUDINAL *2 SAMPLING POSITION B:BASE METAL *3 E:ABSORBED ENERGY S:SHEAR AREA

*4 UNIT J:Joule F:ft･lbf %:%

VISUAL & DIMENSIONS: ACCEPTABLE

DRIFT TEST: ACCEPTABLE (O.D.:153.90㎜ SPECIAL LENGTH:914.00㎜)

HYDROSTATIC TEST 51.5MPa(7500psi)X5sec.: ACCEPTABLE

ULTRASONIC EXAMINATION

APPLICABLE STANDARD/REFERENCE: ISO11960 SECTION10.15(L&T L2 NOTCH-OD&ID): ACCEPTABLE

ELECTRO MAGNETIC EXAMINATION

APPLICABLE STANDARD/REFERENCE: ISO11960 SECTION10.15(L&T L2 NOTCH-OD): ACCEPTABLE

ULTRASONIC WALL THICKNESS CHECK & LAMINATION CHECK: ACCEPTABLE

THREAD GAUGING: ACCEPTABLE

STATOIL MATERIAL NO.

304910

TR0048REV.6

EN 10204 3.1

NO.




HEAD OF DEPARTMENT





8


HARDNESS TEST( HRC )

*1*2 *3 *4 *5 *V.A.

SPEC. MIN. B C - 14.0 -

　　　MAX. B C - 23.0 -

OUTER WALL INNER WALLAVG.

HEAT- IMPRESSION NO. IMPRESSION NO.QUAD

HEAT NO. LOT NO. -RANT (1) (2) (3) AVG. (1) (2) (3) AVG.

J3L2A86 707 B C T 17.8 A 18.0 17.6 18.6 18.1 17.4 17.6 17.6 17.5 0.6

707 B C B 18.3 A 17.5 18.2 18.2 18.0 18.6 18.7 18.6 18.6 0.6

J3LB677 710 B C T 18.2 A 18.3 18.3 18.2 18.3 18.0 18.5 17.9 18.1 0.2

710 B C B 18.4 A 18.2 17.9 18.4 18.2 18.3 18.9 18.7 18.6 0.4

J3LC743 706 B C T 18.5 A 18.8 19.0 18.7 18.8 18.2 18.1 18.1 18.1 0.7

706 B C B 18.2 A 17.8 18.1 18.4 18.1 18.0 18.5 18.3 18.3 0.2

J4L1765 709 B C T 18.2 A 18.0 18.2 18.5 18.2 18.4 18.1 18.2 18.2 0.0

709 B C B 17.4 A 16.9 16.6 17.3 16.9 18.0 18.2 17.7 18.0 1.1

J4L1772 708 B C T 18.4 A 18.6 18.6 17.7 18.3 18.9 18.8 17.9 18.5 0.2

708 B C B 17.6 A 18.0 17.4 17.2 17.5 17.9 17.7 17.1 17.6 0.1

J4L1B50 701 B C T 18.0 A 18.1 17.6 18.1 17.9 18.4 18.3 17.6 18.1 0.2

701 B C B 19.1 A 19.3 18.8 19.2 19.1 18.9 19.3 19.0 19.1 0.0

702 B C T 18.7 A 18.9 18.9 19.5 19.1 18.2 18.3 18.3 18.3 0.8

702 B C B 19.0 A 19.3 19.2 19.3 19.3 18.4 19.1 18.5 18.7 0.6

703 B C T 19.0 A 19.2 19.1 19.1 19.1 19.3 19.0 18.6 19.0 0.1

703 B C B 18.8 A 19.0 18.8 18.6 18.8 19.1 18.7 18.6 18.8 0.0

704 B C T 18.8 A 18.9 18.6 19.0 18.8 18.9 19.2 18.0 18.7 0.1

704 B C B 18.0 A 17.7 17.5 18.1 17.8 18.1 18.5 17.9 18.2 0.4

705 B C T 18.0 A 18.2 18.2 18.0 18.1 18.6 17.9 17.4 18.0 0.1

705 B C B 18.3 A 18.7 18.3 18.8 18.6 18.1 18.2 17.6 18.0 0.6

*ALL 18.3

*1 SAMPLING POSITION B:BASE METAL *2 LOCATION C:CROSS SECTION *3 SAMPLING LOCATION T:TOP B:BOTTOM *4 EACH

*5 AVERAGE *V.A.:VARIATION AVERAGE MAX.-MIN. * ALL:ALL AVG.

NO.

/

HEAT NO. PRODUCT PCS.

(PCS.)

HEAT LOT/NO. SETTING TEMPERING TEMPERATURE

(ﾟC)

HEAD OF DEPARTMENT






INSPECTION CERTIFICATE DATE :2014-03-24 5PAGE :CERTIFICATE NO. :BYYF1157



8

TEMPERING TEMPERATURE

J3L2A86 16 707 680

J3LB677 50 710 680

J3LC743 2 706 680

J4L1765 5 709 680

J4L1772 10 708 680

J4L1B50 100 701 680

J4L1B50 100 702 680

J4L1B50 99 703 680

J4L1B50 99 704 680

J4L1B50 54 705 680

TOTAL 535REMARKS : TEMPERING TEMPERATURE CONTROL RANGE : SETTING TEMPERATURE +,-10ﾟC

NO.

/INSPECTION CERTIFICATE(COUPLING) DATE :2014-03-24 6PAGE :CERTIFICATE NO. :BYYF1157



HEAD OF DEPARTMENT





8


MATERIAL WORK NO.:WCFK5792

HEAT TREATMENT:QUENCHED & TEMPERED

CHEMICAL COMPOSITION(%)

C Si Mn P S Cu Cr Ni Mo Ti B Al

*1 *2 *2 *2 *2 *2

SPEC. MIN. R - - - - - - 80 - - - - -

　　　MAX. R 43 45 190 20 10 35 120 25 - - 2 -

HEAT NO.

J4K1020 L 25 30 84 11 3 2 115 2 32 10 0 37

P 25 29 84 10 3 2 115 2 33 9 0 35

P 25 29 84 10 3 2 115 2 33 9 0 35

*1 R:LADLE & PRODUCT ANALYSIS L:LADLE ANALYSIS P:PRODUCT ANALYSIS *2:X1000 OTHER:X100

TENSILE TEST

YS YS TS TS EL

*1 *2 *3 *3 *3 *3 %

SPEC. MIN. PIPE L B M 552 P 80.0 M 655 P 95.0 15

　　　MAX. NO. L B M 655 P 95.0 M - P - -

HEAT NO.

J4K1020 80 L B M 606 P 87.9 M 753 P 109.2 27

91 L B M 617 P 89.5 M 762 P 110.5 26

TYPE OF SPECIMEN:ROUND BAR 12.7mm(0.5in.) DIAMETER *1 SAMPLING DIRECTION L:LONGITUDINAL

*2 SAMPLING POSITION B:BASE METAL *3 UNIT M:MPa P:ksi GAUGE LENGTH:50.8mm(2.0in.)

KIND OF YS:0.5% EXTENSION UNDER LOAD

IMPACT TEST(-10.0ﾟC +14.0ﾟF 2mm V-Notch 10X10)

*1 *2 *3 *4 *4*3 AVG AVG

SPEC. MIN. PIPE T B E J *5 F E 40 *5 30 30/40 22/30

　　　MAX. NO. T B E J F E - - -/- -/-

[1] [2] [3] [1] [2] [3]

HEAT NO.

J4K1020 80 T B E J 188 202 204 F E 198 139 149 150 146

*1 *2 *3 *4 AVG

SPEC. MIN. PIPE T B S % *6 - -

　　　MAX. NO. T B S % - -

[1] [2] [3]

HEAT NO.

J4K1020 80 T B S % 100 100 100 100

[1] [2] [3]: SPECIMEN NO.

ABSORBED ENERGY *5:VALUE OF ONE PIECE/EACH VALUE OF TWO PIECES AVG:AVERAGE VALUE OF ONE SET(3 PIECES)

SHEAR AREA *6:VALUE OF ONE PIECE AVG:AVERAGE VALUE OF ONE SET(3 PIECES)

*1 SAMPLING DIRECTION T:TRANSVERSE *2 SAMPLING POSITION B:BASE METAL *3 E:ABSORBED ENERGY S:SHEAR AREA

*4 UNIT J:Joule F:ft･lbf %:%

VISUAL & DIMENSIONS: ACCEPTABLE

NO.




HEAD OF DEPARTMENT





8


MAGNETIC PARTICLE EXAMINATION

APPLICABLE STANDARD/REFERENCE: ISO11960 SECTION9.14(JIS Z 2320 TYPE A1/BURMAH-Castrol): ACCEPTABLE

THREAD GAUGING: ACCEPTABLE

EN 10204 3.1

NO.




HEAD OF DEPARTMENT





8


HARDNESS TEST( HRC )

*1*2 *3 *4 *5 *V.A.

SPEC. MIN. B C - 14.0 -　　　MAX. B C - 23.0 -

OUTER WALL MID WALL INNER WALLAVG.

PIPE IMPRESSION NO. IMPRESSION NO. IMPRESSION NO.QUAD

HEAT NO. NO. -RANT (1) (2) (3) AVG. (1) (2) (3) AVG. (1) (2) (3) AVG.

J4K1020 80 B C T 19.5 A 18.3 19.0 19.3 18.9 20.3 20.2 20.6 20.4 19.2 19.1 19.3 19.2 1.5

91 B C B 19.7 A 19.2 19.2 19.1 19.2 20.2 20.3 20.6 20.4 19.7 19.4 19.2 19.4 1.2

*ALL 19.6

*1 SAMPLING POSITION B:BASE METAL *2 LOCATION C:CROSS SECTION *3 SAMPLING LOCATION T:TOP B:BOTTOM *4 EACH

*5 AVERAGE *V.A.:VARIATION AVERAGE MAX.-MIN. * ALL:ALL AVG.