ME495 Laboratory II-IM- 1
Injection Molding
• Introduction
• Injection Molding Machines and Operations
• Safety
• Polystyrenes
• Dimension Stability
• Measure Residual Stress Using Photoelasticity
• Weld-line Influence on Strength
• Breaking Gear Teeth
ME495 Laboratory II-IM- 2
Importance of Plastics
World consumption of raw material by weight
Plastic industry ~ 100 billion/yr business, 1.4 million production jobs
ME495 Laboratory II-IM- 3
Importance of Injection Molding for Plastics
Plastic consumption by processes
ME495 Laboratory II-IM- 4
Injection Molding Machines (1000GGB)
ME495 Laboratory II-IM- 5
Basic Elements of an Injection Molding Machine
Mold
ClampingUnit
Screw
Heaters
Materialhopper Gear
train
Motor
Hydraulicpressure
Limit switchesSpline
Main IM machine spec. include clamp force (tons), shot size (ounces or pounds) and injection rate (in3/sec)
ME495 Laboratory II-IM- 6
The Basic Operation1. Raising the temperature of the plastic to melt it. This is achieved by heaters and the screw (mixing + friction heat). This overall process is called plastification of the material.2. Inject the melted plastic (through various flow channels) into the mold cavity and allow it to solidify in the mold.3. Open the mold and eject the product
ME495 Laboratory II-IM- 7
Typical IM Process Cycle
ME495 Laboratory II-IM- 8
Functions of IM Elements
ME495 Laboratory II-IM- 9
Safety
• The barrel temperature is usually 350-550° F (177-288°C), and can be as high as 700° Fahrenheit (371° Celsius).
• Plastic at its molding temperatures is hot and sticky. If it gets on skin or clothes, usually it is not easy to remove it.
ME495 Laboratory II-IM- 10
Safety (cont.)
• The electrical wires to the heater bands are high voltage (typically 460 volts) and very high current.
• Operating personnel must be aware of all the moving parts in the molding machine. Protective guards are placed around potentially hazardous areas but caution from operators is still necessary.
ME495 Laboratory II-IM- 11
PolystyrenesPolystyrenes (Comes in two forms: foam and solid)
- Foamed polystyrene is used to make cups, bowls, plates, trays, clamshell containers, meat trays and egg cartons as well as protective packaging for shipping electronics and other fragile
items. - Solid polystyrene is used in products such as cutlery, yogurt and cottage cheese containers, cups, clear salad bar containers and video and audiocassette housings.
Recycling Symbols
ME495 Laboratory II-IM- 12
Mechanical Properties of Various Plastics
ME495 Laboratory II-IM- 13
Thermofluid Properties of Polymers
• Thermoplastic
• Glass transition temperature
• Low thermal conductivity (good insulator)
• Extremely high viscosity (high pumping pressure and losses)
• Viscosity is temperature sensitive
• Non–Newtonian: Viscosity decreases as shear rate increases (shear thinning)
ME495 Laboratory II-IM- 14
Temperature and Shear–rate Dependence of Viscosity
ME495 Laboratory II-IM- 15
IM process is quite complicated
Molding parameters and part properties are linked through fluid flow.We will limit ourselves to 2 variables: temperature and flow rate
ME495 Laboratory II-IM- 16
Lab 1 Process Parameters
190oC, 200oC, and 210oC at 600 bar
5–6 parts/condition
ME495 Laboratory II-IM- 17
Problems from Improper Processing
• “Short shots” — results when insufficient polymer is injected into the mold.
• “Flash” — caused by excessive packing and/or holding pressure prying open the mold and driving polymer through the resulting crack
• Dimensional instability — from removing part without proper cooling time
• “Sink marks” — caused by excessive shrinkage of the polymer during the cooling cycle
ME495 Laboratory II-IM- 18
Importance of Proper Temperature and Pressure
TIME
CA
VIT
Y P
RE
SS
UR
E
START INJECTION
MOLD FILLING
PACKING
HOLDING
GATE SOLIDIFICATION
IN-MOLD SHRINKAGE
MOLD OPEN
PEAK PRESSURE
Temperature: Too high: chemical degradation, cooling time, shrink mark Too low: high viscosity
Pressure: without proper holding pressure, excessive shrink mark or flashing may result
ME495 Laboratory II-IM- 19
Dimensional Stability (Shrinkage)
At temperatures higher than T2 = Tg(shown below), the higher energy level of molecules creates a “free volume”.This free volume may be “frozen in” during rapid cooling.
Theoretical density at 0, 10, 100and 210 sec during quenching (PS)
ME495 Laboratory II-IM- 20
Effect of manufacturing parameters on quality
• Gear strength is influenced by – Shrinkage (gear size and geometry)
– Homogeneity (weld line? Residual stress due to uneven cooling?)
u _bending( p,T )
ME495 Laboratory II-IM- 21
Effect of Flow Orientation on Strength
ME495 Laboratory II-IM- 22
Effect of Weld Line on Strength
GATE 1
GATE
GATE 2
(a)
(b)FLOW OBSTRUCTION
FLOW FRONTS WELD LINES
MELT FLOW
MELT FLOW
WELD LINE
NO DIFFUSION
PARTIAL DIFFUSION
COMPLETE DIFFUSION
ME495 Laboratory II-IM- 23
Measure Residue Stress by Photoelasticity
Photoelasticity is a nondestructive, graphic stress-analysis technique based on the birefringence property possessed by many transparent polymers. It is mainly used for 2-dimensional (planar) problems.
A polariscope (polarimeter) measures birefringence in specimens. It consists of a light source, a polarizer, an optional quarter-wave plate, a specimen, another optional quarter-wave plate, and a second polarizer called the analyzer.
ME495 Laboratory II-IM- 24
Working Principle of Polariscopes
The theory of photoelasticity is based on light refraction that depends on the orientation of polarized light
Refraction: When light passes through any medium other than a vacuum, its velocity decreases
ME495 Laboratory II-IM- 25
Double Refraction
If similar light waves pass through the same thickness h of two media having indices of refraction n1 and n2, a phase difference between the two waves after they emerge from the media results
ME495 Laboratory II-IM- 26
Birefringence
Photoelastic materials are birefringent, i.e., they refract lightdifferently depending upon the state of stress in the material.
In an unloaded state, the material exhibits an index of refraction n0 independent of orientation. In the loaded state, however, the magnitudes of the principal stresses, determine the index of refraction for that light wave. The change in index of refraction is found to be (Maxwell Equations)
n1 n0 c11 c2 (2 3)
n2 n0 c12 c2(3 1 )
n3 n0 c13 c2 (1 2 )
For birefringent material, c1 c2.
n2 n1 (c2 c1)(1 2 )
Stress-optic coefficients
ME495 Laboratory II-IM- 27
Example Birefringence Patterns
crack tensile
bending
ME495 Laboratory II-IM- 28
Additional Safety Issues• Sessions 1&2 involve bending fracture of the gears, so it
is very important to wear safety glasses in the lab.
ME495 Laboratory II-IM- 29
Torque Test
Single tooth: Torque is carried by one tooth‚ easier to analyze.
Normal engagement: true torque capacity of the gear.
ME495 Laboratory II-IM- 30
Thickness b
width h
Force W
Length L
23
6
12
)2/(
bh
WL
bh
hWL
I
yM
yy
b
Model the gear tooth as a rectangular prism:
ME495 Laboratory II-IM- 31
Predicting Gear Strength
• Given the gear geometry you can relate gear torque to the stress at the root of a gear tooth.
• If you knew the stress that would cause the polystyrene to fail in tension‚ you could predict the torque at which the gear teeth would fail.
• Guess what you’ll be doing in lab next week?
ME495 Laboratory II-IM- 32
Process Conditions for Session #2
Polystyrene: 190oC, 200oC, 210oC500 bar
5 parts each for the case with and without weld lines
ME495 Laboratory II-IM- 33
Analysis of Session 1 Results
• Make gears at given temperatures and flow rates. Qualitatively explain which combinations of processing conditions lead to short shot, flash and sink marks. How do processing conditions affect final part dimensions?
• Measure pertinent geometrical quantities, including contact point position when two gears are meshed together.
• From your optical observations, identify regions of high residual stress in molded part. Qualitatively assess effect of injection rate and melt temperature (processing parameters) on residual stress field. What other processing parameters will impact residual stress field? Qualitatively explain why residual stress is concentrated only in certain regions.
ME495 Laboratory II-IM- 34
Analysis of Session 1 Results, Continued
• Break gear teeth and record failure torque. Does failure torque depend on temperature or flow rate?
• Perform a strength analysis on gear and relate failure torque to gear tooth stress. You will measure failure stress for polystyrene in Session 2.
• Observe fill and cooling times of current injection molding cycle. Also observe and record mold temperature for your analysis and computer simulation.