nucleation & crystallization
out of 21
Post on 25-Dec-2014
Embed Size (px)
- 1. NUCLEATION &CRYSTALLIZATION
- 2. FOR MORE HELP CONTACT MEMuhammad Umair Bukhari Engr.firstname.lastname@example.org www.bzuiam.webs.com 03136050151
- 3. INTRODUCTION The formation of first nano-sized crystallites from molten material. In a broader sense, the term nucleation refers to the initial stage of formation of one phase from another phase. So nucleation is a phenomenon associated with the phase transformation. As water begins to freeze, nano-sized ice crystals forms 1st.
- 4. PROCESS THERMODYNAMICS At the thermodynamic melting or freezing temperature, the probability of forming stable, sustainable nuclei is extremely small. Therefore, solidification does not begins at thermodynamic melting or freezing temperature. If the temperature is decreased from the freezing point of the material, the liquid is considered as under-cooled.
- 5. PROCESS THERMODYNAMICS A material is solidify when the liquid cools to just below its freezing temperature because the energy associated with the crystalline structure of the solid is less than the energy of the liquid. This energy difference between the liquid and the solid is the free energy per unit volume and is the driving force for solidification.
- 6. PROCESS ENERGETIC When the solid forms, a solid-liquid interface is created. A surface free energy associated with this interface. The larger the solid the greater the increase in the surface energy. An interface is created when a solid forms from the liquid
- 7. AN INTERFACE IS CREATED WHEN A SOLID FORMS FROM THE LIQUID
- 8. PROCESS FREE ENERGY The total energy change is given as: G=4/3r3 Gv + 4r2sl4/3r3=the volume of a spherical embryo of radius r4r2=the surface area of spherical embryosl=surface energy of solid liquid interfaceGv = free energy change per unit volume.
- 9. The Top Curve shows the parabolic variations of total surface energy. The Bottom Curve shows the total volume free energy change. The Middle Curve shows the net variation of G.
- 10. NUCLEATION The total free energy of solid-liquid system changes with the size of the solid. The solid is an Embryo, if its radius is less than the critical radius and is a Nucleus if its radius is greater than the critical radius. The critical radius is the minimum size of the crystal that must be formed by the atoms clustering together in a liquid before the solid particle is stable and begins to grow.
- 11. The total free energy of the solid-liquid system changes with the size of the solid. The solid is an embryo if its radius is less than the critical radius, and is a nucleus if its radius is greater than the critical radius
- 12. INITIATION OF GROWTH The new solid is then stable and sustainable since nucleation has occurred, and growth of solid particle which are now called a Nucleus begins.
- 13. GROWTH The growth process which follow nucleation determine the following crystallographic structure of the solid. The mode of the growth, both of individual grains and of general mass of solid, depends upon thermal conditions in the solidification zone.
- 14. SEGREGATION Segregation means to isolate something according to specific laws. Here, Segregation means Change in the average composition of the metal as one moves from place to place in an ingot. The liquid which are frozen to form industrial alloys usually contain many impurity elements. These impurity elements are frequently eliminated during smelting and refining operation. The refractory lining of furnaces and the gases in the furnace atmospheres may be the sources of these impurities.
- 15. SEGREGATION Elements enter the liquid metal in the form of dissolved gases. The various elements dissolved in the liquid metals can and often do react with each other to form compounds. In many cases, these compounds are less dense than the liquid and rise to the surface and join the slag which float on the top of the liquid metals. On the other hand, it is quiet possible for small impurity particles to exist in the liquid.
- 16. SEGREGATION When an alloy is frozen, a rule applies is that solute elements, whether present as alloying elements or as impurities, are more soluble in liquid state than in the solid state. This fact usually leads to the segregation of solute elements in finished castings.
- 17. SEGREGATION There are two basic ways of looking at the resulting non-uniformity of the solute. As freezing point progresses, the solute concentration in a casting tend to rise in those regions which solidify in the last (centre of ingot). In general, segregation means to change in the average composition of the metal as one moves from place to place in an ingot.
- 18. SEGREGATION Gravitational effects are often a factor in producing the segregation. The crystal which form freely in the liquid often have a different density from that of liquid. As a result, they may either Rise towards the surface of the casting or Settled towards the bottom.
- 19. MACRO-SEGREGATION The basic factor is the accumulation of rejected solute by transport over long distances through the casting. The other factor is the movement of growing crystals from their nucleation sites from gravity or turbulence and long range capillary flow of liquids during the final stages of freezing.
- 20. MICRO-SEGREGATION It results from accumulation of rejected solute between the growing crystals and its failure due to either inadequate time to diffuse into the main body of residual liquid. The micro-segregation of alloying elements and impurities can effect the strength and the ductility.
- 21. GRAVITY SEGREGATION Macro-segregation are frequently influenced by the mass movement of precipitated phases due to difference in density compared with their parent liquid. Metals crystals growing independently in the melt tend to sink and produce a corresponding upward displacement of solute enriched liquid. Gravity concentration is mainly encountered in heavy sections.