phase transformation physical metallurgy
TRANSCRIPT
Chapter 11
Phase Transformations
Fe3C (cementite)- orthorhombic
Martensite - BCT
Austenite - FCC
Ferrite - BCC
Phase Transformations• Transformation rate• Kinetics of Phase Transformation
– Nucleation: homogeneous, heterogeneous– Free Energy, Growth
• Isothermal Transformations (TTT diagrams)• Pearlite, Martensite, Spheroidite, Bainite• Continuous Cooling• Mechanical Behavior• Precipitation Hardening
Phase Transformations Phase transformations – change in the
number or character of phases. Simple diffusion-dependent
No change in # of phases No change in composition Example: solidification of a pure metal, allotropic transformation,
recrystallization, grain growth
More complicated diffusion-dependent Change in # of phases Change in composition Example: eutectoid reaction
Diffusionless Example: metastable phase - martensite
Phase Transformations Most phase transformations begin with the formation of
numerous small particles of the new phase that increase in size until the transformation is complete.
• Nucleation is the process whereby nuclei (seeds) act as templates for crystal growth.
• Homogeneous nucleation - nuclei form uniformly throughout the parent phase; requires considerable supercooling (typically 80-300°C).
• Heterogeneous nucleation - form at structural inhomogeneities (container surfaces, impurities, grain boundaries, dislocations) in liquid phase much easier since stable “nucleating surface” is already present; requires slight supercooling (0.1-10ºC).
Supercooling During the cooling of a liquid, solidification
(nucleation) will begin only after the temperature has been lowered below the equilibrium solidification (or melting) temperature Tm. This phenomenon is termed supercooling (or undercooling.
The driving force to nucleate increases as T increases
Small supercooling slow nucleation rate - few nuclei - large crystals
Large supercooling rapid nucleation rate - many nuclei - small crystals
Nucleation of a spherical solid particle in a liquid
Liquid
The change in free energy G (a function of the internal energy and enthalpy of the system) must be negative for a transformation to occur.
Assume that nuclei of the solid phase form in the interior of the liquid as atoms cluster together-similar to the packing in the solid phase.
Also, each nucleus is spherical and has a radius r.Free energy changes as a result of a transformation: 1) the difference between the solid and liquid phases (volume free energy, GV); and 2) the solid-liquid phase boundary (surface free energy, GS).
Transforming one phase into another takes time.
G = GS + GV
Fe
(Austenite)
Eutectoid transformation
C FCC
Fe3C(cementite)
(ferrite)
+(BCC)
r* = critical nucleus: for r < r* nuclei shrink; for r >r* nuclei grow (to reduce energy)
Homogeneous Nucleation & Energy Effects
GT = Total Free Energy = GS + GV
Surface Free Energy- destabilizes the nuclei (it takes energy to make an interface)
24 rGS
= surface tension
Volume (Bulk) Free Energy – stabilizes the nuclei (releases energy)
GrGV3
34
volume unitenergy free volume
G
Solidification
THTr
f
m
2*
Note: Hf and are weakly dependent on T
r* decreases as T increases
For typical T r* ~ 10 nm
Hf = latent heat of solidification (fusion)Tm = melting temperature= surface free energy
T = Tm - T = supercooling
r* = critical radius
Transformations & Undercooling
• For transformation to occur, must cool to below 727°C
• Eutectoid transformation (Fe-Fe3C system): + Fe3C0.76 wt% C
0.022 wt% C6.7 wt% C
Fe3C
(cem
entit
e)
1600
1400
1200
1000
800
600
4000 1 2 3 4 5 6 6.7
L
(austenite)
+L
+Fe3C
+Fe3C
L+Fe3C
(Fe) C, wt% C
1148°C
T(°C)
ferrite
727°C
Eutectoid:Equil. Cooling: Ttransf. = 727ºC
T
Undercooling by Ttransf. < 727C
0.76
0.02
2
2
• Fraction transformed depends on time.
fraction transformed time
y1 e ktnAvrami Eqn.
• Transformation rate depends on T.
1 10 102 104050
100 135°
C11
9°C
113°
C10
2°C
88°C
43°Cy (%)
log (t) min
Ex: recrystallization of Cu
r 1t0.5
Ae Q /RT
activation energy
• r often small: equil not possible
y
log (t)
Fixed T0
0.5
1
t0.5
FRACTION OF TRANSFORMATION
Generation of Isothermal Transformation Diagrams
• The Fe-Fe3C system, for Co = 0.76 wt% C• A transformation temperature of 675°C.
100
50
01 10 2 104
T = 675°C
% tr
ansf
orm
ed
time (s)
400
500
600
700
1 10 102 103 104 105
0%pearlite
100%
50%
Austenite (stable) TE (727C)Austenite (unstable)
Pearlite
T(°C)
time (s)
isothermal transformation at 675°C
Consider:
Coarse pearlite formed at higher temperatures – relatively soft
Fine pearlite formed at lower temperatures – relatively hard
• Transformation of austenite to pearlite:
pearlite growth direction
Austenite ()grain boundary
cementite (Fe3C)Ferrite ()
• For this transformation, rate increases with ( T) [Teutectoid – T ].
675°C (T smaller)
0
50
% p
earli
te600°C
(T larger)650°C
100
Diffusion of C during transformation
Carbon diffusion
Eutectoid Transformation Rate ~ T
5
• Reaction rate is a result of nucleation and growth of crystals.
• Examples:
% Pearlite
0
50
100
Nucleation regime
Growth regime
log (time)t50
Nucleation rate increases w/ TGrowth rate increases w/ T
Nucleation rate highT just below TE T moderately below TE T way below TENucleation rate lowGrowth rate high
pearlite colony
Nucleation rate med Growth rate med. Growth rate low
Nucleation and Growth
Isothermal Transformation Diagrams2 solid curves are plotted:
one represents the time required at each temperature for the start of the transformation;
the other is for transformation completion.
The dashed curve corresponds to 50% completion.
The austenite to pearlite transformation will occur only if the alloy is supercooled to below the eutectoid temperature (727˚C).
Time for process to complete depends on the temperature.
• Eutectoid iron-carbon alloy; composition, Co = 0.76 wt% C• Begin at T > 727˚C• Rapidly cool to 625˚C and hold isothermally.
Isothermal Transformation Diagram
Austenite-to-Pearlite
Transformations Involving Noneutectoid Compositions
Hypereutectoid composition – proeutectoid cementite
Consider C0 = 1.13 wt% C
Fe3C
(cem
entit
e)
1600
1400
1200
1000
800
600
4000 1 2 3 4 5 6 6.7
L
(austenite)
+L
+Fe3C
+Fe3C
L+Fe3C
(Fe) C, wt%C
T(°C)
727°CT
0.76
0.02
2
1.13
Stre
ngth
Duc
tility
Martensite T Martensite
bainite fine pearlite
coarse pearlite spheroidite
General Trends
Possible Transformations
Coarse pearlite (high diffusion rate) and (b) fine pearlite
- Smaller T: colonies are larger
- Larger T: colonies are smaller
10 103 105
time (s)10-1
400
600
800
T(°C)Austenite (stable)
200
P
B
TE
0% 100%
50%
A
A
Bainite: Non-Equil Transformation Products elongated Fe3C particles in -ferrite matrix diffusion controlled lathes (strips) with long rods of Fe3C
100% bainite
100% pearlite
Martensite
Cementite
Ferrite
Bainite Microstructure
• Bainite consists of acicular (needle-like) ferrite with very small cementite particles dispersed throughout.
• The carbon content is typically greater than 0.1%.
• Bainite transforms to iron and cementite with sufficient time and temperature (considered semi-stable below 150°C).
10
Fe3C particles within an -ferrite matrix diffusion dependent heat bainite or pearlite at temperature just below eutectoid for long times driving force – reduction of -ferrite/Fe3C interfacial area
Spheroidite: Nonequilibrium Transformation
10 103 105time (s)10-1
400
600
800T(°C)
Austenite (stable)
200
P
B
TE
0% 100%
50%
A
A
Spheroidite100% spheroidite
100% spheroidite
Pearlitic Steel partially transformed to Spheroidite
single phase body centered tetragonal (BCT) crystal structure BCT if C0 > 0.15 wt% C Diffusionless transformation BCT few slip planes hard, brittle % transformation depends only on T of rapid cooling
Martensite Formation• Isothermal Transformation Diagram
10 103 105 time (s)10-1
400
600
800
T(°C)Austenite (stable)
200
P
B
TE
0%100%50%
A
A
M + AM + A
M + A
0%50%90%
Martensite needlesAustenite
An micrograph of austenite that was polished flat and then allowed to transform into martensite. The different colors indicate the displacements caused when martensite forms.
Isothermal Transformation Diagram
Iron-carbon alloy with eutectoid composition.
A: AusteniteP: PearliteB: BainiteM: Martensite
Other elements (Cr, Ni, Mo, Si and W) may cause significant changes in the positions and shapes of the TTT curves:
Change transition temperature; Shift the nose of the austenite-to-
pearlite transformation to longer times;
Shift the pearlite and bainite noses to longer times (decrease critical cooling rate);
Form a separate bainite nose;
Effect of Adding Other Elements
4340 Steel
plain carbonsteel
nose
Plain carbon steel: primary alloying element is carbon.
Example 11.2: Iron-carbon alloy with
eutectoid composition. Specify the nature of the
final microstructure (% bainite, martensite, pearlite etc) for the alloy that is subjected to the following time–temperature treatments:
Alloy begins at 760˚C and has been held long enough to achieve a complete and homogeneous austenitic structure.
Treatment (a) Rapidly cool to 350 ˚C Hold for 104 seconds Quench to room temperature
Bainite, 100%
Martensite, 100%
Example 11.2: Iron-carbon alloy with
eutectoid composition. Specify the nature of the
final microstructure (% bainite, martensite, pearlite etc) for the alloy that is subjected to the following time–temperature treatments:
Alloy begins at 760˚C and has been held long enough to achieve a complete and homogeneous austenitic structure.
Treatment (b) Rapidly cool to 250 ˚C Hold for 100 seconds Quench to room temperature
Austenite, 100%
Bainite, 50%
Example 11.2: Iron-carbon alloy with
eutectoid composition. Specify the nature of the
final microstructure (% bainite, martensite, pearlite etc) for the alloy that is subjected to the following time–temperature treatments:
Alloy begins at 760˚C and has been held long enough to achieve a complete and homogeneous austenitic structure.
Treatment (c) Rapidly cool to 650˚C Hold for 20 seconds Rapidly cool to 400˚C Hold for 103 seconds Quench to room temperature
Austenite, 100%
Almost 50% Pearlite, 50% Austenite
Final: 50% Bainite, 50% Pearlite
Continuous Cooling Transformation Diagrams
Isothermal heat treatments are not the most practical due to rapidly cooling and constant maintenance at an elevated temperature.
Most heat treatments for steels involve the continuous cooling of a specimen to room temperature.
TTT diagram (dotted curve) is modified for a CCT diagram (solid curve).
For continuous cooling, the time required for a reaction to begin and end is delayed.
The isothermal curves are shifted to longer times and lower temperatures.
Moderately rapid and slow cooling curves are superimposed on a continuous cooling transformation diagram of a eutectoid iron-carbon alloy.
The transformation starts after a time period corresponding to the intersection of the cooling curve with the beginning reaction curve and ends upon crossing the completion transformation curve.
Normally bainite does not form when an alloy is continuously cooled to room temperature; austenite transforms to pearlite before bainite has become possible.
The austenite-pearlite region (A---B) terminates just below the nose. Continued cooling (below Mstart) of austenite will form martensite.
For continuous cooling of a steel alloy there exists a critical quenching rate that represents the minimum rate of quenching that will produce a totally martensitic structure.
This curve will just miss the nose where pearlite transformation begins
Continuous cooling diagram for a 4340 steel alloy and several cooling curves superimposed.
This demonstrates the dependence of the final microstructure on the transformations that occur during cooling.
Alloying elements used to modify the critical cooling rate for martensite are chromium, nickel, molybdenum, manganese, silicon and tungsten.
Mechanical Properties
• Hardness• Brinell, Rockwell• Yield Strength• Tensile Strength• Ductility• % Elongation• Effect of Carbon Content
Mechanical Properties: Influence of Carbon Content
C0 > 0.76 wt% CHypereutectoid
Pearlite (med)Cementite(hard)
C0 < 0.76 wt% CHypoeutectoid
Pearlite (med)ferrite (soft)
Mechanical Properties: Fe-C System
Tempered martensite is less brittle than martensite; tempered at 594 °C. Tempering reduces internal stresses caused by quenching. The small particles are cementite; the matrix is -ferrite. US Steel Corp.
Tempered Martensite
4340 steel
Hardness as a function of carbon concentration for steels
Hardness versus tempering time for a water-quenched eutectoid plain carbon steel (1080); room temperature.
Rockwell C and Brinell Hardness
Precipitation Hardening• The strength and hardness of some metal
alloys may be improved by the formation of extremely small, uniformly dispersed particles (precipitates) of a second phase within the original phase matrix.
• Other alloys that can be precipitation hardened or age hardened:
Copper-beryllium (Cu-Be) Copper-tin (Cu-Sn) Magnesium-aluminum (Mg-Al) Aluminum-copper (Al-Cu) High-strength aluminum alloys
Criteria:Maximum solubility of 1 component in the other (M);Solubility limit that rapidly decreases with decrease in temperature (M→N).Process:Solution Heat Treatment – first heat treatment where all solute atoms are dissolved to form a single-phase solid solution.Heat to T0 and dissolve B phase.Rapidly quench to T1
Nonequilibrium state ( phase solid solution supersaturated with B atoms; alloy is soft, weak-no ppts).
Phase Diagram for Precipitation Hardened Alloy
The supersaturated solid solution is usually heated to an intermediate temperature T2 within the region (diffusion rates increase).
The precipitates (PPT) begin to form as finely dispersed particles. This process is referred to as aging.
After aging at T2, the alloy is cooled to room temperature.
Strength and hardness of the alloy depend on the ppt temperature (T2) and the aging time at this temperature.
Precipitation Heat Treatment – the 2nd stage
0 10 20 30 40 50wt% Cu
L+L
+L
300
400
500
600
700
(Al)
T(°C)
composition range available for precipitation hardening
CuAl2
A
Precipitation Hardening• Particles impede dislocation motion.• Ex: Al-Cu system• Procedure:
-- Pt B: quench to room temp. (retain solid solution)-- Pt C: reheat to nucleate small particles within phase.
Temp.
Time
-- Pt A: solution heat treat (get solid solution)
Pt A (solution heat treat)
B
Pt B
C
Pt C (precipitate
At room temperature the stable state of an aluminum-copper alloy is an aluminum-rich solid solution (α) and an intermetallic phase with a tetragonal crystal structure having nominal composition CuAl2 (θ).
Precipitation Heat Treatment – the 2nd stage
PPT behavior is represented in the diagram:
With increasing time, the hardness increases, reaching a maximum (peak), then decreasing in strength.
The reduction in strength and hardness after long periods is overaging (continued particle growth). Small solute-enriched regions in a
solid solution where the lattice is identical or somewhat perturbed from that of the solid solution are called Guinier-Preston zones.
24
• Hard precipitates are difficult to shear. Ex: Ceramics in metals (SiC in Iron or Aluminum).
Large shear stress needed to move dislocation toward precipitate and shear it.
Side View
Top View
Slipped part of slip plane
Unslipped part of slip plane
S
Dislocation “advances” but precipitates act as “pinning” sites with spacing S.
precipitate
• Result: y ~1S
PRECIPITATION STRENGTHENING
Several stages in the formation of the equilibrium PPT () phase. (a)supersaturated solid solution; (b)transition (”) PPT phase; (c)equilibrium phase within the matrix phase.
• 2014 Al Alloy:
• TS peak with precipitation time.• Increasing T accelerates process.
Influence of Precipitation Heat Treatment on Tensile Strength (TS), %EL
precipitation heat treat time
tens
ile s
treng
th (M
Pa)
200
300
400
100 1min 1h 1day 1mo 1yr
204°C
non-
equi
l. so
lid s
olut
ion
man
y sm
all
prec
ipita
tes
“age
d”
fewe
r lar
gepr
ecip
itate
s
“ove
rage
d”149°C
• %EL reaches minimum with precipitation time.
%E
L (2
in s
ampl
e)10
20
30
0 1min 1h 1day 1mo 1yr
204°C 149°C
precipitation heat treat time
Effects of Temperature
Characteristics of a 2014 aluminum alloy (0.9 wt% Si, 4.4 wt% Cu, 0.8 wt% Mn, 0.5 wt% Mg) at 4 different aging temperatures.
Aluminum rivets
Alloys that experience significant precipitation hardening at room temp and after short periods must be quenched to and stored under refrigerated conditions.
Several aluminum alloys that are used for rivets exhibit this behavior. They are driven while still soft, then allowed to age harden at the normal room temperature.