Rockwell scaleFrom Wikipedia, the free encyclopediaJump to: navigation, search
A hardness tester of the Rockwell type.
A closeup of the indenter and anvil on a Rockwell-type hardness tester.
A digital Rockwell tester
The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test determines the hardness by measuring the depth of penetration of an indenter under a large load compared to the penetration made by a preload.[1] There are different scales, denoted by a single letter, that use different loads or indenters. The result is a dimensionless number noted as HRA, where A is the scale letter.
When testing metals, indentation hardness correlates linearly with tensile strength.[2] This important relation permits economically important nondestructive testing of bulk metal deliveries with lightweight, even portable equipment, such as hand-held Rockwell hardness testers.[citation
needed]
Contents
1 History 2 Operation 3 Scales and values
o 3.1 Typical values 4 Standards 5 See also 6 References 7 External links
History
The differential depth hardness measurement was conceived in 1908 by a Viennese professor Paul Ludwik in his book Die Kegelprobe (crudely, "the cone trial").[3] The differential-depth method subtracted out the errors associated with the mechanical imperfections of the system, such as backlash and surface imperfections. The Brinell hardness test, invented in Sweden, was developed earlier—in 1900—but it was slow, not useful on fully hardened steel, and left too large an impression to be considered nondestructive.
Not being direct relatives, Hugh M. Rockwell (1890–1957) and Stanley P. Rockwell (1886–1940) from U.S. State Connecticut co-invented the so-called Rockwell hardness tester, a differential-depth machine. They applied for a patent on July 15, 1914.[4] The requirement for this tester was to quickly determine the effects of heat treatment on steel bearing races. The application was subsequently approved on February 11, 1919, and holds U.S. Patent 1,294,171. At the time of invention, both Hugh and Stanley Rockwell worked for the New Departure Manufacturing Co. of Bristol, CT. New Departure was a major ball bearing manufacturer that, in 1916, became part of United Motors and, shortly thereafter, General Motors Corp. After leaving the Connecticut company, Stanley Rockwell, then in Syracuse, NY, applied for an improvement to the original invention on September 11, 1919, which was approved on November 18, 1924. The new tester holds U.S. Patent 1,516,207.[5][6] Rockwell moved to West Hartford, CT, and made an additional improvement in 1921.[6] Stanley collaborated with instrument manufacturer Charles H. Wilson of the Wilson-Mauelen Company in 1920 to commercialize his invention and develop standardized testing machines.[7] Stanley started a heat-treating firm circa 1923, the Stanley P. Rockwell Company, which still exists in Hartford, CT. The later-named Wilson Mechanical Instrument Company has changed ownership over the years, and was most recently acquired by Instron Corp. in 1993.[8]
Operation
The determination of the Rockwell hardness of a material involves the application of a minor load followed by a major load, and then noting the depth of penetration, vis a vis, hardness value directly from a dial, in which a harder material gives a higher number. The chief advantage of Rockwell hardness is its ability to display hardness values directly, thus obviating tedious calculations involved in other hardness measurement techniques.
It is typically used in engineering and metallurgy. Its commercial popularity arises from its speed, reliability, robustness, resolution and small area of indentation.
In order to get a reliable reading the thickness of the test-piece should be at least 10 times the depth of the indentation.[9] Also, readings should be taken from a flat perpendicular surface, because convex surfaces give lower readings. A correction factor can be used if the hardness of a convex surface is to be measured.[10]
Scales and values
There are several alternative scales, the most commonly used being the "B" and "C" scales. Both express hardness as an arbitrary dimensionless number.
Various Rockwell scales[11]
Scale Abbreviation Load Indenter Use
A HRA 60 kgf 120° diamond cone† Tungsten carbide
B HRB 100 kgf1⁄16-inch-diameter (1.588 mm) steel sphere
Aluminium, brass, and soft steels
C HRC 150 kgf 120° diamond cone Harder steels >B100
D HRD 100 kgf 120° diamond cone
E HRE 100 kgf1⁄8-inch-diameter (3.175 mm) steel sphere
F HRF 60 kgf1⁄16-inch-diameter (1.588 mm) steel sphere
G HRG 150 kgf1⁄16-inch-diameter (1.588 mm) steel sphere
†Also called a brale indenter
Except for testing thin materials in accordance with A623 the steel indenter balls have been replaced by tungsten carbide balls of the varying diameters. When a ball indenter is used, the letter "W is used to indicate a tungsten/carbide ball was used, and the letter "S" indicates the use of a steel ball. E.g.: 70 HRCW indicates the reading was 70 in the Rockwell C scale using a Tungsten/Carbide indenter.[12]
The superficial Rockwell scales use lower loads and shallower impressions on brittle and very thin materials. The 45N scale employs a 45-kgf load on a diamond cone-shaped Brale indenter, and can be used on dense ceramics. The 15T scale employs a 15-kgf load on a 1⁄16-inch-diameter (1.588 mm) hardened steel ball, and can be used on sheet metal.
Readings below HRC 20 are generally considered unreliable, as are readings much above HRB 100.
Typical values
Very hard steel (e.g. chisels, quality knife blades): HRC 55–66 ( Hardened High Speed Carbon and Tool Steels such as M2, W2, O1, CPM-M4, and D2, as well as many of the newer powder metallurgy Stainless Steels such as S30V, 154CM, ZDP-189, etc. )[13]
Axes: about HRC 45-55 Brass: HRB 55 (Low brass, UNS C24000, H01 Temper) to HRB 93 (Cartridge Brass,
UNS C26000 (260 Brass), H10 Temper)[14]
Several other scales, including the extensive A-scale, are used for specialized applications. There are special scales for measuring case-hardened specimens.
Standards
International (ISO)
ISO 6508-1: Metallic materials -- Rockwell hardness test -- Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T)
ISO 2039-2: Plastics -- Determination of hardness -- Part 2: Rockwell hardness
US standard (ASTM International)
ASTM E18 : Standard methods for Rockwell hardness and Rockwell superficial hardness of metallic materials
See also
Brinell hardness test Hardness comparison Holger F. Struer Knoop hardness test
Leeb Rebound Hardness Test Meyer hardness test Shore durometer Vickers hardness test
References
1. ̂ E.L. Tobolski & A. Fee, "Macroindentation Hardness Testing," ASM Handbook, Volume 8: Mechanical Testing and Evaluation, ASM International, 2000, p 203-211, ISBN 0-87170-389-0.
2. ̂ Correlation of Yield Strength and Tensile Strength with Hardness for Steels , E.J. Pavlina and C.J. Van Tyne, Journal of Materials Engineering and Performance, Volume 17, Number 6 / December 2008
3. ̂ G.L. Kehl, The Principles of Metallographic Laboratory Practice, 3rd Ed., McGraw-Hill Book Co., 1949, p 229.
4. ̂ H.M. Rockwell & S.P. Rockwell, "Hardness-Tester," U.S. Patent 1,294,171, Feb 1919.5. ̂ S.P. Rockwell, "The Testing of Metals for Hardness, Transactions of the American
Society for Steel Treating, Vol. II, No. 11, August 1922, p 1013–1033.6. ^ a b S.P. Rockwell, "Hardness-Testing Machine," U.S. Patent 1,516,207, Nov 1924.7. ̂ V.E. Lysaght, Indentation Hardness Testing, Reinhold Publishing Corp., 1949, p 57-
62.8. ̂ R.E. Chinn, "Hardness, Bearings, and the Rockwells," Advanced Materials &
Processes, Vol 167 #10, October 2009, p 29-31.9. ̂ Fundamentals of Rockwell Hardness Testing, retrieved 2010-09-1010. ̂ PMPA's Designer's Guide: Heat treatment, retrieved 2009-06-19.11. ̂ Smith, William F.; Hashemi, Javad (2001), Foundations of Material Science and
Engineering (4th ed.), McGraw-Hill, p. 229, ISBN 0-07-295358-612. ̂ E18-08b Section 5.1.2.1 & 5.2.313. ̂ Knife blade materials
14. ̂ matweb.com, accessed 2010-06-23
External links
Video on the Rockwell hardness test Rockwell scale conversion chart Rockwell to brinell conversion chart
Categories:
Dimensionless numbers Hardness tests
Navigation menu
Create account Log in
Article Talk
Read Edit Edit source View history
Main page Contents Featured content Current events Random article Donate to Wikipedia
Interaction
Help About Wikipedia Community portal Recent changes Contact Wikipedia
Toolbox
Print/export
Languages
العربية Català Česky Dansk Deutsch Español فارسی Français Galego Hrvatski Italiano עברית Magyar Nederlands 日本語 Norsk bokmål Polski Português Română Русский Slovenčina Slovenščina Svenska Українська 中文 Edit links
This page was last modified on 16 April 2013 at 06:21. Text is available under the Creative Commons Attribution-ShareAlike License;
additional terms may apply. By using this site, you agree to the Terms of Use and Privacy Policy. Wikipedia® is a registered trademark of the Wikimedia Foundation, Inc., a non-profit organization.
Privacy policy About Wikipedia Disclaimers Contact Wikipedia Mobile view