Technical Data SheetTempo Aerospace Inc. Tel: 416.746.2233 Fax: 416.746.2235
Updated May 2012
4500-P-215YHigh Solids Low V.O.C. Chromated Epoxy Primer Yellow
Premium quality high solids epoxy primer formulated for excellent adhesion to prepared aluminum and ferrous metal substrates. This product is predominantly used on aerospace defense and commercial rotocraft platforms.
Specification
MIL-PRF-23377, Type I - Class C2
outStanding characteriSticS
• Excellent impact resistance• Excellentflexibility<1/8”mandrel• Low V.O.C.• Tenacious adhesion
phySical data
Finish: Low GlossColour: YellowWeightSolids: 73.4%+/-2%mixedVolumeSolids: 60%+/-2%mixedV.O.C. 296grams/litermixed 2.47lbs/usgal.mixedDensity: 10.08lbs/USG/MixedDryFilmWeight: 0.0076lbs/sqft/mil 1.48g/m²/µ
recommended SyStemS
• 9600DurathaneGlossPolyurethaneEnamel.MeetsMIL-PRF-85285D,TypeI
• 9800DurathaneSemi-GlossPolyurethaneEnamel• 9700DurathaneFlatPolyurethaneEnamel
inStructionS for uSe
mixing inStructionS
Surface preparation
IMPORTANT - The information contained in this data sheet pertains to material currently offered and represents the results of laboratory evaluation and is intended as a guide. Sincethecustomer’sapplicationrequirementsarenotunderourcontrol,TempoAerospaceInc.cannotmakeanywarrantiesorguaranteesfortheresultsobtained.
Spraying ViScoSity
application method
4500-P-215Y
SAE-AMS-QQ-A-250/4(T3temper):MIL-C-5541,class1A(conversioncoating_pretreatment.SAE-AMS-QQ-A-250/4(0temper):MIL-A-8625,typeIorIC(anodized)pretreatmentSAE-AMS-QQ-A-250/5(T3temper):Deoxidized1pretreatment.SAE-AMS-QQ-A-250/5(T3temper):MIL-C-5541,class1A(conversioncoating)pretreatment..Applyoverpretreatedmetal.Onfiberglass-reinforcedplastic,apriorcoatingofprimertoMIL-C-8514willfacilitatestrippingwithoutdamagetothefiberglass.
Components: TwoCure: 4500-C-215MixRatio: 3:1byvolume,Base/CureInductionTime: 30minutesPotLIfe: 4hours@25°C(75°F)Reducer: 20-4301or4500-S-81(MIL-T-81772,TypeII)
Mix3:1byvolumeBase/Cure.Werecommendusingasquirrelmixerorequivalentandmixthoroughlyfor5minutesminimum.Allow30minutesinductiontimebeforeusing.Mixonlysufficientmaterialtousewithina4-hourperiod.AlwaysaddCure componenttoBasecomponent-NEVER THE REVERSE. Never mix coating or individual component from one vendor with that of another vendor.
20-40#4FordCup
Allowforapplicationlossandsurfaceirregularities.Application: Conventionalairspray;HVLPorairassisted airless are recommended for best atomization.Reduction: Reducewith20-4301orthinnerconforming toMIL-T-81772,Ty.IIwhenrequiredby contract.Inareaswhereairquality regulationsrestrictvolatileemissions, DO NOT EXCEED 340g/L (2.8 lb/gal) with thinner (approx 8% by volume).
![Page 2: Tecprior coating of primer to MIL-C-8514 will facilitate stripping without tothefiberglass. Components: Two Cure: 4500-C-215 Mix Ratio: 3:1 by volume, Base / Cure Inductionime: 30](https://reader035.vdocuments.net/reader035/viewer/2022071418/611672cf5146424ffa100395/html5/thumbnails/2.jpg)
Technical Data SheetTempo Aerospace Inc. Tel: 416.746.2233 Fax: 416.746.2235
Updated May 2012
reSiStance table
Impact Resistance GE,Model#172 3.6 lbs
Solvent Resistance >+25MEKDoubleRubs
Hydraulic Fluid Resistance
[email protected]°C±2°C(150°±5°F)in synthetic hydraulic fluid conformingtoMIL-PRF-83282(Skydrol500B).
Salt Spray Resistance >2000hourssaltsprayresistance
Distilled Water 4daysimmersionat49°C(120°F)
SubStrateS:• Aluminum• Fiberglass-reinforcedplastic• Composite
Note: all physical and chemical resistance tests conducted afterone-weekcuretimeat20-25°C(70-75°F)onproperlycleaned substrate.
AirSpray:DeVibissJGAorMBCgunwith“E”needletip,#704caporequivalent.Adjustpressureandfluiddeliveryforproperatomization.
TotalDryFilmRecommendation0.6-0.9Mils(15-23microns)Calculated Coverage at:1.0Mils: 976ft²25Microns: 90.7m²
Temperature: 15-35°C(59-95°F)RelativeHumidity: 35-75%Note:Substrateandairtemperaturemustbeaminimumof3°C(5°F)abovetheDewPoint
Drytimeat24°C+/-3°C(75°F),50%relativehumidity.ToTouch: 2-2.5hoursTackFree: 3.5-4hoursToRecoat: Min5hours<20hoursDryThrough: 24hoursMaybeforceddriedat60-71°C(140-160°F)for20-30minutes NOTE:Allow15-30minflashoffbeforeforcedry
Cleaner: 20-4301,4500-S-81,S-10
FlashPoint: 37°C(98.6°F)SetaflashclosedcupShelfLife: 18monthsunmixedStoreinasafe,dryareaatatemperaturebetween5and38°C(40and100°F).Ensuretherearenosparksorpossibleignitionsources.
PleaserefertotheMaterialSafetyDataSheet(MSDS)forinformationregardinghealth,physicalandenvironmentalhazards,handlingprecautionsandrecommendedfirstaidprocedures.Forindustrial and automotive use only. Spray equipment must be adequately grounded.
recommended film build thickneSS & coVer rate
Storage & Shipping
dry time
Safety precautionS
clean up
IMPORTANT - The information contained in this data sheet pertains to material currently offered and represents the results of laboratory evaluation and is intended as a guide. Sincethecustomer’sapplicationrequirementsarenotunderourcontrol,TempoAerospaceInc.cannotmakeanywarrantiesorguaranteesfortheresultsobtained.
enVironmental conditionS
4500-P-215Y
equipment