CHAPTER-II Thin Film Deposition Processes and Characterization Techniques Part-A Thin Film Deposition Processes 2A.1. Introduction to Thin Films 45 2A.2. Applications of Thin Films 46 2A.3 Thin Film Deposition Processes 53 2A.3.1 Physical Processes 56 2A.3.2 Chemical and Electrochemical Processes 57 Part-B Characterization Techniques 2. B.1. Introduction 77 2. B.1.1. Cyclic Voltammetery (CV) and Linear 77 Sweep Techniques (LSV) 2. B.1.2. Thickness Measurements 82 2. B.1.3.Optical Absorption 82 2. B.1.4. X-Ray Diffraction Technique (XRD) 85 2. B.1.5. Raman Spectral Study 86 2.B.1.6 Scanning Electron Microscopy (SEM). 92 2. B.1.7. Energy Dispersive Analysis by x- Rays 95 measurement (EDS) 2. B.1.8.Transport Properties 95 2. B.1.9. Atomic Force Microscopy (AFM) 100 References 102

Upload: vantruc

Post on 23-Mar-2018

239 views

Category:

Documents


3 download

TRANSCRIPT

Page 1: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

CHAPTER-II

Thin Film Deposition Processes and Characterization Techniques

Part-A

Thin Film Deposition Processes

2A.1. Introduction to Thin Films 45

2A.2. Applications of Thin Films 46

2A.3 Thin Film Deposition Processes 53

2A.3.1 Physical Processes 56

2A.3.2 Chemical and Electrochemical Processes 57

Part-B

Characterization Techniques

2. B.1. Introduction 77

2. B.1.1. Cyclic Voltammetery (CV) and Linear 77

Sweep Techniques (LSV)

2. B.1.2. Thickness Measurements 82

2. B.1.3.Optical Absorption 82

2. B.1.4. X-Ray Diffraction Technique (XRD) 85

2. B.1.5. Raman Spectral Study 86

2.B.1.6 Scanning Electron Microscopy (SEM). 92

2. B.1.7. Energy Dispersive Analysis by x- Rays 95

measurement (EDS)

2. B.1.8.Transport Properties 95

2. B.1.9. Atomic Force Microscopy (AFM) 100

References 102

Page 2: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

45

Chapter-II

Part-A

Thin Film Deposition Processes

2. A.1 Introduction to Thin Films

The field of material science and engineering community’s ability to conceive the novel

materials with extraordinary combination of chemical, physical and mechanical,

properties has changed the modern society. There is a increasing technological

progress. Modern technology requires thin films for different applications [1]. Thin film

technology is the basic of astounding development in solid state electronics. The

usefulness of the optical properties of metal films, and scientific curiosity about the

behavior of two-dimensional solids has been responsible for the immense interest in the

study science and technology of the thin films. Thin film studies have directly or

indirectly advanced many new areas of research in solid state physics and chemistry

which are based on phenomena uniquely characteristic of the thickness, geometry, and

structure of the film [1].

When we consider a very thin film of some substance, we have a situation in which the

two surfaces are so close to each other that they can have a decisive influence on the

internal physical properties and processes of the substance, which differ, therefore, in a

profound way from those of a bulk material. The decrease in distance between the

surfaces and their mutual interaction can result in the rise of completely new

phenomena. Here the one dimension of the material is reduced to an order of several

atomic layers which creates an intermediate system between macro systems and

molecular systems, thus it provides us a method of investigation of the microphysical

nature of various processes. Thin films are especially appropriate for applications in

microelectronics and integrated optics. However the physical properties of the films like

electrical resistivity do not substantially differ from the properties of the bulk material.

For a thin film the limit of thickness is considered between tenths of nanometer and

several micrometers.

Page 3: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

46

Thin film materials are the key elements of continued technological advances

made in the fields of optoelectronic, photonic, and magnetic devices. The processing of

materials into thin films allows easy integration into various types of devices. The

properties of material significantly differ when analysed in the form of thin films. Most of

the functional materials are rather applied in thin film form due to their specific electrical,

magnetic, optical properties or wear resistance. Thin film technologies make use of the

fact that the properties can particularly be controlled by the thickness parameter. Thin

films are formed mostly by deposition, either physical or chemical methods. Thin films,

both crystalline and amorphous, have immense importance in the age of high

technology. Few of them are: microelectronic devices, magnetic thin films in recording

devices, magnetic sensors, gas sensor, A. R. coating, photoconductors, IR detectors,

interference filters, solar cells, polarizer’s, temperature controller in satellite,

superconducting films, anticorrosive and decorative coatings.

2.A.2. Applications of Thin Films

Although the study of thin film phenomena dates back well over a century, it is

really only over the last four decades that they have been used to a significant extent in

practical situations. The requirement of micro miniaturization made the use of thin and

thick films virtually imperative. The development of computer technology led to a

requirement for very high density storage techniques and it is this which has stimulated

most of the research on the magnetic properties of thin films. Many thin film devices

have been developed which have found themselves looking for an application or,

perhaps more importantly market. In general these devices have resulted from research

into the physical properties of thin films.

Secondly, as well as generating ideas for new devices, fundamental research

has led to a dramatic improvement in understanding of thin films and surfaces. This in

turn has resulted in a greater ability to fabricate devices with predictable, controllable

and reproducible properties. The cleanliness and nature of the substrate, the deposition

conditions, post deposition heat treatment and passivation are vital process variables in

thin film fabrication. Therefore, prior to this improvement in our understanding of thin

films, it has not really been possible to apply them to real devices.

Page 4: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

47

Thirdly, much of the finance for early thin film research originated from space and

defence programmes to which the device cost is less important than its lightweight and

other advantages, the major applications of thin film technology are not now exclusively

in these areas but rather often lie in the domestic sector in which low cost is essential

[1,2].

Thin film materials have already been used in semiconductor devices, wireless

communications, telecommunications, integrated circuits, rectifiers, transistors, solar

cells, light-emitting diodes, photoconductors, light crystal displays, magneto-optic

memories, audio and video systems, compact discs, electro-optic coatings, memories,

multilayer capacitors, flat-panel displays, smart windows, computer chips, magneto-

optic discs, lithography, micro electromechanical systems (MEMS), and multifunctional

emerging coatings, as well as other emerging cutting technologies.

i) Optical Coatings:

An optical coating is one or more thin layers of material deposited on an optical

component such as a lens or mirror, which alters the way in which the optic reflects and

transmits light. One type of optical coating is an antireflection coating, which reduces

unwanted reflections from surfaces, and is commonly used on spectacle and

photographic lenses. Another type is the high-reflector coating which can be used to

produce mirrors which reflect greater than 99.99% of the light which falls on them. More

complex optical coatings exhibit high reflection over some range of wavelengths, and

anti-reflection over another range, allowing the production of dichroic thin-film optical

filters.

ii) Photovoltaic:

In the familiar rigid solar panel, the energy of incoming photons is converted to

electricity in cells containing two thin layers of crystalline silicon. What makes roll-to-roll

production of flexible film solar products possible is replacement of the crystalline silicon

with amorphous silicon, supplied in high-solids slurries that can be deposited onto

substrates by web-converting processes like slot die coating. Microlayer film, EDI can

Page 5: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

48

outfit its Contour cast film dies with a new system, based on technology licensed from

‘The Dow Chemical Company’, which makes it possible to produce film of standard

thickness, yet with dozens of exceedingly thin ‘micro-layers’. The multiple layer-to-layer

interfaces create a torturous path for gas molecules and thus substantially increase the

barrier properties of the film. This is critical for photovoltaic applications, which require

barrier layers to prevent performance losses caused by infiltration of oxygen or moisture

vapour.

"Though as yet little known in the solar industry, the continuous-web production

methods familiar to EDI and its converter customers are a key to developing high-

volume, low-cost production of solar electric systems," said Miller. "In working with solar

product manufacturers, EDI draws on extensive experience in other applications that

require thin-gauge, optically clear, close-tolerance films and coatings with critical

functionalities, including films and coatings for flat panel displays and flexible batteries

particularly relevant, since solar cells are a kind of battery. In comparison with

conventional coating methods, such as spray, roll, and spin coating, slot dies provide

greater control over coating weight and distribution because they are closed systems

into which coating material is pumped at closely pre-determined rates; in turn this

greater control makes possible thinner coatings,"

Many in the solar power industry and the investment community, believe the

arrival of grid parity, the point when cost of electricity generated by a rooftop

photovoltaic (PV) cell system is equivalent to that purchased from an electrical utility will

mark a major inflection point for the market that will deliver a huge increase in growth.

However, even when true grid parity arrives, it’s unlikely to generate an abrupt rise in

solar system installations due to the high upfront costs and the long-term return of

investing in a rooftop photovoltaic system, according to iSuppli Corp. In fact, growth is

set to moderate during the years when grid parity arrives for various regions of the world

as the industry enters a more mature phase.

Page 6: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

49

iii) Semiconductor:

Historically, the semiconductor industry has relied on flat, two-dimensional chips

upon which to grow and etch the thin films of material that become electronic circuits for

computers and other electronic devices. This thin layer (only a couple of hundred

nanometers thick) can be transferred to glass, plastic or other flexible materials,

opening a wide range of possibilities for flexible electronics. In addition, the

semiconductor film can be flipped as it is transferred to its new substrate, making its

other side available for more components. This doubles the possible number of devices

that can be placed on the film. By repeating the process, layers of double-sided, thin-

film semiconductors can be stacked together, creating powerful, low-power, three-

dimensional electronic devices. "It's important to note that these are single-crystal films

of strained silicon or silicon germanium. The strain is introduced in the way we form the

membrane. Introducing strain changes the arrangement of atoms in the crystal such

that we can achieve much faster device speed while consuming less power."

For non-computer applications, flexible electronics are beginning to have

significant impact. Solar cells, smart cards, radio frequency identification (RFID) tags,

medical applications, and active-matrix flat panel displays could all benefit from the

development. The techniques could allow flexible semiconductors to be embedded in

fabric to create wearable electronics or computer monitors that roll up like a window

shade. "This is potentially a paradigm shift. The ability to create fast, low-power,

multilayer electronics has many exciting applications. Silicon germanium membranes

are particularly interesting. Germanium has a much higher adsorption for light than

silicon. By including the germanium without destroying the quality of the material, we

can achieve devices with two to three orders of magnitude more sensitivity." That

increased sensitivity could be applied to create superior low-light cameras, or smaller

cameras with greater resolution.

iv) Photo Electrochemical Cells (PEC):

In photoelectrochemical experiments, irradiation of an electrode with light that is

absorbed by the electrode material causes the production of a current (a photocurrent).

Page 7: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

50

The dependence of the photocurrent on wavelength, electrode potential, and solution

composition provides information about the nature of the photoprocess, its energetics,

and its kinetics. Photocurrents at electrodes can also arise because of photolytic

processes occurring in the solution near the electrode surface. Photoelectrochemical

studies are frequently carried out to obtain a better understanding of the nature of the

electrode-solution interface. Photoelectrochemistry and Electrogenerated

Chemiluminescence photocurrent can represent the conversion of light energy to

electrical and chemical energy; such processes are also investigated for their potential

practical applications. Since most of the studied photoelectrochemical reactions occur at

semiconductor electrodes, we will review briefly the nature of semiconductors and their

interfaces with solutions. Consideration of semiconductor electrodes also helps in

gaining a microscopic understanding of electron-transfer processes at solid-solution

interfaces.

v) Optoelectronic:

An optoelectronic thin-film chip, comprising at least one radiation-emitting region

in an active zone of a thin-film layer and a lens disposed downstream of the radiation-

emitting region, said lens being formed by at least one partial region of the thin-film

layer, the lateral extent of the lens being greater than the lateral extent of the radiation-

emitting region. The thin-film layer is provided for example by a layer sequence which

is deposited epitaxially on a growth substrate and from which the growth substrate is at

least partly removed. That is to say that the thickness of the substrate is reduced. In

other words, the substrate is thinned. It is furthermore possible for the entire growth

substrate to be removed from the thin-film layer. The thin-film layer has at least one

active zone suitable for generating electromagnetic radiation. The active zone may be

provided for example by a layer or layer sequence which has a pn junction, a double

heterostructure, a single quantum well structure or a multiple quantum well structure.

Particularly preferably, the active zone has at least one radiation-emitting region. In this

case, the radiation-emitting region is formed for example by a partial region of the active

zone. Electromagnetic radiation is generated in said partial region of the active zone

during operation of the optoelectronic thin-film chip.

Page 8: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

51

vi) Flat Panel Displays:

Developed from the Mykrolis contamination control technologies, Entegris

provides a broad portfolio of liquid and gas contamination control technologies for the

flat panel display fabrication. The Flat Panel Display (FPD) fabrication environment is

among the world’s most competitive and technologically complex. Device designers and

manufacturers continually strive to satisfy the worldwide consumer’s appetite for larger

displays, greater pixel resolution and feature-rich performance – all at a lower cost than

the previous generation of technology. The need to control contamination in air, gas and

liquid process streams is now a paramount focus of process engineers and designers.

Entegris provides the solutions to succeed under these extreme conditions.

vii) Data Storage:

As the data storage density in cutting edge microelectronic devices continues to

increase, the superparamagnetic effect poses a problem for magnetic data storage

media. One strategy for overcoming this obstacle is the use of thermomechanical data

storage technology. In this approach, data is written by a nanoscale mechanical probe

as an indentation on a surface, read by a transducer built into the probe, and then

erased by the application of heat. An example of such a device is the IBM millipede,

which uses a polymer thin film as the data storage medium. It is also possible, however,

to use other kinds of media for thermomechanical data storage, and in the following

work, we explore the possibility of using thin film Ni-Ti shape memory alloy (SMA).

Previous work has shown that nanometer-scale indentations made in martensite phase

Ni-Ti SMA thin films recover substantially upon heating. Issues such as repeated

thermomechanical cycling of indentations, indent proximity, and film thickness impact

the practicability of this technique. While there are still problems to be solved, the

experimental evidence and theoretical predictions show SMA thin films are an

appropriate medium for thermomechanical data storage.

Page 9: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

52

viii) Super Capacitor:

Since first patents were in the 1950, the idea of storing charge in the electric

double layer that founds at the interface between a solid and an electrolyte has

presented itself as an attractive notation while was considerable development was

carried out by the slander oil company, Cleveland, Ohio (SOHIO) in the 1960 a lack of

sales lead them to license the technology to Nippon electric company. The first high

power double layer capacitor were developed for military applications by the pinnacle

research institute in 1982.

Conventional capacitor stores energy electrostatically on two electrode separated by a

dielectric, the capacitance of which is C= €A/d, where € being the dielectric constant, A

surface area and d the dielectric thickness. In a double layer capacitor, charges

accumulate at the boundary between electrode and electrolyte to form two charge

layers with separation of several Angstroms. Super capacitors are electrochemical

energy storage device. The away that super capacitor store energy is based in principal

on two types capacitive behaviour the electrical double layer capacitance from the pure

electrostatic charge accumulation at the electrode interface and the pseudo-capacitance

developed from fast and reversible surface redox process at characteristic potential.

Super capacitor integrated in to hybrid vehicle, power source, power control, multi

source supply, fuel save etc.

ix) Gas Sensors:

Advancements in micro technology and the evolution of new nonmaterial and

devices have been playing a key role in the development of very accurate and reliable

sensors. The technology of sensors has developed tremendously in the last few years

owning many scientific achievements from various experiments, offering newer

challenges and opportunity to the quest for every smaller devices capable of molecular

level imaging and monitoring of pathological samples and the macromolecules has

lately gained the focus of attention of the scientific community, particularly for remote

monitoring due to the increasing need for environmental safety and health monitoring.

Page 10: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

53

Gas sensors generally operate different principles and various gas sensing

elements have been developed have been past years, out of which resistive metal oxide

sensors comprise a significant part. However these sensing elements typically operate

at an elevated temperature for maximum performance. This makes higher power

consumption which is not suitable for the inflation. Over the last decayed carbon

nanotube has attracted considerable attention, and great efforts have been made to

exploit their unusual electronic and mechanical properties. These properties make them

potential candidates for building blocks of active materials in nanoelectronics, field

emission devices, gas storage and gas sensors. Among these the room temperature

gas sensing property is very attractive for many applications.

2. A.3. Thin Film Deposition Processes:

The vast varieties of thin film materials, their deposition processing and

fabrication techniques, spectroscopic characterization and optical characterization

probes that are used to produce the devices. It is possible to classify these techniques

in two ways [1, 2].

Physical Process

Chemical Process.

Physical method covers the deposition techniques which depends on the

evaporation or ejection of the material from a source, i.e. evaporation or sputtering,

whereas chemical methods depend on physical properties.Structure-property

relationships are the key features of such devices and basis of thin film technologies.

Underlying the performance and economics of thin film components are the

manufacturing techniques on a specific chemical reaction [3]. Thus chemical reactions

may depend on thermal effects, as in vapour phase deposition and thermal growth.

However, in all these cases a definite chemical reaction is required to obtain the final

film.

When one seeks to classify deposition of films by chemical methods, one finds

that they can be classified into two classes. The first of these classes is concerned with

the chemical formation of the film from medium, and typical methods involved are

Page 11: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

54

electroplating, chemical reduction plating and vapour phase deposition. A second class

is that of formation of this film from the precursor ingredients e.g. iodization, gaseous

iodization, thermal growth, sputtering ion beam implantation, CVD, MOCVD and

vacuum evaporation.

The methods summarized in table 2.1 are often capable of producing films

defined as thin films, i.e. 1 µm or less and films defined as thick films, i.e. 1 µm or more.

However, there are certain techniques which are only capable of producing thick films

and these include screen printing, glazing, electrophoretic deposition, flame spraying

and painting.

Page 12: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

55

Table:2.1 Classification of Thin Film Deposition Techniques

Sputtering Evaporation Gas Phase Liquid Phase Glow discharge

DC sputtering

Vacuum

Evaporation

Chemical vapour

Deposition

Electro-deposition

Triode

sputtering

Resistive

heating

Evaporation

Laser Chemical

vapour deposition

Chemical bath

deposition (CBD) /

Arrested

Precipitation

Technique (APT)

Getter

sputtering

Flash

Evaporation

Photo-chemical

vapour deposition

Electro less

deposition

Radio

Frequency

sputtering

Electron beam

Evaporation

Plasma enhanced

vapour deposition

Anodisation

Liquid phase

Epitaxy

Magnetron

sputtering

Laser Evaporation Metal-Organo

Chemical Vapour

Deposition (MO-

CVD)

Sol- gel

Spin Coating

Ion Beam

sputtering

Spray-pyrolysis

technique (SPT)

A.C.

Sputtering

Arc Ultrasonic (SPT)

7) R. F. Heating Polymer assisted

deposition (PAD)

PHYSICAL CHEMICAL

Thin Film Deposition Techniques

Page 13: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

56

2.A.3.1. Physical Processes

2.A.3.1.1 Physical Vapour Deposition (PVD):

PVD processes proceed along the following sequence of steps:

a) The solid material to be deposited is physically converted to vapour

phase;

b) The vapour phase is transported across a region of reduced pressure

from the source to the substrate;

c) The vapour condenses on the substrate to form the thin film.

The conversion from solid to vapour phase is done through physical

dislodgement of surface atoms by addition of heat in evaporation deposition or by

momentum transfer in sputter deposition. The third category of PVD technique is the

group of so called augmented energy techniques including ion, plasma or laser assisted

depositions.

2.A.3.1.2 Evaporation:

Evaporation or sublimation techniques are widely used for the preparation of thin

layers. A very large number of materials can be evaporated and, if the evaporation is

undertaken in vacuum system, the evaporation temperature will be very considerably

reduced, the amount of impurities in the growing layer will be minimised.

In order to evaporate materials in a vacuum, a vapour source is required that will

support the evaporant and supply the heat of vaporisation while allowing the charge of

evaporant to reach a temperature sufficiently high to produce the desired vapour

pressure, and hence rate of evaporation, without reacting chemically with the evaporant.

To avoid contamination of the evaporant and hence of growing film, the support material

itself must have a negligible vapour pressure and dissociation temperature of the

operating temperature.Laser beam evaporation has also come in to use recently. The

laser source is situated outside the evaporation system and the beam penetrates

through a window and is focused on to the evaporate material, which is usually fine

powder form [4].

Page 14: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

57

2.A.3.1.3 Sputtering:

If a surface of target material is bombarded with energetic particles, it is possible

to cause ejection of the surface atom: this is the process known as sputtering. The

ejected atoms can be condensed on to a substrate to form a thin film. This method has

various advantages over normal evaporation techniques in which no container

contamination will occur. It is also possible to deposit alloy films which retain the

composition of the parent target material. DC sputtering, radio frequency sputtering and

magnetron sputtering methods are the oldest types of sputtering used[5]. High pressure

oxygen sputtering and facing target sputtering are the two new methods introduced for

deposition of thin films for applications in superconducting and magnetic films.

2.A.3.1.4. Ion Plating:

In this atomistic, essentially sputter-deposition process the substrate is subjected

to a flux of high energy ions, sufficient to cause appreciable sputtering before and

during film deposition.

The advantages of physical methods are laid in dry processing, high purity and

cleanliness, compatibility with semiconductor integrated circuit processing and epitaxial

film growth. However, there are certain disadvantages such as slow deposition rates,

difficult stoichiometry control, high temperature post deposition annealing often required

for crystallization and high capital expenditure[6].

2.A.3.2. Chemical and Electrochemical Methods:

Among chemical and electrochemical methods the most important are chemical vapour

deposition, cathode electrolytic deposition, anodic oxidation and Chemical Bath

Deposition

2.A.3.2.1.Chemical Vapour Deposition:

Chemical vapour deposition can be defined as a material synthesis method in

which the constituents of vapour phase react together to form a solid film at surface.

The chemical reaction is an essential characteristic of this method; therefore, besides

Page 15: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

58

the control of the usual deposition process variables, the reactions of the reactants must

be well understood. Various types of chemical reactions are utilised in CVD for the

formation of solids are pyrolysis, reduction, oxidation, hydrolysis, synthetic chemical

transport reaction etc.

2.A.3.2.2. Chemical Bath Deposition (Deposition by Chemical Reactions):

Thin films can be deposited by number of physical and chemical techniques and

can be classified as shown in Table 2.1. Among the methods mentioned in the Table

2.1, the chemical methods are economical and easier than that of the physical methods.

Physical methods are expensive but give relatively more reliable and more reproducible

results. Most of the chemical methods are cost effective, but their full potential for

obtaining devise quality films has not been fully explored [2]. But there is no ideal

method to prepare thin films, which will satisfy all possible requirements. Among the

chemical methods, the electrodeposition technique (ED) is the most popular technique

today because large number of conducting and semiconducting thin films can be

prepared by this technique.

Among the chemical methods of thin film depositions, Chemical Bath Deposition

(CBD) is probably the most simplest method available for this purpose and it is also

known as Chemical Solution Deposition (CSD) or Chemical Deposition (CD). It is not a

new technique as early as in 1835 Liebig reported the first deposition of silver, the silver

mirror deposition using a chemical solution technique. The deposition technique was

first described in 1869. The only requirements of these methods are a vessel to contain

the solution (usually an aqueous solution of common chemicals) and the substrate on

which deposition is to be carried out. In addition to this various complications such as

some mechanism for stirring and a thermostated bath to maintain a specific and

constant temperature are options that may be useful. The first general review on this

topic was published by Chopra et al. in 1982[7]. Next review was published by

Lokhande [8]. Then a comprehensive and general review was published by Lincoln et

al. in 1998[9].

Page 16: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

59

Chemical deposition is the deposition of films on a solid substrate from a reaction

occurring in a solution using the prototypical MS (metal sulphide) as an example, a M

salt in solution can be converted to MS by adding sulphide ions (eg. H2S), MS

immediately precipitates unless the solution is very dilute- a few milli molar or less in

which case MS often forms as a colloidal solution. Another pathway for MS formation,

one that does not require free sulphide ions, is decomposition of a MS-thiocomplex. In

MS, the trick is to control the rate of these reactions so that they occur slowly enough to

allow the MS either to form gradually on the substrate itself (at the early stages of

deposition) or to the growing film, rather than aggregate in to larger particles in solution

and precipitate out.

This rate control can be accomplished by generating the sulphide slowly in the

deposition solution. The rate of generation of sulphide, and therefore reaction, can be

controlled through a number of parameters, in particular the concentration of sulphide

forming precursor, solution temperature, and pH. Although CBD can be carried out both

acidic and alkaline solutions, most of the CBD reactions have been carried out in

alkaline solutions.

a) Basic Mechanism of Chemical Bath Deposition:

In spite of the fact that CBD has been in use for a long time and that the

reactions involved appear to be quite simple, the mechanism of the CBD process is

often ambiguous There are several different mechanisms of CBD. These can be divided

into four fundamentally different types. Deposition of Cdmium Sulphide is taken as an

example.

The simple ion by ion mechanism:

[Cd(NH3)4]2+ Cd2+ + 4NH3 (dissociation of complex to free Cd2+ ions) ------ (2.1)

(NH2)2CS + 2OH- S2- + CN2H2 + 2H2O (formation of sulphide ions) --(2.2)

Cd2+ + S2- CdS (CdS fromation by ionic reaction) -------------- (2.3)

Page 17: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

60

The simple cluster (hydroxide) mechanism:

nCd2+ + 2nOH [Cd(OH)2]n (formation of a Cd(OH)2 cluster) ------------ (2.4)

[Cd(OH)2]n + nS2- nCdS + 2nOH (exchange reaction) ------------- (2.5)

The complex decomposition ion - by - ion mechanism:

(NH2)2CS + Cd2+ [(NH2)2CS-Cd]2+ --------------- (2.6)

[(NH2)2CS-Cd]2+ + 2OH- CdS + CN2H2 + 2H2O -------------- (2.7)

The complex decomposition cluster mechanism:

[Cd(OH)2]n + (NH2)2CS [Cd(OH)2](n-1) (OH)2Cd------S-----C(NH2)2---------- (2.8)

[Cd(OH)2](n-1) (OH)2Cd-----S----C(NH2)2 [Cd(OH)2](n-1) + CdS + CN2H2 + 2H2O

------------ (2.9)

The last reaction continues until conversion of all the Cd(OH)2 to CdS.

The first two mechanisms involved free sulphide ions (or other anions). While the

last two are based on breaking of a carbon-chalcogen bond and do not involve

formation of free chalcogenide [10].

Chemical reaction either takes place on the surface of the dipped substrate or in

the solution itself, where a mixing of components on the surface to be coated is

required. Most of the coatings are formed in a two step fashion;

i) “Sensitizing” the surface for the nucleation reaction of the adhering coating

layer.

ii) Deposition of coating by selected reactions.

The most widely used deposition methods are listed below

A) Homogeneous chemical reduction of a metal ion solution by a reducing

agent regardless the substrates.

Page 18: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

61

B) Electroless plating for the deposition of metallic coating by controlled

chemical reduction that is catalysed by the metal or alloy being deposited.

C) Conversion coatings forming a sacrificial layer containing compound of the

metal substrate.

D) Displacement deposition or galvanic deposition makes use of the

electronegativity differences of metals.

E) Arrested precipitation technique means a metal ion is arrested by organic

complexing agent which is then made available by slow dissociation of the

organometallic complex at specific pH value.

Among the various chemical deposition systems, chemical bath deposition has

attracted a great deal of attention because of its overriding advantages over the other

conventional thin film deposition methods.

The chemical bath deposition method for the preparation of thin films has

recently been shown to be an attractive technique because of its simplicity,

convenience, low cost and low temperature, and it has been successfully used for

depositing ternary metal chalcogenide thin films [11]. Understanding of the chemistry

and physics of the various process involved in a deposition processes has now made

possible to obtain undoped/doped, multicomponent semiconductor thin films of

usual/unusual and metastable structure.

b) Selection of Deposition Process:

No single technique is ideally suited for preparation of large area thin films with

all the desired properties. Hence choice and selection of deposition process plays a vital

role in the formation of good quality thin films, and while selecting a particular technique

it should be tested satisfactorily for the following aspects:

Cost effectiveness.

It should be able to deposit desired material.

Film microstructure and deposition rate should be controlled.

Stoichiometry should be maintained as that of the starting materials.

Operation at reduced temperature.

Page 19: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

62

Adhesive at reduced temperature.

Abundance of deposit materials

Scaling up of the process.

Masking of the substrates.

Control on film substrate interface and defects created in the film.

Among the various techniques discussed above, arrested precipitation technique

as well as electrodeposition technique used for synthesis of binary transition metal

dichalcogenides and hybrid process of these two is employed in the synthesis of ternary

mixed transition metal dichalcogenide in the present investigation.

2.A.3.2.3. Arrested Precipitation Technique:

Arrested precipitation technique (APT) is modified chemical bath

deposition process. The arrested precipitation technique based on Ostwald ripening law

is simple and inexpensive method used for deposition of wide variety of metal

chalcogenide thin films. Arrested precipitation technique can be distinguished from other

conventional techniques as follows:

It is ideally suited for large area thin film depositions; substrate surfaces of

both accessible and non-accessible nature could easily be deposited.

It is simple, inexpensive and does not require sophisticated instrumentation.

The deposition is usually at low temperature and avoids oxidation or corrosion

of the metallic substrates.

Stoichiometry of the deposits can be maintained since the basic building

blocks are ions rather than atoms.

Slow film formation process facilitates better orientation of the crystallites with

improved grain structures over the substrate surface.

Doped and mixed films could be obtained by merely adding the mixant /

dopant solution directly into the reaction bath.

Electrical conductivity of the substrate material is not an important criterion.

Page 20: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

63

An intimate contact between reacting species and the substrate material

permits pinhole free and uniform deposits on the substrates of complex shapes

and sizes.

Wide varieties of conducting / nonconducting substrate materials can be

used.

Dissociation rate of organometallic complex to release free metal ions for

reaction is well control by maintaining the pH of reacting solution.

2.A.3.2.4 Anodic Oxidation:

Anode oxidation (anode electrolytic deposition) is used mainly in the formation of

films of the oxides of certain metals, e.g. ,Al, Ta, Nb, Ti, and Zr. The oxidized metal is

an anode dipped in the electrolyte from which it attracts the oxygen ions. The ions pass

through the already formed oxide film by diffusion forced by a strong electric field and

combine with metallic atoms to form molecules of the oxide. For anode oxidation it is

possible to use either the constant current or constant voltage method. Solutions or

melts of various salts or in some cases acids are used as electrolytes. This is an

electrolytic method for producing oxide films on the surface of metal.

2. A.3.2.5. Cathodic Deposition:

This is a standard method of electroplating. Two metal electrodes are dipped into

an electrolyte solution and on application of an external field across the electrodes;

metal ions from the solution are deposited on cathode as a film. Deposition of the films

is mainly controlled by the electrical parameters such as, electrode potential and current

density.The mass of the substance deposited is proportional to the amount of electrical

charge. The proportionality constant is the electrochemical equivalent of the given

substance, which is for example, is 2.04 x 10-3 g./C, for Au and 0.09 x 10-3 g/C for Al.

By this method it is possible to deposit films only on conducting substrates.

a) Basics of Electrochemical Processing:

Electrodeposition, also known as electrochemical deposition or electro

crystallization, it is one of the most useful techniques for preparing thin films on the

Page 21: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

64

surface of conducting substrate. Besides advantages such as low temperature and

pressure, the technique is directly related to many academic challenges in materials

chemistry and physics. Electrochemical technique such as cyclic voltammetry (CV) and

chronoamperometry (CA) play dual roles, firstly, being the techniques for deposition and

secondly, being utilized for determination of reaction mechanism [3].

The electrodeposition is the simplest of the chemical methods, and it has many

advantages [2] like

1. Structurally and compositionally modulated alloys and compounds can be deposited

which are not possible with other deposition techniques.

2. In most of the cases the deposition can be carried out at room temperature enabling

to form the semiconductor junctions without interdiffusion.

3. Deposition on complex shapes is possible.

4. Toxic gaseous precursors need not to be used (unlike gas phase methods).

5. The deposition process can be controlled more accurately and easily

Electrodeposition of metallic films has long been known and used for preparing

metallic mirrors and corrosion resistant surfaces, etc. During last two decades,

electrodeposition has become a tool of materials technology for obtaining films of wide

variety of materials including binary-ternary semiconductors, high Tc superconductors,

polymer films etc.

b) Mechanism of Electrodeposition:

Electrodeposition is process of depositing metal atoms on a conducting substrate

by passing direct current through solution containing the metal(s) ions to be deposited.

The schematic diagram explaining the electrodeposition is shown in figure 2.1.

The typical electrodeposition set up consists of following,

1. Electrolyte

2. Cathode and anode

3. Source of electricity.

Page 22: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

65

When direct current is passed through cathode and anode, immersed in electrolyte

containing the metal(s) ions, the metal ions get attracted towards the cathode,

neutralized electrically by receiving electrons and get deposited on cathode. The

deposition is controlled by monitoring the amount and the rate of charge passing

through the electrolyte. Thus the electrical energy is used to cause chemical change.

This electrodeposition process can be written as

Mn+ + ne- M ------ (2.10)

On the other hand, if the electrolyte contains more than one ionic species that can be

simultaneously deposited then the electrodeposition process for, say two types of ionic

species can be written as

Mn+ + ne- M ------ (2.11)

N+ + e- N ------ (2.12)

Or

Page 23: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

66

M+ + N+ + 2e- MN --------- (2.13)

Accordingly, one can deposit a compound or an alloy of a multicomponent system [12].

c) Faraday’s Laws of Electrolysis:

Michael Faraday (1834) established the relationship between the electricity

passed through the electrolyte and the chemical change produced in terms of solid

material liberated/deposited at the electrode.

Faraday’s First Law

“The amount of substance liberated or deposited on the electrode is

proportional to the quantity of electricity passed.”

Mathematically, W Q where, W is the amount of substance liberated in grams, and Q

is the quantity of electricity passed through electrolyte, in coulombs. If current strength I

is passed for t seconds, then the quantity of electricity.

Quantity of electricity = Current strength x time

Q = c t ……….(2.14)

W c t or W = z c t ……….(2.15)

Here z is the proportionality constant, known as ‘Electrochemical equivalent’. It

can be defined as, “The amount of substance liberated (in gm) on the electrode on

passing a current 1 A for 1 Sec. or passing 1 coulomb of electricity”.

Faraday’s Second Law

“If same quantity of electricity is passed through different electrolytes, then

the amounts of substance liberated on the respective electrodes are in the ratio

of their equivalent weights.”

An important implication of the Faraday’s second law is that the ratio of the mass

of electrodeposit to its gramequivalent weight is a constant equivalent to 1 Faraday or

96,500 Coulombs (c) or 26.3 ampere-hour (Ah).

Page 24: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

67

d) Electrode-Electrolyte Interface:

The electrode-electrolyte interface plays an important role in electrodeposition

process. The electrode used in electrodeposition should necessarily be a good

conductor. When an electrode is immersed in the liquid electrolyte, the anisotropic

forces developed at the interface, results in a new arrangement of solvent dipole and

ions of the electrolyte. At the beginning, the charge comes in two phases (one electrode

and other electrolyte), start accumulating at the phase boundary and giving rise to the

interface, acting as a barrier to flow of charge in either direction. As the built-up grows

on the two sides, the electrical forces overpower the barrier, resulting in the flow of

charges. The charge flow stops when the electrochemical potential on the two sides of

the interface become equal. The interfacial region thus acquires a potential gradient that

acts as a barrier to the further flow of charges. The whole process occurs at about 1000

Å region at the phase boundary. The layer of charges is developed on both sides of the

boundary and hence termed as an “electrical double layer.”

The electrode-electrolyte interface according to Stern’s model can be divided into

two parts:

1. A compact double layer, known as Helmholtz double layer adjacent to the electrode,

and

2. A diffuse layer known as Gouy-Chapman layer.

The Helmholtz Layer:

The Helmholtz double layer is a dense layer of ions stuck to the electrode. In this

region the potential varies linearly with distance as shown in fig. 2.2(b). This dense layer

is divided into inner and outer Helmholtz planes. The inner Helmholtz Plane (IHP) is

adjacent to the electrode surface and consists of completely oriented solvent dipoles

and specifically adsorbed (or contact-adsorbed) ions. The orientation of solvent dipoles

depends on the specific interaction with the electrode surface as well as the electric

field. Large ions with negative free energy of contact adsorption are expected to be

contact adsorbed. In aqueous system, the cations react rather strongly with the water

molecule, and their inner hydration sphere is retained. This limits their closest distance

Page 25: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

68

of approach to the electrode. They are thus separated from the electrode by

approximately one or two electrolyte molecules. On the other hand, anions interact

weakly with electrolyte; hence hydration sheath is not covered on them. Thus the

closest distance of approach could correspond to direct contact; they can be a part of

IHP. The Outer Helmholtz Plane (OHP) consists of solvated ions (usually cations) at the

closest distance of approach from the electrode surface. The OHP thus consists of

partly ionized electrolyte molecule dipole layers.

Bockris et al. [13] developed a model of electrode-electrolyte interface and is

shown in figure 2.2(a). In presence of contact adsorbed ions, it can be seen from figure

2.2(b) that the potential distribution () changes across the double layer. The schematic

of electrode immersed in electrolyte is shown in figure 2.2(c). OHP is the site at which

non-specifically adsorbed ions arrive to take part in the charge transfer processes.

Gouy-Chapman Layer or Diffuse Layer:

The size of the ions forming the outer Helmholtz plane (OHP) is such that the

sufficient number of them cannot neutralize the charge on the electrode. Therefore, the

remaining charges are held with increasing disorder as the distance from the electrode

surface increases and the electrostatic forces become weaker and dispersion by

thermal motion is more effective. These less ordered charges forcing opposite to that on

the electrode constitutes the diffuse part of double layer. Thus, all the charges, which

neutralize on the electrode, are held in a region between OHP and the bulk of

electrolyte. The additional charges required to neutralize the total charge on the

electrode forms the Gouy-Chapman layer or diffuse layer.

e) Steps Involved in Electrodeposition Process:

Electrodeposition of ionic species from the electrolyte occur in following

successive steps (fig. 2.3)

1. Ionic transport

2. Discharge

Page 26: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

69

3. Breaking of ion-ligand bond (if the bath is complexed)

4. Incorporation of a atoms on the substrate surface followed by nucleation and

growth.

All above steps occur within 1–1000Ao from the substrate; however each has its

own region of operation. These various processes can be classified with respect to

distance from the electrolyte as:

a. In the electrolyte

b. Near the electrode

c. At the electrode

Page 27: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

70

Figure 2.2 (a) Electrode Electrolyte Interface, (b) Potential Distribution across the double layer & (c) The schematic of electrode immersed in electrolyte

Page 28: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

71

a. Process in the Electrolyte:

The ions in the electrolyte can move towards the electrode under the influence

of;

1. Potential gradient leading to ion drift, d/dx

2. Concentration gradient leading to diffusion of ions, dc/dx

3. A density convective current, d/dx due to consumption of ions at the electrode.

The general mathematical equation including all these processes can be written as

Nernst-Planck equation,

cvdx

dcD

dx

d

RT

DzFj C

…….. (2.16)

Where, F is the Faraday’s constant, is the viscosity of the electrolyte, R is the gas

constant and D is the diffusion coefficient. The three terms in the parenthesis

respectively describe the contributions of migration, diffusion and convection processes

to the mass transport towards the electrode.

b. Processes Near the Electrode but Within Electrolyte:

Ionic species are normally surrounded by hydration sheath or by other complex

forming ion or legand present in the electrolyte. They move together as a single entity

and arrive near the electrode surface where the ion-legand system either accepts

Dissociation of ion-ligand bond

Incorporation into lattice

1000 A

Electrode

Discharge

Electrolyte Ionic transport

Fig.2.3 Approximate region in which various stages of ion transport occur leading to

various steps involved in electrodeposition process.

Page 29: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

72

electrons from the cathode (or donates electrons to the anode). This ionic discharge

occurs between 10 to 1000 Å from the electrode.

c. Processes that Occur on the Electrode Surface:

The discharged ions arrive near the electrode, where step by step they lead to

the formation of a new solid phase or the growth of an electrodeposit. The atoms

deposited have a tendency to form either an ordered crystalline phase or a disordered

amorphous phase.

The electrodeposit formation steps of transport, discharge, nucleation, and

growth are interlinked.

d) Pathways for the Growth of an Electrodeposition:

The entire pathway for the growth can be divided into following steps (figure 2.4) [2]

Figure-2.4 Pathways for the growth of an electrodeposition

Page 30: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

73

1. Transport of ions in the electrolyte bulk towards the interface.

2. Discharge of ions reaching the electrode surface, giving rise to generation of

adatoms.

3. Nucleation and growth, where again alternative routes are possible

a. Growth assisted by surface diffusion.

b. Growth assisted by formation of clusters and critical nuclei.

c. Formation of monolayer and final growth of electrodeposit.

Surface defects such as steps, kinks and dislocations generally control the growth

kinetics. The kinks sites and screw dislocations together sustain the growth of the

electrodeposit.

e) Factors Governing Electrodeposition:

The preparative parameters directly affect the structural, morphological and optical

properties of the electrodeposits. The various preparative parameters like substrate,

applied field and current density, bath temperature, complexant and pH of the bath etc.

should be controlled to obtain uniform, smooth and stoichiometric electrodeposits [14-

15]. Some preparative parameters are discussed below.

i. Substrate:

Substrates play an important role in electrodeposition. Besides providing

mechanical support to the electrodeposition, influences on the morphological

characteristics of the growing layer and on the electronic and optical properties of the

electrodeposition. For the choice of suitable substrate following criteria should be

applied for their selection [16].

i. It should have good conductivity because it is one of the electrodes in

electrodeposition. A good conductivity is beneficial in improving carrier collection

efficiency.

ii. The thermal expansion coefficient should match with that of electrodeposition. A

mismatch may cause cracking or peeling of the film.

Page 31: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

74

iii. It should have good mechanical strength.

iv. It should be stable in electrolyte bath.

v. It should be smooth. Uneven, porous, voids and other irregularities influence the

local current distribution.

Metals have been widely used as substrates because of their good conductivity, easy

availability, lower cost and relative ease of handling.

ii. Bath Temperature:

The rise in bath temperature enhances the rate of diffusion and increases ionic

mobility, hence the increase in conductivity of the bath. The increase in temperature

increases the rate of crystalline growth favoring the coarse deposits. This increase in

crystal size corresponds to decrease in polarization. At higher temperature, current

densities increase, which increases the rate of nucleation, hence fine-grained, smooth

deposits can be obtained. The rise in bath temperature decreases the hydrogen over

voltage so facilitates the evolution of gas, as well as precipitation of basic salts. The

opposing effects make it difficult to predict the choice of bath temperature, however, it

can be optimized by performing actual experiments.

iii. Current Density:

At lower current densities (or over-potentials) the discharge of ions occurs slowly,

so the growth rate decreases but increases the crystallinity forming closely packed

structures. As the current density is raised, the nuclei formation rate will increase and

the deposits become fine grained. At higher current densities, the rate of discharge of

ions becomes greater compared to rate of supply of ions and there is duplicity of ions

near the cathode, which favours the growth perpendicular to the substrate surface.

Usually spongy, dendritic growth can be observed under this condition. Secondly, at

very higher current densities, hydrogen evolution occurs at faster rate, which interferes

the crystal growth and spongy, porous deposits may be obtained. This can also favour

the precipitation of hydrous oxides or basic salts due to increase in local pH.

Page 32: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

75

iv. Metal Ion Concentration:

The plating bath is always an aqueous solution containing compound of metal to

be deposited. It is always advantageous to use higher concentration of metal

components in the bath solution. A high current density can be employed in high metal

bearing bath. An increase in metal concentration, under given condition, decreases the

cathode polarization and increases the crystallite size.

v. Hydrogen Ion Concentration (pH):

In order to operate a bath with optimum efficiency and maintain the desired

physical properties of the deposit, control of pH of plating bath is necessary. Besides

too low pH may lead accumulation of hydroxide ions in the vicinity of the cathode and

consequent precipitation of basic salts, which may get included in electrodeposition,

thereby altering deposit properties. All aqueous solutions contain H+ ions, infact in every

deposit from an aqueous bath, there is a possibility of the hydrogen gas evolution at the

cathode due to H+ ions. It takes place, the efficiency of metal deposition is lowered. As

this efficiency and hydrogen discharge potential partly depends upon hydrogen ion

concentration, at low pH, the bath permits the use of higher current density to produce a

sound deposit with relatively high efficiency.

vi. Addition Agents:

In almost all cases of electrodeposition of metals, it is observed that addition of

small quantities of certain substances often result in production of smooth, fine grained

and nanocrystalline deposits. Such substances are known as addition agents. Addition

agent such as brightening agents, surfactants, complexants etc. are often added to the

bath to obtain smoother, brighter deposits, controllable reaction rates, better adhesion

and better texture. The adsorbed additives influence the rate of deposition by i)

changing Helmholtz layer potential, ii) acting as a bridge for mediating electron transfer

reactions between electrode and discharging species iii) forming complexes between

the adsorbed additive and the ionic species to be plated.

Page 33: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

76

vii. Complexing Agent

The unstable metal ions are capable of combining chemically with neutral

molecules and with ions of opposite sign to form stable complex ion. The combination is

through the covalent bond, when neutral molecules interact with positively charged

metal ions to yield negatively charged complex ions. Complex compound in a plating

bath serves two purposes. Firstly they make possible to maintain a high metal

concentration but low metal ion concentration. The complex ions of the complex

compound serve as reserves and continuously supply of the simple ions necessary for

the discharge at the cathode occurs. A low metal ion concentration enables the

production of deposits with small grains and improves the throwing power. Secondly,

complex formation enables us to enhance appreciably the solubility of slightly soluble

salts.

Page 34: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

77

Part-BThin Film Characterization Techniques

2. B.1 Introduction

In the advancement of science and technology the discovery of novel materials

those are having varied characteristics and applications have played an important role.

Characterization is an important step in the development of exotic materials. The

complete characterization of any material consists of phase analysis, compositional

characterization, structural elucidation, micro-structural analysis and surface

characterization, which have strong bearing on the properties of materials. This has led

to the emergence of variety of advanced techniques in the filed of materials science. In

this section different analytical instrumental techniques used to characterize our thin

films are described with relevant principles of their operation and working.

2. B.1.1 Cyclic Voltammetry (CV) and Linear Sweep Techniques (LSV):

Cyclic voltammetry is often the first experiment performed in an electro analytical

study. In particular, it offers a rapid location of redox potentials of the electroactive

species, and convenient evaluation of the effect media upon the redox process. In cyclic

voltammetry a reversible dc potential sweep (using a triangular potential waveform) was

applied between working electrode (film) and counter electrode and resulting current

response versus a reference electrode (SCE) is measured.

Fig.2.5 Variation of applied potential for Cyclic Voltammetry

t1

Page 35: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

78

In cyclic voltammetry, on reaching t=t1 the sweep direction is inverted as shown in

figure 2.5 and sweep until Emin, then inverted and sweep to Emax etc. The important

parameters involved are

The initial Potential Ei

The initial sweep direction

The sweep rate

The maximum potential, Emax

The minimum potential, Emin

The final Potential, Ef

A faradic current, If due to the electrode reaction, is registered in the relevant

zone of applied potential where electrode reaction occurs. There is also a capacitive

contribution: on sweeping the potential, the double layer charge changes: This

contribution increases with increasing sweep rate [17]. The total current is

I=Ic+If= Cd (dE/dt) +If= Cd+If (2.17)

Thus Ic = and it can be shown that If = 2

This means that at very high sweep rates capacitive current must be subtracted in order

to obtain accurate values of the rate constant.

The applicability of Nernst equation and therefore, reversibility has to do with

time allowed for the electrode to reach equilibrium. The concentration of the species at

the interface depends on the mass transport of these species from bulk solution, often

described by mass transfer coefficient Kd. A reversible reaction corresponds to the case

where the kinetics of the electrode reaction is much faster than the transport. The

kinetic is expressed by standard rate constant, K0which is the rate constant when E=E’

E- Actual potential and E’- Formal potential [E- standard potential]

The kinetics of electrode reactions does not measure the rate of electron transfer

itself, as this is an adiabatic process, following Frank-Condon principle, and occurs in

Page 36: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

79

approx. 10-16s. What it measures is the time needed for the species, once they have

reached the interfacial region, to arrange themselves and their ionic atmospheres into

position for electron transfer to be able to occur. According to kinetics of the reactions

there are three types of reactions,

1. Reversible

2. Irreversible

3. Quasi reversible

Reversible system

Fig. 2.6 shows a typical curve for linear sweep voltammetry recorded for

reversible reaction of the type O + ne- R. The curve can be understood in the

following way. On reaching a potential where the electrode reaction begins, the current

rises as in a steady state voltammogram. However, the creation of a concentration

gradient and consumption of electroactive species means that, continuing to sweep the

potential, from a certain value just before the maximum value of the current, peak

current, the supply of electroactive species begins to fall. Owing to depletion, the current

then begins to decay, following a profile proportional to t-1/2 which is shown in Fig.2.9,

similar to application of potential step. Fig. 2.7 shows the typical cyclic voltammetry for

reversible system.

Nor

mal

ized

cur

rent

Fig. 2.6. The typical curve of Linear Sweep Voltammetry for

reversible system.

Page 37: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

80

Information as a diagnostic for linear sweep and cyclic voltammogram of

reversible reactions are [18]

Ip 2 ……….(2.18)

Ep independent of

Ep- Ep/2 = 56.6/n Mv ………(2.19)

And for cyclic voltammetry alone

Epa - Epc = 59.0/n mV ………(2.20)

| Ipa/ Ipc| = 1 ……….(2.21)

Another practical factor affecting the voltammogram is the solution resistance

between working and reference electrode. This resistance leads to a shift in the

potential of the working electrode by IpR where R is the resistance (uncompensated)

of the solution.

Irreversible System

In the case of an irreversible reaction of the type O + ne- R. liner sweep and

cyclic voltammetry lead to the same voltammetry profile, since no inverse peak appears

on inverting the scan direction.

Fig. 2.7 The typical curve of cyclic Voltammetry for

reversible system

Nor

mal

ized

cur

rent

Page 38: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

81

Fig. 2.8 shows a voltammogram for irreversible system. With respect to

reversible system, the waves are shifted to more negative potential (reduction), Ep

depending on the sweep rate. The peaks are broader and lower.

Quasi Reversible Systems

The extent of irreversibility increases with increase in sweep rate, while at the

same time there is a decrease in the peak current relative to the reversible case and an

increasing separation between anodic and cathodic peaks. On increasing sweep rate,

there is less time to reach equilibrium at the electrode surface; reactions which appear

as reversible at low sweep rates, can be quasi reversible at high sweep rates. Fig. 2.9

shows the effect of increasing irreversibility on the shape of cyclic voltammogram.

Fig. 2.9. The effect of increasing irreversibility on the shape of

cyclic

Nor

mal

ized

cur

rent

Fig. 2.8 Voltammogram for irreversible system

Page 39: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

82

2. B.1.2.Thickness Measurement Using Weight Difference Method:

Film thickness is an important parameter in the study of the film properties.

Amongst different methods for measuring the film thickness, the weight difference

method is simple and convenient and thickness‘t’ is measured using the relation.

t = m / A.b . ...........(2.22 )

where, ‘m’ is the mass of the film deposited on area ‘A’ of the substrate and ρb is the

density of the material in the bulk form. The mass ‘m’ of the film has been measured by

using a single pan microbalance. As reported in many studies [19, 20], the thin film

density varies between 0.74 to 0.87 times the bulk densities owing to the porosity.

Hence a correction factor of 0.8 is applied to the bulk density in equation 2.22.

2. B.1.3. Optical Absorption:

The equilibrium situation in semiconductor can be disturbed by generation of

carriers due to optical photon absorption. Optical photon incident on any material may

either be reflected, transmitted or absorbed. The phenomena of radiation absorption in

a material is all together considered to be due to 1) inner shell electrons, 2) valence

band electrons, 3) free carriers including electrons and 4) electrons bound to localized

impurity centers or defects of some type. In the study of fundamental properties of the

semiconductors, the absorption by the second type of electrons is of great importance.

In an ideal semiconductor, at absolute zero temperature the valence band would be

completely full of electrons, so that electron could not be excited to higher energy state

from the valence band. Absorption of quanta of sufficient energy tends to transfer of

electrons from valence band to conduction band. The optical absorption spectra of

semiconductors generally exhibits a sharp rise at a certain value of the incident photon

energy which can be attributed to the excitation of electrons from the valence band to

conduction band (may also involve acceptor or donor impurity levels, traps, excitons

etc.) The conservation of energy and momentum must be satisfied in optical absorption

process.

Basically there are two types of optical transitions that can occur at the

fundamental edge of the crystalline semiconductor, direct and indirect. Both involve the

Page 40: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

83

interaction of an electromagnetic wave with an electron in the valence band, which is

rose across the fundamental gap to the conduction band. However, indirect transition

involves simultaneous interaction with lattice vibration. Thus the wave vector of the

electron can change in the optical transition. The momentum change being taken or

given up by phonon. Direct interband optical transition involves a vertical transition of

electrons from the valence band to the conduction band such that there is no change in

the momentum of the electrons and energy is conserved as shown in Fig. 2.12 (a). The

optical transition is denoted by a vertical upward arrow. The forms of the absorption

coefficient ‘’ as a function of photon energy h depend on energy of N(E) for the bands

containing the initial and final states. For simple parabolic bands and for direct

transitions [21].

= A (h Eg)n / h 2.23

where A is a constant depending upon the transition probability for direct transition, n =

1/2 or 3/2 depending on whether the transition is allowed or forbidden in the quantum

mechanical sense. Eg is the optical gap.

Let’s visualize a situation given in Fig. 2.10 (b) where interband transition takes

place between different kstates. Since these must satisfy the momentum conservation

laws, the only way such transition can take place is through the emission or absorption

of a phonon with wave vector q i.e.

k' q = k + K 2.24

The transitions defined by equation (2.10) are termed as indirect transitions. For

indirect transitions [22]

= A (h Eg)n / h 2.25

For allowed transition n = 2 and for forbidden transitions n = 3.

The band gap energy ‘Eg’ is determined by extrapolating the linear portion of the

plot of (h)n against h to the energy axis at = 0.

Page 41: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

84

(a)

Valance Band

Conduction Band

'k

k k

Valance Band

Conduction Band

h = Eg

O

E

k

'k

k

(b)

While discussing the optical absorption edges observed in amorphous

semiconductors the following assumptions are made: (a) the matrix elements for the

electronic transitions are constant over the range of photon energies of interest and (b)

Kconservation selection rule is relaxed. This assumption is made in amorphous

semiconductors because near the band edges at least, k k and thus k is not a good

quantum number. On E k diagram such transitions would be nonvertical. However,

no phonon absorption or emission processes are invoked to conserve momentum and

all the energy required is provided by the incident photons. Such transitions are termed

nondirect as opposed to indirect. Without knowledge of the form of N(E) at the band

edges, and under the assumption of parabolic bands, the absorption in many

amorphous material is observed to obey the relation (2.11) with n = 2. Thus absorption

edge of many amorphous semiconductors can be described by a simple power law, at

least over a limited range of the absorption coefficients, which enables an optical gap

‘Eg’ to be defined.

Fig. 2.10 - “Direct interband optical transitions” for a) direct band and b) indirect

band semiconductors. The transitions are represented by vertical arrow.

Page 42: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

85

2. B.1.4 X- Ray Diffraction (XRD) Technique :

X-ray diffraction (XRD) is a powerful technique for determination of crystal

structure and lattice parameters. The basic principles of X-ray diffraction are found in

textbooks e.g. by Buerger [23], Klug and Alexander [24], Cullity [25], Tayler [26], Guinier

[27], Barrett and Massalski [19].

Figure 2.11 shows the schematics of X-ray diffractometer. Diffraction in general

occurs only when the wavelength of the wave motion is of the same order of magnitude

as the repeat distance between scattering centers. This condition of diffraction is

nothing but Bragg’s law and is given as,

2d sin = n 2.26

where,

d = interplaner spacing

= diffraction angle

= wavelength of x-ray

n = order of diffraction

2

X-raySource

Sample

Detector

Receiving SlitDiverging Slit

Fig. 2.11 Schematics of X-ray diffractometer.

For thin films, the powder technique in conjunction with diffractometer is most

commonly used. In this technique the diffracted radiation is detected by the counter

Page 43: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

86

tube, which moves along the angular range of reflections. The intensities are recorded

on a computer system. The‘d’ values are calculated using relation (2.8) for known

values of , and n. The X- ray diffraction data thus obtained is printed in tabular form

on paper and is compared with Joint Committee Power Diffraction Standards (JCPDS)

data to identify the unknown material. The sample used may be powder, single crystal

or thin film. The crystallite size of the deposits is estimated from the full width at half

maximum (FWHM) of the most intense diffraction line by Scherrer's formula as follows

[28]

cos

9.0D 2.27

where, D is crystallite size, is wavelength of X-ray used, is full width at half maxima

of the peak (FWHM) in radians, is Bragg's angle. The X- ray diffraction data can also

be used to determine the dimension of the unit cell. This technique is not useful for

identification of individuals of multilayer or percentage of doping material.

2. B.1.5. Raman Spectral Study

Raman spectroscopy is different from the rotational and vibrational spectroscopy

considered above in that it is concern with the scattering of radiation by the simple,

rather than an absorption process. It is named after the Indian physicists who first

observe it in 1928, C. V. Raman. Both rotational and vibrational spectroscopies are

possible. The energy of the exciting radiation will determine which type of the transition

occurs-rotational transitions are lower in energy than vibrational transitions.

In addition to this, rotational transitions are around three orders of magnitude

slower than vibrational transitions. Therefore, collisions with other molecule may occur

in the time in which the transition is occurring. A collision is likely to change the

rotational state of the molecule, and so the definition of the spectrum obtained will

destroyed. Rotational spectroscopy is therefore carried out on gases at low pressure to

ensure that the time between the collision is greater than the time for transition.

Page 44: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

87

Scattered Radiations

Laser Source Sample

Detector

The basic set up of Raman spectrometer is shown below.

Fig.2.12 Basic set up of Raman Spectrometer.

Note that the detector is orthogonal to the direction of the incident radiation, so

as to observe only scattered light. The source needs to provide intense monochromatic

radiation, and usually laser. The criteria for a molecule to be Raman active are also

different to other types of spectroscopy, which required permanent magnetic dipole

moment, at least for diatomic molecules. A molecule will only be Raman if the following

gross selection rule is fulfilled.

1) Gross Selection Rule:

For spectroscopic techniques such as infrared spectroscopy, as seen in the first

section it is necessary for the molecule being analyzed to have a permanent electric

dipole. This is not the case for Raman spectroscopy; rather it is the polarizability () of

the molecule which is important.

The oscillating electric field of a photon causes charged particles (electrons and,

to a lesser extent, nuclei) in the molecule to oscillate. This leads to an induced electric

dipole moment, µind,

Page 45: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

88

where µind = () E …………..2.28

This induced dipole moment then emits a photon, leading to either Raman or

Raleigh scattering. The energy of this interaction is also dependent on the polarizability:

Energy of interaction = -1/2E 2

By comparison with the equation for the interaction energy for other forms of

spectroscopy, it can be seen that the energies of Raman transitions are relatively weak.

To counter this, a higher intensity of the exciting radiation is used.

For Raman scattering to occur, the polarizability of the molecule must vary with

its orientation. One of the strengths of Raman spectroscopy is that this will be true for

both heteronuclear and homonuclear diatomic molecules. Homonuclear diatomic

molecules do not possess a permanent electric dipole, and so are undetectable by other

methods such as infrared.

2) Selection Rules Arising from Quantum Mechanics:

A detailed discussion of the quantum mechanical basis for spectroscopy is

beyond the scope of this brief introduction. Here, the quantum numbers and the allowed

transitions involved are simply stated.

2.1 Rotational

To find allowed rotational transitions, the total angular momentum quantum

number for rotational energy states, J, must be considered. Raman spectroscopy

involves a 2 photon process, each of which obeys:

J=±1 ……….2.29

Therefore, for the overall transition

J=±2 ………..2.30

Where, =0 for corresponds to Raleigh scattering,

Page 46: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

89

Source Moleculeh

h

J=0 corresponds to a Stokes transition,

and J= -2 corresponds to an anti-Stokes transition.

2.2 Vibrational

To find allowed transitions the vibrational quantum number, �must be

considered.

For the overall transition,

= ±1 ………2.31

Transitions where = ±2 are also possible, but these are of weaker

intensity.

2.3 Types of Scattering

Consider a light wave as a stream of photons each with energy h When each

photon collides with a molecule, many things may happen, 2 of which are

considered below:

a) Elastic, or Raleigh Scattering

This is when the photon simply 'bounces' off the molecule, with no exchange in

energy. The vast majority of photons will be scattered in this way.

Page 47: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

90

Source Moleculeh

hr hr

b) Inelastic, or Raman Scattering

This is when there is an exchange of energy between the photon and the

molecule, leading to the emission of another photon with a different frequency

to the incident photon:

This scattering phenomenon takes place as shown follows.

Fig.2.13. Scattering phenomenon in Raman Spectroscopy

Page 48: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

91

3) Raman Scattering

The molecule may either gain energy from, or lose energy to, the photon. In the

diagram below, 3 energy states of the molecule are shown (E1, E2, E3). The molecule is

originally at the E2 energy state. The photon interacts with the molecule, exciting it with

an energy h. However, there is no stationary state of the molecule corresponding to

this energy, and so the molecule relaxes down to one of the energy levels shown. In

doing this, it emits a photon. If the molecule relaxes to energy state E1, it will have lost

energy, and so the photon emitted will have energy hr1, where h1 > h. These

transitions are known as anti-Stokes transitions. If the molecule relaxes to energy state

E3, it will have gained energy, and so the photon emitted will have energy hr2, where

hr2 < h. These transitions are known as Stokes transitions

For rotational spectroscopy, both Stokes and anti-Stokes transitions are seen.

For vibrational spectroscopy, Stokes transitions are far more common, and so anti-

Stokes transitions can effectively be ignored [29].

Fig.2.14.Stokes and anti- stokes transition

Page 49: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

92

Fig. 2.15 Photograph of MultiRAM (Brucker)FT-Raman Spectrometer

2. B.1.6.Scanning Electron Microscopy (SEM):

Scanning electron microscope is an instrument that is used to observe the

morphology of the solid sample at higher magnification, higher resolution and depth of

focus as compared to an optical microscope [30]. When an electron strikes the atom,

variety of interaction products are evolved. Figure 2.16 illustrates these various products

and their use to obtain the various kinds of information about the sample. Scattering of

electron from the electrons of the atom results into production of backscattered

electrons and secondary electrons. Electron may get transmitted through the sample if it

is thin. Primary electrons with sufficient energy may knock out the electron from the

inner shells of atom and the excited atom may relax with the liberation of Auger

electrons or X-ray photons. All these interactions carry information about the sample.

Auger electron, ejected electrons and X-rays are energies specific to the element from

which they are coming. These characteristic signals give information about the chemical

identification and composition of the sample.

Page 50: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

93

Principle of Scanning Electron Microscope

A well-focused mono-energetic (~25KeV) beam is incident on a solid surface

giving various signals as mentioned above. Backscattered electrons and secondary

electrons are particularly pertinent for SEM application, their intensity being dependent

on the atomic number of the host atoms. Each may be collected, amplified and utilized

to control the brightness of the spot on a cathode ray tube. To obtain signals from an

area, the electron beam is scanned over the specimen surface by two pairs of electro-

magnetic deflection coils and so is the C.R.T. beam in synchronization with this.

Fig. 2.16 Variety of interaction products evolved due to interaction of electron

beam and sample

Secondary Electrons

Back Scattered Electrons

Auger Electrons

X-rays

Cathodolumenescence

Electromotive force

Electron Beam

Transmitted Beam

Page 51: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

94

The signals are transferred from point to point and signal map of the scanned

area is displayed on a long persistent phosphor C.R.T. screen. Change in brightness

represents change of a particular property within the scanned area of the specimen [31].

The ray diagram of scanning electron microscope is shown in Fig. 2.17. The scattering

cross section for back-scattered electrons is given as [32],

2cot102.162

30 E

ZQ 2.32

where, Z is atomic number and E is electric field.

Here the cross-section is proportional to Z2. Hence, the back-scattered electrons are

used for the Z contrast or for compositional mapping.

Fig. 2.17. The ray diagram of scanning electron microscope.

Page 52: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

95

2. B.1.7. Energy Dispersive Analysis by X-Rays Measurement (EDS):

In EDS technique a sample is made the target in an X- ray tube and is

bombarded with electrons of suitable energy, it emits characteristics X-rays. This is the

basis of a method of chemical analysis. The emitted X-rays are analyzed in an X-ray

spectrometer and the elements present in the sample are qualitatively identified by their

characteristics wavelengths. For compositions greater than or about 1% and elements

separated by few atomic numbers, energy dispersion analysis is very useful because

the intensities are increased about 100-Fold [33]. The resolution however, of an energy

dispersion instruments is as much as 50 times less than the wavelength dispersion

spectrometer using a crystal; thus overlapping of lines from nearby elements may occur.

If a sample is irradiated with X-rays of sufficiently high energy, it will emit fluorescent

radiation. This radiation may be analysized in an X-ray spectrometer and the elements

present in the sample identified by their characteristics wavelengths. Study of thin films,

ferrites, composites, biological samples and pharmaceutical samples are the common

application areas.

2. B.1.8. Transport Properties:

Surface transport phenomena are well known to have a strong influence on the

electronic properties of bulk semiconductors. When transport takes place through thin

specimens, the carriers are being subjected to considerable scattering by the boundary

surface in addition to normal bulk scattering. This additional scattering will reduce the

effective carrier mobility below the bulk value and will thus give rise to quantum size

effects. A study of these size effects can yield information on the electronic structure of

a surface and is therefore of considerable fundamental and practical importance. These

phenomena play an important role in the transport properties of semiconducting film of

about 1m thickness and having carrier concentration upto 1018 cm-3. Surface transport

phenomena in bulk semiconductor have received much attention in recent years. An

excellent review of the subject is given by Pulliam et al. [34]. The important transport

properties i.e. electrical resistively, thermoelectric power (TEP) are discussed below.

Page 53: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

96

a) Electrical Conductivity:

The use of thin films as resistors, contacts and interconnections has lead to

extensive study of conductivity, its temperature dependence, the effect of thermal

processing stability and so on. Investigations of the electrical resistivity as a highly

structure sensitive properties make it possible to gain insight into the structural and

electrical properties of the metal film which is important from both the theoretical and

practical point of view. The contact techniques are most widely used for the

measurement of resistivity. These techniques include two-point probe, four point probe

and the spreading resistance methods. The two-point method is simple and easy to use.

In this technique a constant current I is passed through a sample of known dimensions

(cross-sectional area ‘A’). And the d.c. voltage ‘V’ between two fixed position probes

(separation‘d’) measured either with impedance voltmeter or potentiometrically. For

uniform sample resistively is given by

= (A/I) (V/d) 2.33

In case of semiconducting thin films, the resistivity decreases with increase in

temperature. The thermal activation energies ‘Ea’ are calculated by using following

relation:

exp (-E /T) 2.34

Where E is the activation energy for the conduction is Boltzmann constant and 0 is

the pre exponential constant depending on the material.

Fig. 2.18 A and 2.18 B shows photograph and schematic diagram of the

electrical conductivity measurement unit. The two brass plates of the size 10 x 5 x 0.5

cm are grooved at the centre to fix the heating elements. Two strip heaters (65 Watts)

were kept parallel in between these two brass plates to achieve uniform temperature.

The two brass plates are then screwed to each other. The sample was mounted on the

upper brass plate at the centre. To avoid the contact between the film and the brass

plate, a mica sheet was placed between the film and brass plate. The area of the film

Page 54: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

97

was defined and silver emulsion (paste) was applied to ensure good electrical contact to

the films. The working temperature was recorded using a Chromel-Alumel thermocouple

(24 gauge) fixed at the centre of the brass plates. Testronix model 34 C (power supply

unit ) was used to pass the current through the sample. The potential drop across the

film was measured with the help of Meco 801 digital multimeter and current passed

through the sample was noted with a sensitive 4 digit picoammeter (Scientific

equipment, Roorkee DPM 111).The measurements were carried out by keeping the film

system in a light tight box, which was kept at room temperature.

Fig 2.18 a. Photograph showing the electrical conductivity measurement

assembly

Fig. 2.18 b Cross sectional view of of electrical conductivity measurement unit.

Page 55: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

98

b) Thermoelectric Power (TEP):

If some metal contacts are applied to the two ends of a semiconductor and if one

junction is maintained at higher temperature than the other, a potential difference is

developed between the two electrodes. This thermoelectric or Seebeck voltage is

produced partly because

i) The majority carriers in the semiconductor diffuse from hot to cold junction, thus giving

a potential difference between the ends of the specimen. This voltage builds upto a

value such that the return current just balances the diffusion current when a steady

state is reached.

ii) Other part which contributes to the thermoelectric voltage is the contact potential

difference between metal and semiconductor, which occurs at two junctions.

In the semiconductor, if the charge carriers are predominantly electrons, the cold

junction becomes negatively charged and if the charge carriers are positive holes, the

cold junction becomes positively charged. The magnitude of the developed voltage is

proportional to the difference in temperature between the hot and cold junction, if the

temperature difference is small. From the sign of the thermoelectric voltage it is thus

possible to deduce whether a given specimen exhibits n-or p-type conductivity.

The thermoelectric power (TEP), which is defined as the ratio of thermally

generated voltage to the temperature difference across the piece of semiconductor,

gives the information about the type of carriers in the semiconductor.

Fig. 2.19 A and 2.19 B shows photograph and schematic diagram of the TEP

measurement unit. Thermoelectric power measurement apparatus consist of two brass

blocks. One brass block was used as a sample holder-cum-heater. Other brass block

was kept at room temperature. The hot and cold junction was kept thermally isolated by

inserting an insulated barrier between the junctions. The size of the film used in this

study was 40 mm x 12.5 mm x 1.35 mm on amorphous glass substrates, were fixed on

two brass blocks. Chromel – Alumel thermocouples (24 gauze) were used to sense the

working temperature. A 65 watt strip heater was used for heating the sample. The

temperature of the hot junction was raised slowly from room temperature, with a regular

interval of 10 K. the thermo emf was noted up to the highest temperature of 500 K.

Silver paste contacts were made to films with copper wire. A backellite box was used for

Page 56: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

99

proper shielding of the TEP unit, which also minimises to some extent, thermal radiation

losses. The mean temperature was measured with a Meco 801 digital multimeter while

the differential thermal gradient and thermoelectric voltage were measured with digital

Testronix microvoltmeter.

Fig 2.19 a. Photograph showing the thermoelectric power measurement

assembly.

Fig. 2.19 b. Cross sectional view of the thermoelectric power measurement unit.

Page 57: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

100

2. B.1.9. Atomic Force Microscopy (AFM):

The atomic force microscopy (AFM) probes the surface of a sample with a sharp

tip, a couple of microns long often less than 100 Å in diameter. The tip is located at the

free end of a cantilever, which is 100 to 200 m long. The forces between the tip and

sample surface cause the cantilever to bend or deflect. A detector measures the

cantilever deflection as tip is scanned over the sample or the sample is scanned under

the tip. The measured cantilever deflection allows a computer to generate a map or

surface topography.

Several forces typically contribute to the deflection of an AFM cantilever. AFM

operates by measuring the attractive or repulsive forces between a tip and the sample.

The forces most commonly associated with atomic force microscopy are interatomic

force called the Van der Waals force. The dependence of the Van der Waals force upon

the distance between the tip and the sample is shown in figure 2.20. The two distance

regimes are labeled in the figure are (a) the contact regime and (b) non-contact regime.

In the contact regime, the cantilever is held at a distance less than few

angstroms from the sample surface, and the inter-atomic force between the cantilever

and the sample is repulsive. In the non-contact regime, the cantilever is held at a

distance of the order of tens to hundred of angstroms from the sample surface, and the

inter-atomic force between the cantilever and sample is attractive. Figure 2.21 shows

schematic diagram of AFM [35-36].

In principle, AFM resembles the record player as well as the surface profilometer.

However, AFM incorporates a number of refinements that enable it to achieve atomic–

scale resolution: Sensitive detection, flexible cantilever, sharp tips, high-resolution tip-

sample positioning and Force feedback

Page 58: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

101

Figure 2.20 Inter-atomic force versus distance curve for the operation of AFM

Figure 2.21 Schematic diagram of Atomic Force Microscope (AFM)

Repulsive forceForce

contact

Attractive force

Intermitted contact

non- contact

distance

(tip –to-sample separation)

(a)

(b)

Page 59: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

102

References

1] A.R. West,’Solid State Chemistry’ John willey & Sons, Singapore, (2003).

2] K. L. Chopra,’Thin Film Phenomena’, McGraw Hill, New York (1969)

3] Y. Gao, H. Niu, C. Q. Chen, Chem. Phys. Lett., 367 (2003) (1-2) 141

4] Zeng Acosta, R.E., Romankiw, L.T., VonGutfeld, R. J.,: Thin Sol. Films 95

(1982),131

5] Behrisch, R.: ‘Sputtering by Particle Bombardment’, Springer, Berlin (1981).

6] A. Y. Cho.: Thin Solid Films,100(1983),291

7] K.L. Chopra, R.C. Kainthla, D.K. Pandya, A.P. Thakoor. In: Physics of Thin

Films, Vol. 12, Academic press, London, (1982), 167.

8] C.D. Lokhande, Mater. Chem.Phys.28 (,1991) 1.

9] D.Lincol, M. Forment, H.Cachet, In. R.C.Alkite, D.M.Kolb, Fds. Adv.Electrochem.

Sci. Eng., New York: Wiley-VCH. 6 (1998)165.

10] Gary Hodes: ‘Chemical Solution Deposition of Semiconductor Films’; Marcel

Dekker, Inc. New York. (2003), 89.

11] R. P. Sharma, S. V. Patil, S. V. Bhavsar, A. R. Patil, Dori. Indian J. Pure. Appl.

Phys., 37(1999) 876

12] R. K. Pandey, S. N. Sahu and S. Chandra, ‘Handbook of Semiconductor

Electrodeposition’ Marcel Dekker, Inc. (1996).

13] J Bockris. O.M., Devanathan M. A. and Muller K. Proc. Roy. Soc. (Lond.), A 55

(1963) 274.

14] D. K. Sarkar, X.J. Zhou, A. Tannous, M.Louie and K.T. Leung,Solid State Comm.

125(2003)365

15] N.S. Gaikwad, V.M. Nikale and C.H. Bhosale, J.of Phys. Chem. Solids

64(2003)723

16] J.H. Min,J.H. Wu,J.U.Cho,Q.X.Liu,J.H.Lee,Y.D.Ko,J.S.Chung, Y.K. Kim J. Magn.

Mater.304(2006)100

17] D.J.G. Ives and G.J.Janz (ed.),Reference Electrode, Academic Press, New York

(1961).

18] Christopher M.A. Brett and Ana Maria Oliveira Brett, ‘Electrochemistry Principles,

Methods ,and Applications’,, Oxford University Press (1993).

Page 60: Thin Film Deposition Processes and Characterization ...shodhganga.inflibnet.ac.in/bitstream/10603/4025/8/08_chapter 2.pdf · Thin Film Deposition Processes and Characterization Techniques

103

19] O. Bohnke and G. Robert, Solid State Ionics, 6 (1982) 115.

20] Y. Hiruta, M. Kitao and S.Yamada, Journal of Appl. Phys., 23 (1984) 1624

21] F. Micheltti and P. Mark, J. Appl. Phys. Lett., 10 (1967) 136.

22] E. Becquerel, Comt. Rend. H. A. 9 (1839) 561.

23] M. J. Buerger, “X-ray Crystallography”, Wiley, New York, (1942).

24] H. P. Klug and L. E. Alexander, “X-ray Diffraction Procedures”, Wiley, New York,

(1954).

25] B. D. Cullity, “Elements of X-ray Diffraction”, Addison Wesley, Massachusetts

(1956).

26] A. Taylor, “X-ray Metallography”, Wiley, New York, (1942).

27] A. Guinier, “X-ray Diffraction “, Freeman, San Francisco (1963).

28] B.D. Cullity, Elements of X-rays 2nd edition Addiso Wesley, London, (1978).

29] D. W. Mayo, F. A. Miller, R. W. Hannah “Course Notes on the Interpretation of

Infrared and Raman Spectra” by John Wiley & Sons Inc. (2003).

30] S. Banerjee, “Proc. of National Workshop on Advanced Methods for Materials

Characterization” (NWMMC-2004) Mat. Res. Soc. India (2004).

31] Oatley, D. McMullan and K. C. A. Smith, The Development of the Scanning

Electron Microscope, in The Beginnings of Electron Microscopy, ed P. W.

Hawkes. Advances in Electronics and Electron 1Physics Suppl. 16 (London:

Academic Press) (1985) 443.

32] Oliver C. Wells, Scanning Electron Microscopy, McGraw Hill, Inc. USA. EDAX.

33] B. E. stern, D. Lewis, Pitman Pub. Corp. (1971) 205.

34] G. R. Pulliam; J. Appl. Phys. 38 (1967) 1120.

35] C. S. Barrett and T.B. Massalski, “Structure of metals”, McGraw-Hill, New York,

(1966).

36] T. R. Albrecht,J. Appl. Phys. 69 (1991) 668