“tissue compatible bio-integrated functional-esthetic - implant prosthodontics dr. samuel waknine,...
TRANSCRIPT
“Tissue Compatible
Bio-Integrated Functional-Esthetic -
Implant Prosthodontics
Dr. Samuel Waknine, M.D.M.S., Ph.D.
DiamondCrown Conventional Ti-Implant Superstructure
(7 years Post-Op.)
TM
Case no. 1
Clinical Implications 2
1 Kg /mm2 = 10 N/mn2 = 1 MPa = 145 psi
Biomechanical Concepts
Porcelain Fused to MetalShear Bond Strength - 12 MPa
DiamondCrown IDC - Abutment Post Shear Bond Strenght - 35 MPa
(x 3)
TM
DiamondCrown IDC Accelerated Cyclic Fatigue Studies
(3 years In-Vivo Correlation)
TM
Clinical Implications 3
Average Human Masticatory ForceAnterior - 9 MPaPosterior - 31 MPaBruxer - 41 MPaPistachio Sealed Shell - 16 MPa
1 Kg /mm2 = 9.807 N/mn2 = 1 MPa = 145 psi
IDC (Molar) - 500 MPa (3000N/6mm2)
Biomechanical Concepts
x55x16x12x31
IDC-Abutment-Implant Cross-Section
Metal Opaque
Opaque-Dentin
Dentin
Enamel
Integrated
Implant Post - ZTi
Superstructure - DiamondCrown
TM
TM
IDC+ZTi™
DiamondCrown IDC StratificationDiamondCrown IDC StratificationTM
DC Metal Cupler / Opaque
ZTiImplant
Post
ZTi Abutment Post
DC Opaque Dentin
DC Dentin
DC Enamel
DC Incisal
DiamondCrown™ Implant-Superstructure(s) IDC Clinical
Application5-Year Post-Op.
Case no. 2
Biocompatibility
A Novel Polycrystalline Reinforced Superstructure for Aesthetic - Restorative - Prosthodontic & Implant
Dentistry
DiamondBond-001 - DiamondFlow - DiamondLite -DiamondLink & DiamondCrown™
Dr. Samuel Waknine, M(D.M.S.), Ph.D.
New York University College of DentistryDRM Research Laboratories, Inc. USA