tofd - by nicholas bublitz - usa
TRANSCRIPT
TOFDTime of Flight Diffraction
By: Nick Bublitz
2
Diffraction
Each point of the defect generates new elementary spherical waves called diffraction
The incoming wave vibrates the defect.
Based on Huygens’ principal
3
Waves
FLAW
Diffractedwaves
Diffractedwaves
Incidentwave
Reflectedwave
All directions
Low energy
Independent of incidence angle
4
Diffraction
– Modification or deflection of sound beam– Sound striking defect causes oscillation– Ends of defect become point sources– Not related to orientation of defect– Weaker signal than reflected – needs higher gain or
amplification (preamp on receive side)– Sharp defects provide best emitters– Tip signals are located accurately– Time of flight of tip signals used to size– Wide beam longitudinal
5
How it Happens
defined exit point60 deg
beam spread in shoe
beam spread in material
center beam
shear wave beam spread
shear wave component appro. ½ long. center beam
6
Beam SpreadConventional theory only focuses on dominant frequency.In reality differences in wavelength occur due to the range of frequencies produced by a single probe. (bandwidth)Beam spread can be recalculated using lower frequency component.The presence of a lateral wave for 45 degree and above can be justified.
7
Rough Examples 60 Degree Wedge (2.7mm/us, 6mm crystal @ 5 MHz
Beam spread in wedge- center beam 23.3 deg. (incident)
2MHz +/- 10.3 deg. (13-33.6deg)3 MHz +/- 6.8 deg. (16.5-30.1 deg)4 MHz +/- 5.1 deg. (18.2-28.4 deg)5 MHz +/- 4.1 deg. (19.2-27.1 deg)
8
Beam Spread in Material-60 degree (refracted)
2 MHz- 29.4-90 deg3 MHz- 38.3-90 deg 4 MHz- 43-90 deg5 MHz- 45.9-90 deg
9
Modes of travelSome waves may go all the way as LWSome will go part way as LW, part way as SWSome will go all the way as SW
This is why we use LW!- LWs are about twice as fast as SW so they are sure to get to the receive probe first. We never use the mode-converted area for depth measurements as we are unsure of how those waves traveled.
10
The display
LW
volume of material
BW
mode-converted area
mode converted bw
11
A-Scan SignalsTransmitter Receiver
Lateral wave
LW
Upper tip Lower tip
Back-wall reflection
BW
12
The Lateral WaveThe lateral wave- compression velocity, arrives first, for curved surfaces will travel straight across the metal. Not a true surface wave, but a bulk wave generated at the edge of the wide beam generated by the send transducer. Frequency content tends to be lower than the center of the beam. Becomes weaker with increased PCS.
13
The LW BackwallCombination of reflected/diffracted energy.Strong signal
14
Mode Converted signalsOccur after LW Backwall due to slower speed.Strong signals typicallyNot used for measurement of defects as velocity is uncertain.Near surface defects may be more resolvable here due to more spatial resolution.
15
Why RF?To observe phase shifts to observe “tips”A wave traveling in a higher acoustic impedance material will shift 180 deg in phase when it is reflected at an interface of lower impedance. (ex: steel to air).
16
The EffectIf the wave starts in a positive cycleand hits a vertical defect-1. the wave from the top tip acts like energy reflected off the bw and changes phase 180 deg. (-)2. the wave from the bottom of the defect acts like it “runs around”the bottom without a phase changeand remains like the lateral wave (+)
Slag and porosity are often too thin to produce separate top and bottom signals.
17
Data Visualization
D-scan
Uppersurface
Back wall
A-scanLW
BW
18
Why Grayscale?Typical pulse echo techniques often associate a full color scale based on % FSH amplitude with red being highest amplitude because it is a natural attention getter for people.Since TOFD does not rely on amplitude but rather TOF, we want to take out an natural preference of color and view each defect individually.
19
Data Visualization
White+
Black-
Amplitude
Time
Time
One A-scan picture is replaced by one gray-coded line
20
Typical TOFD Scans2 typical TOFD scans used-– nonparallel scans-
ultrasonic beam is perpendicular to the scan axis-most common
– parallel scan-ultrasonic beam is parallel to scan axis
21
Non-parallel scan
SDHNotch
22
The View-D-scan (Omniscan=B-scan)
ViewScan axis
23
Non-Parallel
24
Non-parallel ScansLocate flawsDetermine depthlength in scan axisnot the highest precision for TW height measurementsrapid, easiest to employ, especially with weld capsProbes usually centered around area of interest in index axis- weld etc
25
Parallel Scan
Notch top of plate
26
Parallel Scansprecision TW height determinationwidth assessmenttiltlateral positioning-amplitude will be greatest when flaw is directly center of probes
27
The View-B-scan
View Scan axis
28
Other Types of ScansDouble Skip-used when there are problems resolving near surface defects-skipping off backwall
29
Other Types of ScansOff-axis Scans-Non-parallelIf a near surface flaw lies close to one probe in a normal centered non-parallel
scan, the signal from the defect can have a short time delay from the LW, causing poor resolution. Resolution can often be improved by performing off-axis scan. Depth measurement may become less accurate depending on positioning.
30
Other Types of ScansManual scanning- unencodedUsed only when is only resort typicallyNegatives-
1.Sampling interval not constant-operator left to try to match PRF - works best
in teams with area marked out at intervals-no better than +/- 5mm accuracy should be expected
31
Permanent data recording with B-scan type imaging (side view)Accurate sizing capability (height)-through-wall height most critical for fracture mechanics.Technique allows for rapid scanningDetection and sizing almost orientation independent.Based on TOF so avoid common amplitude technique sizing errorsTOFD has a potential through-wall dimension accuracy of ±1 mm and monitoring capability of ±0.3 mm Setup virtually independent of weld configurationWide coverage area
TOFD Advantages
32
Blind areas :– near surface Width of the lateral wave and timing error (can be
reduced by reducing PCS, using higher frequency, using highly dampened broadband probes, and software tools (lateral wave removal).
– back wall Large signal from reflected energy Off axis flaws at the back wall can be missed (can be reduced by off center scans and wider PCS)Flaw classification limitation (some cases)-no simple amplitude criteria Sensitive to grain noise (frequency and material flaws)If not experienced user, analysis can be difficult = TrainingLack of index positioning (non-parallel scans: can be compensated by parallel scans or pulse echo prove up)Parent material indications can be perceived as weld indications
TOFD Limitations
33
Ellipse of Equal Time
Ellipse of Equal Time- defects at either location plotthe same time-exists for anywhere on the ellipse
34
Lateral Positioning
35
Defect Position Uncertainty
Transmitter ReceiverS S
t2t1
dmin dmax
In practice:Maximum error on absolute depth position lies below 10 %.Error on height estimation of internal (small) defect is negligible.Caution for small defects situated at the back wall.
36
Missed off-axis flaws
missed or obscured bylarge bwsignal
37
The Non-Linearity of DepthWith a constant 5us change in depth, (expressed here in time), we can observe the total
time from transmit to receive does not hold constant.This causes a distortion of depth on our display, indications appear to be much closer to the
surface then were they lie in reality. Calibrations for true depth determination are critical.
LW time 50us
12
3
4
Total Time S to R.99beam 1=50.99us2.85beam 2= 53.85us4.45beam 3= 58.3us5.73beam 4= 64.03us
S R Depth in Time
5 us10 us
15 us
20us
38
Main Fact-the deeper in thematerial=less error
39
Recommended Solution
TOFD: YESBUT: do not forget the good things offered by the standard Pulse-Echo techniqueSOLUTION: do both TOFD and PE simultaneously, without reducing the scan speedPulse Echo channels can focus on the cap and root, TOFD’s weak spot!
40
Recommended Solution : PV-100
The system allows for simultaneous acquisition and analysis (inTomoview
only) of TOFD and PE
TOFDPE 45° SW PE 60° SW
41
PV100-Tomoview
42
PV-100
43
Multiple Tofd
44
Scanner/Fixture NecessitiesAbsolute-
1. good contact with surface2. control of PCS3. able to scan straight lineGood features1. magnetic wheels for ferrous mat.2. preamp3. couplant feeds4. rulers for adjustment of PCS5. adjustable for curved surfaces6. umbilical wiring7. probes/wedges individually sprung and gimballed8. laser or other guides
45
Single Tofd Pair
46
Multiple Tofd or Tofd/PE
47
Tofd and Phased Array
48
Couplant ConsiderationsWater usually best- uniformCouplant feeds allow even application while scanning-holes bore in bottom of wedge for flow- IHC (irrigation, holes, carbides)
49
Wedge ConsiderationsTo prevent wear, carbide pins useful on bottom of wedge (gap scanning)typical- .2mmGaps of ¼ and ½ wavelength should be avoided to avoid interference effects
50
AnalysisNormal characterization-
1. position in scan axis2. length3. depth and height4. type- (surface/bottom breaking or
embedded)
51
Defect ShapeDue to beam spread, many defects often have a curved look.
52
Flaws Parallel to the SurfaceFlaws relatively parallel to the surface will have a minimum time delay when the probes are directly in line with the flaw-parabolic shape will be seen as probes approach and leave the flaw as seen previously
Flaw
diff. signals
signal
53
Parabolic CursorsTo aid in measuring the defect as if the beam is a point source,parabolic (curved) cursors areoften used. After calibration these are available to fit theparabolic shape of the flaw to eliminate/reduce the effect of the beam spread in the scan axis.
54
Parabolic CursorsTo acquire defect length the cursors are often placed to fit the natural curve of the defect to eliminate the effectsof beam spread. Fromthe cursors defect startand length can bedetermined.
position of ref.cursor in scan axis-flaw start
dist. between two cursors-length in scan axis
55
Parabolic CursorsUsing phase information, the cursors can also be positionedat the highest amplitude response from each tip- for depth and through wall height information.
position of ref. cursor in ut axis (depth to top of flaw) distance between two
cursors in ut axis- height
56
Surface Breaking DefectsSince only one tip will be present in surface breaking defects, the back wall or LW can be used as second reference point.
57
Parabolic CursorsIndications that exactly fit the curve of the parabolic cursors are normally regarded as having little to no length-small gas pores, grain responses, etc
Some Typical Defects-non-parallel scans
Upper surface breaking crackBack Wall breaking crackHorizontal planar defect
TOFD Typical Defects
60
Horizontal Planar Defect(Lack of Inter-Run Fusion, Laminations)
Transmitter ReceiverLateral wave
LW
Back wall reflection
BW
Reflection echo
Reflected signal
61
Upper Surface Breaking CrackTransmitter Receiver
Crack tip
Back-wall reflection
BW
Lateral wave is blocked
No Lateral wave
62
Back Wall Surface Breaking CrackTransmitter Receiver
Lateral wave
LW
Tip
Back wall echo blocked
No back wall echo-not always the case!
63
Near Surface Crack
The crack blocks the Lateral WaveAnd the lower tip appears on the A-scan
21
1
2
64
Incomplete Root Penetration
21
Note the two signals from the top & bottom
12
3
4
1 2 3 4
65
Lack of Root Penetration
Note the inverted phase between LW and defect
1
23
1
23
66
Lack of Fusion - Side Wall
Note the two signals from the top & bottom
12
3
4
1
2
3
4
67
Porosity
Porosity may image in many forms whether individual or cluster
12
3
1
2
68
Transverse Crack
In the LW we can observe the wide beam effect on the crack
1
2
3
4
1
2
3
12
3
69
Concave Root
Distortion of back-wall echo
1
23
1
2
3
70
Lack of Fusion - Interpass
12
3
Setting up TOFD
2
Determine PCS2 d Tan ( theta ) to focus at a determined point4/3 d Tan (theta) to focus at 2/3 dd= depth of focus or part thicknesstheta = refracted angle of wedgeex: 25 mm butt-weld-focus at center using 70 degree wedges
2 (12.5) (Tan 70)= 69mm PCSfocus at 2/3 in the material-4/3 (25) (Tan 70)= 92 mm PCS
3
PCS-Probe Center SeparationDistance between exit points of send and receive probes
4
How is It Determined?
4/3 D x Tan theta
General rule- for linear joints focus at 2/3 total T.D= total part T
23
T
5
Focus at Point of InterestUsed when expected indications are at predetermined location (ex: root) or multiple Tofd pairs to cover large volumes.
D=where want to focus
2D Tan θ
6
Effect of PCSIn general a wider PCS results in more coverage ofthe material but can lead tomissed areas- impropercalculations can be detrimental to coverage!
7
Effect of Angle
From Charlesworth & Temple
The amplitude response from the bottom and top tip of a vertical crack varies as a function of beam angle. The amplitude has the greatest response around 65 degrees. Between 45 and 80 degrees the amplitude difference is less than 6 db. Notice around 38 deg. the signal from the bottom crack tip drops off in amplitude greatly.
Optimum Upper tip q ≈ 64°Optimum Lower tip q ≈ 68°
8
Calculator
TOFD probe separation can be calculated with basic mathematical formula or Excel calculator tools
9
Choosing Probes- Give and Take-OverviewHighly dampened- to reduce ring time and increase near surface resolutionFrequency- lower frequency will give more beam spread for detection with less resolution. Higher frequency probes attenuate faster. Increased frequency= more cycles occur= better depth resolutionDiameter- smaller crystals will create more beam spread, but again beam intensity is less.A number of guides are available
10
Choosing Probes-Frequency and depth resolutionmore cycles within the time frame between LW and BW=better depth resolutiongeneral rule- aim for 20 or better cycles (30 and over optimum)positive-increased frequency= increased cyclesnegative-beam spread reduced, attenuation/scatter increased
11
T in mmfocus 2/3 T
LW-BW time us
1 MHz# cycles
3 MHz# cycles
5 MHz# cycles
10 MHz# cycles
20 MHz# cycles
10 1.25 1.3 3.8 6.3 12.5 25.1
25 3.13 3.1 9.4 15.7 31.3 62.7
50 6.265 6.3 18.8 31.3 62.7 125.3
100 12.53 12.5 37.6 62.7 125.3 250.7
12
Probe examplesPCS 84 mm
PCS 84 mm
narrow bs
big beam spread
10 MHz 15mm dia
3 MHz 6mm dia
13
Effect of Frequency on Beam Spread
14
Effect of Crystal Diameter on Beam Spread
3mm dia
6mm dia
12mm dia
15
Effect of Wedge Angle
16
Comparing Wedge Angles
45 60 70In general, the higher thewedge angle, the morethe time scale will becompressed.In general a higher wedge angle givesmore coverage.
17
Setting FiltersGeneral ruleHigh pass- ½ FrequencyLow pass- 2x Frequency
18
RangeGeneral Rule-leave at least 1 us before LWleave 1 us after mode-converted back wall
19
Digitization FrequencyHigher = better if possibleAbsolute minimum 2x Frequency (10mhz x2=20mhz)
Ideal minimum 5x frequency (10 MHz x 5 = 50 MHz)100 MHz if possible
20
PRFLook for ghost echoesLook at trace before lateral wave, should be flat or near flat or prf may be to highOn Omniscan-optimum is usually adequate
21
Sampling interval/Encoder Resolution
1mm typical- 2 or 3mm to reduce data file sizes if necessary for long scans
22
Averaging32 maximum realistic value8 or 16 usually betterAveraging can increase SNR
23
Pulse WidthGeneral Rule- LW = 1 ½ cycles, maximum 2
On OmniScan, optimum is usually adequate
24
Sensitivity/gainGeneral rulesLW to 20- 50% FSH
backwall to 100% FSH +10dbSensitivity not related to size of defect-FBH and SDH should be avoided-signal from FBH is simply related to area and signal from SDH will give two signals-reflection from top of hole and creeping wave that runs around bottom of hole.-stnds /guides differ on the proper targets to use for calibration
25
Using Calibration Blockusing series of thin slots and setting response from bottom (BS 7706) Slot must be upper surface breaking- signal from top largely reflected, while bottom gives response similar to fatigue crack. Slots often 1/3 and 2/3 T. Block should be similar material and T.Using slots at varying depths covering material T. Gain set on deepest slot so signal is 60% FSH.
26
Using grass/noiseSetting gain on calibration block, then increasing gain until noise is 5% FSH in between LW and BW.
27
Velocity and Wedge Delay Calibration
Unlike most UT inspections, the calibration of velocity and wedge delay are performed after acquisition. Normally carried out by telling the inspection system three things-
28
Reference Good A-scanCursor positioned in area free of flaws for reference LW and BW.
29
Input Test Parameters
1.PCS2.Thickness3.Geometry
30
Input and Train Top and BottomMany conventions- key is consistency!One popular method is to use first + peak of lateral wave and - peak of long. BW
ref. cursor positioned on first+ peak of LW
software told this is 0 or Top
31
Input and Train Top and Bottom
measure cursor positioned at –peak of BWsoftware told this is this thickness
32
Calibration performed
33
No Signal?Check gainCheck couplant in and under shoesCheck Cables-undamaged, connected correctlyCheck orientation- wedges facing each other Check flaw detector circuitsCheck preamp (if used)- make sure on and connected correctly-check battery
By: Nick Bublitz
Tofd Demo on Sonaspection Plate 2.0 SW OmniScan
2
Required EquipmentOmniScan (16:16,16:64,16:128, 2/4/8 channel) w/ Tofd option and 2.0R2 SWTofd scanner (HST-X04)(2) 60 degree wedges (ST1-60L-IHC)(2) 5MHz probes- (C543-SM)Weld (Sonaspection .5”)Cables- (2) Lemo-MD, (1) Lemo-Lemo as demonstrated)Preamp- (5682), 9 volt batteryBNC-Lemo adapters (2) as demonstratedCouplant- water for plate, grease for wedge as demonstratedEncoder- Old mini-encoder used
3
Setting up Equipment
turn on
receive probe
send probeencoder
preamplifier
flaw detector
4
Boot up and Select UTTurn the OmniScan on, start the SW and if necessary switch from PA to UT from the menu
1
2
5
Access the Wizard
1
2
6
Start the Group Wizard
choose modifyand Next
1
2
3
7
Set Part Parameters
Flatpart T
Material
8
Connection Type
Tofd inspection
12
9
Choose Probe
angle beam type
then probe 1
23
10
Choose Wedge
Tofd type
then wedge
1
2 3
11
Position
leave 0 for demoor input distance from side of plate start and scan start
choose non-parallel
set PCS- distancepin to pin of wedges-general demo on .5”29-35 mmas cap allows
12
Finish!
13
Set rangecouple wedges flat on base metal-can remove encoderto aid
adjust start and range untilLW,BW, and mode converted BW are on screen with at least 1 us before LW and after Mode BW
1
3
2
tip- if you can’t see signals, set start at 0 and range to 30us, thenstart adjusting start/range back and forth until dialed in
14
Overlays
if necessary turn off gates and cursors
1
2
3
15
Adjust Gain
adjust gain so LW is20-50% FSH
1
2
16
Adjust Pulser
if necessary adjust voltageand PRF/PW- signal before LWshould be relatively flat
1
2
3
17
Adjust Receiver
1
2
choose filtering ifneeded- auto or 5MHz probably sufficient
18
Setup Encoder
1
24
scan length and resolutionone line/encoder 1
3 5
19
Set Polarity
move direction want to scan and make sure getting larger
change here if needed
1
2
20
Calibrate Encoder
1
2
3
4
21
Set Origin
position at 0 point andhit next
1
23
22
Set Distance
set distance going to move, move that distancethen hit calibrate
1
2
3
23
Accept or Restart
to verify: move back tozero point and look at axis position
1
2
24
Scan the PlateApply couplant over the plateApply the scanner in proper orientationhit start acquisition scan the plate and freeze data
1
2
3
4
25
Turn Analyze Aids onTurn Cursors back on
Turn readings on
1
2
3
4
5
6
7
26
Calibrate
1
2
3
4
27
Select Reference A-scan
Show the OmniScan a good area with no flaws,LW/BW only
12
28
Input Parameters-As needed
1
2
29
Set Cursor Position and Depth
1 move ref. cursor tofirst + cycle of LW
2-input 0 fortop surface
3 move meas. cursor tofirst - cycle of BW
4-input T forback
surface5
30
Accept or Restart
1
view vel /delay
2 Accept or restart