![Page 1: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/1.jpg)
CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY
SEPARATORR. Waterhouse, D. Walker, A. Brown, D. Merritt, J. Emanuel, E. Hostetler, C. La, C. Rogers, and R.W. Pekala
ENTEK International LTDENTEK International LLC
September 9, 2015
![Page 2: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/2.jpg)
2
UHMWPE
Silica
Oil
Twin ScrewExtrusion
(‐CH2‐CH2‐) x
UHMWPE GEL PROCESSING
![Page 3: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/3.jpg)
UHMWPE + OIL + SHEAR → CHAIN DISENTANGLEMENT
3
![Page 4: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/4.jpg)
4
SILICA AGGREGATES DISPERSED THROUGHOUT THE POLYMER MATRIX
SILICA
![Page 5: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/5.jpg)
OIL EXTRACTION + SOLVENT DRYING → POROUS SEPARATOR
5
![Page 6: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/6.jpg)
Silica Aggregates
UHMWPE fibrils
![Page 7: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/7.jpg)
DEGRADATION MECHANISM ‐ SHEAR
UHMWPE chains are susceptible to chain scission during twin‐screw extrusion
Reactive end groups Hydrogen abstraction Oxidation Crosslinking
7
R● + O2→ ROO●
![Page 8: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/8.jpg)
EVIDENCE OF SHEAR DEGRADATION
Soxhlet extraction Para‐xylene 138°C
8
![Page 9: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/9.jpg)
9
CHAIN SCISSION VS. CROSSLINKING IN BATTERY ENVIRONMENT
More crosslinking → less extractables
![Page 10: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/10.jpg)
PROCESS OILS ARE COMPLEX CHEMICAL MIXTURES
10
C-13 NMR Analysis provides a chemical fingerprint for process oils
Naphthenic Oil #1
X
Naphthenic Oil #2
X
![Page 11: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/11.jpg)
C‐13 NMR ANALYSIS (ALIPHATICS)
11
![Page 12: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/12.jpg)
C‐13 NMR ANALYSIS (AROMATICS)
12
![Page 13: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/13.jpg)
13
PROCESS OIL ‐‐‐ CHEMICAL CHANGES IN BATTERY ENVIRONMENT
![Page 14: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/14.jpg)
SEPARATOR OXIDATION RESISTANCE
Test methods Perox 80 Potassium dichromate Oxidation induction time Electrochemical oxidation test High temperature battery life test
Material considerations Polymer matrix Residual oil Oil / PE ratio
14
![Page 15: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/15.jpg)
CHEMICAL RESISTANCE VS. OXIDATION RESISTANCE
15
After 20 hrs in H2SO4 at 80 °C After 20 hrs in H2SO4/H2O2 at 80 °C
Phenolic/polyester PE/SiO2 Phenolic/glass
![Page 16: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/16.jpg)
PEROX 80 ‐‐‐ % XMD ELONGATION VS EXPOSURE TIME
Polymer content : XLR > LR > STD
16
![Page 17: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/17.jpg)
PEROX 80 ‐‐‐ PUNCTURE STRENGTH VS EXPOSURE TIME
Polymer content : XLR > LR > STD
706050403020100
20
15
10
5
0
ox time (hrs)
Punc
ture
(N)
0.15 LR0.15 std
0.15 XLR0.15 XLR no oil
formula
0.15 mm backweb
17
![Page 18: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/18.jpg)
PEROX 80 ‐‐‐ % XMD ELONGATION VS EXPOSURE TIME
Polymer content : XLR > LR > STD
706050403020100
800
700
600
500
400
300
200
100
0
ox time (hrs)
XMD
% s
trai
n
0.25 LR0.25 std
0.25 XLR
formula
0.25 mm backweb
18
![Page 19: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/19.jpg)
PEROX 80 ‐‐‐ PUNCTURE STRENGTH VS EXPOSURE TIME
Polymer content : XLR > LR > STD
706050403020100
20
15
10
5
0
ox time (hrs)
Punc
ture
(N)
0.25 LR0.25 std
0.25 XLR
formula
0.25 mm backweb
19
![Page 20: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/20.jpg)
CAN A 0.15 BW SEPARATOR BE DESIGNED TO HAVE AS GOOD OF OXIDATION RESISTANCE AS 0.25 BW?
Polymer content : XLR > LR > STD
706050403020100
800
700
600
500
400
300
200
100
0
ox time (hrs)
XMD
% s
trai
n
0.15 LR0.15 XLR0.25 std
formula
20
![Page 21: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/21.jpg)
CAN A 0.15 BW SEPARATOR BE DESIGNED TO HAVE AS GOOD OF OXIDATION RESISTANCE AS 0.25 BW?
Polymer content : XLR > LR > STD
706050403020100
20
15
10
5
0
ox time (hrs)
Punc
ture
(N)
0.15 LR0.15 XLR0.25 std
formula
p
21
![Page 22: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/22.jpg)
SURFACE SEM ‐‐‐ BEFORE AND AFTER PEROX 80 TEST
STD Separator
BEFORE AFTER
22
![Page 23: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/23.jpg)
SURFACE SEM ‐‐‐ BEFORE AND AFTER PEROX 80 TEST
XLR Separator
BEFORE AFTER
23
![Page 24: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/24.jpg)
ELECTROCHEMICAL OXIDATION TEST
5cm x 5cm specimens were overcharged with 200mA/cm² current between 2 pure lead plates at 75°C:
Three specimens per separator type Samples “fail” when ΔV/Δt ≥ 0.2 V/min
The polymer matrix within the separator is oxidized, allowing PbSO4 to eventually grow to the positive plate, resulting in short‐circuit.
24
![Page 25: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/25.jpg)
ELECTROCHEMICAL OXIDATION RESISTANCE
Polymer content : XLR > LR > STD
25
![Page 26: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/26.jpg)
ELECTROCHEMICAL OXIDATION RESISTANCE (CONT’D)
Fully Extracted0% oil
Polymer content : XLR > LR > STD
Even after aggressive oxidation test, 0.15 XLR has comparable puncture strength to pristine 0.25 STD
26
![Page 27: CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE …static.entek.com/150909_ENTEK_-16ABCWeb.pdf · 2016-05-23 · CHEMICAL AND PHYSICAL CHANGES THROUGHOUT THE LIFE OF A BATTERY SEPARATOR](https://reader033.vdocuments.net/reader033/viewer/2022042007/5e70b8a7769f9b6b38525919/html5/thumbnails/27.jpg)
SUMMARY
PE/SiO2 separators are susceptible to many chemical and physical changes both during their manufacture and within a Pb‐acid battery environment
The polymer content and oil/PE ratio are two critical parameters in the design and engineering of battery separators
ENTEK has introduced a series of LR and XLR separators that have low electrical resistance, good mechanical properties, and excellent oxidation resistance
Although some OEMs are reluctant to use thinner backweb separators in their battery designs, 0.15 XLR outperforms many 0.25 STD separators.
27