This may be the author’s version of a work that was submitted/acceptedfor publication in the following source:
Sun, Zhiming, Yang, Xiaoping, Zhang, Guangxin, Zheng, Shuilin, & Frost,Ray(2013)A novel method for purification of low grade diatomite powders in centrifu-gal fields.International Journal of Mineral Processing, 125, pp. 18-26.
This file was downloaded from: https://eprints.qut.edu.au/65157/
c© Consult author(s) regarding copyright matters
This work is covered by copyright. Unless the document is being made available under aCreative Commons Licence, you must assume that re-use is limited to personal use andthat permission from the copyright owner must be obtained for all other uses. If the docu-ment is available under a Creative Commons License (or other specified license) then referto the Licence for details of permitted re-use. It is a condition of access that users recog-nise and abide by the legal requirements associated with these rights. If you believe thatthis work infringes copyright please provide details by email to [email protected]
License: Creative Commons: Attribution-Noncommercial-No DerivativeWorks 2.5
Notice: Please note that this document may not be the Version of Record(i.e. published version) of the work. Author manuscript versions (as Sub-mitted for peer review or as Accepted for publication after peer review) canbe identified by an absence of publisher branding and/or typeset appear-ance. If there is any doubt, please refer to the published source.
https://doi.org/10.1016/j.minpro.2013.09.005
1
A novel method for purification of low grade diatomite powders in 1
centrifugal fields 2
3
Zhiming Suna,b, Xiaoping Yanga, Guangxin Zhanga, Shuilin Zhenga∗, Ray L. Frost b∗ 4 5
a School of Chemical and Environmental Engineering, China University of Mining & Technology, Beijing 6 100083, P.R. China 7
8 b Nanotechnology and Molecular Science, Faculty of Science and Technology, Queensland University of 9
Technology, 2 George Street, GPO Box 2434, Brisbane, Queensland 4001, Australia 10
2
Abstract. 11
This study presented a novel method for purification of three different grades diatomite from China by 12
scrubbing technique using sodium hexametaphosphate (SHMP) as dispersant combined with 13
centrifugation. Effects of pH value and dispersant amount on the grade of purified diatomite were 14
studied and the optimum experimental conditions were obtained. The characterizations of original 15
diatomite and derived products after purification were determined by scanning electron microscopy 16
(SEM), X-ray diffraction (XRD), infrared spectroscopy (IR) and specific surface area analyzer (BET). 17
The results indicated that the pore size distribution, impurity content and bulk density of purified 18
diatomite were improved significantly. The dispersive effect of pH and SHMP on the separation of 19
diatomite from clay minerals was discussed systematically through zeta potential test. Additionally, a 20
possible purification mechanism was proposed in the light of the obtained experimental results. 21
22
Keywords: Diatomite; Centrifugal separation; Purification; Sodium hexametaphosphate 23
• Corresponding authors. Fax: +86 10 62330972 (S. Zheng), +61 7 3138 2407(R. L. Frost) 24
E-mail addresses: [email protected] (S. Zheng), [email protected] (R. L. Frost) 25
3
1. Introduction 26
Diatomite or diatomaceous earth is a non-metallic material composed mainly of a wide variety of shape 27
and sized skeletal remains of diatoms [1, 2]. Because of highly porous structure, low density, high 28
absorption capacity, low thermal conductivity, chemical inertness, relatively low price and high 29
abundance, diatomite can be used extensively as filtration media, adsorbents, conventional catalyst 30
supports [3-8]. It can also be applied in manufacturing of certain membranes and in the 31
separation of biocatalytic proteins and cells [9]. China has substantial diatomite resources, most of 32
which are of moderate quality, having a SiO2 content of about 60 %~80 %. There are a lot of 33
impurities such as alkaline and alkaline earth metals and some organic substance, which decrease the 34
microporosity and limit the use of diatomite. Hence, raw diatomite needs to be industrially purified 35
before its commercial utilization. Several approaches have been reported, such as acid leaching, 36
classification, crushing, gravitational sedimentation, calcinations and ultrasonic treatment [9-13]. 37
Chemical treatments, such as acid treatment, can significantly improve the quality of raw diatomite. 38
However, waste water generated after acid leaching is very difficult to deal with, which causes severe 39
environmental problems and great operative expenses. Other beneficiation processes have some other 40
weaknesses, such as inefficiency, high processing cost, inadequate effect, fusion problem and 41
destruction of diatom structure. The advantages and disadvantages of different diatomite purification 42
techniques are concluded in Table 1. Among these methods, scrubbing technique has been preferred 43
due to its cheapness and the high-efficiency of the low grade diatomite purification especially for 44
pretreatment. However, there are few industrial achievements on diatomite purification now. 45
High speed scrubbing technique is applied to make the impurities coated on the surface of raw 46
diatomite separated from the diatom units initially. Agitator scrubbing machine is a kind of 47
conventional dressing equipment, which has an extensive application in mineral processing. 48
Centrifugal separation is one of the technically and economically acceptable solutions for the treatment 49
of waste water, flotation slurries and chemical industry [14-16]. The advantage of centrifugal 50
separators lines in the fact that the settling velocity is much higher than that of gravitational separators, 51
which results in smaller separator dimensions, higher separation efficiency and precision. Because of 52
small particle size of impurities and diatomite, the centrifugal separation can shorten the particles 53
settling time, which can ensure the separation process efficiently and continuously. 54
Some kinds of dispersants, such as sodium hexametaphosphate and sodium pyrophosphate, are 55
4
employed during the scrubbing process. Uniform and relatively stable dispersion of diatomite and its 56
impurities in the scrubbing suspension is the premise of effective centrifugal separation. The sodium 57
hexametaphosphate (SHMP) is widely used in mineral processing as floatation regulator and dispersant 58
[17]. The influence and mechanism of SHMP on the floatation and dispersion of different minerals has 59
been studied by many researchers [18-19]. However, the relationship between the settling property and 60
the dispersion of diatomite and its impurities has not been systematically studied before. 61
In the light of these, three natural diatomite powders, selected from different regions of China, 62
were purified by scrubbing technique combined with centrifugal separation using sodium 63
hexametaphosphate as the dispersant. It is the aim of the investigation to show whether different grades 64
of raw diatomite can be effectively purified through this method. Effects of pH value and dispersant 65
amount on the grade of purified diatomite were discussed. The influence of pH and sodium 66
hexametaphosphate on the dispersion of the diatomite and clay minerals was systematically studied 67
based on the zeta potential analysis of pure materials, and the possible purification mechanism was 68
further proposed. 69
70
2. Materials and methods 71
2.1. Materials 72
Three typical natural original diatomite powders were obtained from Linjiang of Jilin province 73
(LJ-DE), Huade of Inner Mongolia (HD-DE), and Shengxian of Zhejiang province (SX-DE) in China 74
respectively, respectively. Sodium hexametaphosphate and sodium hydroxide were purchased from 75
Beijing Chemical Reagent Company (Beijing, China). The chemical compositions of the raw diatomite 76
are listed in Table 2. As shown in Table 2, the main component of raw diatomite is SiO2. Ferric oxide 77
and alumina are the main impurities in raw diatomite. Based on the SiO2 content, the grade of three 78
diatomites decreases in the following order: LJ-DE > HD-DE > SX-DE. The pure minerals for zeta 79
potential analysis were purchased from NCS Testing Technology Co., Ltd. (Beijing, China) without 80
any further purification. The chemical compositions of the pure minerals were summarized in Table 2. 81
The microstructure of the pure diatomite is displayed in Fig. 1. It is clear that the purity of the diatomite 82
sample was very high from the chemical compositions analysis and SEM pictures. 83
84 2.2. Purifying methods 85
5
The flowsheet for the processing of raw diatomite is given in Fig. 2. As showen in Fig. 2, the 86
purification was undertaken by the following procedure: 100g of raw diatomite samples was initially 87
dispersed in 400 mL of water with a laboratory-scale model XFD12 agitator scrubbing machine for 88
about 25 min with a stirring rate of 1500 rpm. A certain amount of sodium hydroxide was 89
pre-dissolved in 20 mL of deionised water and then it was slowly added to the scrubbing suspension at 90
room temperature in order to adjust the pH value of the suspension. The suspension was stirred for 91
further 10 min, and then the selected amount of sodium hexametaphosphate was added to the 92
suspension. After stirring for a further 5 min, the suspension was collected and sieved using a 325 mesh 93
standard screen (45 μm). After sieving, the oversized products were collected and dried in an oven at 94
105 °C for 12h. The obtained sample was labeled as oversized product. The undersized suspension was 95
then transferred to a 100 mL centrifuged tube. After shaking, the mixture was centrifuged at 1500 rpm 96
(RCF (relative centrifugal force) = 300) for 15 min. After the centrifugation, the centrifugal sediment 97
was obtained and then dried at 105 °C for 12 h. The centrifugal overflow was filtrated by vacuum filter 98
and washed with distilled water 2-3 times and then dried at 105 °C for 12h. 99
100
2.3. Characterization 101
The chemical compositions of raw diatomite and purified diatomite are determined by X-ray 102
fluorescence (SPECTRO X-LAB2000). The crystalline phase identification of samples was undertaken 103
by a PANalytical X’Pert PRO X-ray diffractometer employing CuKα radiation at a goniometer rate of 104
2θ= 4°/min. Morphology of samples was examined by a scanning electron microscopy (S-3500N, FEI 105
Company). Infrared emission spectroscopy was carried out on a Nicolet Nexus 870 FTIR spectrometer, 106
which was modified by replacing the IR source with an emission cell. Spectral manipulation such as 107
baseline adjustment, smoothing and normalization was performed using the Spectra calc software 108
package (Galactic Industries Corporation, NH, USA). Surface area analyses based upon N2 109
adsorption/desorption were carried out with a Micromeritics Tristar 3000 automated gas adsorption. 110
From the measurement, pore structure parameters were also characterized at liquid nitrogen 111
temperature. The samples were pre-heated at 105 °C under the flow of N2 on a Micrometrics Flowprep 112
060 degasser before the measurement. 113
114
2.4. Zeta potential measurement 115
6
A certain amount of pure diatomite, kaolin and montmorillite was added into distilled water firstly. 116
The suspension was stirred for 15 min using a magnetic stirring apparatus before the test. At different 117
pH values, zeta potential of different samples was measured in a Nano ZS90 type ξ-potential analyzer 118
(Malvern, Britain). The pH value of the solution was automatically adjusted by adding HC1 or NaOH 119
in range of 2–12. 120
3. Results and discussion 121
3.1 Characterizations of purified diatomite 122
3.1.1 Chemical analysis 123
The effect of pH values of the scrubbing suspension on SiO2 content of purified diatomite was 124
examined through a series of centrifugal separation experiments while other variable kept constant. The 125
dosage of SHMP keeps 3 wt. ‰. Changes of the SiO2 content of the purified diatomite at different pH 126
are given in Fig. 3. It is clear that the SiO2 content of purified diatomite was enhanced with the 127
increase in pH. The SiO2 content of purified diatomite reached the highest values when the pH was 128
up to 10, so the optimum pH value is determined as 10. It can be confirmed that a high-grade silica 129
material, more than 87 wt. % SiO2 was obtained when pH was 10 for the purification of LJ-DE and 130
HD-DE. On the other hand, the removal of the impurities for SX-DE was more difficult compared with 131
the other two diatomites, and the SiO2 content of the purified diatomite was just increased to 74.01 wt. % 132
when pH was 10. 133
The dosage of SHMP is another key factor on the grade of purified diatomite and its influence is 134
shown in Fig. 4. The pH values of the scrubbing suspension were kept 10. From the Fig. 4, the SiO2 135
content of purified diatomite was increased with the increase in the dosage of SHMP. As for LJ-DE, 136
when the dosage of SHMP was up to 2 wt. ‰, the grade of purified diatomite reached the highest 137
value. As for HD-DE and SX-DE, the optimum SHMP dosages are determined as 3.5 wt. ‰ and 3 138
wt. ‰, respectively. The difference of optimum SHMP dosage might be caused by the different 139
contents and forms of impurities in three raw diatomites. The yield of the purified diatomite for LJ-DE, 140
HD-DE and SX-DE are 81.37%, 64.21% and 77.28% respectively under the optimum experimental 141
conditions. 142
143
3.1.2 Mineralogical analysis 144
X-ray diffraction (XRD) is one of the most useful techniques to study the structural geometry and 145
7
texture of impurities in diatomites. The XRD patterns of three raw diatomites before purification and 146
different products (oversized product, centrifugal overflow and centrifugal sediment) obtained after 147
purification are presented in Fig. 5. An essentially amorphous phase was observed in three raw 148
diatomites, but a significant amount of crystalline phases were also found. Among three raw 149
diatomites, the XRD pattern of LJ-DE showed the highest content of amorphous SiO2, followed by 150
HD-DE and then SX-DE. The main impurities in raw LJ-DE samples can be divided into two types. 151
One is clay minerals such as montmorillite, kaolin and muscovite, and the other one is crystalline 152
siliceous sands, such as quartz and feldspar. The main mineral compositions of the oversized product 153
are coarse feldspar and quartz, which agrees with our expectations. The typical XRD patterns of clay 154
minerals such as montmorillite, kaolin and muscovite appear in the centrifugal overflow, determined as 155
the tailings. All the purified powder samples exhibit less crystalline structure after purification. From 156
Fig. 5 (a) and (b), it can be seen that a high-grade amphorous silica material with less crystalline 157
structure is obtained after purification. As shown in Fig. 5(c), the reduction of impurities is rather 158
insignificant for SX-DE, indicating that the purification effect of SX-DE is the worst. In addition, the 159
content of clay minerals is the highest for SX-DE among three diatomites. The results indicate the 160
effect of purification might be influenced to a large extent by the content of clay minerals in raw 161
diatomites and the relative higher content of clay minerals in SX-DE results in the undesirable 162
purification effect. 163
164
3.1.3 Microstructural analysis 165
Microstructural observations have been applied to identify the success of producing highly-porous 166
diatomite particles and maintaining porous structural integrity of diatom through the applied scrubbing 167
and centrifugation treatment. A selection of SEM images of raw diatomite and purified diatomite from 168
Linjiang are present in Fig. 6. The characteristic disc-shaped structure of diatom particles is clearly 169
shown in raw LJ-DE with the diameter of about 20 μm. Compared with purified diatomite, the raw 170
diatomite exhibits diatomite frustules with closed-pores dispersed in clay and some other fine particles. 171
In addition, integrated morphology of diatom in raw diatomite and purified diatomite is also displayed 172
(Fig. 6 LJ-a2 and LJ-b2). It was found that the pores on the surface of diatoms could be seen more 173
clearly after purification, which might be due to the fact that the impurities were removed from the 174
clogged pores. Moreover, the purified diatomite still kept integrality after purification. 175
8
Naturally it is also observed that some impurities have been deposited on the diatomite particles in 176
HD-DE (see Fig. 7 HD-a1 and HD-a2). The diatoms in raw HD-DE are mostly cracked inherently. The 177
diameter of integrated diatom in HD-DE sample is approximately 10 μm, which is smaller than that of 178
LJ-DE sample. There are fewer impurities in purified diatomite (Fig.7 HD-b1). Fig.7 HD-b2 indicates 179
undamaged forms of diatom in purified diatomite with extremely clean pores, which demonstrates the 180
approach has a significant improvement on the pore structure of diatomite. 181
Fig. 8 displays the microstructure of raw SX-DE sample and purified diatomite samples. The 182
presence of cylindrical diatom together with small particles of impurities could be noticed in 183
micrographs of raw SX-DE sample and purified diatomite. Considerable content of small impurities 184
such as quartz, feldspar and clay minerals was detected on the surface of diatomaceous earth and such 185
high content of impurities makes SX-DE greyer than the other two raw diatomite samples. Compared 186
with the undamaged forms of diatomaceous earth in raw SX-DE sample, the outside pore structure on 187
the surface of cylindrical diatom looks cleaner after purification. However, there are still a mass of 188
impurities embedded in the pore of cylindrical diatom. The shearing force under the current scrubbing 189
conditions can not remove such embedded impurities quickly and effectively. The embedded 190
distribution of impurities might be another key factor why the SX-DE sample is harder to be purified 191
than the other two samples. 192
193
3.1.4 IR analysis 194
A comparison of the IR spectra of three raw diatomite samples and purified diatomite are 195
presented in Fig. 9. As for all samples, the IR spectra show two major absorption bands which were 196
observed at about 3430 and 1630 cm-1 [21]. The band at 3430 cm-1 is due to the stretching vibrations of 197
adsorbed water, and the band at 1630 cm-1 represents H-O-H bending vibration of water. The bands at 198
about 1100 cm-1 reflects the asymmetric stretching modes of Si–O–Si bonds and the Si-O-Si symmetric 199
stretching vibration peaks appear at about 800 cm-1 [22, 23]. Compared with the raw LJ-DE and 200
HD-DE sample, the bending modes of Al-O-H at 912 and 914 cm-1 appear in the IR spectrum of 201
centrifugal overflow sample, which indicates that the presents of some clay minerals [24]. The bending 202
vibrations of Al-O-H are observed in all three samples of SX-DE, which means the content of clay 203
minerals are high and the removal effect after purification is not very well, which is in line with the 204
result of the previous SEM analysis. 205
9
206
3.1.5 Surface area measurement 207
As shown in Fig. 10, the nitrogen adsorption/desorption isotherms of raw diatomite, centrifugal 208
overflow and sediment exhibit a type II sorption behavior in the classification of Brunauer, Deming, 209
Deming and Teller (BDDT) [25]. The specific surface area, pore volume and average pore size of raw 210
diatomites and products after purification are summarized in Table 3. It is clear that the raw diatomite, 211
tailing and purified diatomite have the same form of isotherms and hysteresis loop. The hysteresis loop 212
is associated with the filling and emptying of the mesopores by capillary condensation [26]. The 213
adsorption of N2 of centrifugal overflow is much higher than that of purified diatomite, indicating that 214
the overflow possesses a higher specific surface area. The result is in line with the XRD result since the 215
overflow is mainly composed of clay minerals. Compared with the raw diatomite, purification did not 216
evidently change the shape of the isotherms. However, purification resulted in a dramatic increase in 217
nitrogen adsorption and an enhancement of the hysteresis, indicating the improvement of the 218
microporous structure of diatom. As shown in Table 3, the specific surface areas of purified diatomite 219
powder become smaller than that of raw diatomites. It is easy to understand that the decrease of 220
specific surface areas is caused by the removal of impurities with relative higher specific surface areas. 221
Similar specific surface areas changes were also obtained in previous studies [9, 10, 27, 28]. 222
223
3.2 Mechanism of purification 224
The relationship between zeta potential and pH value of pure diatomite, kaolin and 225
montmorillite is presented in Fig. 11. It can be seen that the pH value at the isoelectric point of 226
diatomite, kaolin and montmorillite is about 2.0. The surface of diatomite, kaolin and montmorillite 227
particles shows negative electricity in the pH range of 2-12. In the acidic environment, the absolute 228
value of zeta potential of diatomite, kaolin and montmorillite particles is remarkably lower and 229
aggregation occurs easily among the particles due to the relative lower electrostatic repulsive force 230
[18, 19]. Moreover, with the increase in the concentration of SHMP, it is obvious that sodium 231
hexametaphosphate could lower the zeta potential of diatomite, kaolin and montmorillite. As for 232
diatomite and kaolin, the absolute value of surface charge of diatomite and kaolin kept increasing 233
with increase of pH in the range of 2-12. On the other hand, the surface charge of montmorillite 234
decreased firstly and then increased when pH was up to 9. A similar variation trend for the three 235
10
minerals was observed in different concentrations of SHMP. The above results illustrate that the 236
optimum dispersion conditions for diatomite and clay minerals are in the weak alkaline condition at 237
a relative high concentration of SHMP, which is in agreement with the previous obtained optimum 238
purification conditions. 239
Based on the above results, the mechanism of purification can be comprehensively concluded as 240
follows: Under the high speed shear force, the impurities were taken out from the surface and the 241
porous structure of raw diatomite. Due to the high electrostatic repulsive force, uniform and 242
relatively stable dispersion of diatomite and impurities in the scrubbing suspension can be obtained 243
in the weak alkaline condition at a relative high concentration of SHMP. Then, the coarse fractions 244
(+45 μm) containing mainly quartz and feldspar were firstly removed to prevent these large and 245
heavy impurities from entering the centrifugal process. After suitable centrifugation, the diatom and 246
impurities were separated from each other. The grade of diatomite was further improved due to the 247
remarkable difference of particle density and size in centrifugal field. 248
4. Conclusions 249
Purification effects of scrubbing technique combined with centrifugal separation using sodium 250
hexametaphosphate as dispersant on three typical diatomite powders were studied. The simple 251
technique could effectively remove most of the impurities containing clay minerals and organic matters 252
from LJ-DE and HD-DE samples. From the SEM analysis, the porous structure of all three raw 253
diatomites can be improved after purification. It is deduced that the strong centrifugal force in 254
scrubbing process can effectively separate the diatomite and impurities. Uniform and relatively stable 255
dispersion of diatomite and clay minerals in the scrubbing suspension can be obtained in the weak 256
alkaline condition at a relative high concentration of SHMP. Based on the difference of partial density 257
and size between diatom and impurities, the diatomite was effectively purified in centrifugal field. The 258
embedded distribution and relatively high content of clay minerals result in the inadequate separation 259
before centrifugation, which might be the main reason for the undesirable purification effect of SX-DE. 260
It is concluded that the technique will be potentially used as good purification method of low grade 261
diatomite in the industry. 262
263
Acknowledgement 264
The work is supported by National Technology R&D Program in the 12th Five year Plan of China 265
11
(2011BAB03B07). The first author also thanks the China Scholarship Council (CSC) for financial 266
support. 267
268
References 269
[1] Davis L., 1991. Diatomite. Am. Ceram. Soc. Bull. 70, 860-861. 270
[2] Koruniv Z., 1998. Review: diatomaceous earths, a group of natural insecticides. J. Stored Prod. Res. 271
34, 87-97. 272
[3] Akhtar F., Rehman Y., 2010. Bergström L., A study of the sintering of diatomaceous earth to 273
produce porous ceramic monoliths with bimodal porosity and high strength. Powder Technol. 201, 274
253-257. 275
[4] Wang H., et al., 2011. Mechanical properties of dental resin composites by co-filling diatomite and 276
nanosized silica particles. Mater. Sci. Eng. C 31, 600-605. 277
[5] Bahramian B., et al., 2008. Diatomite-supported manganese Schiff base: An efficient catalyst for 278
oxidation of hydrocarbons. Appl. Catal. A-Gen 345, 97-103. 279
[6] Hadjal H., Hamdi B., Kessaissia Z., 2004. Adsorption of heavy metal ions on composite materials 280
prepared by modification of natural silica. Desalination 167, 165-174. 281
[7] Xiong W.H., Peng J., 2008. Development and characterization of ferrihydrite-calcined diatomite as 282
a phosphorus adsorbent. Water Res. 42 , 4869-4877. 283
[8] Sun Z.M., Zhang Y. Z., Zheng S. L., et al., 2013. Preparation and thermal energy storage properties 284
of paraffin/calcined diatomite composites as form-stable phase change materials, Thermochim. Acta 285
558, 16-21. 286
[9] Şan O., Gören R., Özgür C., 2009. Purification of diatomite powder by acid leaching for use in 287
fabrication of porous ceramics. Int. J. Miner. Process.93, 6-10. 288
[10] Ediz N., Bentli İsmail, Tatar İlknur, 2010. Improvement in filtration characteristics of diatomite by 289
calcinations. Int. J. Miner. Process. 94, 129-134. 290
[11] Zhang G., Cai D., Wang M., 2013. Microstructural modification of diatomite by acid treatment, 291
high-speed shear, and ultrasound. Micropor. Mesopor. Mat.165, 106-112. 292
[12] Şan O., İmaretli A., 2011. Preparation and filtration testing of diatomite filtering layer by acid 293
leaching. Ceram. Int. 37, 73-78. 294
12
[13] Sun Z.M., Bai C.H., Zheng S. L., et al., 2013. A comparative study of different porous amorphous 295
silica minerals supported TiO2 catalysts, Appl. Catal. A-Gen 458, 103– 110. 296
[14] Batalović V., 2011. Centrifugal separator, the new technical solution, application in mineral 297
processing. Int. J. Miner. Process. 100, 86-95. 298
[15] Brouwers J.J.H., 2002. Phase separation in centrifugal fields with emphasis on the rotational 299
particle separator. Exp. Therm. Fluid Sci. 26 , 325-334. 300
[16] Huang C.H., Tsai C.J., Shih T.S., 2000. Particle collection efficiency of small inertial impactors 301
considering particle gravitational effect, J. Aerosol Sci. 31, 375-387. 302
[17] Chagnon P. L., Bradley R. L., On the use of sodium hexametaphosphate to extract spores of 303
arbuscular mycorrhizal fungi from soil, Soil Biol. Biochem. 43, 2273-2274. 304
[18] Lu Y.P., et al., 2011. Effect of sodium hexametaphosphate on separation of serpentine from pyrite. 305
Trans. Nonferrous Met. Soc. China 21, 208-213. 306
[19] Andreola F., et al., 2004. The role of sodium hexametaphosphate in the dissolution process of 307
kaolinite and kaolin. J. Eur. Ceram. Soc. 24, 2113-2124. 308
[20] Huang J., et al., 2007. Adsorption studies of a water soluble dye, reactive redMF-3B, using 309
sonication-surfactant-modified attapulgite clay, J. Hazard. Mater. 143, 541-548. 310
[21] Yuan P., et al., 2013. Surface silylation of mesoporous/macroporous diatomite (diatomaceous 311
earth) and its function in Cu (II) adsorption: The effects of heating pretreatment, Micropor. Mesopor. 312
Mat. 170, 9-19. 313
[22] Kenisarin M. M., Kenisarina K. M., 2012. Form-stable phase change materials for thermal energy 314
storage, Renew. Sust. Energ. Rev. 16, 1999-2040. 315
[23] Wang W., et al., 2009. Preparation and performance of form-stable polyethylene glycol/silicon 316
dioxide composites as solid–liquid phase change materials. Applied Energy 86, 170-174. 317
[24] Cheng H.F., et al.. 2010. Infrared and infrared emission spectroscopic study of typical Chinese 318
kaolinite and halloysite. Spectrochim Acta A Mol Biomol Spectrosc. 77, 1014-1120. 319
[25] Brunauer S., et al., 1940. On a Theory of the van der Waals Adsorption of Gases. J. Am. Chem. 320
Soc. 62, 1723-1732. 321
[26] Sing K., The use of nitrogen adsorption for the characterisation of porous materials. 2001. Colloid. 322
Surfaces A 187–188, 3-9. 323
[27] Ibrahim S.S., Selim A.Q., 2010. Producing a micro-porous diatomite by a simple 324
13
classification-calcination process. J. Ore Dressing 12, 24-32. 325
[28] Al-Wakeel M. I., 2009. Characterization and process development of the Nile diatomaceous 326
sediment, Int. J. Miner. Process. 92, 128–136. 327
328
14
LIST OF FIGURES 329
Fig. 1. SEM pictures of pure diatomite sample, (a)×600 and (b)×1500. 330
Fig. 2. Proposed flowsheet for the purification of low grade diatomites. 331
Fig. 3. Relationship between the SiO2 content and pH value in purification of three diatomites. 332
Fig. 4. Relationship between the SiO2 content and the dosage of SHMP in purification of three 333
diatomites. 334
Fig. 5. XRD patterns of three raw diatomites and different products obtained after purification, 335
(a) LJ-DE, (b) HD-DE, (c) SX-DE. 336
Fig. 6. SEM pictures of raw diatomite sample (LJ-a1 ×500 and LJ-a2×1000) and purified 337
diatomite sample (LJ-b1 ×800 and LJ-b2×1500) from Linjiang. 338
Fig. 7. SEM pictures of raw diatomite sample (HD-a1 ×500 and HD-a2×1000) and purified 339
diatomite sample (HD-b1 ×1000 and HD-b2×1500) from Huade. 340
Fig. 8. SEM pictures of raw diatomite sample (SX-a1 ×500 and SX-a2×1000) and purified 341
diatomite sample (SX-b1 ×1000 and SX-b2×1500) from Shengxian. 342
Fig. 9. Infrared emission spectra of three raw diatomite samples (LJ-R, HD-R and SX-R), 343
centrifugal sediment samples (LJ-S, HD-S and SX-S) and centrifugal overflow samples (LJ-S, 344
HD-S and SX-S). 345
Fig. 10. Nitrogen adsorption-desorption isotherms of three raw diatomites and different products 346
obtained after purification, (a) LJ-DE, (b) HD-DE, (c) SX-DE. 347
Fig. 11. Relationship between zeta potential and pH value at different concentrations of SHMP, 348
(a) diatomite, (b) kaolin, (c) montmorillite 349
350
15
351
Fig. 1. SEM pictures of pure diatomite sample, (a)×600 and (b)×1500. 352
353
16
354
Fig. 2. Proposed flowsheet for the purification of low grade diatomites. 355
356
17
357
Fig. 3. Relationship between the SiO2 content and pH value in purification of three 358
diatomites. 359
360
Fig. 4. Relationship between the SiO2 content and the dosage of SHMP in purification of 361
three diatomites. 362
18
363
364
Fig. 5. XRD patterns of three raw diatomites and different products obtained after 365
purification, (a) LJ-DE, (b) HD-DE, (c) SX-DE. 366
19
367
Fig. 6. SEM pictures of raw diatomite sample (LJ-a1 ×500 and LJ-a2×1000) and purified 368
diatomite sample (LJ-b1 ×800 and LJ-b2×1500) from Linjiang. 369
370
20
371
Fig. 7. SEM pictures of raw diatomite sample (HD-a1 ×500 and HD-a2×1000) and purified 372
diatomite sample (HD-b1 ×1000 and HD-b2×1500) from Huade. 373
374
21
375
Fig. 8. SEM pictures of raw diatomite sample (SX-a1 ×500 and SX-a2×1000) and purified 376
diatomite sample (SX-b1 ×1000 and SX-b2×1500) from Shengxian. 377
22
378
Fig. 9. Infrared emission spectra of three raw diatomite samples (LJ-R, HD-R and SX-R), 379
centrifugal sediment samples (LJ-S, HD-S and SX-S) and centrifugal overflow samples (LJ-S, 380
HD-S and SX-S). 381
382
23
383
384
385
Fig. 10. Nitrogen adsorption-desorption isotherms of three raw diatomites and different 386
products obtained after purification, (a) LJ-DE, (b) HD-DE, (c) SX-DE. 387
24
388
389
25
390 Fig. 11. Relationship between zeta potential and pH value at different concentrations of 391
SHMP, (a) diatomite, (b) kaolin, (c) montmorillite. 392
26
LIST OF TABLES 393
Table 1. Main advantages and disadvantages of different diatomite purification methods [8-11]. 394
Table 2. Chemical compositions of three raw diatomite samples (wt. %). 395
Table 3. BET specific surface area (SBET), pore volume (Vp) and pore diameter for raw 396
diatomites and products after purification. 397
27
Table 1. Main advantages and disadvantages of different diatomite purification methods [8-11] 398
Techniques Main advantages Main disadvantage
Acid leaching treatment Good removal of impurities
High cost; Release of a large
amount of acid wastewater
causing environmental problems
Scrubbing method Simplicity of application Not effective for purification of all
raw diatomite
Classification Simplicity of application Low efficiency; Difficult for large
scale industrial application
Calcination Simplicity of application; good
removal of organic matters
High energy consumption;
Incapable of removal of some
impurities, such as clay minerals
Gravitational sedimentation Simplicity of application
Low efficiency; Large water
consumption; Rigorous weather
conditions
Ultrasound treatment
Effective purification at lab scale;
Good removal of impurities
embedded in the porous structure of
diatom
Difficult for large scale industrial
application
Magnetic separation Good removal of magnetic impurities Incapable of removal of
nonmagnetic substance
Flotation Good removal of impurities
High cost; Release of a large
amount of wastewater causing
environmental problems because
of the addition of the flotation
reagents
Grinding
Good removal of impurities
embedded in the porous structure of
diatom
Undesirable damage of original
porous structure of diatom
399
400
28
Table 2. Chemical compositions of three raw diatomite samples (wt. %). 401
Samples SiO2 Al2O3 Fe2O3 TiO2 CaO MgO K2O Na2O P2O5 L.O.I.a
LJ-DE 81.78 5.49 2.01 0.20 1.05 0.52 1.07 0.29 0.075 6.89
HD-DE 76.60 10.13 3.36 0.26 0.89 0.91 1.07 0.45 0.024 7.00
SX-DE 66.88 17.49 2.90 0.21 0.38 0.17 1.07 0.32 0.035 8.78
Pure DE 96.47 0.031 0.12 0.013 0.10 0.05 0.02 0.032 0.021 2.79
Pure kaolin 54.55 34.41 0.50 0.69 0.34 0.05 0.012 0.12 0.099 11.94
Pure montormolite 66.86 15.07 3.06 0.13 1.68 3.09 0.59 2.18 0.003 7.33
a Loss on ignition 402
29
Table 3. BET specific surface area (SBET), pore volume (Vp) and pore diameter for raw 403
diatomites and products after purification. 404
Sample ID SBET (m2 g-1) Vpa (cm3 g-1) BETb (nm)
Raw diatomite (LJ-DE) 22.182 0.061679 12.5903
Centrifugal overflow(LJ-DE) 49.6763 0.086132 10.1253
Centrifugal sediment(LJ-DE) 11.7082 0.039341 21.0529
Raw diatomite (HD-DE) 38.0799 0.055558 6.7341
Centrifugal overflow(HD-DE) 42.4162 0.087123 9.2536
Centrifugal sediment(HD-DE) 8.0296 0.030652 17.1252
Raw diatomite (SX-DE) 28.1562 0.062092 8.0125
Centrifugal overflow(SX-DE) 41.2365 0.082122 9.1253
Centrifugal sediment(SX-DE) 18.5692 0.048569 13.5624
a BJH desorption cumulative pore volume of pores between 1.7 and 300 nm in diameter. 405
b Adsorption average pore diameter (4V/A by BET) 406