- 2 -

Contents

BOPP Film Grade [5014L CB, CB-4-1, HCS-1]

BOPP Film Grade [HF5003, HF5103]

Matt Film Grade [5014L MAT, MAT-1, MAT-2, MAT-3]

Master Batch Grade

- Antistatic & Slip- Antiblocking

---- 03

---- 18

---- 27

---- 29

- 3 -

CHARACTERISTICS AND USES

[ 5014L CB ]- Characteristics : Good Processibility & High Clarity- Uses : Metallizing & High Transparent Tape

[ 5014L CB-4-1 ]- Characteristics : Superior Processibility, High Clarity- Uses : Paper Lamination, Matt & Pearl Film Core

[ 5014L HCS-1 ]- Characteristics : Superior Processibility, High Clarity- Uses : Paper Lamination

YUHWA POLYPRO (BOPP) YUHWA POLYPRO (BOPP) [BOPP Film Grade : 5014L]

Note) It can be used with Antiblocking, Antistatic and Slip Agent MP for special film properties.

- 4 -

5014L CB5014L CB

• Korea Petrochemical Ind. Co., Ltd.• R&D Center

YUHWA POLYPRO (BOPP) YUHWA POLYPRO (BOPP) [BOPP Film Grade : 5014L]

- 5 -

PHYSICAL PROPERTIES

3.5

97

1,600

>500

36

0.90

3.0

5014L CB

R scaleASTM D 785Hardness(Rockwell)

kgfㆍcm/cmASTM D 256Izod Impact Strength

MPaASTM D 790Flexural Modulus

%ASTM D 638Elongation at Break

MPaASTM D 638Tensile at Yield

g/cm3ASTM D 792Density

g/10mmASTM D1238MI

UNITTEST METHODITEM

5014L CB [Metallizing & High Transparent Tape]

• Properties are measured on injection moulded specimens, conditioned at 22℃ and 55% relative humidity

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

- 6 -

2,000/4,500MPaASTM D 882YOUNG'S MODULUS MD/TD

0.35/0.34-ASTM D1894COEFF. OF FRICTION 靜 / 動

3.0/0.5% ASTM D1204SHRINKAGE MD/TD

150/40%ASTM D 882ELONGATION MD/TD

150/300MPaASTM D 882TENSILE STRENGTH MD/TD

0.0~0.1%ASTM D1003HAZE

5014L CBUNITTEST METHODITEM

• Bruckner Line : 25㎛ BOPP film.• Above data are typical laboratory averages.

They are intended to serve as guides only, and are not sales specification limits.

5014L CB [Metallizing & High Transparent Tape]

OPP FILM PROPERTIES

- 7 -

PROCESSING CONDITIONSCylinder temperature : 200 - 280 ℃Die temperature : 220 - 270 ℃Stretching temperature : 150 - 200 ℃

ADDITIVESAntioxidant, Neutralizer

5014L CB [Metallizing & High Transparent Tape]

- 8 -

5014L CB [Metallizing & High Transparent Tape]

KOREA (S.Y.C) 28㎛High Transparent OPP Film for Tape

5014L CB (99%) + 5014L AB505 (1%)Skin Layer-2

5014L CB (100%)Core Layer

5014L CB (99%) + 5014L AB505 (1%)Skin Layer-1

5014L CBBruckner Line

0.65/0.600.58/0.57

outside

0.3%ASTM D1003HAZE

Inside-ASTM D1894COEFF. OF FRICTION 靜 / 動

2.0/1.0% ASTM D1204SHRINKAGE MD/TD

149/42%ASTM D 882ELONGATION MD/TD

150/300MPaASTM D 882TENSILE STRENGTH MD/TD

28μm-THICKNESSBruckner Line (5014L CB)UNITTEST METHODITEM

[Formulation]

[Resin Selection]

[Film Test Results]

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

- 9 -

5014L CB [Metallizing & High Transparent Tape]

NANYA 28㎛ High Transparent OPP Film for Tape

5014L CB (98%) + 5014L AB202 (2%)Skin Layer-2

5014L CB (100%)Core Layer

5014L CB (98%) + 5014L AB202 (2%)Skin Layer-1

5014L CBBruckner Line

0.58/0.570.88/0.86

outside

0~0.1%ASTM D1003HAZE

Inside-ASTM D1894COEFF. OF FRICTION 靜 / 動

2.5/2.0% ASTM D1204SHRINKAGE MD/TD

150/43%ASTM D 882ELONGATION MD/TD

150/280MPaASTM D 882TENSILE STRENGTH MD/TD

28μm-THICKNESSBruckner Line (5014L CB)UNITTEST METHODITEM

[Formulation]

[Resin Selection]

[Film Test Results]

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

- 10 -

5014L CB5014L CB--44--11

• Korea Petrochemical Ind. Co., Ltd.• R&D Center

YUHWA POLYPRO (BOPP) YUHWA POLYPRO (BOPP) [BOPP Film Grade : 5014L]

- 11 -

3.5

97

1,600

>500

36

0.90

3.0

5014L CB-4

R scaleASTM D 785Hardness(Rockwell)

kgfㆍcm/cmASTM D 256Izod Impact Strength

MPaASTM D 790Flexural Modulus

%ASTM D 638Elongation at Break

MPaASTM D 638Tensile at Yield

g/cm3ASTM D 792Density

g/10mmASTM D1238MI

UNITTEST METHODITEM

PHYSICAL PROPERTIES

5014L CB-4-1 [Paper Lamination, Matt & Pearl Film Core]

• Properties are measured on injection moulded specimens, conditioned at 22℃ and 55% relative humidity

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

- 12 -

2,000/4,500MPaASTM D 882YOUNG'S MODULUS MD/TD

0.35/0.34-ASTM D1894COEFF. OF FRICTION 靜 / 動

3.0/0.5% ASTM D1204SHRINKAGE MD/TD

150/40%ASTM D 882ELONGATION MD/TD

150/300MPaASTM D 882TENSILE STRENGTH MD/TD

0.7%ASTM D1003HAZE

5014L CB-4UNITTEST METHODITEM

• Bruckner Line – Paper Lami : 12~15㎛ BOPP film (Line Speed : >350m/min)• Above data are typical laboratory averages.

They are intended to serve as guides only, and are not sales specification limits.

5014L CB-4-1 [Paper Lamination, Matt & Pearl Film Core]

OPP FILM PROPERTIES

- 13 -

5014L CB-4-1 [Paper Lamination, Matt & Pearl Film Core]

PROCESSING CONDITIONSCylinder temperature : 200 - 280 ℃Die temperature : 220 - 270 ℃Stretching temperature : 150 - 200 ℃

ADDITIVESAntioxidant, Neutralizer, Antistatic Agent (5,000ppm)

- 14 -

5014L HCS5014L HCS--11

• Korea Petrochemical Ind. Co., Ltd.• R&D Center

YUHWA POLYPRO (BOPP)YUHWA POLYPRO (BOPP) [BOPP Film Grade : 5014L]

- 15 -

4.0

96

1,600

>500

36

0.90

2.0

5014L HCS-1

R scaleASTM D 785Hardness(Rockwell)

kgfㆍcm/cmASTM D 256Izod Impact Strength

MPaASTM D 790Flexural Modulus

%ASTM D 638Elongation at Break

MPaASTM D 638Tensile at Yield

g/cm3ASTM D 792Density

g/10mmASTM D1238MI

UNITTEST METHODITEM

5014L HCS-1 [Paper Lamination]

PHYSICAL PROPERTIES

• Properties are measured on injection moulded specimens, conditioned at 22℃ and 55% relative humidity

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

- 16 -

2,400/5,000MPaASTM D 882YOUNG'S MODULUS MD/TD

0.30/0.25-ASTM D1894COEFF. OF FRICTION 靜 / 動

3.0/2.0% ASTM D1204SHRINKAGE MD/TD

150/40%ASTM D 882ELONGATION MD/TD

170/320MPaASTM D 882TENSILE STRENGTH MD/TD

1.0%ASTM D1003HAZE

5014L CB-4UNITTEST METHODITEM

• Mitsubishi Line : 12~15㎛ BOPP film (Line Speed : >350m/min)• Above data are typical laboratory averages.

They are intended to serve as guides only, and are not sales specification limits.

OPP FILM PROPERTIES

5014L HCS-1 [Paper Lamination]

- 17 -

PROCESSING CONDITIONSCylinder temperature : 200 - 280 ℃Die temperature : 220 - 270 ℃Stretching temperature : 150 - 200 ℃

ADDITIVESAntioxidant, Neutralizer, Antistatic Agent (5,500ppm)

5014L HCS-1 [Paper Lamination]

- 18 -

CHARACTERISTICS- Good Processibility- High Clarity- High Stiffness- Low Thermal Shrinkage- Less Drop of Wetting Tension after Metallization (HF5003)

USES[ HF5003 ]

- BOPP film for Metallizing[ HF5103 ]

- BOPP film for Printing, Album & Garment

YUHWA POLYPROYUHWA POLYPRO ((BOPPBOPP -- High Stiffness & Low Thermal Shrinkage) High Stiffness & Low Thermal Shrinkage) [BOPP Film Grade : HF5003, HF5103]

Note) It can be used with Antiblocking, Antistatic and Slip Agent MP for special film properties.

- 19 -

HF5003HF5003

• Korea Petrochemical Ind. Co., Ltd.• R&D Center

YUHWA POLYPRO (BOPPYUHWA POLYPRO (BOPP -- High Stiffness & Low Thermal Shrinkage) High Stiffness & Low Thermal Shrinkage) [BOPP Film Grade : HF5003, HF5103]

- 20 -

97

1,600

500<

36

0.90

3.0

General OPP Grade

3.0g/10 min ASTM D1238 MI

0.91g/cm3ASTM D 792 Density

39MPaASTM D 638Tensile at Yield

500<%ASTM D 638Elongation at Break

1,900MPaASTM D 790Flexural Modulus

101 R scaleASTM D 785Hardness(Rockwell)

HF5003UNITTEST METHODITEM

HF5003 [Metallizing]

PHYSICAL PROPERTIES

• Properties are measured on injection moulded specimens, conditioned at 22℃ and 55% relative humidity

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

- 21 -

3.0/1.5

0.30/0.30

2,000/4,500

150/40

150/300

0.7

General OPP Grade

3,000/5,600MPaASTM D 882YOUNG'S MODULUS MD/TD

0.36/0.35-ASTM D1894COEFF. OF FRICTION 靜 / 動

1.5/0% ASTM D1204SHRINKAGE MD/TD

150/40%ASTM D 882ELONGATION MD/TD

150/340MPaASTM D 882TENSILE STRENGTH MD/TD

0.7%ASTM D1003HAZE

HF5003UNITTEST METHODITEM

OPP FILM PROPERTIES

HF5003 [Metallizing]

• Bruckner and Mitsubishi Line ; 20㎛ BOPP film, Draw Ratio 5:1 • Above data are typical laboratory averages.

They are intended to serve as guides only, and are not sales specification limits

- 22 -

PROCESSING CONDITIONSCylinder temperature : 210 - 290 ℃Die temperature : 230 - 280 ℃Stretching temperature : 160 - 210 ℃

ADDITIVESAntioxidant, Neutralizer

HF5003 [Metallizing]

- 23 -

HF5103HF5103

• Korea Petrochemical Ind. Co., Ltd.• R&D Center

YUHWA POLYPRO (BOPPYUHWA POLYPRO (BOPP -- High Stiffness & Low Thermal Shrinkage) High Stiffness & Low Thermal Shrinkage) [BOPP Film Grade : HF5003, HF5103]

- 24 -

97

1,600

500<

36

0.90

3.0

General OPP Grade

3.0g/10 min ASTM D1238 MI

0.91g/cm3ASTM D 792 Density

38MPaASTM D 638Tensile at Yield

500<%ASTM D 638Elongation at Break

1,850MPaASTM D 790Flexural Modulus

100 R scaleASTM D 785Hardness(Rockwell)

HF5103UNITTEST METHODITEM

PHYSICAL PROPERTIES

• Properties are measured on injection moulded specimens, conditioned at 22℃ and 55% relative humidity

• Above data are typical laboratory averages.They are intended to serve as guides only, and are not sales specification limits.

HF5103 [Printing & Album & Garment]

- 25 -

3.0/1.5

0.30/0.30

2,000/4,500

150/40

150/300

0.7

General OPP Grade

2,800/5,300MPaASTM D 882YOUNG'S MODULUS MD/TD

0.32/0.30-ASTM D1894COEFF. OF FRICTION 靜 / 動

1.5/0% ASTM D1204SHRINKAGE MD/TD

150/40%ASTM D 882ELONGATION MD/TD

150/340MPaASTM D 882TENSILE STRENGTH MD/TD

0.7%ASTM D1003HAZE

HF5003UNITTEST METHODITEM

OPP FILM PROPERTIES

HF5103 [Printing & Album & Garment]

• Bruckner and Mitsubishi Line ; 20㎛ BOPP film, Draw Ratio 5:1 • Above data are typical laboratory averages.

They are intended to serve as guides only, and are not sales specification limits

- 26 -

PROCESSING CONDITIONSCylinder temperature : 210 - 290 ℃Die temperature : 230 - 280 ℃Stretching temperature : 160 - 210 ℃

ADDITIVESAntioxidant, Neutralizer, Antistatic Agent (5,000ppm)

HF5103 [Printing & Album & Garment]

- 27 -

5014L MAT- Homo Polymer Base- Printing & Paper Lamination

5014L MAT-1- Copolymer Base- Printing & Paper Lamination

5014L MAT-2- Copolymer Base- Paper Lamination

5014L MAT-3- Copolymer Base- Paper Lamination

YUHWA POLYPRO (Matt Film Grade) YUHWA POLYPRO (Matt Film Grade) [Matt Film Grade : 5014L MAT, MAT-1, MAT-2, MAT-3]

Note) It can be used with Antiblocking, Antistatic and Slip Agent MP for special film properties.

- 28 -

Low haze,CO-Ext' skinHigh speed

OPP film(PaperLami)

40 ~ 50150.30±0.150.15>20>5.0~8.0

5014L MAT-3(Copolymer Base)

High haze,CO-Ext' skinHigh speed

OPP film(PaperLami)

78∼856.50.30±0.150.15>20>5.0±1.0

5014L MAT-2(Copolymer Base)

High haze,CO-Ext' skin,High speed

OPP film(Printing & PaperLami)

78∼855.50.30±0.150.15>20>6.0±2.0

5014L MAT-1(Copolymer Base)

High haze,CO-Ext' skin

OPP film(Printing & PaperLami)

78∼855.00.30±0.150.15>20>4.8~6.0

5014L MAT(Homopolymer

Base)

RemarksApplicationsHaze(%)

Gloss

value

30 pellets(g)

V.M(%)

YIMI

(g/10min)

PropertyGrade

5014L MAT, MAT-1, MAT-2, MAT-3

- 29 -

YUHWA POLYPRO (MASTER BATCH GRADE) YUHWA POLYPRO (MASTER BATCH GRADE) [Anti static & Slip Master Batch Grade]

5014L AS210

- Antistatic Agent 10% (Amine)

5014L AS310

- Antistatic Agent 10% (GMS + Amine)

5014L ASL015

- Antistatic Agent 8% (Amine) + Slip Agent 7% (Erucamide)

5014L SL205

- Slip Agent 5% (Erucamide)

1077 SL110

- Slip Agent 10% (Oleylamide)

- 30 -

5014L AS210, AS310, ASL015, SL205, SL110

Slip AgentOleylamideCPP Film0.5±0.20.2>30>1015.0±5.01077 SL110

Slip AgentEucamideOPP, CPP Film0.5±0.20.15

>30>54.0±2.05014L SL205

Antistatic & Slip Agent

Amine + Erucamide

OPP, CPP, IPP Film0.5±0.20.2>30>158.0±3.05014L ASL015

Antistatic Agent

GMS + Amine

OPP, CPP, IPP Film0.5±0.20.2>30>105.5±2.55014L AS310

Antistatic AgentAmineOPP, CPP,

IPP Film0.5±0.20.2>30>105.5±2.55014L AS210

RemarksAgent TypeApplication

30 pellets

(g)

V.M(%) YI

Content

(%)

MI(g/10min)

Property Grade

- 31 -

YUHWA POLYPROYUHWA POLYPRO (MASTER BATCH GRADE) (MASTER BATCH GRADE) [Anti Blocking Master Batch Grade]

5014L AB202- Antiblocking Agent 2% (SiO2)

5014L AB205- Antiblocking Agent 5% (SiO2)

5014L AB305- Antiblocking Agent 5% (Organic)

5014L AB505- Antiblocking Agent 5% (SiO2)

5014L AB605- Antiblocking Agent 5% (SiO2)

5014L AB805- Antiblocking Agent 5% (SiO2)

5014L AB1005C- Antiblocking Agent 5% (Organic)

5014L AB605C- Antiblocking Agent 5% (SiO2)

- 32 -

5014L AB202, AB205, AB305, AB505, AB605, AB805, AB1005C, AB605C

MetallizingAntiblocking Agent

SiO2OPP, CPP

film3.50.5±0.20.25>25>57.0±3.05014L AB605C

MetallizingAntiblocking Agent

SiO2OPP, CPP,

IPP film20.5±0.20.25>25>53.5±1.55014L AB805

Antiblocking AgentSiO2OPP, CPP,

IPP film4.00.5±0.20.25>25>57.5±4.55014L AB505

High TransparencyAntiblocking Agent

SiO2OPP, CPP,

IPP film1.6~1.80.5±0.20.2>25>52.0±0.55014L AB205

Super SlipAntiblocking Agent

OrganicOPP, CPP film20.5±0.20.2>25>57.5±4.55014L AB1005C

Antiblocking AgentSiO2OPP, CPP,

IPP film3.50.5±0.20.25>25>57.5±4.55014L AB605

High SlipAntiblocking Agent

OrganicOPP, CPP, IPP film2.5~3.00.5±0.20.2>25>516.0±2.05014L AB305

High TransparencyAntiblocking Agent

SiO2OPP, CPP,

IPP film1.6~1.80.5±0.20.2>25>22.0±1.05014L AB202

RemarksAgent TypeApplication

Particle Size (μm)

30 pellets

(g)

V.M(%) YI Content

(%)MI

(g/10min)Property

Grade