i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6
Avai lab le at www.sc iencedi rect .com
journa l homepage : www.e lsev ie r . com/ loca te /he
Hydrogen permeability of PdeAg membrane modules withporous stainless steel substrates
Donglai Xie a,*, Jinfeng Yu a, Fang Wang a, Ning Zhang a, Weixing Wang a, Hao Yu a,Feng Peng a, Ah-Hyung A. Park b
aMOE Key Laboratory of Enhanced Heat Transfer & Energy Conservation, South China University of Technology, Guangzhou 510640, ChinabDepartment of Earth and Environmental Engineering, Columbia University, 9500 W. 120th Street, NY 10027, USA
a r t i c l e i n f o
Article history:
Received 5 May 2010
Received in revised form
10 October 2010
Accepted 11 October 2010
Available online 10 November 2010
Keywords:
Hydrogen
Palladium membrane
Porous stainless steel
* Corresponding author. Tel./fax: þ86 20 2223E-mail address: [email protected] (D. Xie
0360-3199/$ e see front matter ª 2010 Profedoi:10.1016/j.ijhydene.2010.10.030
a b s t r a c t
Palladium-based membranes are attractive for their nearly perfect permselectivity to
hydrogen. Membrane modules, consisting of a membrane foil, porous stainless steel
substrate, test frame and flange were assembled and tested in an electrically heated vessel.
Instantaneous hydrogen permeation flux was measured. Influences of operation condi-
tions on the membrane performance were examined. Microstructure and morphology of
the membrane surface and the cross-sectional surface of the substrate and membrane foil
were characterized by scanning electron microscopy. It was observed that for an operation
temperature higher than 755 K, the hydrogen permeation flux through the membrane
module with 0.2 mm grade porous 316L stainless steel substrate decayed continuously due
to the inter-metallic diffusion between the membrane and the substrate. For a temperature
of around 869 Ke943 K, a stable hydrogen permeation flux through the membrane module
with 0.5 mm grade stainless steel substrate was observed. Pretreatment of the 0.5 mm grade
substrate with polishing and etching helped to smooth the membrane foil surface.
However, it changed the surface structure of the material and led to a decrease in hydrogen
permeability. Under the conditions investigated, the permeation factor of the module
increased by raising the hydrogen pressure in the vessel side and decreasing the
membrane module temperature. By decreasing the hydrogen exit partial pressure by
sweep gas, the membrane module permeation flux increased, while the permeation factor
decreased.
ª 2010 Professor T. Nejat Veziroglu. Published by Elsevier Ltd. All rights reserved.
1. Introduction dwindling fossil fuel supply and an approach to a future lasting
The increased demand for pure hydrogen gas in recent years in
many sectors, ranging from petroleum processing, materials
treatment to renewable energy related applications, has led to
a revival of interest in economical hydrogen production tech-
nologies. Hydrogen energy is looked upon as a savior in
combating the deterioration of the global environment, as
a means of securing energy that is independent of the
6985.).ssor T. Nejat Veziroglu. P
supply of an energy resource [1e3]. Most of the world’s
hydrogen is generated by steam reforming or partial oxidation
of natural gas in parallel fixed bed reactors within huge top-
fired or side-fired furnaces, coupled with Pressure Swing
Adsorption (PSA) for hydrogen purification [4]. Hydrogen
separation accounts for a large fraction of energy expenditure
and capital investment in the hydrogen production process.
The most widely used technology for hydrogen purification is
ublished by Elsevier Ltd. All rights reserved.
Fig. 1 e Structure of the PdeAg membrane module
assembly.
i n t e r n a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6 1015
PSA. Palladium and its alloy membranes have attracted
growing interests for their capability to separate ultra-pure
hydrogen from gaseous mixtures [5e7]. They can also be inte-
grated with chemical reactors where chemical reaction and
hydrogen separation occur simultaneously to simplify the
hydrogen production process. Various membrane reactors
havebeenproposedand tested for hydrogenproduction [8e13].
The driving force for hydrogen transportation through
a membrane is the hydrogen partial pressure difference
between the two surfaces of the palladium membrane [14].
Thin palladium membrane itself cannot stand the pressure
difference imposed on it. Hence, membrane modules should
be constructed with thin palladium or palladium alloy
membranes supported on porous substrates, such as ceramics,
porous glass and porous stainless steel [6,15]. Of all of these
substrates, porous stainless steel has shown advantages for its
close thermal expansion coefficient to palladium [16,17].
The fabrication and performance of palladiummembranes
have been investigated by many researchers. Hydrogen
permeates through palladium or palladium alloy membranes
via the “solution e diffusion” mechanism. It can be described
by the Sieverts’ Law [18,19] as:
Ms ¼ KS1
t1e�
EpRT�PnH � Pn
L
�(1)
where MS is the hydrogen permeation rate, K is the pre-
exponential factor, S1 is the effective area of membrane
surface for hydrogen permeation, t1 is the thickness of palla-
diumor palladium alloymembrane, Ep is the activation energy
for permeation, R is the gas constant, T is the temperature, PHis the hydrogen partial pressure in vessel side, PL is the
average hydrogen partial pressures in the membrane
permeate side, and n is the parameter whose value depends
on the limiting transport mechanism of hydrogen permeation
through palladium or its alloy membrane. The hydrogen flux
follows the Sieverts’ Law when the hydrogen pressure expo-
nent n is equal to 0.5, which is usually valid for thick Pd films
[15]. Deviations from the Sieverts’ Law (n > 0.5) were reported
for very thin membranes [20,21]. Based on a hydrogen
permeation model, Ward and Dao [22] showed that for
temperatures above 673 K, n was equal to 0.5 for membranes
thicker than 1 mm. Usually to use Sieverts’ Law correctly with
an exponent of 0.5, the thickness of membrane should be
higher than 10 mm [15].
When stainless steel substrates are applied to form
membrane modules, it can affect the membrane permeability
by adding a flow resistance to the hydrogen transportation
process. It can also decrease the membrane foil permeability
by inter-diffusion between the stainless steel substrate and
the membrane metal under high temperature [23]. Other
factors, such as the existence of gas species other than
hydrogen, can also affect the membrane permeability [24].
Some researchers used an efficiency factor h to denote the
difference between the actual permeability (Ma) and those
predicted from Sieverts’ Law (Ms) [8,25e28]:
Ma ¼ hMs (2)
h is reported in literatures to be from 0.39 to nearly 1.0
[8,25e27].
The permeability of membrane modules is critical to the
design and sizing of membrane reactors and separators.
Experiments were carried out to study the permeability
performance of membrane modules with porous stainless
steel substrates. The work can help to understand the influ-
ence of stainless steel substrate on the permeability of the
membrane module and find measures to improve the
membrane module performances.
2. The test membrane module andexperimental setup
2.1. The test membrane module
As shown in Fig. 1, the membrane module consists of the
following parts: frame, substrate, membrane foil, graphite
gasket and flange. These parts were tightened together with
bolts and nuts through the holes on the edge of the flange and
frame. Channels were machined inside the frame for
permeate side hydrogen flow. The geometries of the frame
and flange are shown in Fig. 2. Three types of membrane
module sets, denoted as type I, II and III, were fabricated, with
their dimensions listed in Table 1.
PdeAg membrane foils of 75% (wt) palladium and 25% (wt)
silver with thicknesses of 10 mm, 25 mm and 50 mmwere tested
in the experiments. The membrane foils were supplied by
Good-Fellow (10 mm) and Alfa-Aesar (25 mm and 50 mm). The
following performance data of suchmembrane foils was used:
activation energy 9.18 kJ/mol, pressure order 0.5, pre-expo-
nential factor 2.07 � 10�3(mol m)/(m2 min bar0.5) [29]. Two
types of porous stainless steel material were employed as
a substrate: one with a thickness of 1.2 mm and media grade
of 0.5 mm, while the other with a thickness of 1.0 mm and
media grade of 0.2 mm. The media grade is defined by the
supplier of the material (Mott Corporation) as over 95% of
particles or the other fluid with the size of the grade (in mm)
cannot pass through the substrate during filtering.
Fig. 2 e Geometry of the test frame (top) and flange
(bottom).
i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 61016
2.2. Experimental setup
After the membrane module was assembled, it was installed
inside an electrically heated pressure vessel. The vessel was
designed and fabricated for pressure up to 2.0 MPa and
temperature of 973 K. As illustrated in Fig. 3, hydrogen and
Table 1 e Dimensions in Fig. 2 (unit: mm).
Module type A B C D E F G H I J
I 3 5 5 28 32 1.2 8 24 28 6
II 3 5 5 28 32 1.2 8 22 20 6
III 3 5 5 24 26 1.0 8 20 22 6
argon were directed to the vessel from gas cylinders through
Mass Flow Controllers (MFC). The vessel pressure was
controlled by a back pressure regulator in the off gas stream. A
cylindrical electrical heater of 10 kWwas installed around the
vessel for controlling the vessel temperature. The vessel and
electrical heater were sufficiently insulated. Sweep gas
nitrogen was delivered to the permeate side of the membrane
module. Pure hydrogen, or a mixture of the sweep gas and
hydrogen from the permeate side of the membrane was
metered by a bubble gas meter.
Seven sets of experiments have been carried out. The
configurations and test conditions of these tests are listed in
Table 2.
2.3. Experimental procedure
2.3.1. Porous stainless steel substrate pretreatmentsFor tests 1 to 6, the porous stainless steel substrates were
treated with ultra-sonic cleaning only. It was suspected that
the rough surface of the substrate could lead tomembrane foil
failure. Hence for the test 7, the substrate surface was pre-
treated by a process similar to that described by Li et al. [23]:
1. Polishing: the surface of the substrate was polished using
sandpaper with increasing grits step by step. The substrate
was finally polished with 1200 grit sandpaper.
2. Etching: the substrate was etched at an ambient tempera-
ture with a mixed solution of nitric acid and hydrochloric
acid (volumetric ratio 1HNO3: 3HCl) for several minutes.
After etching, the substrate was immediately washed with
clean water in an ultra-sonic bath to remove acid solution
remaining in the pores. Fig. 4 shows the substrate surface
as received, after polishing by sandpapers and after etching
with acid solution under a Hitachi S-3700N Scanning Elec-
tronic Microscopy (SEM).
2.3.2. Substrate pressure drop measurementsFor all tests, the flow resistance of these substrates under
ambient temperature was measured before they were
assembled to the module. Bottled air was employed to
measure the pressure drop across the substrate at certain air
flow fluxes. For test 7, the pressure drops across the substrate
after it was polished and etched were also measured. The
pressure drop can also be calculated by the equation provided
by the supplier of these materials:
DP ¼ KG � fS2
� y� t2 (3)
where KG is a constant given by the supplier of the porous
substrate, f is the gas flow rate, S2 is the area of substrate, y is
the gas viscosity, and t2 is the thickness of substrate.
Fig. 5 shows the pressure drops across the 0.5 mm grade
substrates for tests 1, 2, 6 and 7 and the 0.2 mm grade
substrates for tests 3 to 5, respectively. It can be seen that for
the 0.5 mm grade substrate, polishing with sandpaper added
a strong flow resistance to the material. As can be seen from
Fig. 4, the substrate pores near the surface were blocked by
sandpaper polishing, which contributed to the flow resistance
increase. The etching process helped to open these pores and
Fig. 3 e Schematic diagram of the experimental setup.
i n t e r n a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6 1017
lower the flow resistance. The pressure drops across the un-
treated substrates were very close to that calculated from
Equation (3).
The supplier of the porous sintered metal suggested that
the maximum application temperature for the 316L stainless
steel porous material under reducing atmosphere is 755 K.
Usually, palladium alloy membrane modules are operated
under a temperature range of 773e973 K [8,11,28]. Too high
a temperature will damage the membrane, while too low
a temperature will cause a low chemical reaction conversion
in the membrane reactor and membrane permeability. This
temperature range is beyond the recommended operating
temperature of the substrate. The high temperature may
destroy the porosity of the substrate, hence block the gas
transportation passage and lead to low membrane perme-
ability. To study this possibility, a 0.5 mm grade test substrate
module and a 0.2 mm grade test substrate module were
assembled. The 0.5 mm grade test substrate module was
identical to the Type II membrane module, without assem-
bling the membrane foil. The 0.2 mm grade test substrate
modulewas identical to the Type IIImembranemodule, again,
without assembling the membrane foil. Both modules were
installed in the pressure vessel as shown in Fig. 3, and heated
at temperature of 923 K under hydrogen environment for 8 h
(the heating period from ambient temperature to 923 K was
not included in the 8 h). The pressure drop across these
modules under certain hydrogen flux was measured before,
Table 2 e Test configurations and conditions.
Test t2mm
Substrate grademm
t1mm
Module typeP
1 1.2 0.5 25 I
2 1.2 0.5 25 I
3 1.0 0.2 10 III
4 1.0 0.2 25 III
5 1.0 0.2 25 III
6 1.2 0.5 50 II
7 1.2 0.5 25 I
after, and during the heating process as shown in Fig. 6. It can
be seen that during the heating process, the flow resistances
across the 0.2 mmgrade substrate increased slightly with time,
while the increase of pressure drop with time across the
0.5 mmgrade substrate was not noticeable. The pressure drops
across the substrates after the heating process were slightly
higher than those before the heating process for both
substrates. From the stability point of view, 0.5 mm grade
sintered metal was more suitable to be used as membrane
substrate than the 0.2 mmgrade one. Considering the pressure
potential required for hydrogen to permeate through the
membrane layer in a membrane module was much higher
than the pressure drop for hydrogen to flow across the
substrate, this slow increase in pressure drop across the
0.2 mmsubstrate itself should not cause any quick decay in the
module permeability.
2.3.3. Membrane module permeability test procedureAfter the membrane module was assembled, it was installed
in the pressure vessel. The permeability of the membrane
module was studied by the following procedure:
1. Displacement of the air in the pressure vessel. Pure argon
gas was directed to the vessel until its pressure reached
0.2 MPa, and then released through the back pressure
regulator. This procedure was repeated 8 times. The vessel
pressure was then kept at 0.2 MPa with argon inside.
Substrateretreatment
TemperatureK
PressureMPa
Vesselenvironment
No 869e917 0.2 H2
No 923 0.2 H2
No 923 0.2 H2
No 913 0.4 H2 þ Ar
No 723 0.3 H2
No 943 0.3 H2
Yes 920 0.2 H2
Fig. 4 e Surface of the 0.5 mm grade substrate under SEM as
received (top), after polishing with sandpaper (middle) and
after etching with acid solution (bottom).
0 50 100 150 200 250 300 350 400 4500.00
0.02
0.04
0.06
0.08
0.10
0.12
0.14
0.16
0.18
)aPM(
porderusser
P
Air flow flux (Nm3 h-1m-2)
Equation (3) Test 7 after polishing Test 7 without pretreatment Test 7 after etching Test 1 Test 2 Test 6
50 100 150 200 250 300 350 400 4500.00
0.02
0.04
0.06
0.08
0.10
0.12
0.14
0.16
)aPM(
porderusserP
Air flow flux (Nm3 h-1m-2)
Equation (3) Test 3 Test 4 Test 5
Fig. 5 e Pressure drops across the 0.5 mm grade substrates
under ambient temperature for tests 1, 2, 6 and 7 (top) and
0.2 mm grade substrates for tests 3e5 (bottom).
i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 61018
2. Displacement of the air in the permeate side of the
membrane module. When the vessel was pressurized,
nitrogen was directed to the permeate side of the
membrane module to purge the air out. A small flow of
nitrogen (about 1 ml/min) was maintained during the test,
until hydrogen was confirmed to have been permeated
from the vessel to the permeate side of the membrane.
3. Heating in argon environment: the vesselwas heated by the
electrical heater to 523 K. The vessel pressure was main-
tained at 0.2 MPa during the heating process.
4. Displacement of argon with hydrogen: when the vessel
temperature reached 523 K, the argon gas inside the pres-
sure vessel was released. For test 4, pure hydrogen was
forced into the vessel until the vessel pressure reached
0.4 MPa for four times. Then both hydrogen and argon with
molar flow rates controlled at 1:1 were charged to the vessel
and the vessel pressure was maintained at 0.4 MPa by the
back pressure regulator. For other tests, pure hydrogen gas
was directed to the vessel until its pressure reached
0.2 MPa, and then released through the back pressure
regulator. This procedure was again repeated 8 times. For
tests 5 and 6, the final vessel pressure was controlled to be
0.3 MPa, while for tests 1, 2, 3 and 7, the final pressure was
0.2 MPa. As soon as the displacement of argon was
completed, the hydrogen permeation flow rate through the
membrane module was measured by the bubble gas meter
at a time interval of approximately 30 min. For each
measurement, three readings were performed and an
average value was taken.
5. Heating in hydrogen (and for test 4 hydrogen/argon) envi-
ronment until the desired temperature (590 Ke913 K) was
reached. The membrane permeability data was continu-
ously recorded during this period.
200 400 600 800 1000 12000.00
0.02
0.04
0.06
0.08
0.10
0.5 m before heating0.5 m after heating Pr
essu
re d
rop
(MPa
)
Hydrogen flow flux (Nm3 h-1m-2)
0.2 m before heating 0.2 m after heating
200 400 600 800 1000 12000.00
0.05
0.10
0.15
0.20
0.25
0.30
0.5 m, 0 h after being heated @ 923K0.5 m, 4 h after being heated @ 923K0.5 m, 8 h after being heated @ 923KPr
essu
re d
rop
(MPa
)
Hydrogen flow flux (Nm3 h-1m-2)
0.2 m, 0 h after being heated @ 923K 0.2 m, 4 h after being heated @ 923K 0.2 m, 8 h after being heated @ 923K
Fig. 6 e Pressure drops across the 0.2 and 0.5 mm grade
substrates before, after (top) and during (bottom) being
heated under hydrogen environment at temperature of
923 K for 8 h.
Fig. 7 e Variation of membrane module permeation flux
(top) and factor (bottom) with time for tests 1e7.
i n t e r n a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6 1019
6. Permeability tests under stable vessel temperatures: the
vessel inner temperature was maintained at �2 K around
the desired temperature by the temperature controller for
several days. For test 1, the vessel temperature was main-
tained at 869 K for the first 47 h, and then 917 K for the next
47e75 h. The membrane permeability data was continu-
ously recorded.
7. For the tests 1, 2, 5 and 6, the hydrogen permeability of the
membrane module became almost stable after hours test
under stable vessel temperatures. Hence the vessel pres-
sure was changed by adjusting the back pressure regulator,
inner temperature was varied by adjusting the set point of
the electrical heater controller, and the module perme-
ability under various conditions was measured.
8. After all tests were performed, the vessel was again
charged with pure argon,maintained at pressure of 0.2 MPa
and temperature around 873 K. No flowwas observed in the
permeate side of the membrane module. Hence the
membrane integration was confirmed.
3. Experimental results and discussion
3.1. Instant hydrogen permeation flux and permeationfactor
As the effective membrane surface area varies slightly
between Type I and Type II, III membrane modules, molar
hydrogen permeation flux (Q) is used to denote module
hydrogen permeation performance, and it is defined as
Q ¼ Ma
S1(4)
Fig. 7 shows the variation of the measured permeation flux
and permeation factor with time from these membrane
modules. Since the membrane module permeability was
measured as soon as hydrogen was charged into the vessel at
the point that the vessel temperature reached 523 K, the
module permeation fluxes increased at the heating period for
all tests. At the period when the vessel temperature was
maintained stable, the membrane module permeability in
different tests behaved differently. It can be observed that:
i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 61020
1. For test 1 (0.5 mm grade substrate and 25 mm thick
membrane foil), when the vessel temperature was around
869 K and pressurewas 0.2MPa, themembranemodule had
an initial quick decay in permeation flux from 0.25 to
0.23 mol/(m2 s). The corresponding membrane permeation
factor decreased from 0.89 to 0.78, and then maintained at
around 0.86. When the vessel temperature was adjusted to
917 K, the membrane module permeation flux changed to
0.27 mol/(m2 s), and the membrane permeation factor
changed to around 0.88. The initial decrease in the
membrane permeability could be caused by the inter-
metallic diffusion between the PdeAg membrane and the
sintered stainless steel substrate. Although the inter-
metallic diffusion could be a very slow process, it could be
speeded up in the hydrogen environment. Evidence of the
diffusion bonding is that the membrane foil was totally
bonded with the metal substrate, and it could not be
detached from the support after the experiments. Some
researchers actually used the diffusion bonding to fabricate
membranemodules [5,30]. After the test, the substrate with
the attached membrane foil was cut into halves and the
cross-sectional surface was characterized by SEM (Hitachi
S-3700N) as shown in Fig. 8(a). The distribution of Pd, Ag
and Fe elements along the line (from point A to B) in the
SEM image was characterized using a line scan (Hitachi S-
3700N), as shown in Fig. 8(b). It can be seen that there was
approximately a 0.06 mm thick layer that contains Pd, Ag
and Fe elements. This indicates that some diffusion
occurred between the surface of the PdeAg membrane foil
and the sintered metal, which may have caused the initial
decay in membrane permeability.
2. For test 2, the same substrate and membrane foil as test 1
were applied. The vessel temperature was maintained at
around 923 K and pressure 0.2 MPa. Under such conditions,
the membrane permeation flux was around 0.26 mol/(m2 s)
0
20
40
60
80
100
0
tisnetnIy
020406080
100
0
tisnetnIy
a
c
A BA
C D A
Fig. 8 e (a) SEM micrograph showing the cross-sectional micros
(b) line scan of the cross-sectional elemental distributions of Pd, A
(c) SEM micrograph showing the cross-sectional microstructure
scan of the cross-sectional elemental distributions of Pd, Ag and
to 0.28 mol/(m2 s) and the permeation factor was around
0.83 to 0.87. These were very close to the results from test 1
under the conditions of temperature of 917 K and pressure
of 0.2 MPa. It suggests that the experiments had very good
repeatability.
3. For test 3, 1.0 mm thick 0.2 mm grade substrate and 10 mm
thick membrane foil were employed in the membrane
module. The vessel temperature was maintained at 923 K
and pressure 0.2 MPa. The membrane permeation flux was
observed decreasing from 0.50 to 0.20 mol/(m2 s) during the
stable temperature period, and the corresponding perme-
ation factor decreased from 0.70 to 0.25. The differences of
the membrane module configurations between test 3 and
tests 1 and 2 were the substrate grade and membrane foil
thickness. Hence the continuous decay of hydrogen
permeation performance with time in test 3 should be
caused by the thinner PdeAg membrane foil thickness, the
substrate grade, and/or the inter-action between the
membrane and the substrate under current operation
conditions.
4. For test 4, 1.0 mm thick 0.2 mm grade substrate and 25 mm
thick membrane foil were employed in the membrane
module. The vessel temperature was again maintained at
913 K. Here both hydrogen and argon with their molar flow
rate controlled to be 1:1 were directed to the vessel. The
hydrogen flow rate was controlled at 10 LPM, which was
muchhigher than thehydrogenpermeation rate through the
membranemodule (maximum0.1LPM).Hence thehydrogen
concentrationwasmaintained almost uniform in the vessel.
The vessel pressure was maintained at 0.4 MPa by the back
pressure regulator. Hence the hydrogen partial pressure
inside the vessel was 0.2 MPa. The membrane permeation
flux was observed decreasing from 0.13 to 0.05 mol/(m2 s)
during the period of experiment, and the corresponding
permeation factor decreased from 0.65 to 0.16.
0.2 0.4 0.6 0.8 1 1.2 1.4 1.6 1.8 2
Distance from C to D (µm)
0.2 0.4 0.6 0.8 1 1.2 1.4 1.6 1.8 2Distance from A to B (µm)
b
d
Pd
g Fe
Pd
gFe
tructure of the 0.5 mm substrate and membrane after test 1;
g and Fe of the 0.5 mmsubstrate andmembrane after test 1;
of the 0.2 mm substrate and membrane after test 4; (d) line
Fe of the 0.2 mm substrate and membrane after test 4.
i n t e r n a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6 1021
The configuration differences between test 4 and tests 1e2
were the substrate material grade and vessel environment.
The vessel was filled with hydrogen and argon in test 4, while
it was filled with pure hydrogen in tests 1e2. The original
purpose of introducing argon to the vessel was to see if it can
help smoothing the membrane surface. Gallucci et al. [31]
have studied the effect of mixture gas on hydrogen perme-
ation through a palladium membrane and found that N2/H2,
Ar/H2 and CO2/H2 feed mixtures had no remarkable surface
effects on hydrogen permeation through membrane.
Unemoto et al. [32] also concluded in their studies that the
interference effect of the co-existing gas is negligible at
temperatures higher than 873 K for the membranes thicker
than 10 mm. Hence the influence of argon on the membrane
permeability can be neglected, as long as the hydrogen partial
pressure is used for predicting the permeability with Sieverts’
Law. As for the substrate, test 4 used 0.2 mm grade substrate
while tests 1 and 2 used 0.5 mm grade one. It was then sus-
pected that the substrate had caused the continuous decrease
in permeation flux.
After the test, the substrate with the attached membrane
foil was again cut into halves and the cross-sectional surface
was characterized by SEM as shown in Fig. 8(c). The distribu-
tion of Pd, Ag and Fe elements along the line (frompoint C toD)
in the SEM imagewasmeasured using a line scan, as shown in
Fig. 8(d). It can be seen that there was approximately a 0.16 mm
thick layer that contains Pd, Ag and Fe elements. Comparing to
Fig. 8(b) it can be concluded that themetal element diffusion in
this case was much stronger that that in test 1. Due to the
strong metallic diffusion, the performance of the membrane
foil changed. This should be the reason for the continuous
decay of membrane permeability in tests 3 and 4. Both the
0.2 mm and 0.5 mm substrate plates were supplied by the same
supplier (Mott Corporation). Somehow the 0.2 mm substrate
was more active on molecule diffusion than the 0.5 mm
substrate, possibly due to its low porosity and high effective
contact area with the membrane.
5. For test 5, 1.0 mm thick 0.2 mm grade substrate and 25 mm
thick membrane foil were employed in the membrane
module. The vessel temperature was maintained at 723 K
which was below 755 K. The membrane permeation flux
was observed at 0.30 mol/(m2 s) during the stable temper-
ature period under vessel pressure of 0.3 MPa, and the
corresponding permeation factor was around 0.99e1.01. No
initial decrease of the permeation flux was observed. After
the test, it was observed that the membrane foil was not
attached to the substrate, and the foil could be detached
Table 3 e Membrane module permeation flux and factor.
Test Substrate grademm
Membrane thicknessmm
TemperaK
1 0.5 25 869
1 0.5 25 917
2 0.5 25 923
5 0.2 25 723
6 0.5 50 943
from the substrate easily. Comparing to the permeation
flux of tests 4 and 5, it can be confirmed that the permeation
flux decay in tests 3 and 4 were caused by the temperature
impact on the inter-metallic diffusion between the
membrane foil and the 0.2 mm substrate. The metallic
diffusion was a strong factor of temperature. Under the
temperature of 723 K, the inter-diffusion of Pd/Ag and the
substrate metal was not initiated. The permeation factor
was around 1, which means under such operation condi-
tions, the influence of substrate on membrane module
permeability was negligible and the Sieverts’ Law held.
6. For test 6, 1.2 mm thick 0.5 mm grade substrate and 50 mm
thick membrane foil were employed in the membrane
module. The vessel temperature was maintained at 943 K
and pressure of 0.3 MPa. When the vessel temperature was
stable, the membrane module permeation flux was main-
tained at w0.20 mol/(m2 s). The corresponding permeation
factor was w0.92. The initial decrease in permeation flux
was not noticeable. It could be because that the membrane
foil was so thick that themetallic diffusion near the surface
to the substrate had a limited influence on its total
permeability.
7. For test 7, the 0.5 mmsubstrate was pre-treated as described
previously. It can be observed from Fig. 7 that the perme-
ation flux kept decreasing, similar to what happened with
tests 3 and 4. The pore structure near the surface of the
0.5 mm grade substrate was destroyed by the pretreatment,
as shown in Fig. 4. Hence the actual grade of the substrate
surface was much less than 0.5 mm after the pretreatment
and it behaved like the0.2mmgradesubstrateunder thehigh
temperature operation conditions.
For tests 1, 2, 5 and 6, the permeation flux reached
a constant during the tests under experimental conditions.
The permeation fluxes and factors of these tests are listed in
Table 3 for the reader’s convenience.
3.2. Influences of operation conditions on membranepermeation factor
For tests 1, 2 and 6, the membrane module permeation flux
became stable after more than 40 h of experiments at
temperature ranging from 869 K to 943 K. These threemodules
were used to investigate the influences of the operation
conditions (vessel side temperature, pressure and permeate
side hydrogen partial pressure) on membrane permeation
factor. The vessel pressure was changed by adjusting the back
pressure regulator, inner temperature was varied by adjusting
ture PressureMPa
Permeation fluxmol/(m2 s)
Permeation factor
0.2 w0.22 w0.82
0.2 w0.27 w0.87
0.2 w0.27 w0.85
0.3 w0.30 w1.02
0.3 w0.30 w0.92
Hydrogen + Sweep gas
Permeate flow channel
H2 partial pressure in permeate flow channel
H2 partial pressure in permeate side surface of membrane foil
H2 pressure in vessel
i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 61022
the set point of the electrical heater controller. A wide range of
temperature points were tried and those permeation factors
measured at temperatures within maximum 6 K differences
were grouped together, as shown in Fig. 9. It can be seen that
the permeation factor increasedwith increasing the hydrogen
0.20 0.25 0.30 0.35 0.40 0.45 0.50 0.55 0.600.92
0.94
0.96
0.98
1.00
1.02
1.04
1.06
1.08
1.10
1.12
1.14
1.16
1.18
1.20
659-665K 758-764K 911-917K
PH
0.5-PL
0.5 (MPa0.5)
)-(rotcaf
noitaemreP
0.1 0.2 0.3 0.4 0.5 0.60.84
0.86
0.88
0.90
0.92
0.94
0.96
0.98
1.00
1.02
1.04
1.06
721-727K 820-825K 921-924K
)-(rotcaf
noitaemreP
PH
0.5-PL
0.5 (MPa0.5)
0.20 0.25 0.30 0.35 0.40 0.45 0.50 0.550.92
0.94
0.96
0.98
1.00
1.02
1.04
1.06
1.08
1.10
1.12
1.14
672-676K 718-724K 912-918K
)-(rotcaf
noitaemreP
PH
0.5-PL
0.5 (MPa0.5)
Fig. 9 e Influence of vessel temperature and hydrogen
pressure on permeation factor for test 1 (top), test 2
(middle) and test 6 (bottom) (permeate side pressure:
0.1 MPa).
0 PEPL1 PL2 PH
Hydrogen partial pressure
Sweep gas
Porous substrate
Membrane
Fig. 10 e Profile of hydrogen partial pressure in the
membrane module.
pressure in the vessel side and decreasing the vessel inner
temperature, i.e., the membrane temperature. Permeation
factors higher than 1 were observed for some conditions. The
highest permeation factor observed was approximately 1.18.
One possible contribution for this phenomenon could be the
error on estimating the membrane foil thickness. The
suppliers of the membrane foils (Alfa-Aesar for 25 and 50 mm
foils, and Good-Fellow for 10 mm foils) claimed an error of
�15% on these membrane foil thicknesses. For an extreme
case, if the membrane foil was 15% thinner than the claimed
thickness, the calculated hydrogen permeation flux from
Sieverts’ Law would be 15% higher than actual one. Another
possible reason could be the contact between the membrane
foil and the metal substrate. The vessel was under pressure
(0.2e0.4 MPa) during the tests. Some substance of the
0.16 0.18 0.20 0.22 0.24 0.26 0.28 0.30 0.32
0.65
0.70
0.75
0.80
0.85
0.90
0.95
1.00
0.00
0.05
0.10
0.15
0.20
0.25
0.30
0.35
)-(rotcaf
noitaemreP
PL
0.5 ( MPa0.5)
672-678K 720-724K 820-825K
mlom(
xulfnoitae
mreP2-
s1-)
Fig. 11 e Influence of permeate side hydrogen pressure at
the module exit and vessel temperature on permeation
flux and factor for test 2 (Vessel pressure: 0.2 MPa solid
symbols: permeation flux; open symbols: permeation
factor).
Fig. 12 e SEM images of the PdeAg membrane foils after the test (Test conditions were listed in Table 2).
i n t e r n a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6 1023
membrane material was squeezed into the pores of the
substrate, leading to a thinner effective foil thickness than the
original foil thickness.
To study the influence of permeate side hydrogen partial
pressure on the permeation factor, the permeate side of the
membrane module was swept by nitrogen. The sweep gas
entered the membranemodule from the bottom and left from
the top. The hydrogen partial pressure at the module exit (PE)
can be calculated from:
PE ¼ qt � qN
qtPP (5)
where qt is the total permeate flow rate of gas at the exit of
membranemodule, qN is the sweep gas flow rate, and PP is the
permeate side total pressure.
The actual hydrogen partial pressure in the permeate side
of the membranemodule is then between 0 at the entrance of
the sweep gas and PE at the exit. When calculating the
hydrogen permeation rate from Equation (1), PE was used to
represent the hydrogen partial pressure at the low pressure
side. The permeation factor can be calculated from Equation
(2). As a substrate layer was placed between the membrane
foil and the permeate flow channel, the sweep gas could not
fully flush the permeated hydrogen out from the membrane
surface, and the hydrogen partial pressure at the permeate
side of the membrane surface should be higher than that in
the permeate flow channel. A possible hydrogen partial
pressure profile in the membrane module is illustrated in
Fig. 10. Using PE to represent the hydrogen partial pressure at
the permeate side of the membrane could introduce
Table 4 eMajor features of the SEM images of membranefoil after test.
Test Major feature of membrane surface
1 Grain-like bump on surface
2 Smooth, tiny and discrete cracks observable
3 Bumps on and cracks in surface
4 Frost-like bumps on surface
6 Continuous cracks
7 Smooth, cracks hardly observable
i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 61024
a calculation error on estimating the permeation flux.
However, it could reveal the correct trend of the influence of
the permeate side hydrogen partial pressure on the perme-
ation factor. Fig. 11 shows the influence of the permeate side
hydrogen pressure at the module exit and vessel temperature
on the permeation flux and factor for test 2. It can be seen that
with decreasing the hydrogen exit partial pressure, hydrogen
permeation flux was increased, while the permeation factor
was decreased. Similar results were obtained from test 6.
Hence, it was concluded that if PE is used as the permeate side
hydrogen partial pressure, it can actually over-estimate the
membrane module permeation flux under the conditions
studied in these experiments.
3.3. Membrane foil surface smoothness
After each test, themembranemodulewas taken out from the
pressure vessel. SEM was used to characterize microstructure
and morphology of the membrane surfaces. Various types of
membrane surface morphologies were observed as shown in
Fig. 12. Major features of these SEM photos are summarized in
Table 4. It can be seen that for test 7, a very smooth surface
was achieved via the pretreatment of the porous substrate.
However, the pretreatment caused a decrease in membrane
permeability. The surface cracks in the 10 mm thickness
membrane used in test 3 were very serious. These differences
betweenmembrane surface features, however, are difficult to
explain. For example, the membrane modules in test 1 and
test 2 were made on the same type of membrane supports
under similar operating temperatures and vessel environ-
ment, but the surfaces shown in Fig. 12 were extremely
different. It is difficult to draw any conclusions on the effects
of the operation temperature, atmosphere, and the substrate
grade on the morphological structures of membranes. More
studies are desired to understand the mechanisms that
caused such morphologies.
4. Conclusions and recommendations
Membrane modules, consisting of PdeAg membrane foil with
thickness of 10 mm, 25 mm and 50 mm, porous stainless steel
substrate of 0.5 mm and 0.2 mm grade, test frame and flange
were assembled and tested in an electrically heated vessel. It
can be concluded from the experimental observations that:
1. For operation temperatures higher than 755 K, hydrogen
permeation flux through the membrane module with
0.2 mm grade porous 316L stainless steel substrate contin-
uously decayed due to the inter-metallic diffusion between
the membrane and the substrate. Hence the 0.2 mm grade
porous 316L stainless steel material is not suitable as
a membrane module substrate.
2. Under the conditions studied (temperatures around
869 Ke943 K), stable hydrogen permeation flux through the
membrane module with 0.5 mm grade stainless steel
substrate was observed. Although the supplier of the mate-
rial does not recommend the application of such material
above 755 K in reducing environment, the flow resistances
across the 0.5 mm grade substrate did not significantly
increase during the 8 h test period that was performed in
hydrogen environment at temperature of 923 K.
3. Pretreatment of the 0.5 mm grade substrate helped to
smooth the membrane foil surface. However, it changed
the surface structure of thematerial and led to a decrease in
the permeability of the membrane module.
4. For temperatures below 755 K, the influence of porous
stainless steel substrate on the membrane module perme-
ability was negligible and the Sieverts’ Law held.
5. Under the operation conditions investigated, the perme-
ation factor of the module increased by increasing the
hydrogen pressure in the vessel side and decreasing the
membrane temperature. By decreasing the hydrogen exit
partial pressure using sweep gas, the membrane module
permeation flux increased, while the permeation factor
decreased.
6. Various membrane surface morphologies were observed
via SEM. Small crackswere observed inmost of SEM images,
which could lead to failure of these membrane modules in
future. Efforts need to be made to smooth the substrate
surface while avoiding the reduction in membrane module
permeability.
Acknowledgment
Financial support fromtheNationalHighTechnologyResearch
and Development Program of China (2009AA05Z102) and the
Fundamental Research Funds for the Central Universities
(project # 2009ZZ0013) are gratefully acknowledged.
Nomenclature
A-G dimensions in Fig. 2, mm
Ep activation energy for permeation, J mol�1
f gas flow rate, m3 s�1
H-J dimensions in Fig. 3, mm
K pre-exponential factor, mol m�1 s�1 MPa�n
KG constant given by the supplier of the porous
substrate, m�2
Ma actual hydrogen permeation rate, mol s�1
MS hydrogen permeation rate calculated from Sieverts’
Law, mol s�1
n parameter whose value depends on the limiting
transport mechanism of hydrogen permeation
through palladium or its alloy membrane
i n t e r n a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 6 1025
PE permeate side hydrogen partial pressure at the exit
of membrane module, MPa
PH hydrogen partial pressure in vessel side, MPa
PL average hydrogen partial pressures in themembrane
permeate side, MPa
PL1 hydrogen partial pressure at the bottom of the
surface between membrane foil and substrate, MPa
PL2 hydrogen partial pressure at the top of the surface
between membrane foil and substrate, MPa
PP permeate side total pressure, MPa
Q hydrogen permeation flux, mol m�2 s�1
qN sweep gas flow rate, mol s�1
qt total permeate flow of gas at the exit of membrane
module, mol s�1
R gas constant, J mol�l K�1
S1 effective area of membrane surface for hydrogen
permeation, m2
S2 area of substrate, m2
T temperature, K
t1 thickness of palladium or palladium alloy
membrane, m
t2 thickness of substrate, m
Greek letter
y gas viscosity, MPa s
h permeation factor
DP pressure drop of substrate, MPa
r e f e r e n c e s
[1] Tong HD, Gielens FC, Gardeniers JGE, Jansen HV, Rijn CJM,Elwenspoek MC, et al. Microfabricated palladiumesilveralloy membranes and their application in hydrogenseparation. Ind Eng Chem Res 2004;43:4182e7.
[2] Steele BHC, Heinzel A. Materials for fuel-cell technology.Nature 2001;414:345e52.
[3] Ramachandram R, Menon RK. An overview of industrial usesof hydrogen. Int J Hydrogen Energy 1998;23:593e8.
[4] Xie D, LimCJ, Grace JR, Adris AEM. Gas and particle circulationin an internally circulating fluidized bed membrane reactorcold model. Chem Eng Sci 2009;64:2599e606.
[5] Ryi SK, Park JS, Kim SH, Kim DW, Kim HK. Low temperaturediffusion bonding of Pd-based composite membranes withmetallic module for hydrogen separation. J Membr Sci 2009;326:589e94.
[6] Pizzi D, Worth R, Baschetti MG, Sarti G, Noda KI. Hydrogenpermeability of 2.5 mm palladiumesilver membranesdeposited on ceramic supports. J Membr Sci 2008;325:446e53.
[7] Ma YH, Mardilovich I, Engwall E. Thin composite palladiumand palladium/alloy membranes for hydrogen separation.Ann N Y Acad Sci 2003;984:346e60.
[8] Xie D, Adris AM, Lim CJ, Grace JR. Test on a modular fluidizedbed membrane reactor for autothermal steam methanereforming. Acta Energiae Solaris Sinica 2009;30:704e7.
[9] Chen Z, Grace JR, Lim CJ, Li A. Experimental studies of purehydrogen production in a commercialized fluidized bedmembrane reactor with SMR and ATR catalysts. Int JHydrogen Energy 2007;32:2359e66.
[10] Xie D, Grace JR, Lim CJ. Development of an internallycirculating fluidized bed membrane reactor for hydrogenproduction from natural gas. J Wuhan Univ Technol 2006;28:252e7.
[11] Mahecha-Botero A, Boyd T, Gulamhusein A, Comyn N,Lim CJ, Grace JR, et al. Pure hydrogen generation ina fluidized-bed membrane reactor: experimental findings.Chem Eng Sci 2008;63:2752e62.
[12] Shirasaki Y, Tsuneki T, Ota Y, Yasuda I, Tachibana S,Nakajima H, et al. Development of membrane reformersystem for highly efficient hydrogen production from naturalgas. Int J Hydrogen Energy 2009;34:4482e7.
[13] Patil CS, Annaland M, Kuipers JAM. Fluidised bed membranereactor for ultrapure hydrogen production via methanesteam reforming: experimental demonstration and modelvalidation. Chem Eng Sci 2007;62:2989e3007.
[14] Hurlbert RC, Konecny JO. Diffusion of hydrogen throughpalladium. J Chem Phys 1960;34:655e8.
[15] Federico G, Erik EE, Ma YH. Effects of surface activity, defectsand mass transfer on hydrogen permeance and n-value incomposite palladium e porous stainless steel membrane.Catal Today 2006;118:24e31.
[16] Rothernberger KS, Cugini AV, Howard BH, Killmeyer RP,Ciocco MV, Morreale BD, et al. High pressure hydrogenpermeance of porous stainless steel coated with a thinpalladium film via electroless plating. J Membr Sci 2004;244:55e68.
[17] Chen SC, Tu GC, Caryat CY, Hung CA, Rei MH. Preparation ofpalladium membrane by electroplating on AISI 316L porousstainless steel supports and its use for methanol steamreformer. J Membr Sci 2008;314:5e14.
[18] Sieverts A, Zapf G. Solubility of H and D in solid Pd(I). Z PhysChem 1935;A 174:359e64.
[19] Holleck GC. Diffusion and solubility of hydrogen inpalladium and palladium e sliver alloys. J Phys Chem 1970;74:503e11.
[20] Nam SE, Lee SH, Lee KH. Preparation of a palladium alloycomposite membrane supported in a porous stainlesssteel by vacuum electrodeposition. J Membr Sci 1999;153:163e73.
[21] McCool BA, Lin YS. Nanostructured thin palladium-silvermembranes: effects of grain size on gas permeationproperties. J Mater Sci 2001;36:3221e7.
[22] Ward TL, Dao T. Model of hydrogen permeation behavior inpalladium membrane. J Membr Sci. 1999;153:211e31.
[23] Li AW, Grace JR, Lim CJ. Preparation of thin Pd-basedcomposite membrane on planar metallic substrate. Part II.Preparation of membranes by electroless plating andcharacterization. J Membr Sci. 2007;306:159e65.
[24] Unemoto A, Atsushi K, Kazuhisa S, Takanori O, Yashiro K,Mizusaki J, et al. The effect of co-existing gases from theprocess of steam reforming reaction on hydrogenpermeability of palladium alloy membrane at hightemperatures. Int J Hydrogen Energy 2007;32:4023e9.
[25] Ye GY, Xie D, QiaoWY, Grace JR, Lim CJ. Modeling of fluidizedbed membrane reactors for hydrogen production from steammethane reforming with aspen plus. Int J Hydrogen Energy2009;34:4755e62.
[26] Mahecha-Botero A, Grace JR, Lim CJ, Elnashaie SSEH, Boyd T.Pure hydrogen generation in a fluidized bed membranereactor: application of the generalized comprehensivereactor model. Chem Eng Sci 2009;64:3826e46.
[27] Adris AM, Lim CJ, Grace JR. The fluidized-bed membranereactor for steammethane reforming: model verification andparametric study. Chem Eng Sci 1997;52:1609e22.
[28] Xie D, Qiao W, Wang Z, Wang W, Yu H, Peng F. Reaction/separation coupled equilibrium modeling of steam methanereforming in fluidized bed membrane reactors. Int JHydrogen Energy 2010;35:11798e809.
[29] Li A, Lim CJ, Grace JR. Staged-separation membranereactor for steam methane reforming. Chem Eng J 2008;138:452e9.
i n t e rn a t i o n a l j o u r n a l o f h y d r o g e n en e r g y 3 6 ( 2 0 1 1 ) 1 0 1 4e1 0 2 61026
[30] Li A, Diffusion bonding of metallic membrane joining withmetallic module, US patent # 2005/0109821A1, May 26,2005.
[31] Gallucci F, Chiaravalloti F, Tosti S, Drioli E, Basile A. Theeffect of mixture gas on hydrogen permeation througha palladium membrane: experimental study and
theoretical approach. Int J Hydrogen Energy 2007;32:1837e45.