Furukawa Techno Material2E-GISI-08-01_Rev.2-1
Furukawa Ni-Ti Tube has been selected for many medical devices such as Stents. Available in
wide range of sizes with the strict OD & ID dimensions throughout the length assuring the tight
WT uniformity to meet different requirements for various customers.
Furukawa has unique vacuum melting and production lines. The most durable (good fatigue
life) alloys available in the market are manufactured through fine control of the disperse of
inclusions. Our alloy conforms with ASTM F 2063, the Ni-Ti alloy standard for medical devices.
A truly integrated production brings customized formulations available. You can choose a
custom designed super-elasticity.
Comparison of inclusions (after SPEED method (Selective Potentiostatic Etching
by Electrolytic Dissolution))
Furukawa
10mm
0.5 inch
Ni-Ti Tubes for Medical Devices
Email: [email protected]: www.furukawa-ftm.com
5μm
Company A
Furukawa Techno Material2E-GS-2001
10mm
0.5 inch
Ni-Ti Tube for Medical Devices
Email: [email protected]: www.furukawa-ftm.com
Rapid Response Program for Nitinol Tubes
• Nitinol Tubes made to your Spec.• Dispatch within 3 weeks from order
(best case, may vary by order stat. & availability of jig for the tube size)
• Qty varies according to the size and is always subject to production availability.
• Available in Furukawa Binary NT-Nalloy (Ingot Af (DSC) : 0±10℃)
• ASTM F 2063-18 compliance readyPlease contact us for more details.
Web Stock Nitinol Tubes
• Stocked Nitinol Tubes are available in our Web sitehttps://www.furukawa-ftm.com/english/nt-e/stock/index.php
• Dispatch within 1~2 weeks from orderPlease contact us for more details.
Tube OD (mm)
Max. Volume(m)
0.3 ~ 0.8 20
~ 1.0 10
~ 4.0 5
~ 8.0 3
~ 15.0 1
Furukawa Techno Material2E-GISI-12-23-1
2. Dimension
(mm) (inch)
OD WT OD WT
0.3 ~ 0.6 0.040 ~ 0.060 0.015 0.015 0.013 ~ 0.024 0.0016 ~ 0.0024 0.0006 0.0006
0.8 ~ 2.5 0.100 ~ 0.400 0.020 0.020 0.031 ~ 0.098 0.0039 ~ 0.0157 0.0008 0.0008
3.5 ~ 5.0 0.160 ~ 0.400 0.030 0.030 0.138 ~ 0.197 0.0063 ~ 0.0157 0.0012 0.0012
5.0 ~ 10.0 0.200 ~ 0.460 0.050 0.030 0.197 ~ 0.394 0.0079 ~ 0.0181 0.0020 0.0012
10.0 ~ 11.0 0.350 ~ 0.600 0.050 0.030 0.394 ~ 0.433 0.0138 ~ 0.0236 0.0020 0.0012
11.0 ~ 13.0 0.400 ~ 0.700 0.050 0.040 0.433 ~ 0.512 0.0157 ~ 0.0276 0.0020 0.0016
Standard tolerance +/-
Outer diameter Wall thickness
Standard tolerance +/-
Wall thicknessOuter diameter
Available range Available range
4. Surface condition
No oxide
Thin - black oxide
OuterNo oxide
Centerless grinding
Thin oxide
Pickled
InnerPickled
3. Transformation temperature and mechanical property
Mechanical Af* 3% UPS 6% PS UTS Elongation
℃ MPa (ksi) % MPa (ksi) %
NT-N -5 ~ 10 > 400 (58) 0.5 > 1050 (152)
NT-E4 0 ~ 15 > 350 (50) 0.5 > 1000 (145) > 10
NT-E9 10 ~ 25 > 320 (46) ― > 1000 (145)
* Based on BFR (Bending Free Recovery)
** Tensile test at Room Temperature
Alloy type
10mm
0.5 inch
Ingot Af
at% mass% ℃ C max. 0.050
NT-N 50.95Ni-Ti 56.01Ni-Ti -10 ~ 12 Co max. 0.050
NT-E4 50.85Ni-Ti 55.91Ni-Ti 5 ~ 28 Cu max. 0.010
NT-E9 50.70Ni-Ti 55.76Ni-Ti 20 ~ 35 Cr max. 0.010
H* max. 0.005
Fe max. 0.050
Nb max. 0.025
N+O max. 0.050
Comply with ASTM F 2063-05
Comply with ASTM F 2063-05 * H: final tube
Minor elements, mass%
Metallurgical properties
Dimension of inclusions
and porositiesArea
< 39 μm < 2.5 %
1. Alloy type & composition
Alloy typeComposition
Ni-Ti Tube for Medical Devices
Email: [email protected]: www.furukawa-ftm.com
Ni-Ti Line-up & New Ni-Ti-Co for Medical Guidewires
Furukawa Techno Material2EGS-1267-01-1
Furukawa has powerful line-up of Ni-Ti wires for medical Guidewires !!!
【FHP-NT】
Furukawa recently launched a new range of FHP-
NT(Furukawa High Pushability) wires, which are
Furukawa patented products. The well-known FHP-
NT wires have already penetrated the Guidewire
market. Now, FHP3-NT and FHP4-NT are available
to develop superior recovery performance and small
stress hysteresis whilst retaining high upper stress.
【New Super-elastic Ni-Ti-Co】
Now, let’s take a look at a revolutionary Ni-Ti super-
elastic alloy! Our NT-K wire has much higher Upper
Plateau Stress than Ni-rich binary alloy. It is ideal for
super-elastic Guidewires, which request higher
stiffness. The narrow stress hysteresis can also
acheive no whip during the Guidewire rotation.
NT-N
NT-E4
【NT-Super-elastic】
FHP4-NT
FHP3-NT
FHP-NT
NT-K
NT-N
Email: [email protected]: www.furukawa-ftm.com
Ni-Ti Wire for Medical Devices
Furukawa Techno Material2E-GS-1334-1
3. Transformation temperature and mechanical property
Mechanical Af* 3% UPS 6% PS UTS Elongation
℃ MPa (ksi) % MPa (ksi) %
NT-N -5 ~ 10 > 400 (58) 0.5 > 1050 (152)
NT-E4 0 ~ 15 > 350 (50) 0.5 > 1000 (145) > 10
NT-E9 10 ~ 25 > 320 (46) ― > 1000 (145)
* Based on BFR (Bending Free Recovery)
** Tensile test at Room Temperature
Alloy type
Ingot Af
at% mass% ℃ C max. 0.050
NT-N 50.95Ni-Ti 56.01Ni-Ti -10 ~ 12 Co max. 0.050
NT-E4 50.85Ni-Ti 55.91Ni-Ti 5 ~ 28 Cu max. 0.010
NT-E9 50.70Ni-Ti 55.76Ni-Ti 20 ~ 35 Cr max. 0.010
H* max. 0.005
Fe max. 0.050
Nb max. 0.025
N+O max. 0.050
Comply with ASTM F 2063-05
* H: final wire
Minor elements, mass%
1. Alloy type & composition
Alloy typeComposition
2. Dimension
0.04 ~ 0.10
0.10 ~ 1.00
1.00 ~ 1.50
1.50 ~ N/A
Available Range of
Diameter
Standard tolerance
mm
+/-0.005
+/-0.010
+/-0.015
4. Surface condition
Thin Oxide(Light Oxide)
Pickled (without Oxide)
Email: [email protected]: www.furukawa-ftm.com
Furukawa Techno Material2E-GISI-00-21_Rev.2-1
Furukawa has a complete line of Ni-Ti wires to meet every needs of your medical
Guidewires. In addition to the superior super-elasticity and straightness, you have choices
of stiffness and surface finishes to find the best wire for your application.
【FHP-NT】 A Ni-Ti wire with high stiffness like no other, FHP-NT is 3 times stiffer than the
ordinary Ni-Ti wires. It does not have yield point. It is a Furukawa patented product.
Type Composition
Upper Stress
at 4% Strain
MPa (ksi)
Stress Hysteresis
at 2% Strain
MPa (ksi)
Permanent Set
after 4%Strain
(%)
Straightness
(mm)
FHP-NT54 ~ 57 wt% Ni-Ti
1270 (185) 80 (12) 0.05 3
NT-E4 (SEA) 490 (71) 265 (39) 0.00 2
Composition and Mechanical Properties
Furukawa Company A
介在物の比較(SPEED法による介在物の抽出後)
【Super-elastic Ni-Ti】 All Furukawa NT-E4
and NT-N super-elastic wires are made in-house
from ingots. Our integrated manufacturing
process realizes products to meet details of your
requests on strength of super-elasticity to finish
of wire surface. Our wires are highly favored by
major medical device makers world wide.
Ni-Ti Wires for Medical Guidewires
FHP-NT NT-E4 (Super-elastic type)
Email: [email protected]: www.furukawa-ftm.com
Furukawa Extra Low Inclusion wire
F-ELI wire for medical devices
Furukawa Techno Material2E-GS-1504-1
Email: [email protected]
Actual Inclusion Distribution
Alloy type Nominal Composition
(mass%)
Ingot Af
℃ (°F)
Wire Dia. Surface
NT-N-FELI 56.0 Ni-Ti -10~12 (14~53) 0.002”~0.040”
(0.05~1.00 mm)
Thin oxide
or PickledNT-E4-FELI 55.9 Ni-Ti 5~28 (41~82)
Inspection comply with ASTM F2063-12(inspected at hot-worked condition)
F-ELI
Size≦15μm Area%≦0.5% GUARANTEED !
½ of ASTM F2063-12 requirement !!
Superior Fatigue Life !!!
Full Range Traceability (In-House Melting)
Company A
5μm
┗━┛
5μm
┗━┛
Web: www.furukawa-ftm.com
0
5
10
15
20
Fre
qu
en
cy
Area, %
Area percent
ASTM F2063-12
≦2.8%
F-ELI
≦0.5%
0
5
10
15
20
Fre
qu
en
cy
Size, µm
Max. inclusions and voids(Stringer)
ASTM F2063-12
≦39μm
F-ELI
≦15μm
0
5
10
15
20
Fre
qu
en
cy
Size, µm
Max. inclusion(Individual)
ASTM F2063-12
≦39μm
F-ELI
≦15μm
1,000
800
600
400
200
00 1 2 4
Strain (%)
Str
ess (
MP
a)
Str
ess (
ksi)
100
50
0
Pt-cored NiTi Tube NiTi Wire
Furukawa developed a Pt-Cored Ni-Ti
wire for high visibility under the x-ray
observation.
Ni-Ti alloy with a Platinum core made
the wire with high radiopacity clearly
visible under the x-ray without spoiling
its super-elasticity. The wire is
available in 0.05~1.0mm diameter with
a core area ratio of 10~20%.
Furukawa Techno Material2E-GISI-02-34_Rev.3
* X-Ray images
Pt - cored Ni-Ti wire
Web: www.furukawa-ftm.com Email: [email protected]
NT-M3-TTR & NT-H7-TTR wiresFor miniaturizing and cost down your actuators
NT-TTR wire for Compact Actuator
Furukawa Techno Material2E-GS-1504-2
Email: [email protected]
Nitinol (Shape memory) wire can offer;- Easy actuation - just apply electric current
Makes your system small, light, simple, and cost effective
- Actuation power & speed are both controllable via the level of electric current
- Lightweight but high output- Silent and smooth actuation2 types of alloys (M3/NiTi and H7/NiTiCu) available based on our melting technology.*Patent:JPN3956613
Web: www.furukawa-ftm.com
Contraction &
Expansion
NT Wire
Heat-up
NT Wire
Cool down
Electricity OnElectricity Off
Heating Cooling
(sec) (sec)
50 (0.0020) 400 110 0.3 0.7 60 (300)
100 (0.0039) 100 300 0.6 2.5 200 (250)
200 (0.0078) 25 700 1.5 7.0 640 (200)
50 (0.0020) 550 90 0.5 1.0 80 (400)
100 (0.0039) 140 200 1.0 3.0 280 (350)
200 (0.0078) 35 500 2.5 9.0 960 (300)
Max. actual
strain
(%)
Max. pulling
force
(gf (MPa))
~5
Ni-Ti-CuNT-H7-TTR ~5
AlloyProduct#Wire dia.
(μm (inch))
Ni-TiNT-M3-TTR
Resistance
at RT
(Ω/m)
Min. current
to actuate
at RT (mA)
Actuation time at RT