Qty Total/Item Desc

1 1197 24 inch Carbon Fiber 9oz UNI (cost for 300 ft) T700 Fiber

Subtotal: $1197

Shipping = $0.00 (Texas A&M University Discount)

Total = $1197

Fully insured

Cheapest Way UPS (USA only)

Best Regards,

Jon Soller

Soller Composites, LLC

55 Industrial Park Dr

Franklin, NH 03235

www.sollercomposites.com

603 998 1947

Highes t s t reng th , s tandard modu lus f i be r a va i l ab le w i th exce l l en t p rocess ingcharac te r i s t i cs f o r f i l amen t w ind ing and p rep reg . Th i s neve r tw is ted f i be r i s used i nh igh tens i l e a pp l i ca t i ons l i ke p ressu re vesse l s , rec rea t i ona l , and i ndus t r i a l .

F I B E R P R O P E R T I E S

English Metric Test Method

Tensile Strength 711 ksi 4,900 MPa TY-030B-01Tensile Modulus 33.4 Msi 230 GPa TY-030B-01Strain 2.1 % 2.1 % TY-030B-01Density 0.065 lbs/in3 1.80 g/cm3 TY-030B-02Filament Diameter 2.8E-04 in. 7 µm

Yield 6K 3,724 ft/lbs 400 g/1000m TY-030B-0312K 1,862 ft/lbs 800 g/1000m TY-030B-0324K 903 ft/lbs 1,650 g/1000m TY-030B-03

Sizing Type 50C 1.0 % TY-030B-05& Amount 60E 0.3 % TY-030B-05

F0E 0.7 % TY-030B-05

Twist Never twisted

F U N C T I O N A L P R O P E R T I E S

CTE -0.38 α⋅10-6/˚CSpecific Heat 0.18 Cal/g⋅˚CThermal Conductivity 0.0224 Cal/cm⋅s⋅˚CElectric Resistivity 1.6 x 10-3 Ω⋅cmChemical Composition: Carbon 93 %

Na + K <50 ppm

C O M P O S I T E P R O P E R T I E S *

Tensile Strength 370 ksi 2,550 MPa ASTM D-3039Tensile Modulus 20.0 Msi 135 GPa ASTM D-3039Tensile Strain 1.7 % 1.7 % ASTM D-3039

Compressive Strength 215 ksi 1,470 MPa ASTM D-695Flexural Strength 245 ksi 1,670 MPa ASTM D-790Flexural Modulus 17.5 Msi 120 GPa ASTM D-790

ILSS 13 ksi 9 kgf/mm2 ASTM D-234490˚ Tensile Strength 10.0 ksi 69 MPa ASTM D-3039

* To r a y 2 5 0 ˚ F E p o x y R e s i n . N o r m a l i z e d t o 6 0 % f i b e r v o l u m e .

T O R A Y C A R B O N F I B E R S A M E R I C A , I N C .

®

T700S DATA SHEETTECHNICALDATA SHEET

No. CFA-005

T O R A Y C A R B O N F I B E R S A M E R I C A , I N C .6 H u t t o n C e n t r e D r i v e , S u i t e # 1 2 7 0 , S a n t a A n a , C A 9 2 7 0 7 T E L : ( 7 1 4 ) 4 3 1 - 2 3 2 0 FA X : ( 7 1 4 ) 4 2 4 - 0 7 5 0

S a l e s @ To r a y c f a . c o m Te c h n i c a l @ To r a y c f a . c o m w w w. t o r a y u s a . c o m

P A C K A G I N GThe tab le be lo w summar i zes the to w s i zes , tw is t s , s i z i ng t ypes , and packa g ing a va i l ab lefo r s tandard ma te r i a l . O the r bobb in s i zes may be a va i l ab le on a l im i ted bas i s .

Bobbin Spools CaseTow Net Bobbin Bobbin Size (mm) per NetSizes Twist1 Sizing Weight Type2

a b c d e Case Weight(kg) (kg)

6K C 50C 2.0 III 76.5 82.5 280 140 252 12 24

C 50C 6.0 III 76.5 82.5 280 200 252 4 24

12K C 60E 6.0 III 76.5 82.5 280 200 252 4 24

C F0E 6.0 III 76.5 82.5 280 200 252 4 24

C 50C 6.0 III 76.5 82.5 280 200 252 4 24

24K C 60E 6.0 III 76.5 82.5 280 200 252 4 24

C F0E 6.0 III 76.5 82.5 280 200 252 4 24

1 Twist A: Twisted yarn B: Untwisted yarn made from a twisted yarn through an untwisting process C: Never twisted yarn

2 Bobbin Type See Diagram below

T Y P E I T Y P E II T Y P E III

C O M P O S I T E P R O P E R T I E S * *

Tensile Strength 355 ksi 2,450 MPa ASTM D-3039Tensile Modulus 18.0 Msi 125 GPa ASTM D-3039Tensile Strain 1.7 % 1.7 % ASTM D-3039

Compressive Strength 230 ksi 1,570 MPa ASTM D-695Compressive Modulus --- Msi --- GPa ASTM D-695

In-Plane Shear Strength 14 ksi 98 MPa ASTM D-3518ILSS 15.5 ksi 11 kgf/mm2 ASTM D-234490˚ Tensile Strength 10.0 ksi 70 MPa ASTM D-3039

** Toray Semi-Toughened 350˚F Epoxy Resin. Normalized to 60% fiber volume.

See Section 4 for Safety & Handling information. The above properties do not constitute any warranty or guarantee of values.

These values are for material selection purposes only. For applications requiring guaranteed values, contact our sales and technical team

to establish a material specification document.

T700S