Zirconia in Dentistry :Overview
Mohamed Mahmoud Abdul-MonemAssistant lecturer
Dental Biomaterials Department
![Page 2: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/2.jpg)
Contents•Introduction•What is Zirconia ?•History of Zirconia as a biomaterial•Zirconia phase transformation•Zirconia (Ceramic steel)•Properties of Zirconia•Uses of Zirconia •Uses of Zirconia in dentistry•Bonding to Zirconia•References
![Page 3: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/3.jpg)
Introduction
• Ceramics are very important in the science of dental biomaterials.
•Among all dental ceramics, Zirconia is the dental biomaterial of choice in contemporary restorative dentistry.
![Page 4: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/4.jpg)
What is Zirconia ?
• Zirconium oxide (ZrO2), or zirconia, is a metal oxide that was identified as a reaction product of heating the gem( zircon) by the German chemist Martin Heinrich Klaproth in 1789 .
•The name of the metal, zirconium, comes from the Arabic Zargon (golden in colour) which in turn comes from the two Persian words Zar (Gold) and Gun (Colour).
![Page 5: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/5.jpg)
•Zirconia occurs as a natural mineral called baddeleyite.
•Baddeleyite was first found in Sri Lanka in
1892. It was named for Joseph Baddeley.
•This mineral contains 80–90% zirconium oxide(zirconia). The major impurities are usually TiO2, SiO2 and Fe2O3.
![Page 6: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/6.jpg)
Baddeleyite
![Page 7: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/7.jpg)
• It shouldn’t be confused with Zirconium (Zr ) which is found in the form of (zircon) or zirconium silicate(ZrSiO4 ) .
• It is lusturous gray-white transition metal .
![Page 8: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/8.jpg)
History of zirconia as a biomaterial•Zirconia has been used as a biomaterial
since the 1970s.•It has been widely used as a hip
replacement material.• Its use in dentistry began in 2004.
![Page 9: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/9.jpg)
Zirconia hip implants
![Page 10: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/10.jpg)
Zirconia phase transformation• Zirconium oxide exists in three different crystal
structures: monoclinic at room temperature, tetragonal at ~1200°C and cubic at 2370°C.
• Zirconium oxide is transformed from one crystalline state to another during firing.
• At the firing temperature, zirconia is tetragonal and at room temperature, it is monoclinic, with a unit cell of monoclinic occupying about 4.4% more volume than when tetragonal.
![Page 11: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/11.jpg)
Zirconia phase transformation
![Page 12: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/12.jpg)
![Page 13: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/13.jpg)
•The volume expansion caused by the cubic to
tetragonal to monoclinic transformation induces large stresses, and these stresses cause ZrO2 to crack upon cooling from high temperatures.
•When the zirconia is blended with some other oxides, the tetragonal and/or cubic phases are stabilized.
•Effective stabilizers include magnesium oxide (MgO), yttrium oxide (Y2O3, yttria), calcium oxide (CaO), and cerium(III) oxide (Ce2O3).
![Page 14: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/14.jpg)
![Page 15: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/15.jpg)
•Zirconia is often more useful in its phase 'stabilized' state. Upon heating, zirconia undergoes disruptive phase changes.
• By adding small percentages of yttria, these phase changes are eliminated, and the resulting material has superior thermal, mechanical, and electrical properties.
![Page 16: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/16.jpg)
•In some cases, the tetragonal phase can be metastable.
• If sufficient quantities of the metastable tetragonal phase is present, then an applied stress, magnified by the stress concentration at a crack tip, can cause the tetragonal phase to convert to monoclinic, with the associated volume expansion(4.4%).
![Page 17: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/17.jpg)
•This phase transformation can then put the crack into compression, retarding its growth, and enhancing the fracture toughness.
•This mechanism is known as transformation toughening, and significantly extends the reliability and lifetime of products made with stabilized zirconia.
![Page 18: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/18.jpg)
Zirconia transformation toughening
![Page 19: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/19.jpg)
![Page 20: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/20.jpg)
Zirconia = Ceramic steel•It may be noted that zirconia has many
features in common with systems based on iron (stainless steel )as :
1. Three allotropes2. Martesnitic transformation3. Metastable phases
Thus it is known as ceramic steel (Garvie et al , 1975).
![Page 21: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/21.jpg)
Properties of ZirconiaPhysical properties :•Low thermal conductivity (20% that of
alumina)•OpaqueChemical properties:•Chemically inert and corrosion resistantBiological properties:•Biocompatible
![Page 22: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/22.jpg)
Mechanical properties:•Flexural strength 900 Mpa•Compresive strength 2000MPa•Fracture toughness 8-10 MPa · m1/2
•High fracture resistance•Wear of opposing dentition (Monolithic
Zirconia)•Difficulty in adjusting occlusion
![Page 23: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/23.jpg)
Hydrothermal degradation of zirconia•Hydrothermal degradation of zirconia
occurs between 200-400 ˚C .
•Longer exposure times at oral temperature may also degrade zirconia leading to increased surface roughness , fragmanted grains and microcracks .
![Page 24: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/24.jpg)
Uses of Zirconia •Protective coating on particles of TiO2
pigments.•Refractory material .• In Oxygen sensors.•Electroceramics.•Thermal barrier coating (low thermal
conductivity) in jet and diesel engines.•Ceramic knives.•Diamond simulant (cubic zirconia).
![Page 25: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/25.jpg)
![Page 26: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/26.jpg)
Uses of Zirconia in dentistry•Crowns and bridges•Inlays and Onlays•Veneers•Endodontic post and cores•Fillers in dental composite•Implants•Implant abutments•Orthodontic brackets•Pedodontic crowns
![Page 27: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/27.jpg)
Zirconia as fillers in dental composite• Surface-modified
zirconia/silica with a median particle size of approximately 3 microns or less
![Page 28: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/28.jpg)
Zirconia inlays ,onlays and crowns
![Page 29: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/29.jpg)
Zirconia bridges
![Page 30: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/30.jpg)
Multilayered monolithic zirconia
![Page 31: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/31.jpg)
Zirconia CAD/CAM BlocksSoft machining Hard machining
• Mostly, they are fabricated from a porous block, milled oversized by about 25%, and sintered to full density in a 4 - 6 hours cycle.
• Alternatively, fully dense blocks are milled.
• However, this approach requires approximately 2 hours of milling time per unit whereas milling of the porous block necessitates only 30 to 45 minutes for a three-unit bridge.
![Page 32: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/32.jpg)
Zirconia sintering Temperature•Currently available zirconia for soft
machining of dental restorations utilize final sintering temperatures varying between 1350 and 1550 ◦C depending on the manufacturer.
•The microstructure of 3Y-TZP ceramics for dental applications consists of small equiaxed grains (0.2–0.5 µm) in diameter, depending on the sintering temperature
![Page 33: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/33.jpg)
Steps of fabrication of zirconia restorations
![Page 34: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/34.jpg)
Digital impression
![Page 35: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/35.jpg)
Virtual model on software
![Page 36: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/36.jpg)
Milling of zirconia blocks
![Page 37: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/37.jpg)
Zirconia cores
![Page 38: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/38.jpg)
Zirconia toughened alumina ZTA• 70-90% alumina• 10-20% zironia• Toughened by a stress-
induced transformation mechanism of zirconia leading to compressive stresses within alumina.
• The strength of alumina is doubled and toughness is increase 2-4 times .
![Page 39: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/39.jpg)
![Page 40: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/40.jpg)
Zirconia veneers
![Page 41: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/41.jpg)
Zirconia endodontic post and cores
![Page 42: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/42.jpg)
Zirconia implants and abutments
![Page 43: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/43.jpg)
Surface treatment of zirconia implants•Changing the surface chemistry using
bioactive coating with different materials (calcium phosphates, bisphosphonate, collagen, etc.)
•Optimizing surface architecture and microroughness using different techniques.
![Page 44: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/44.jpg)
Scanning electron microscopy (SEM) observation of fibroblasts cultured on zirconia: cells grow on the whole zirconia surface, covering it with a cellular layer.
![Page 45: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/45.jpg)
Zirconia individualized CAD/CAM implants• Austrian Surgeons have
designed a system to produce via CAD/CAM individualized Zirconium Dental Implants for use in case of immediate implant placement.
• In short, after a tooth is extracted it is scanned and a zirconium copy is milled.
• The milled copy has macro-retentive features which help secure the new implant in the extraction socket. They report a 90% success rate.
![Page 46: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/46.jpg)
Zirconia orthodontic brackets
![Page 47: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/47.jpg)
Pedodontic zirconia crowns
![Page 48: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/48.jpg)
Bonding to Zirconia • One problem of zirconia application is its adhesion to
different substrates.
• Surface treatment of zirconia produces an activated surface in different applications.
• Since zirconia is resistant to aggressive chemical treatment.
• Very aggressive mechanical abrasion methods must be used to provide sufficient surface roughness.
![Page 49: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/49.jpg)
Conventional surface treatment techniques are:
(1)acid etching with hot acids • This procedure based on corrosion–
controlled process and metallic nature of pure zirconium.
• It selectively etches the zirconia and creates micro-retentions on the surface by modifying the grain boundaries through removal of the less arranged atoms .
![Page 50: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/50.jpg)
• Hot acid etching with combinations of highly corrosive acids (HNO3, H2SO4, and HF) improves both initial bond strengths and durability .
• Sulfuric acid in solution with hydrogen peroxide (H2O2) (Piranha solution) appeared to have a positive effect on the bonding of zirconia with resin cements .
![Page 51: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/51.jpg)
(2)Abrasion with diamond (or other) rotary instruments (can cause microcracks)
(3)Coatings of low melting temperature porcelain micro pearls.
![Page 52: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/52.jpg)
(4)Selective infiltration etching (SIE)•SIE uses a heat-induced maturation
process to pre-stress surface grain boundaries in ZrO2 to allow infiltration of boundaries(1) with molten glass.
•The glass is then etched out (2)using HF, creating a network of inter-granular porosity that allows nano-mechanical interlocking of resin cement .
![Page 53: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/53.jpg)
SIE of Zirconia
![Page 54: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/54.jpg)
(5)Fusion sputtering : • Fusion sputtering is a new technique used to
create rough zirconia surface by spraying an air-water jet carrying microscopic zirconia particles onto unsintered zirconia frameworks.
• Upon impact with the surface, the particles achieve good contact and adherence.
• After sintering, these particles become structurally fused with the underlying framework and create undercuts suitable for establishing mechanical retention with resin adhesives.
![Page 55: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/55.jpg)
(6) Air abrasion with alumina (Mechnical)
low pressure particle abrasion (LPPA)(7)Application of different laser types(8) Plasma oxyfluoride This process presents a method to
chemically modify zirconia by creating thin oxyfluoride conversion layer on its surface that is receptive to organosilane attachment .
![Page 56: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/56.jpg)
(9) Tribiochemical silica coating
(1o) Plasma spray (siloxane coating)
![Page 57: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/57.jpg)
Conclusion in bonding to zirconia•The use of phosphate monomer luting
cements on freshly air-abraded zirconia is the simplest and most effective way for zirconia cementation procedure.
•These resin cements have shown good mechanical retention.
![Page 58: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/58.jpg)
MDP resin cements• MDP-containing resin
cement continues to be a popular choice for luting ZrO2 prosthetics in clinical applications due to its low failure rate and loss of retention.
• The hydroxyl groups of the passive zirconia surface bond to the phosphate ester group of the MDP.
• 10-Methacryloyloxydecyl dihydrogen phosphate
![Page 59: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/59.jpg)
![Page 60: Zirconia overview](https://reader033.vdocuments.net/reader033/viewer/2022061610/58d0f2e51a28abc00b8b47e7/html5/thumbnails/60.jpg)
References 1. A D Bonna et.alZirconia as a dental
biomaterial.Materials.2015;8:4978-912. Z Khamverdi et al.Zirconia :An up- to-date literature
review.DJH.2012;4:1-153. MN Aboushelib et al.Bonding to Zirconia(A systematic
review).Open Access Journal of Dental Sciences.20164. K Nakamura et al.Zirconia as a Dental Implant
AbutmentMaterial: A Systematic Review.Int. J Prosth.2010
5. R Pandero et al .Zirconia in fixed prosthesis. A literature review . Journal Clin Exp Dent.2014;6:66-73
6. Philips’ science of dental materials.12th edition.